CN105086671A - Heat-insulation waterproof coating - Google Patents
Heat-insulation waterproof coating Download PDFInfo
- Publication number
- CN105086671A CN105086671A CN201510473803.3A CN201510473803A CN105086671A CN 105086671 A CN105086671 A CN 105086671A CN 201510473803 A CN201510473803 A CN 201510473803A CN 105086671 A CN105086671 A CN 105086671A
- Authority
- CN
- China
- Prior art keywords
- heat
- waterproof coating
- parts
- add
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses heat-insulation waterproof coating. The heat-insulation waterproof coating is composed of, by weight, 50-60 parts of acetic styrene-acrylic emulsion, 3-4 parts of phosphorous acid bisphenol A ester, 2-3 parts of locust bean gum, 0.1-1 part of cadmium chloride, 0.3-1 part of succinic acid, 0.05-0.1 part of alkylphenol ethoxylates, 1-2 parts of glycerinum, 6-10 parts of sepiolite powder, 10-12 parts of superfine barium sulfate, 0.1-1 part of dipropylene glycol methyl ether, 10-12 parts of bonding promoter and 8-20 parts of deionized water. The heat-insulation waterproof coating has the good heat insulation effect, meanwhile, has good waterproof performance, and is high in bonding performance and weathering resistance and good in protection performance on base materials. In addition, the coating surface of the heat-insulation waterproof coating has the porcelain imitating effect.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of heat-insulating waterproof coating.
Background technology
Waterproof paint has a variety of in the market, and some hardness is higher, easily ftractures along with the strain cracking of basic unit, the easy bulge infiltration had; Some environment protectings are poor, therefore produce the strong waterproof paint of a kind of over-all properties for nation-building and people life improvement have good promoter action.
Summary of the invention
The object of the invention is just to provide a kind of heat-insulating waterproof coating.
The present invention is achieved by the following technical solutions:
A kind of heat-insulating waterproof coating, it is made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 50-60, phosphorous acid dihydroxyphenyl propane ester 3-4, Viscogum BE 2-3, Cadmium chloride fine powder 0.1-1, succinic acid 0.3-1, alkylphenol polyoxyethylene 0.05-0.1, glycerine 1-2, sepiolite powder 6-10, ultra-fine barium sulfate 10-12, dipropylene glycol methyl ether 0.1-1, adhesive aid 10-12, deionized water 8-20;
Described adhesive aid is made up of the raw material of following weight parts:
Vinyl acetate-ethylene copolymerization emulsions 20-35, Viscogum BE 4-6, chitosan 1-2, stearyl methacrylate 3-5, Chinese Angelica Root 1-2, gibbsite 3-4, water are appropriate;
By above-mentioned stearyl methacrylate heat fused, add chitosan, stir, add gibbsite, Chinese Angelica Root, abundant mixing, joined in 6-8 times of water by above-mentioned mixed material, ball milling 1-2 hour, adds Viscogum BE, insulated and stirred reaction 15-20 minute at 60-85 DEG C, add each raw material of residue, abundant ball milling, obtains described adhesive aid.
A preparation method for heat-insulating waterproof coating, comprises the following steps:
By above-mentioned sepiolite powder, ultra-fine barium sulfate, adhesive aid mixing, 200-300 rev/min of dispersed with stirring 3-5 minute, add alkylphenol polyoxyethylene, glycerine, 400-600 rev/min of dispersed with stirring 6-10 minute, add each raw material of residue, high-speed stirring, to mixing, obtains described heat-insulating waterproof coating.
Advantage of the present invention is:
Heat-insulating waterproof coating of the present invention has excellent effect of heat insulation, also has good water resistance concurrently simultaneously, and cohesiveness, weathering resistance are strong, and good to the protectiveness of base material, in addition, the surface of smearing of heat-insulating waterproof coating of the present invention also has imitative porcelain effect.
Embodiment
Embodiment 1
A kind of heat-insulating waterproof coating, it is made up of the raw material of following weight parts (kilogram):
Acrylate and vinyl acetate emulsion 60, phosphorous acid dihydroxyphenyl propane ester 4, Viscogum BE 2, Cadmium chloride fine powder 0.1, succinic acid 0.3, alkylphenol polyoxyethylene 0.05, glycerine 1, sepiolite powder 10, ultra-fine barium sulfate 12, dipropylene glycol methyl ether 0.1, adhesive aid 12, deionized water 20;
Described adhesive aid is made up of the raw material of following weight parts:
Vinyl acetate-ethylene copolymerization emulsions 35, Viscogum BE 6, chitosan 2, stearyl methacrylate 5, Chinese Angelica Root 1, gibbsite 3, water are appropriate;
By above-mentioned stearyl methacrylate heat fused, add chitosan, stir, add gibbsite, Chinese Angelica Root, abundant mixing, joined by above-mentioned mixed material in 8 times of water, ball milling 2 hours, adds Viscogum BE, at 85 DEG C, insulated and stirred reacts 20 minutes, add each raw material of residue, abundant ball milling, obtains described adhesive aid.
A preparation method for heat-insulating waterproof coating, comprises the following steps:
By above-mentioned sepiolite powder, ultra-fine barium sulfate, adhesive aid mixing, 300 revs/min of dispersed with stirring 3 minutes, add alkylphenol polyoxyethylene, glycerine, 600 revs/min of dispersed with stirring 10 minutes, add each raw material of residue, high-speed stirring, to mixing, obtains described heat-insulating waterproof coating.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. a heat-insulating waterproof coating, is characterized in that what it was made up of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 50-60, phosphorous acid dihydroxyphenyl propane ester 3-4, Viscogum BE 2-3, Cadmium chloride fine powder 0.1-1, succinic acid 0.3-1, alkylphenol polyoxyethylene 0.05-0.1, glycerine 1-2, sepiolite powder 6-10, ultra-fine barium sulfate 10-12, dipropylene glycol methyl ether 0.1-1, adhesive aid 10-12, deionized water 8-20;
Described adhesive aid is made up of the raw material of following weight parts:
Vinyl acetate-ethylene copolymerization emulsions 20-35, Viscogum BE 4-6, chitosan 1-2, stearyl methacrylate 3-5, Chinese Angelica Root 1-2, gibbsite 3-4, water are appropriate;
By above-mentioned stearyl methacrylate heat fused, add chitosan, stir, add gibbsite, Chinese Angelica Root, abundant mixing, joined in 6-8 times of water by above-mentioned mixed material, ball milling 1-2 hour, adds Viscogum BE, insulated and stirred reaction 15-20 minute at 60-85 DEG C, add each raw material of residue, abundant ball milling, obtains described adhesive aid.
2. a preparation method for heat-insulating waterproof coating as claimed in claim 1, is characterized in that comprising the following steps:
By above-mentioned sepiolite powder, ultra-fine barium sulfate, adhesive aid mixing, 200-300 rev/min of dispersed with stirring 3-5 minute, add alkylphenol polyoxyethylene, glycerine, 400-600 rev/min of dispersed with stirring 6-10 minute, add each raw material of residue, high-speed stirring, to mixing, obtains described heat-insulating waterproof coating.