CN109517415A - A kind of water-based anticorrosive paint - Google Patents
A kind of water-based anticorrosive paint Download PDFInfo
- Publication number
- CN109517415A CN109517415A CN201710837098.XA CN201710837098A CN109517415A CN 109517415 A CN109517415 A CN 109517415A CN 201710837098 A CN201710837098 A CN 201710837098A CN 109517415 A CN109517415 A CN 109517415A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- acrylate monomer
- isooctyl acrylate
- anticorrosive paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of water-based anticorrosive paints, in parts by weight include following component: 50 ~ 70 parts of Isooctyl acrylate monomer, 12-18 parts of water-compatible amino resin, 7 ~ 13 parts of deionized water, 0.2 ~ 0.5 part of defoaming agent, 0.1 ~ 0.3 part of levelling agent, 3 ~ 4 parts of aqueous carbon black, 6 ~ 8 parts of aluminium powder, 1~5 part of mica powder, 3 ~ 6 parts of nano silica, 10-15 parts of Isooctyl acrylate monomer, 6-10 parts of polyurethane resin, 3 ~ 5 parts of vinyltrimethoxysilane, 2 ~ 5 parts of ethylene glycol ethyl ether.The present invention is compared with prior art, and technological progress is significant.By hardness of film with higher after water-based anticorrosive paint film of the invention, gloss and to the contact angle of water, make it possible to using traditional application field in conventional solution-type polyurethane coating.Moreover, because reaction condition is simple, reaction method is mature, and preparation process is simple, is suitable for large-scale production.
Description
Technical field
The invention belongs to paint fields, are related to a kind of coating, and in particular to a kind of water-based anticorrosive paint.
Background technique
The market demand of China's anticorrosive coating and distribution are concentrated mainly on following industry: (1) chemical industry and petrochemical industry row
Industry；(2) railway, highway bridge；(3) electric power and energy industry；(4) ship, container industry (5) lathe and machinery industry.It is molten
It is a variety of that dosage form anticorrosive coating is widely used in marine worker, petrochemical industry, pipeline, industrial antisepsis coating etc. due to its excellent performance
Application field.In recent years, the concern due to world community to environmental protection has substituted solvent based coating with water paint technology
Through the development trend for becoming coating.Compared with solvent based coating, water paint have lower VOC content, few smell,
Many advantages, such as nonflammable, use is safe, can wash by water.Water-based anticorrosive paint is similar with solvent type anticorrosive paint system,
Anticorrosive paint system is made of three-layer coating mostly, wherein finishing coat will include (1) protection inner coating；(2) ultraviolet light is covered, with
Reduce the destruction to coating；(3) it plays role in decoration.It need to be added to reach above-mentioned requirements and have in the manufacturing process of anticorrosive paint
Main film forming substance-water-base resin of good antiseptic property, weather resistance.
Current existing anticorrosive paint finishing coat water-base resin mainly has waterborne acrylic paint, aqueous polyurethane tree
Rouge, aqueous organic fluorine, this resinoid function is relatively simple, only has weather resistance or only has film forming function etc..Limitation
Use of this kind of water-base resin on water-based anticorrosive paint.
Summary of the invention
For above-mentioned technical problem in the prior art, the present invention provides a kind of water-based anticorrosive paint, described is this
It is relatively simple that water-based anticorrosive paint and preparation method thereof will solve anticorrosive paint finishing coat water-base resin function in the prior art,
Only have weather resistance or only there is the technical issues of film forming function.
The specific technical solution of the present invention is as follows:
A kind of water-based anticorrosive paint includes following component in parts by weight: 50 ~ 70 parts of Isooctyl acrylate monomer, aqueous amino
12-18 parts of resin, 7 ~ 13 parts of deionized water, 0.2 ~ 0.5 part of defoaming agent, 0.1 ~ 0.3 part of levelling agent, 3 ~ 4 parts of aqueous carbon black, aluminium powder
6 ~ 8 parts, 1~5 part of mica powder, 3 ~ 6 parts of nano silica, 10-15 parts of Isooctyl acrylate monomer, 6-10 parts of polyurethane resin, second
3 ~ 5 parts of alkenyl trimethoxy silane, 2 ~ 5 parts of ethylene glycol ethyl ether.
