CN104278311A - 一种自清洁二氧化钛纳米管阵列的制备方法 - Google Patents

一种自清洁二氧化钛纳米管阵列的制备方法 Download PDF

Info

Publication number
CN104278311A
CN104278311A CN201410522899.3A CN201410522899A CN104278311A CN 104278311 A CN104278311 A CN 104278311A CN 201410522899 A CN201410522899 A CN 201410522899A CN 104278311 A CN104278311 A CN 104278311A
Authority
CN
China
Prior art keywords
mixing solutions
cleaning
self
preparation
titanium dioxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410522899.3A
Other languages
English (en)
Other versions
CN104278311B (zh
Inventor
高大伟
王丽丽
毕红军
王春霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QUANJIAO KANGLILAI CLOTHING Co.,Ltd.
Original Assignee
Yangcheng Institute of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yangcheng Institute of Technology filed Critical Yangcheng Institute of Technology
Priority to CN201410522899.3A priority Critical patent/CN104278311B/zh
Publication of CN104278311A publication Critical patent/CN104278311A/zh
Application granted granted Critical
Publication of CN104278311B publication Critical patent/CN104278311B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种自清洁二氧化钛纳米管阵列的制备方法，属于无机纳米材料领域，本发明包括以下步骤：(1)阳极氧化，(2)热处理，(3)制备二氧化硅溶胶，(4)二氧化钛纳米管浸润。本发明的TiO2纳米管阵列经二氧化硅溶胶改性后，具有较好的光催化性能和较强的疏水能力，二氧化硅牢固的吸附在TiO2纳米管上，耐多次清洗，自清洁持久性好，而且本方法制备的二氧化钛纳米管阵列不容易被沾污，使用寿命长；本发明工艺设备简单，操作方便，工艺参数易控制，成本低廉，适合于工业化生产。

