CN104845423A - Composite waterproof coating composition - Google Patents
Composite waterproof coating composition Download PDFInfo
- Publication number
- CN104845423A CN104845423A CN201510294464.2A CN201510294464A CN104845423A CN 104845423 A CN104845423 A CN 104845423A CN 201510294464 A CN201510294464 A CN 201510294464A CN 104845423 A CN104845423 A CN 104845423A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- acid
- water
- coating composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a composite waterproof coating composition. A montmorillonite material modified by lauryl ammonium chloride and triethanolamine is adopted in the composite waterproof coating composition; and the modified montmorillonite material has good dispersibility, thickening property and thixotropy and is capable of improving the stability of the coating. In addition, a specific proportion of modified nanometer composite powder is also adopted in the coating composition, and the nanometer composite powder subjected to surface modification can effectively modify the strength, toughness and scraping resistance of coatings. All the components in the specific composition of the coating interact synergistically so that after forming films, the coating has good adhesiveness, strength, hardness and waterproof performance.
Description
Technical field
The application relates to a kind of composite water-proof paint composition and method of making the same.
Background technology
Traditional water-proof material mainly contains the flexible waterproof materials such as waterproof roll, waterproof paint, sealing cement, and based on cement matrix, adds the rigidity water-proofing material of water-resisting agent and other auxiliary agent.China's major part waterproofing work all adopts conventional waterproof material, conventional waterproof material also exist loss of properties on aging, tensile strength low, to shortcomings such as temperature sensitives.Also there is following problem simultaneously: (1) conventional waterproof coating not environmentally, be corrosive, self material shrink large, puncture resistance is poor; (2) conventional waterproof coating brush less, leak brush be difficult to detect; (3) conventional waterproof coating application basal plane requires strict, must reach solid, smooth and dry requirement, otherwise construction quality is difficult to ensure; (4) conventional waterproof coating process is simple, with low content of technology, fakes easily; (5) as metope brushing big area waterproof paint, be difficult to ensure that facade pastes the requirement of large-size face brick.Conventional waterproof coating is used for roof waterproof, easily cause aging, dry and cracked, be out of shape, fracture, the phenomenon such as layering; For indoor waterproof, for complex-shaped place, constructional difficulties, and to Seepage, quality is more difficult to ensure, people will spend a large amount of funds and labor force to reprocess every several years, not only confuse the orthobiosis of people, work and the production order, and affect the work-ing life of whole building buildings.
Summary of the invention
The object of the present invention is to provide a kind of scientific and reasonable, easy construction of selecting materials, water resistance good composite water-proof paint.Its technical scheme is:
A kind of composite water-proof paint composition, this coating is adopted and is prepared with the following method:
A () is got sodium-based montmorillonite and is mixed with the aqueous solution of 10wt%, add the mixture of lauryl ammonium chloride and trolamine wherein, stirring reaction 2h at 100 DEG C, filter, fully washing 3 times is washed with deionized water, then 80 DEG C of vacuum-drying 1h, are ground to particle and can cross 400 mesh sieves, obtain organic modification montmonrillonite;
B () is got the mixed powder that particle diameter is the silicon oxide of 40-50nm, titanium dioxide and zinc oxide and is added in container, wherein the mass ratio of silicon oxide, titanium dioxide and zinc oxide is 2.5:2:1.8, then add the mixing solutions of isopropyl alcohol and water, stirred at ambient temperature disperses 60 minutes, then adds silane coupling agent KH570 and acid, and wherein KH570 is 1:1 with the mol ratio of acid, 60 DEG C of stirring reaction 4h, then be cooled to room temperature, filter, obtain modified Nano composite granule;
C () is with weight parts, get methyl acrylate 10 parts, ethyl propenoate 10 parts, isobutyl acrylate 8 parts, isoamyl acrylate 8 parts, the organic modification montmonrillonite 7 parts that step (a) is obtained, 8128 type benzene emulsions 5 parts, the modified Nano composite granule 8 parts that step (b) is obtained, mix and blend 10 minutes, then add ammonium persulphate 0.5 part successively, 4 parts, mica, frostproofer 0.5 part, defoamer 0.3 part, silica powder 2 parts, 3 parts, barium sulfate, talcum powder 2 parts, 20 parts, water, 2h is stirred with the speed of 400 revs/min, filtered 400 mesh sieves, tinning obtains coating finished product.
Acid in described step (b) is selected from hydrochloric acid, nitric acid, one or more in formic acid, acetic acid.
The median size of the mixed powder in described step (b) is 45nm.
beneficial effect
Have employed the montmorillonite material of lauryl ammonium chloride and trolamine modification in coating of the present invention, through modified polynite, there is good dispersiveness, thickening property and thixotropy, the stability of coating can be improved in coating.In addition, in coating, additionally use the modified Nano composite granule of specific proportioning, effectively can improve the intensity of coating, toughness and scratch resistance through the above-mentioned composite nano-powder of surface modification.In the specific composition of coating, each component is mutually collaborative, has good tack, intensity, hardness and water resistance after making coating film forming.
