CN104031515A - High-gloss anti-corrosive automotive paint - Google Patents
High-gloss anti-corrosive automotive paint Download PDFInfo
- Publication number
- CN104031515A CN104031515A CN201410200546.1A CN201410200546A CN104031515A CN 104031515 A CN104031515 A CN 104031515A CN 201410200546 A CN201410200546 A CN 201410200546A CN 104031515 A CN104031515 A CN 104031515A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant
- paint
- high light
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed high-gloss anti-corrosive automotive paint is prepared from the following raw materials in parts by weight: 20-30 parts of aqueous methyl methacrylate resin, 15-18 parts of epoxy resin, 0.5-1 part of silicone, 5-10 parts of polyvinylidene chloride, 3-5 parts of butyl acetate, 10-15 parts of deionized water, 8-12 parts of an auxiliary agent, 20-25 parts of titanium dioxide, and 1-3 parts of active copper. The beneficial effects comprise that the paint is scientific and reasonable in raw material ratio, good in adhesive force and not easy to fall off, capable of forming a bright and plump paint film, resistant to sunshine irradiation, durable in color maintenance, resistant to weather ageing, resistant to oil, capable of delaying corrosion caused by environment conditions, long in service life, safe and environment-friendly.
Description
Technical field
The present invention relates to a kind of automobile finish, relate in particular to the anticorrosion automobile finish of a kind of high light.
Background technology
At present, automobile industry of China is mostly being used solvent borne automobile lacker, and organic solvent in solvent borne automobile finish, contain a large amount of to human body and the harmful material of environment, in production and vehicle spray painting process, have a large amount of organic solvent volatilizations, cause atmospheric pollution and potential safety hazard, all caused harm to personnel and ecotope.Traditional paint ubiquity smell weighs, easily comes off, perishable, the problems such as inadequate environmental protection, can not meet the service requirements of human consumer to paint, therefore, need to improve the formula of original paint, the practicality and the weather resistance that increase paint, reduce its harm to environment and human body, and can adapt to various environment for use conditions.
Therefore,, for addressing the above problem, spy provides a kind of new technical scheme to satisfy the demands.
Summary of the invention
The invention provides the anticorrosion automobile finish of a kind of high light.
The technical solution used in the present invention is:
The anticorrosion automobile finish of a kind of high light, made by the raw material of following weight part:
Aqueous methacrylic acid methyl esters resin 20-30 part;
Epoxy resin 15-18 part;
Silicone 0.5-1 part;
Polyvinylidene dichloride 5-10 part;
Butylacetate 3-5 part;
Deionized water 10-15 part;
Auxiliary agent 8-12 part;
Titanium dioxide 20-25 part;
Active copper 1-3 part.
Described auxiliary agent comprises polytetrafluoroethylene powder, talcum powder and sodium laurate, and described tetrafluoroethylene powder, talcum powder and sodium laurate mass ratio are 1:0.5:1.
Also be added with the pigment of 5-8 mass parts.
The invention has the beneficial effects as follows: proportioning raw materials is scientific and reasonable, sticking power is good, difficult drop-off, and paint film light is full, and resistance to terrestrial solar radiation is protected look lasting, also weather-proof aging, and oil resistant delays envrionment conditions corrosion, long service life, safety and environmental protection.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only, for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment 1
The anticorrosion automobile finish of a kind of high light, made by the raw material of following weight part:
20 parts of aqueous methacrylic acid methyl esters resins;
15 parts of epoxy resin;
0.5 part of silicone;
5 parts of polyvinylidene dichloride;
3 parts of butylacetates;
10 parts of deionized waters;
8 parts of auxiliary agents;
20 parts of titanium dioxide;
1 part of active copper;
5 parts of pigment.
Auxiliary agent comprises polytetrafluoroethylene powder, the talcum powder of 1.6 mass parts and the sodium laurate of 3.2 mass parts of 3.2 mass parts.
Embodiment 2
The anticorrosion automobile finish of a kind of high light, made by the raw material of following weight part:
25 parts of aqueous methacrylic acid methyl esters resins;
16 parts of epoxy resin;
0.7 part of silicone;
7 parts of polyvinylidene dichloride;
4 parts of butylacetates;
12 parts of deionized waters;
10 parts of auxiliary agents;
22 parts of titanium dioxide;
2 parts of active copper.
Auxiliary agent comprises polytetrafluoroethylene powder, the talcum powder of 2 mass parts and the sodium laurate of 4 mass parts of 4 mass parts.
Embodiment 3
The anticorrosion automobile finish of a kind of high light, made by the raw material of following weight part:
30 parts of aqueous methacrylic acid methyl esters resins;
18 parts of epoxy resin;
1 part of silicone;
10 parts of polyvinylidene dichloride;
5 parts of butylacetates;
15 parts of deionized waters;
12 parts of auxiliary agents;
25 parts of titanium dioxide;
3 parts of active copper;
8 parts of pigment.
Auxiliary agent comprises polytetrafluoroethylene powder, the talcum powder of 2.4 mass parts and the sodium laurate of 4.8 mass parts of 4.8 mass parts, and tetrafluoroethylene powder, talcum powder and sodium laurate mass ratio are 1:0.5:1.
The invention has the beneficial effects as follows: proportioning raw materials is scientific and reasonable, sticking power is good, difficult drop-off, and paint film light is full, and resistance to terrestrial solar radiation is protected look lasting, also weather-proof aging, and oil resistant delays envrionment conditions corrosion, long service life, safety and environmental protection.
The above, be only preferred embodiment of the present invention, is not the restriction of the present invention being made to any other form, and according to any amendment or equivalent variations that technical spirit of the present invention is done, still belong to the present invention's scope required for protection.
Claims (3)
1. the anticorrosion automobile finish of high light, is characterized in that: the raw material by following weight part is made: aqueous methacrylic acid methyl esters resin 20-30 part;
Epoxy resin 15-18 part;
Silicone 0.5-1 part;
Polyvinylidene dichloride 5-10 part;
Butylacetate 3-5 part;
Deionized water 10-15 part;
Auxiliary agent 8-12 part;
Titanium dioxide 20-25 part;
Active copper 1-3 part.
2. the anticorrosion automobile finish of the high light of one according to claim 1, is characterized in that: described auxiliary agent comprises polytetrafluoroethylene powder, talcum powder and sodium laurate, described tetrafluoroethylene powder, talcum powder and sodium laurate mass ratio are 1:0.5:1.
3. the anticorrosion automobile finish of the high light of one according to claim 1, is characterized in that: the pigment that is also added with 5-8 mass parts.