CN1673303A - Composite waterproof bridge paint and its prepn process - Google Patents
Composite waterproof bridge paint and its prepn process Download PDFInfo
- Publication number
- CN1673303A CN1673303A CN 200410029771 CN200410029771A CN1673303A CN 1673303 A CN1673303 A CN 1673303A CN 200410029771 CN200410029771 CN 200410029771 CN 200410029771 A CN200410029771 A CN 200410029771A CN 1673303 A CN1673303 A CN 1673303A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- kilograms
- bridge floor
- waterproofing paint
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is composite waterproof bridge paint and its preparation process. The paint contains asphalt, water, stuffing and emulsifier as well as two or more of butadiene benzene emulsion, acrylic emulsion, styrene acrylic emulsion and neoprene emulsion. The paint consists of asphalt 20-40 weight portions, butadiene benzene emulsion 0-10 weight portions, neoprene emulsion 0-20 weight portions, styrene acrylic emulsion 0-10 weight portions, acrylic emulsion 0-10 weight portions, water 40-50 weight portions, stuffing 1-3 weight portions, penetrating agent 3-5 weight portions, and stabilizer 1-3 weight portions, and is compounded through certain technological process. The paint has high shearing resistance, great adhesion strength and fast coating drying speed.
Description
Technical field that the present invention belongs to
The invention belongs to building class waterproof paint field, it is the strong compound bridge floor waterproofing paint of a kind of perviousness and cohesiveness.
The prior art background
Cement concrete material is a water-resistant material, and wet condition is that the cement concrete material early strength forms external conditions.But a host of facts prove, do not take the bad bridge of waterproof measure and waterproof system performance before reaching working life far away, and the damage by water that will take place in various degree is bad.Moisture is penetrated in the concrete slit by the bad floor system of waterproof, and various diseases take place, as steel bar corrosion, concrete alkali aggregate reaction, lime blooming etc.
For solving the bridge seepage problem, the technical measures that adopt are that various types of bridge surface waterproof layers are set at present, and concrete and water are kept apart, and make it not possess the condition that reacts.Waterproof layer is except having waterproof action, and another effect is exactly for a good bonding transition layer is provided between decking and the oil mat, and two-layer one-tenth is as a whole about making.
At present, the defective of a maximum of bridge floor waterproofing paint is coating and bilevel cohesive force deficiency, the bonding force of interlayer is poor because if bituminous concrete and bridge deck concrete are mated formation, and is then totally unfavorable to the weather resistance of bridge floor, the serious destruction that must quicken bridge deck pavement.
The purpose and the content of invention
The object of the present invention is to provide the bridge floor waterproofing paint that a kind of slip resistance is big and cohesiveness is strong, make the cement concrete bridge deck plate become as a whole with bituminous concrete.
The bridge floor waterproofing paint that another object of the present invention is to provide, drying and forming-film is fast, as early as possible open to traffic.
It is as follows to reach above-mentioned purpose technical scheme of the present invention:
Waterproof paint of the present invention is characterized in that its recipe ingredient (meter by weight) contains:
0～10 part of 20～40 parts of styrene-butadiene latex of pitch
0～10 part of 0～20 part of propyl benzene emulsion of polychloroprene latex
3～5 parts of 0～10 part of defoamers of acrylic acid emulsion
40～50 parts in 1～3 part of water of emulsifying agent
1～5 part of 1～3 part of infiltration accelerating agent of filler
1～3 part of stablizer
Used emulsifying agent is a kind of quaternary amine emulsifying agent that contains hydroxyl, and filler can be one or more in light calcium carbonate, talcum powder, the sepiolite, and infiltration accelerating agent contains naphthenic oil.Compound method is to get 90
#Petroleum pitch, water, styrene-butadiene emulsion, propyl benzene emulsion, emulsifying agent, defoamer, stablizer, infiltration accelerating agent, that filler carries out mixing manufacture is as follows:
(1) pitch is heated to 100～180 ℃;
(2) add infiltration accelerating agent and pitch blend heating;
(3) the latex pre-treatment is cation emulsion, adds latex cylinder;
(4) stablizer, defoamer, filler are added in the entry, and be preheating to 50～90 ℃;
The pitch and the aqueous solution, latex carry out uniform mixing by colloidal mill in the lump, and mixed emulsified bitumen injects finished cylinder.