Embodiment
For further describing the present invention, for a more detailed description to composite water-proof paint composition and method of making the same of the present invention below in conjunction with embodiment.
embodiment 1
Get sodium-based montmorillonite and be mixed with the aqueous solution of 10wt%, add the mixture of lauryl ammonium chloride and trolamine wherein, stirring reaction 2h at 100 DEG C, filter, fully washing 3 times is washed with deionized water, then 80 DEG C of vacuum-drying 1h, are ground to particle and cross 400 mesh sieves, obtain organic modification montmonrillonite.
Getting the mixed powder that particle diameter is the silicon oxide of 40-50nm, titanium dioxide and zinc oxide adds in container, wherein the mass ratio of silicon oxide, titanium dioxide and zinc oxide is 2.5:2:1.8, then add the mixing solutions of isopropyl alcohol and water, stirred at ambient temperature disperses 60 minutes, then adds silane coupling agent KH570 and acid, and wherein KH570 is 1:1 with the mol ratio of acid, 60 DEG C of stirring reaction 4h, then be cooled to room temperature, filter, obtain modified Nano composite granule.
With weight parts; get methyl acrylate 10 parts, ethyl propenoate 10 parts; isobutyl acrylate 8 parts, isoamyl acrylate 8 parts, aforementioned obtained organic modification montmonrillonite 7 parts; 8128 type benzene emulsions 5 parts; aforementioned obtained modified Nano composite granule 8 parts, mix and blend 10 minutes, then adds ammonium persulphate 0.5 part successively; 4 parts, mica; frostproofer 0.5 part, defoamer 0.3 part, silica powder 2 parts; 3 parts, barium sulfate; talcum powder 2 parts, 20 parts, water, stirs 2h; filtered 400 mesh sieves, tinning obtains coating finished product with the speed of 400 revs/min.
comparative example 1
With weight parts, get methyl acrylate 10 parts, ethyl propenoate 10 parts, isobutyl acrylate 8 parts, isoamyl acrylate 8 parts, aforementioned obtained organic modification montmonrillonite 7 parts, 8128 type benzene emulsions 5 parts, mix and blend 10 minutes, then adds ammonium persulphate 0.5 part successively, 4 parts, mica, frostproofer 0.5 part, defoamer 0.3 part, silica powder 2 parts, 3 parts, barium sulfate, talcum powder 2 parts, 20 parts, water, stir 2h with the speed of 400 revs/min, filtered 400 mesh sieves, tinning obtains coating finished product.
comparative example 2
With weight parts, get methyl acrylate 10 parts, ethyl propenoate 10 parts, isobutyl acrylate 8 parts, isoamyl acrylate 8 parts, 8128 type benzene emulsions 5 parts, aforementioned obtained modified Nano composite granule 8 parts, mix and blend 10 minutes, then adds ammonium persulphate 0.5 part successively, 4 parts, mica, frostproofer 0.5 part, defoamer 0.3 part, silica powder 2 parts, 3 parts, barium sulfate, talcum powder 2 parts, 20 parts, water, stir 2h with the speed of 400 revs/min, filtered 400 mesh sieves, tinning obtains coating finished product.
Carry out coating performance detection to above obtained coating, result is as follows:
Test item | Water tolerance 150h | Abrasion resistance (secondary) | Temperature-change resistance (10 circulations) |
Embodiment 1 | Without exception | 1000 | Without exception |
Comparative example 1 | Change | 700 | Change |
Comparative example 2 | Change | 660 | Change |
Claims (3)
1. a composite water-proof paint composition, is characterized in that, this coating is adopted and prepared with the following method:
A () is got sodium-based montmorillonite and is mixed with the aqueous solution of 10wt%, add the mixture of lauryl ammonium chloride and trolamine wherein, stirring reaction 2h at 100 DEG C, filter, fully washing 3 times is washed with deionized water, then 80 DEG C of vacuum-drying 1h, are ground to particle and can cross 400 mesh sieves, obtain organic modification montmonrillonite;
B () is got the mixed powder that particle diameter is the silicon oxide of 40-50nm, titanium dioxide and zinc oxide and is added in container, wherein the mass ratio of silicon oxide, titanium dioxide and zinc oxide is 2.5:2:1.8, then add the mixing solutions of isopropyl alcohol and water, stirred at ambient temperature disperses 60 minutes, then adds silane coupling agent KH570 and acid, and wherein KH570 is 1:1 with the mol ratio of acid, 60 DEG C of stirring reaction 4h, then be cooled to room temperature, filter, obtain modified Nano composite granule;
C () is with weight parts, get methyl acrylate 10 parts, ethyl propenoate 10 parts, isobutyl acrylate 8 parts, isoamyl acrylate 8 parts, the organic modification montmonrillonite 7 parts that step (a) is obtained, 8128 type benzene emulsions 5 parts, the modified Nano composite granule 8 parts that step (b) is obtained, mix and blend 10 minutes, then add ammonium persulphate 0.5 part successively, 4 parts, mica, frostproofer 0.5 part, defoamer 0.3 part, silica powder 2 parts, 3 parts, barium sulfate, talcum powder 2 parts, 20 parts, water etc., 2h is stirred with the speed of 400 revs/min, filtered 400 mesh sieves, tinning obtains coating finished product.
2. coating composition as claimed in claim 1, is characterized in that: the acid in step (b) is selected from one or more in hydrochloric acid, nitric acid, formic acid, acetic acid.
3. coating composition as claimed in claim 1, is characterized in that: the median size of the mixed powder in step (b) is 45nm.