Description

一种自清洁二氧化钛纳米管阵列的制备方法
技术领域
本发明属于无机纳米材料领域，尤其涉及一种自清洁二氧化钛纳米管阵列的制备方法。
背景技术
纳米材料具有一系列特异的物理化学性质，表现出优异的小尺寸效应、表面效应、量子尺寸效应、宏观量子隧道效应和介电限域效应，从而使材料在热、磁、光、敏感特性和表面稳定性等方面显示出特殊的性能。纳米二氧化钛(TiO2)是一种重要的无机功能材料，因其良好化学稳定性、优越的热稳定性和环境友好等特性使其在自清洁材料、海洋防腐、太阳能电池、传感器、光裂解水及催化降解等领域有着显著的地位。TiO2纳米管具有纳米管的特殊结构，因此具有更大的比表面积和更强的吸附能力，表现出更高的光催化性能和光电转化效率。
超疏水是指水与表面的接触角超过150°，超疏水物质表面具有很多独特的结构特征和表面性能，如自清洁性、防污特性和海洋防腐等特性，这些特殊性能使其在很多领域具有巨大的应用价值。
发明内容
本发明提供了一种具有较好的光催化性能、较强的疏水能力和自清洁功能的TiO2纳米管阵列的制备方法。
为实现上述目的，本发明提供以下技术方案，一种自清洁二氧化钛纳米管阵列的制备方法，包括以下步骤：
(1)、阳极氧化
将高纯钛片表面清洗干净，在电解液中进行阳极氧化，氧化电压为20～60V，氧化时间为2～6小时；
(2)、热处理
将阳极氧化后的高纯钛片在450～600℃下煅烧2～4小时进行热处理；
(3)、制备二氧化硅溶胶
将正硅酸乙酯和乙醇均匀混合，得混合溶液Ⅰ，向此混合溶液Ⅰ中缓慢滴加盐酸与水的混合液，得到混合溶液Ⅱ，将混合溶液Ⅱ静置陈化24小时，即得到透明的二氧化硅溶胶；
(4)、二氧化钛纳米管浸润
将步骤(2)中处理后的高纯钛片浸入到步骤(3)中制得的二氧化硅溶胶中，并反复浸润2～5次，每次浸润1～5分钟。
进一步的，所述的步骤(1)中电解液为含有0.5～8wt％氟化铵和3～5vol％去离子水的乙二醇溶液。
进一步的，所述的步骤(3)中正硅酸乙酯与乙醇的体积比为1:2～1:3，盐酸与水的体积比为1:20～1:10，滴加的盐酸与水混合液与混合溶液Ⅰ的体积比为2:1～3:1。
本发明选择高纯度钛片作为基片，是因为钛片纯度会影响二氧化钛纳米管的形貌及结构，不可替换成低纯度的钛片，纯度过低甚至得不到纳米管。
本发明在高纯钛片浸润二氧化硅溶胶之前进行热处理，可以有效提高阳极氧化膜的抗腐性。
二氧化硅溶胶制备方法简便，材料价格低廉，另外，二氧化硅较牢固的吸附在TiO2纳米管上，耐多次冲洗，自清洁持久性好。
本发明具有以下有益效果：本发明的TiO2纳米管阵列经二氧化硅溶胶改性后，具有较好的光催化性能和较强的疏水能力，二氧化硅能牢固的吸附在TiO2纳米管上，自清洁持久性好，而且本方法制备的二氧化钛纳米管阵列不容易被沾污，使用寿命长；本发明工艺设备简单，操作方便，工艺参数易控制，成本低廉，适合于工业化生产。
具体实施方式
以下结合实施例对本发明作进一步说明。
阳极氧化设备可以选择本领域技术人员熟知的任一种，优选采用特安斯TASI-1603直流电源供应器，电解槽采用100ml的烧杯，其中阴极采用2cm×2cm铂片，阳极为2cm×2cm钛片，电极间距5cm。
光催化性能测试条件：30ml的甲基橙溶液，浓度为20g/L。测试前先将样品放入烧杯中并在黑暗条件下平衡30min，然后置于250W紫外灯(波长为254nm)下进行测试，灯距离液面的距离为30cm。测试时每隔半小时取一个样品用分光光度计进行吸光度测试(分光光度计采用上海菁华科技仪器有限公司，722型分光光度计)在波长为464nm处测吸光度，测试时间为3h。
甲基橙溶液的降解率n＝(Ao-A)/Ao×100％，其中Ao为初始溶液的吸光度，A为各反应阶段的吸光度。
疏水能力通过接触角来表征，采用上海中晨数字技术设备有限公司JC200D3接触角测量仪测量接触角。
实施例1
(1)、将高纯钛片在去离子水和丙酮中多次清洗至表面清洗干净，在1.0wt％氟化铵和4vol％去离子水的乙二醇溶液中进行阳极氧化，氧化电压为60V，氧化时间为3小时；
(2)、将阳极氧化后的高纯钛片在500℃下煅烧2小时进行热处理；
(3)、将正硅酸乙酯和乙醇按照体积比1:2充分均匀混合，得到混合溶液Ⅰ，再向此混合溶液Ⅰ中缓慢滴加盐酸和水(体积比为1:15)的混合液，混合溶液Ⅰ与盐酸和水的混合液的体积比为2:1，得到混合溶液Ⅱ，并且将混合溶液Ⅱ静置陈化24小时，即得到透明的二氧化硅溶胶体系；
(4)、将步骤(2)中处理后的高纯钛片浸入到步骤(3)中制得的二氧化硅溶胶中，并反复浸润2次，每次浸润1分钟；
光催化性能测试，3h后甲基橙的降解率在94％；
疏水能力表征，接触角：157°。
实施例2：
(1)、将高纯钛片在去离子水和丙酮中多次清洗至表面清洗干净，在1.0wt％氟化铵和4vol％去离子水的乙二醇溶液中进行阳极氧化，氧化电压为60V，氧化时间为3小时；
(2)、将阳极氧化后的高纯钛片在500℃下煅烧2小时进行热处理；
(3)、将正硅酸乙酯和乙醇按照体积比1:2充分均匀混合，得到混合溶液Ⅰ，再向此混合溶液中缓慢滴加盐酸和水(体积比为1:15)的混合液，混合溶液Ⅰ与盐酸和水的混合液的体积比为2:1，得到混合溶液Ⅱ，并且将混合溶液Ⅱ静置陈化24小时，即得到透明的二氧化硅溶胶体系；
(4)、将步骤(2)中处理后的高纯钛片浸入到步骤(3)中制得的二氧化硅溶胶中，并反复浸润2次，每次浸润3分钟；
光催化性能测试，3h后甲基橙的降解率在95％；
疏水能力表征，接触角：160°。
实施例3：
(1)、将高纯钛片在去离子水和丙酮中多次清洗至表面清洗干净，在1.0wt％氟化铵和4vol％去离子水的乙二醇溶液中进行阳极氧化，氧化电压为60V，氧化时间为3小时；
(2)、将阳极氧化后的高纯钛片在500℃下煅烧2小时进行热处理；
(3)、将正硅酸乙酯和乙醇按照体积比1:2充分均匀混合，得到混合溶液Ⅰ，再向此混合溶液中缓慢滴加盐酸和水(体积比为1:15)的混合液，混合溶液Ⅰ与盐酸和水的混合液的体积比为2:1，得到混合溶液Ⅱ，并且将混合溶液Ⅱ静置陈化24小时，即得到透明的二氧化硅溶胶体系；
(4)、将步骤(2)中处理后的高纯钛片浸入到步骤(3)中制得的二氧化硅溶胶中，并反复浸润5次，每次浸润3分钟；
光催化性能测试，3h后甲基橙的降解率在93％；
疏水能力表征，接触角：157°。
实施例4：
(1)、将高纯钛片在去离子水和丙酮中多次清洗至表面清洗干净，在1.0wt％氟化铵和4vol％去离子水的乙二醇溶液中进行阳极氧化，氧化电压为60V，氧化时间为3小时；
(2)、将阳极氧化后的高纯钛片在500℃下煅烧2小时进行热处理；
(3)、将正硅酸乙酯和乙醇按照体积比1:2充分均匀混合，得到混合溶液Ⅰ，再向此混合溶液中缓慢滴加盐酸和水(体积比为1:15)的混合液，混合溶液Ⅰ与盐酸和水的混合液的体积比为2:1，得到混合溶液Ⅱ，并且将混合溶液Ⅱ静置陈化24小时，即得到透明的二氧化硅溶胶体系；
(4)、将步骤(2)中处理后的高纯钛片浸入到步骤(3)中制得的二氧化硅溶胶中，并反复浸润2次，每次浸润5分钟；
光催化性能测试，3h后甲基橙的降解率在92％；
疏水能力表征，接触角：151°。
实施例5：
(1)、将高纯钛片在去离子水和丙酮中多次清洗至表面清洗干净，在1.0wt％氟化铵和4vol％去离子水的乙二醇溶液中进行阳极氧化，氧化电压为40V，氧化时间为3小时；
(2)、将阳极氧化后的高纯钛片在500℃下煅烧5小时进行热处理；
(3)、将正硅酸乙酯和乙醇按照体积比1:3充分均匀混合，得到混合溶液Ⅰ，再向此混合溶液中缓慢滴加盐酸和水(体积比为1:10)的混合液，混合溶液Ⅰ与盐酸和水的混合液的体积比为2:1，得到混合溶液Ⅱ，并且将混合溶液Ⅱ静置陈化24小时，即得到透明的二氧化硅溶胶体系；
(4)、将步骤(2)中处理后的高纯钛片浸入到步骤(3)中制得的二氧化硅溶胶中，并反复浸润2次，每次浸润3分钟；
光催化性能测试，3h后甲基橙的降解率在90％；
疏水能力表征，接触角：145°。
实施例6：
(1)、将高纯钛片在去离子水和丙酮中多次清洗至表面清洗干净，在1.0wt％氟化铵和4vol％去离子水的乙二醇溶液中进行阳极氧化，氧化电压为20V，氧化时间为4小时；
(2)、将阳极氧化后的高纯钛片在500℃下煅烧3小时进行热处理；
(3)、将正硅酸乙酯和乙醇按照体积比1:3充分均匀混合，得到混合溶液Ⅰ，再向此混合溶液中缓慢滴加盐酸和水(体积比为1:20)的混合液，混合溶液Ⅰ与盐酸和水的混合液的体积比为3:1，得到混合溶液Ⅱ，并且将混合溶液Ⅱ静置陈化24小时，即得到透明的二氧化硅溶胶体系；
(4)、将步骤(2)中处理后的高纯钛片浸入到步骤(3)中制得的二氧化硅溶胶中，并反复浸润2次，每次浸润3分钟；
光催化性能测试，3h后甲基橙的降解率在92％；
疏水能力表征，接触角：148°。

