CN104194115A - Antioxygenic and adhesive rheological agent cable accessory material - Google Patents
Antioxygenic and adhesive rheological agent cable accessory material Download PDFInfo
- Publication number
- CN104194115A CN104194115A CN201410363624.XA CN201410363624A CN104194115A CN 104194115 A CN104194115 A CN 104194115A CN 201410363624 A CN201410363624 A CN 201410363624A CN 104194115 A CN104194115 A CN 104194115A
- Authority
- CN
- China
- Prior art keywords
- parts
- density polyethylene
- cable accessory
- raw material
- rheological agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antioxygenic and adhesive rheological agent cable accessory material which is prepared from the following raw materials in parts by weight: 60 to 80 parts of low density polyethylene, 30 to 40 parts of high density polyethylene, 2 to 3 parts of 2-methylimidazole, 1 to 2 parts of lithium metasilicate, 10 to 12 parts of precipitated silica, 0.8 to 1.3 parts of sodium pyrophosphate, 5 to 7 parts of polypropylene glycol adipate, 3 to 5 parts of quartz glass fibers, 10 to 14 parts of triethylene glycol di-2-ethylhexoate, 1 to 2 parts of anti-aging agent 4010, 1 to 2 parts of blocky calcareous material, 2 to 4 parts of polyvinyl alcohol, 0.6 to 1 part of fenbendazole and 6 to 10 parts of composite fillers. The cable accessory material disclosed by the invention is strong in aging resistance, stable in mechanical performance, good in fire resistance and high-low temperature resistance and easy to produce, and can ensure that the investment of production equipment is saved so as to realize efficient production. The cable accessory material is stable in performance and high in quality, and can be used for performing strong and durable protection on a cable accessory.
Description
Technical field
The present invention relates generally to cable accessory field, relates in particular to a kind of antioxygen adhesion rheological agent cable annex material.
Background technology
Along with developing rapidly of economic construction; improving constantly of people's standard of living; the fast development of all kinds of Infrastructure in town and country; increasing to all kinds of cable accessory demands; therefore the quality that improves constantly cable accessory seems very important; and improve constantly the performance of cable accessory sheath material, and improve the performances such as anticorrosion, wear-resisting, anti-aging, can guarantee the protection effect to cable accessory.
Summary of the invention
The object of the invention is just to provide a kind of antioxygen adhesion rheological agent cable annex material.
The present invention is achieved by the following technical solutions:
A kind of antioxygen adhesion rheological agent cable annex material, it is made up of the raw material of following weight parts:
Low Density Polyethylene 60-80, high density polyethylene(HDPE) 30-40, glyoxal ethyline 2-3, lithium silicate 1-2, precipitated silica 10-12, trisodium phosphate 0.8-1.3, hexanodioic acid propanediol polyester 5-7, quartz glass fibre 3-5, triglycol two 2-ethylhexoate 10-14, antioxidant 4010 1-2,10000 years grey 1-2, polyvinyl alcohol 2-4, fenbendazole 0.6-1, compounded mix 6-10;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 20-30, metallocene linear-low density polyethylene 10-16, yttrium oxide 2-3, tri (propylene glycol) diacrylate 2-3, Stockholm tar 1-2, methylisothiazolinone 1-2, flue dust 2-3;
Above-mentioned methylisothiazolinone is joined in 4-6 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, at 80-110 DEG C, insulated and stirred 20-30 minute, adds flue dust, mixes, ball milling, add the each raw material of residue, 60-100 rev/min of dispersed with stirring 4-7 minute, dries, grind, be described compounded mix.
A preparation method for antioxygen adhesion rheological agent cable annex material, comprises the following steps:
Above-mentioned quartz glass fibre, precipitated silica, 10000 years ashes, compounded mixs are mixed with hexanodioic acid propanediol polyester, at 80-100 DEG C, be uniformly mixed 3-5 minute, add the each raw material of residue, melt extrude, cooling, granulation, obtains described cable accessory material.
Advantage of the present invention is:
Cable accessory material resistance to deterioration of the present invention is strong, stable mechanical performance, and flame retardant properties is good, and resistant of high or low temperature is good, is easy to produce, and can save production unit and drop into, and is beneficial to efficiency and produces, and product performance are stable, and quality is high, strong and lasting to the protectiveness of cable accessory.
Embodiment
Embodiment 1
A kind of antioxygen adhesion rheological agent cable annex material, it by following weight parts (kilogram) raw material form:
Low Density Polyethylene 60, high density polyethylene(HDPE) 40, glyoxal ethyline 3, lithium silicate 1, precipitated silica 12, trisodium phosphate 1.3, hexanodioic acid propanediol polyester 5, quartz glass fibre 5, triglycol two 2-ethylhexoates 14, antioxidant 4010 2,10000 years ashes 2, polyvinyl alcohol 2, fenbendazole 0.6, compounded mix 10;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 30, metallocene linear-low density polyethylene 16, yttrium oxide 3, tri (propylene glycol) diacrylate 2, Stockholm tar 2, methylisothiazolinone 1, flue dust 3;
Above-mentioned methylisothiazolinone is joined in 6 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, at 110 DEG C, insulated and stirred 30 minutes, adds flue dust, mixes, ball milling, add the each raw material of residue, 100 revs/min of dispersed with stirring 7 minutes, dry, grind, be described compounded mix.
A preparation method for antioxygen adhesion rheological agent cable annex material, comprises the following steps:
Above-mentioned quartz glass fibre, precipitated silica, 10000 years ashes, compounded mixs are mixed with hexanodioic acid propanediol polyester, be uniformly mixed 5 minutes at 100 DEG C, add the each raw material of residue, melt extrude, cooling, granulation, obtains described cable accessory material.
Tensile strength: >=15MPa;
Elongation at break: >=260%.
Claims (2)
1. an antioxygen adhesion rheological agent cable annex material, is characterized in that what it was made up of the raw material of following weight parts:
Low Density Polyethylene 60-80, high density polyethylene(HDPE) 30-40, glyoxal ethyline 2-3, lithium silicate 1-2, precipitated silica 10-12, trisodium phosphate 0.8-1.3, hexanodioic acid propanediol polyester 5-7, quartz glass fibre 3-5, triglycol two 2-ethylhexoate 10-14, antioxidant 4010 1-2,10000 years grey 1-2, polyvinyl alcohol 2-4, fenbendazole 0.6-1, compounded mix 6-10;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 20-30, metallocene linear-low density polyethylene 10-16, yttrium oxide 2-3, tri (propylene glycol) diacrylate 2-3, Stockholm tar 1-2, methylisothiazolinone 1-2, flue dust 2-3;
Above-mentioned methylisothiazolinone is joined in 4-6 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, at 80-110 DEG C, insulated and stirred 20-30 minute, adds flue dust, mixes, ball milling, add the each raw material of residue, 60-100 rev/min of dispersed with stirring 4-7 minute, dries, grind, be described compounded mix.
2. a preparation method for antioxygen adhesion rheological agent cable annex material as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned quartz glass fibre, precipitated silica, 10000 years ashes, compounded mixs are mixed with hexanodioic acid propanediol polyester, at 80-100 DEG C, be uniformly mixed 3-5 minute, add the each raw material of residue, melt extrude, cooling, granulation, obtains described cable accessory material.