The salient features test index sees the following form:
| Index name | Index |
| Outward appearance | Stirring the back is black or blue brown liquid, no obvious particle on the stirring rod |
| Solid content | ＞50% |
| Extensibility (non-processor) | 11mm |
| Low temperature flexibility | At-20 ± 2 ℃, around diameter 10mm mandrel rod half cycle, film does not have check crack, peeling phenomenon |
| Thermotolerance | At 160 ℃, test specimen is vertically placed, and constant temperature 6h does not have trickling, comes off and the downslide phenomenon. |
| Cohesive strength | At 20 ± 2 ℃, with ten from interior extrapolation side cohesive strength 〉=0.4Mpa. |
| Slip resistance | At 20 ± 2 ℃, slip resistance 〉=0.2Mpa. |
| Acid resistance | In 1% sulphuric acid soln, soak 15d, do not have peel off, foaming, layering, phenomenon such as wrinkling. |
| Alkali resistance | Under 20 ± 2 ℃, in saturated calcium hydroxide aqueous solution, soak 15d, do not have peel off, foaming, layering, phenomenon such as wrinkling. |
| Drying property | Surface drying 1h5min does solid work 3h20min |
| Watertightness | Under 20 ± 2 ℃, moving hydraulic pressure 〉=0.1Mpa, film is waterproof in the 30min. |
The advantage of invention
The invention has the advantages that: (1) safety non-toxic, pollution-free; (2) easy to operate, dried coating film is fast, and the engineering time shortens; (3) film alkali resistance, water tolerance, good permeability can be used in the cement concrete basic unit of finish-drying not; (4) cheap, slip resistance and cohesive strength height; (5) high temperature does not trickle, not embrittlement of low temperature.
Embodiment
Embodiment 1:
Get 500 kilograms in 90# petroleum pitch, 340 kilograms in water, 80 kilograms of styrene-butadiene latexes, 80 kilograms of propyl benzene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of light calcium carbonates, making method is as follows:
(1) pitch is heated to 100 ℃;
(2) add infiltration accelerating agent and pitch blend and be heated to 140 ℃;
(3) the latex pre-treatment is cation emulsion, adds latex cylinder;
(4) stablizer, defoamer, filler are added in the entry, and be preheating to 90 ℃;
The pitch and the aqueous solution, latex carry out uniform mixing by colloidal mill in the lump, and mixed emulsified bitumen injects finished cylinder.
Embodiment 2:
Get 500 kilograms in 90# petroleum pitch, 360 kilograms in water, 60 kilograms of acrylic latexs, 80 kilograms of propyl benzene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of talcum powder.Making method is as follows:
(1) pitch is heated to 160 ℃;
(2) add infiltration accelerating agent and pitch blend;
(3) the latex pre-treatment is cation emulsion, adds latex cylinder;
(4) stablizer, defoamer, filler are added in the entry, and be preheating to 50 ℃;
The pitch and the aqueous solution, latex carry out uniform mixing by colloidal mill in the lump, and mixed emulsified bitumen injects finished cylinder.
Embodiment 3:
Get 500 kilograms in 90# petroleum pitch, 360 kilograms in water, 60 kilograms of acrylic latexs, 80 kilograms of neoprene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of sepiolites, making method is as follows:
(1) pitch is heated to 180 ℃;
(2) add infiltration accelerating agent and pitch blend;
(3) the latex pre-treatment is cation emulsion, adds latex cylinder;
(4) stablizer, defoamer, filler are added in the entry, and be preheating to 50 ℃;
The pitch and the aqueous solution, latex carry out uniform mixing by colloidal mill in the lump, and mixed emulsified bitumen injects finished cylinder.
Embodiment 4:
Get 500 kilograms in 90# petroleum pitch, 360 kilograms in water, 60 kilograms of styrene-butadiene latexes, 80 kilograms of neoprene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of light calcium carbonates carry out being mixed as embodiment 1 same technology and make.
Embodiment 5:
Get 500 kilograms in 90# petroleum pitch, 360 kilograms in water, 60 kilograms of acrylic latexs, 80 kilograms of neoprene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of sepiolites carry out being mixed as embodiment 2 same technologies and make.
Embodiment 6:
Get 500 kilograms in 90# petroleum pitch, 340 kilograms in water, 110 kilograms of styrene-butadiene latexes, 50 kilograms of propyl benzene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of light calcium carbonates carry out being mixed as embodiment 3 same technologies and make.
