CN104194199A - Anticorrosion anti-aging cable accessory material - Google Patents
Anticorrosion anti-aging cable accessory material Download PDFInfo
- Publication number
- CN104194199A CN104194199A CN201410367177.5A CN201410367177A CN104194199A CN 104194199 A CN104194199 A CN 104194199A CN 201410367177 A CN201410367177 A CN 201410367177A CN 104194199 A CN104194199 A CN 104194199A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable accessory
- aging
- accessory material
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosion anti-aging cable accessory material. The anticorrosion anti-aging cable accessory material is prepared from the following raw materials in parts by weight: 90-100 parts of polyvinyl chloride, 0.5-1.2 part of isooctyl mercaptoacetate di-n-octyltin, 1-2 parts of 2,6-butylated hydroxytoluene, 1-2 parts of benzotriazole, 0.6-1 part of konjac glucomannan, 6-10 parts of dicapryl phthalate, 8-10 parts of dibutyl maleate, 4-5 parts of drying oil alkyd resin, 3-5 parts of nano titanium dioxide, 1-2 parts of anti-aging agent OD, 10-13 parts of kaoline and 10-14 parts of composite filler. The cable accessory material is high in tensile strength and elongation at break, good in thermal deformation resistance, flame retardance and corrosion resistance, and excellent in comprehensive properties.
Description
Technical field
The present invention relates generally to cable accessory field, relates in particular to a kind of anticorrosion anti-aging cable accessory material.
Background technology
Along with developing rapidly of economic construction; improving constantly of people's standard of living; the fast development of all kinds of Infrastructure in town and country; increasing to all kinds of cable accessory demands; therefore the quality that improves constantly cable accessory seems very important; and improve constantly the performance of cable accessory sheath material, and improve the performances such as anticorrosion, wear-resisting, anti-aging, can guarantee the protection effect to cable accessory.
Summary of the invention
The object of the invention is just to provide a kind of anticorrosion anti-aging cable accessory material.
The present invention is achieved by the following technical solutions:
A kind of anticorrosion anti-aging cable accessory material, it is made up of the raw material of following weight parts:
Polyvinyl chloride 90-100, Imarcaptoacetate dioctyltin 0.5-1.2,2,6 ditertiary butyl p cresol 1-2, benzotriazole 1-2, Rhizoma amorphophalli glucomannan 0.6-1, di-sec-octyl phthalate 6-10, dibutyl maleinate 8-10, drying oil alkyd resin 4-5, nano titanium oxide 3-5, anti-aging agent OD1-2, kaolin 10-13, compounded mix 10-14;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 20-30, metallocene linear-low density polyethylene 10-16, yttrium oxide 2-3, tri (propylene glycol) diacrylate 2-3, Stockholm tar 1-2, methylisothiazolinone 1-2, flue dust 2-3;
Above-mentioned methylisothiazolinone is joined in 4-6 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, at 80-110 DEG C, insulated and stirred 20-30 minute, adds flue dust, mixes, ball milling, add the each raw material of residue, 60-100 rev/min of dispersed with stirring 4-7 minute, dries, grind, be described compounded mix.
A preparation method for anticorrosion anti-aging cable accessory material, comprises the following steps:
Above-mentioned kaolin, drying oil alkyd resin are mixed, at 70-90 DEG C, be uniformly mixed 3-5 minute, add nano titanium oxide, 100-200 rev/min of dispersed with stirring 4-6 minute, adds the each raw material of residue to mix, and melt extrudes, cooling, granulation, obtain described cable accessory material.
Advantage of the present invention is:
Cable accessory material tensile strength of the present invention, elongation at break are high, thermal deformation resistant, flame retardant resistance, good corrosion resistance, and over-all properties is superior.
Embodiment
Embodiment 1
A kind of anticorrosion anti-aging cable accessory material, it by following weight parts (kilogram) raw material form:
Polyvinyl chloride 100, Imarcaptoacetate dioctyltin 1.2,2,6 ditertiary butyl p cresol 1, benzotriazole 2, Rhizoma amorphophalli glucomannan 0.6, di-sec-octyl phthalate 10, dibutyl maleinate 10, drying oil alkyd resin 4, nano titanium oxide 3, anti-aging agent OD2, kaolin 13, compounded mix 14;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 30, metallocene linear-low density polyethylene 16, yttrium oxide 2, tri (propylene glycol) diacrylate 2, Stockholm tar 2, methylisothiazolinone 2, flue dust 2;
Above-mentioned methylisothiazolinone is joined in 6 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, at 110 DEG C, insulated and stirred 20 minutes, adds flue dust, mix, ball milling, adds the each raw material of residue, 100 revs/min of dispersed with stirring 7 minutes, dry, granulation, particle diameter is 6 μ m, is described compounded mix.
A preparation method for anticorrosion anti-aging cable accessory material, comprises the following steps:
Above-mentioned kaolin, drying oil alkyd resin are mixed, be uniformly mixed 3 minutes at 90 DEG C, add nano titanium oxide, 200 revs/min of dispersed with stirring 6 minutes, add the each raw material of residue to mix, and melt extrude, and cooling, granulation, obtains described cable accessory material.
Performance test:
Tensile strength: >=15 MPa;
Elongation at break: >=300%;
Thermal distortion :≤40%;
Heat aging performance (100 DEG C, 170h): tensile strength velocity of variation-5.9%, elongation at break velocity of variation-6.4%.
Claims (2)
1. an anticorrosion anti-aging cable accessory material, is characterized in that what it was made up of the raw material of following weight parts:
Polyvinyl chloride 90-100, Imarcaptoacetate dioctyltin 0.5-1.2,2,6 ditertiary butyl p cresol 1-2, benzotriazole 1-2, Rhizoma amorphophalli glucomannan 0.6-1, di-sec-octyl phthalate 6-10, dibutyl maleinate 8-10, drying oil alkyd resin 4-5, nano titanium oxide 3-5, anti-aging agent OD1-2, kaolin 10-13, compounded mix 10-14;
Described compounded mix is made up of the raw material of following weight parts:
Montmorillonite powder 20-30, metallocene linear-low density polyethylene 10-16, yttrium oxide 2-3, tri (propylene glycol) diacrylate 2-3, Stockholm tar 1-2, methylisothiazolinone 1-2, flue dust 2-3;
Above-mentioned methylisothiazolinone is joined in 4-6 times of water, add montmorillonite powder, metallocene linear-low density polyethylene, yttrium oxide, at 80-110 DEG C, insulated and stirred 20-30 minute, adds flue dust, mixes, ball milling, add the each raw material of residue, 60-100 rev/min of dispersed with stirring 4-7 minute, dries, grind, be described compounded mix.
2. a preparation method for anticorrosion anti-aging cable accessory material as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned kaolin, drying oil alkyd resin are mixed, at 70-90 DEG C, be uniformly mixed 3-5 minute, add nano titanium oxide, 100-200 rev/min of dispersed with stirring 4-6 minute, adds the each raw material of residue to mix, and melt extrudes, cooling, granulation, obtain described cable accessory material.