CN105061932A - Blended easily torn electric wire cable material - Google Patents
Blended easily torn electric wire cable material Download PDFInfo
- Publication number
- CN105061932A CN105061932A CN201510473734.6A CN201510473734A CN105061932A CN 105061932 A CN105061932 A CN 105061932A CN 201510473734 A CN201510473734 A CN 201510473734A CN 105061932 A CN105061932 A CN 105061932A
- Authority
- CN
- China
- Prior art keywords
- parts
- wire cable
- cable material
- add
- electric wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a blended easily torn electric wire cable material. The blended easily torn electric wire cable material comprises, by weight, 70-76 parts of polyvinyl chloride, 15-20 parts of polypropylene, 1-2 parts of 2,2-dibromo-3-nitrilopropionamide, 7-10 parts of expanded perlite, 2-3 parts of glass fibers, 2-3 parts of zinc methacrylate, 1-2 parts of carboxymethylcellulose, 4-6 parts of brucite, 1-2 parts of benzotriazole, 4-6 parts of epoxidized castor oil, 2-3 parts of polyimide, 8-10 parts of butyl benzyl phthalate, 2-3 parts of locust bean gum and 10-13 parts of a composite filling material. The blended easily torn electric wire cable material has good transverse toughness, can be torn along one direction when the electric wire cable material is torn along a vertical direction, does not produce deviation, does not crack easily and has good safety.
Description
Technical field
The present invention relates generally to field of cables, particularly relates to a kind of blendedly easily to tear wire cable material.
Background technology
Along with developing rapidly of economic construction; improving constantly of people's standard of living; the fast development of all kinds of Infrastructure in town and country; increasing to all kinds of cabling requirements amount; therefore the quality improving constantly cable seems very important; and improve constantly the performance of cable jacket material, improve the performances such as anticorrosion, wear-resisting, anti-aging, the protected effect to cable can be guaranteed.
Summary of the invention
The object of the invention is just to provide a kind of blendedly easily tears wire cable material.
The present invention is achieved by the following technical solutions:
One is blended easily tears wire cable material, and it is made up of the raw material of following weight parts:
Polyvinyl chloride 70-76, polypropylene 15-20,2,2-bis-bromo-3-nitrilo propionic acid amide 1-2, pearlstone 7-10, glass fibre 2-3, zinc methacrylate 2-3, carboxymethyl cellulose 1-2, brucite 4-6, benzotriazole 1-2, epoxy castor oil 4-6, polyimide 2-3, butyl benzyl phthalate 8-10, Viscogum BE 2-3, compounded mix 10-13;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 20-30, metallocene linear-low density polyethylene 10-16, yttrium oxide 2-3, tri (propylene glycol) diacrylate 2-3, Stockholm tar 1-2, methylisothiazolinone 1-2, flue dust 2-3;
Above-mentioned methylisothiazolinone is joined in 4-6 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, insulated and stirred 20-30 minute at 80-110 DEG C, adds flue dust, mix, ball milling, adds each raw material of residue, 60-100 rev/min of dispersed with stirring 4-7 minute, dry, grinding, be described compounded mix.
The blended preparation method easily tearing wire cable material, comprises the following steps:
By above-mentioned polypropylene, pearlstone, brucite mixing, add carboxymethyl cellulose after stirring, then add the water of above-mentioned compound weight 4-6%, at 50-60 DEG C, be stirred to water do, add each raw material of residue, melt extrude, cooling, granulation, obtain described CABLE MATERIALS.
Advantage of the present invention is:
CABLE MATERIALS transverse toughness of the present invention is good, tears, do not depart from when longitudinal direction tears according to a direction, and be not easy cracking, security is good.
Embodiment
Embodiment 1
One is blended easily tears wire cable material, and it is made up of the raw material of following weight parts (kilogram):
Polyvinyl chloride 76, the bromo-3-nitrilo propionic acid amide 2 of polypropylene 20,2,2-bis-, pearlstone 10, glass fibre 2, zinc methacrylate 3, carboxymethyl cellulose 2, brucite 6, benzotriazole 1, epoxy castor oil 6, polyimide 2, butyl benzyl phthalate 10, Viscogum BE 3, compounded mix 13;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 20, metallocene linear-low density polyethylene 16, yttrium oxide 2, tri (propylene glycol) diacrylate 3, Stockholm tar 2, methylisothiazolinone 2, flue dust 2;
Above-mentioned methylisothiazolinone is joined in 4 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, at 110 DEG C, insulated and stirred 30 minutes, adds flue dust, mixes, ball milling, add each raw material of residue, 100 revs/min of dispersed with stirring 7 minutes, dry, grinding, is described compounded mix.
The blended preparation method easily tearing wire cable material, comprises the following steps:
By above-mentioned polypropylene, pearlstone, brucite mixing, add carboxymethyl cellulose after stirring, then add the water of above-mentioned compound weight 4%, at 60 DEG C, be stirred to water do, add each raw material of residue, melt extrude, cooling, granulation, obtain described CABLE MATERIALS.
Performance test:
Tensile strength: 11.3MPa;
Elongation at break: 251%.
Claims (2)
1. blendedly easily tear a wire cable material, it is characterized in that what it was made up of the raw material of following weight parts:
Polyvinyl chloride 70-76, polypropylene 15-20,2,2-bis-bromo-3-nitrilo propionic acid amide 1-2, pearlstone 7-10, glass fibre 2-3, zinc methacrylate 2-3, carboxymethyl cellulose 1-2, brucite 4-6, benzotriazole 1-2, epoxy castor oil 4-6, polyimide 2-3, butyl benzyl phthalate 8-10, Viscogum BE 2-3, compounded mix 10-13;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 20-30, metallocene linear-low density polyethylene 10-16, yttrium oxide 2-3, tri (propylene glycol) diacrylate 2-3, Stockholm tar 1-2, methylisothiazolinone 1-2, flue dust 2-3;
Above-mentioned methylisothiazolinone is joined in 4-6 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, insulated and stirred 20-30 minute at 80-110 DEG C, adds flue dust, mix, ball milling, adds each raw material of residue, 60-100 rev/min of dispersed with stirring 4-7 minute, dry, grinding, be described compounded mix.
2. the blended preparation method easily tearing wire cable material as claimed in claim 1, is characterized in that comprising the following steps:
By above-mentioned polypropylene, pearlstone, brucite mixing, add carboxymethyl cellulose after stirring, then add the water of above-mentioned compound weight 4-6%, at 50-60 DEG C, be stirred to water do, add each raw material of residue, melt extrude, cooling, granulation, obtain described CABLE MATERIALS.