Embodiment 7:
Get 400 kilograms in 90# petroleum pitch, 440 kilograms in water, 110 kilograms of styrene-butadiene latexes, 50 kilograms of propyl benzene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of light calcium carbonates carry out being mixed as embodiment 1 same technology and make.
Embodiment 8:
Get 400 kilograms in 90# petroleum pitch, 400 kilograms in water, 100 kilograms of acrylic latexs, 100 kilograms of propyl benzene emulsions,, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of light calcium carbonates carry out being mixed as embodiment 2 same technologies and make.
Embodiment 9:
Get 450 kilograms in 90# petroleum pitch, 400 kilograms in water, 70 kilograms of styrene-butadiene latexes, 80 kilograms of neoprene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of sepiolites carry out being mixed as embodiment 1 same technology and make.
Embodiment 10:
Get 450 kilograms in 90# petroleum pitch, 390 kilograms in water, 80 kilograms of acrylic latexs, 80 kilograms of neoprene emulsions, 20 kilograms of emulsifying agents, 30 kilograms of defoamers, 10 kilograms of stablizers, 20 kilograms of infiltration accelerating agents, 10 kilograms of talcum powder carry out being mixed as embodiment 3 same technologies and make.
Utilizing present embodiment gained coating is that a kind of slip resistance height, cohesive strength are big, the bridge floor waterproofing paint that film forming is fast.
Claims (10)
1. compound bridge floor waterproofing paint, contain pitch, water, filler and emulsifying agent, it is characterized in that also containing two or more emulsions in styrene-butadiene emulsion, ACRYLIC EMULSION, propyl benzene emulsion, the neoprene emulsion, the recipe ingredient of this bridge floor waterproofing paint (by weight) comprises:
0～10 part of 20～40 parts of styrene-butadiene emulsion of pitch
0～10 part of 0～20 part of propyl benzene emulsion of neoprene emulsion
3～5 parts of 0～10 part of defoamers of ACRYLIC EMULSION
40～50 parts in 1～3 part of water of emulsifying agent
1～5 part of 1～3 part of infiltration accelerating agent of filler
1～3 part of stablizer
2. bridge floor waterproofing paint according to claim 1 is characterized in that, described emulsifying agent is a kind of quaternary amine emulsifying agent that contains hydroxyl.
3. bridge floor waterproofing paint according to claim 1 is characterized in that, described filler can be one or more in light calcium carbonate, talcum powder, the sepiolite.
4. bridge floor waterproofing paint according to claim 1 is characterized in that used infiltration accelerating agent contains naphthenic oil.
5. the compound method of employing such as the described bridge floor waterproofing paint of claim 1～4 is characterized in that, gets 90
#Petroleum pitch, water, styrene-butadiene emulsion, propyl benzene emulsion, emulsifying agent, defoamer, stablizer, infiltration accelerating agent, that filler carries out mixing manufacture is as follows:
(1) pitch is heated to 100～180 ℃;
(2) add infiltration accelerating agent and pitch blend heating;
(3) the emulsion pre-treatment is cation emulsion, adds latex cylinder;
(4) stablizer, defoamer, filler are added in the entry, and be preheating to 50～90 ℃;
The pitch and the aqueous solution, latex carry out uniform mixing by colloidal mill in the lump, and mixed emulsified bitumen injects finished cylinder.
6. bridge floor waterproofing paint making method according to claim 5 is characterized in that, it is in 140 ℃ of pitches that infiltration accelerating agent is joined temperature.
7. bridge floor waterproofing paint according to claim 5 is characterized in that, styrene-butadiene emulsion, ACRYLIC EMULSION, propyl benzene emulsion, neoprene emulsion is carried out pre-treatment be cation emulsion.
8. bridge floor waterproofing paint making method according to claim 5 is characterized in that asphalt temperature is 100 ℃, and the water temp that contains stablizer, defoamer, filler is 90 ℃.
9. bridge floor waterproofing paint making method according to claim 5 is characterized in that asphalt temperature is 160 ℃, and the water temp that contains stablizer, defoamer, filler is 50 ℃.
10. bridge floor waterproofing paint making method according to claim 5 is characterized in that asphalt temperature is 180 ℃, and the water temp that contains stablizer, defoamer, filler is 50 ℃.