Claims (3)

1.一种自清洁二氧化钛纳米管阵列的制备方法，其特征在于，包括以下步骤：
(1)、阳极氧化
将高纯钛片表面清洗干净，在电解液中进行阳极氧化，氧化电压为20～60V，氧化时间为2～6小时；
(2)、热处理
将阳极氧化后的高纯钛片在450～600℃下煅烧2～4小时进行热处理；
(3)、制备二氧化硅溶胶
将正硅酸乙酯和乙醇均匀混合，得到混合溶液Ⅰ，再向此混合溶液Ⅰ中缓慢滴加盐酸与水的混合液，得到混合溶液Ⅱ，将混合溶液Ⅱ静置陈化24小时，即得到透明的二氧化硅溶胶；
(4)、二氧化钛纳米管浸润
将步骤(2)中处理后的高纯钛片浸入到步骤(3)中制得的二氧化硅溶胶中，并反复浸润2～5次，每次浸润1～5分钟。
2.根据权利要求1所述的一种自清洁二氧化钛纳米管阵列的制备方法，其特征在于，所述的步骤(1)中电解液为含有0.5～8wt％氟化铵和3～5vol％去离子水的乙二醇溶液。
3.根据权利要求1所述的一种自清洁二氧化钛纳米管阵列的制备方法，其特征在于，所述的步骤(3)中正硅酸乙酯与乙醇的体积比为1:2～1:3，盐酸与水的体积比为1:20～1:10，滴加的盐酸与水的混合液与混合溶液Ⅰ的体积比为2:1～3:1。
CN201410522899.3A 2014-09-30 2014-09-30 一种自清洁二氧化钛纳米管阵列的制备方法 Active CN104278311B (zh)