Preferably, the water-based anticorrosive paint includes following component in parts by weight: 60 parts of Isooctyl acrylate monomer,
15 parts of water-compatible amino resin, 10 parts of deionized water, 0.3 part of defoaming agent, 0.2 part of levelling agent, 3.5 parts of aqueous carbon black, 7 parts of aluminium powder,
4 parts of mica powder, 5 parts of nano silica, 12 parts of Isooctyl acrylate monomer, 8 parts of polyurethane resin, vinyltrimethoxysilane 4
Part, 3 parts of ethylene glycol ethyl ether.
The present invention is compared with prior art, and technological progress is significant.After water-based anticorrosive paint film of the invention
Hardness of film, gloss and the contact angle to water with higher, make it possible to using the biography in conventional solution-type polyurethane coating
System application field, such as automobile, woodenware, industrial maintenance, plastics and wind electricity blade, the high performance technical field of solar battery.
Moreover, because reaction condition is simple, reaction method is mature, and preparation process is simple, is suitable for large-scale production.
Specific embodiment
The present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
A kind of water-based anticorrosive paint includes following component in parts by weight: 70 parts of Isooctyl acrylate monomer, water-compatible amino resin
12 parts, 13 parts of deionized water, 0.2 part of defoaming agent, 0.3 part of levelling agent, 3 parts of aqueous carbon black, 8 parts of aluminium powder, 1 part of mica powder, nanometer
6 parts of silica, 10 parts of Isooctyl acrylate monomer, 10 parts of polyurethane resin, 3 parts of vinyltrimethoxysilane, ethylene glycol ethyl ether 5
Part.
Embodiment 2
A kind of water-based anticorrosive paint includes following component in parts by weight: 50 parts of Isooctyl acrylate monomer, water-compatible amino resin
18 parts, 7 parts of deionized water, 0.5 part of defoaming agent, 0.1 part of levelling agent, 4 parts of aqueous carbon black, 6 parts of aluminium powder, 5 parts of mica powder, nanometer two
3 parts of silica, 15 parts of Isooctyl acrylate monomer, 6 parts of polyurethane resin, 5 parts of vinyltrimethoxysilane, 2 parts of ethylene glycol ethyl ether.
Embodiment 3
A kind of water-based anticorrosive paint includes following component in parts by weight: 60 parts of Isooctyl acrylate monomer, water-compatible amino resin
15 parts, 10 parts of deionized water, 0.3 part of defoaming agent, 0.2 part of levelling agent, 3.5 parts of aqueous carbon black, 4 parts of mica powder, is received by 7 parts of aluminium powder
5 parts of silica of rice, 12 parts of Isooctyl acrylate monomer, 8 parts of polyurethane resin, 4 parts of vinyltrimethoxysilane, ethylene glycol ethyl ether
3 parts.
Claims (2)
1. a kind of water-based anticorrosive paint, which is characterized in that in parts by weight include following component: Isooctyl acrylate monomer 50 ~
70 parts, 12-18 parts of water-compatible amino resin, 7 ~ 13 parts of deionized water are 0.2 ~ 0.5 part of defoaming agent, 0.1 ~ 0.3 part of levelling agent, aqueous
3 ~ 4 parts of carbon black, 6 ~ 8 parts of aluminium powder, 1~5 part of mica powder, 3 ~ 6 parts of nano silica, 10-15 parts of Isooctyl acrylate monomer, polyurethane
6-10 parts of resin, 3 ~ 5 parts of vinyltrimethoxysilane, 2 ~ 5 parts of ethylene glycol ethyl ether.
2. water-based anticorrosive paint according to claim 1, which is characterized in that in parts by weight include following component:
60 parts of Isooctyl acrylate monomer, 15 parts of water-compatible amino resin, 10 parts of deionized water, 0.3 part of defoaming agent, 0.2 part of levelling agent, aqueous charcoal
Black 3.5 parts, 7 parts of aluminium powder, 4 parts of mica powder, 5 parts of nano silica, 12 parts of Isooctyl acrylate monomer, 8 parts of polyurethane resin, ethylene
4 parts of base trimethoxy silane, 3 parts of ethylene glycol ethyl ether.