CN104264198A - 一种铈-镍-磷合金电镀液及其制备方法 - Google Patents

一种铈-镍-磷合金电镀液及其制备方法 Download PDF

Info

Publication number
CN104264198A
CN104264198A CN201410569006.0A CN201410569006A CN104264198A CN 104264198 A CN104264198 A CN 104264198A CN 201410569006 A CN201410569006 A CN 201410569006A CN 104264198 A CN104264198 A CN 104264198A
Authority
CN
China
Prior art keywords
nickel
cerium
electroplate liquid
phosphor alloy
alloy electroplate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410569006.0A
Other languages
English (en)
Inventor
华文蔚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410569006.0A priority Critical patent/CN104264198A/zh
Publication of CN104264198A publication Critical patent/CN104264198A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铈-镍-磷合金电镀液及其制备方法。该铈-镍-磷合金电镀液包含镍盐60～160g/L、亚磷酸30～80g/L、氧化铈0.05～1g/L、硼酸10～20g/L、有机羧酸10～25g/L、光亮剂3～8g/L。本发明的铈-镍-磷合金电镀液稳定性好；使用该铈-镍-磷合金电镀液得到的镀层色泽美观、耐蚀性好。

Description

一种铈-镍-磷合金电镀液及其制备方法
技术领域
本发明涉及电镀技术领域，尤其涉及一种铈-镍-磷合金电镀液及其制备方法。
背景技术
稀土有“工业维生素”的美称。现如今已成为极其重要的战略资源。稀土元素氧化物是指元素周期表中原子序数为57到71的15种镧系元素氧化物，以及与镧系元素化学性质相似的钪(Sc)和铈(Y)共17种元素的氧化物。稀土元素在石油、化工、冶金、纺织、陶瓷、玻璃、永磁材料等领域都得到了广泛的应用，随着科技的进步和应用技术的不断突破，稀土氧化物的价值将越来越大。
目前镍磷合金的镀液主要采用酸性体系和碱性体系。酸性体系成分较简单，镀液稳定，但镀层不均匀，影响耐蚀性。碱性体系采用碱性镀液，其镀层厚度均匀，镀液不稳定。
发明内容
有鉴于此，本发明一方面提供一种铈-镍-磷合金电镀液，该电镀液稳定性好。
一种铈-镍-磷合金电镀液，包含镍盐60～160g/L、亚磷酸30～80g/L、氧化铈0.05～1g/L、硼酸10～20g/L、有机羧酸10～25g/L、光亮剂3～8g/L。
优选的，该铈-镍-磷合金电镀液包含镍盐150g/L、亚磷酸50g/L、氧化铈0.5g/L、硼酸15g/L、有机羧酸20g/L、光亮剂4g/L和余量的去离子水。
优选的，所述镍盐为硫酸盐，所述有机羧酸为酒石酸、丁二酸或乙二酸，所述光亮剂为糖精、甲醛、二甲基己炔醇中一种或至少2种的混合物。
优选的，所述铈-镍-磷合金电镀液的PH值为2～4，所述铈-镍-磷合金电镀液工作温度60～70℃。
本发明另一方面提供一种制备上述电镀液的方法，使用该铈-镍-磷合金电镀液得到的镀层色泽美观、耐蚀性好。
一种制备上述铈-镍-磷合金电镀液的方法，包括以下步骤：
(1)向去离子水中加入有机羧酸10～25g、亚磷酸30～80g、硼酸10～20g、镍盐60～160g搅拌溶解制成混合液；
(2)向该混合液中加入氧化铈0.05～1g和光亮剂3～8g搅拌溶解，再加入余量的去离子水至总体积为1L，得到铈-镍-磷合金电镀液。
优选的，步骤(2)中氧化铈先酸化处理，再加入到混合液中。
本发明的有益效果：本发明的铈-镍-磷合金电镀液包含镍盐60～160g/L、亚磷酸30～80g/L、氧化铈0.05～1g/L、硼酸10～20g/L、有机羧酸10～25g/L、光亮剂3～8g/L。本发明铈-镍-磷合金电镀液稳定性好；使用该铈-镍-磷合金电镀液得到的镀层色泽美观、耐蚀性好。
具体实施方式
下面分别结合具体实施例来对本发明作进一步说明。
以下实施例中所涉及的原料均为市售。
实施例1：本实施例的铈-镍-磷合金电镀液包含以下组分：
制备该铈-镍-磷合金电镀液的方法如下：
向去离子水中加入有机羧酸10g、亚磷酸30g、硼酸10g、硫酸镍60g搅拌溶解制成混合液，向混合液中加入已酸化处理的氧化铈0.1g、糖精3g，加热到60℃搅拌溶解，再加入余量的去离子水至总体积为1L，调节PH至2-4，得到铈-镍-磷合金电镀液。
实施例2：本实施例的铈-镍-磷合金电镀液包含以下组分：
制备该铈-镍-磷合金电镀液的方法如下：
向去离子水中加入有机羧酸15g、亚磷酸50g、硼酸15g、硫酸镍120g搅拌溶解制成混合液，向混合液中加入已酸化处理的氧化铈0.1g、糖精5g，加热到70℃搅拌溶解，再加入余量的去离子水至总体积为1L，调节PH至2-4，得到铈-镍-磷合金电镀液。
实施例3：本实施例的铈-镍-磷合金电镀液包含以下组分：
制备该铈-镍-磷合金电镀液的方法如下：
向去离子水中加入有机羧酸25g、亚磷酸80g、硼酸20g、硫酸镍160g搅拌溶解制成混合液，向混合液中加入已酸化处理的氧化铈0.5g、糖精8g，加热到70℃搅拌溶解，再加入余量的去离子水至总体积为1L，调节PH至2-4，得到铈-镍-磷合金电镀液。
实施例1～3得到的铈-镍-磷合金电镀液使用和储存过程中稳定性好；将铈-镍-磷合金电镀液进行电镀，得到的镀层均分布均匀，色泽美观。
采用本领域所公知的测试方法对实施例1～3的电镀液进行阴极电流效率测试和将其得到的镀层进行盐雾试验以测定耐蚀性，测试结果如下表。
通过上表可以看出使用本发明的电镀液得到的镀层耐蚀性明显比现有镀层好。
本发明铈-镍-磷合金电镀液稳定性好；使用该铈-镍-磷合金电镀液得到的镀层色泽美观、耐蚀性好。
应该注意到并理解，在不脱离后附的权利要求所要求保护的本发明的精神和范围的情况下，能够对上述详细描述的本发明做出各种修改和改进。因此，要求保护的技术方案的范围不受所给出的任何特定示范教导的限制。
申请人声明，本发明通过上述实施例来说明本发明的详细工艺设备和工艺流程，但本发明并不局限于上述详细工艺设备和工艺流程，即不意味着本发明必须依赖上述详细工艺设备和工艺流程才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。

Claims (8)

1.一种铈-镍-磷合金电镀液，其特征在于，包含镍盐60～160g/L、亚磷酸30～80g/L、氧化铈0.05～1g/L、硼酸10～20g/L、有机羧酸10～25g/L、光亮剂3～8g/L。
2.根据权利要求1所述的铈-镍-磷合金电镀液，其特征在于，包含镍盐150g/L、亚磷酸50g/L、氧化铈0.5g/L、硼酸15g/L、有机羧酸20g/L、光亮剂4g/L和余量的去离子水。
3.根据权利要求1所述的铈-镍-磷合金电镀液，其特征在于，所述镍盐为硫酸盐，所述有机羧酸为酒石酸、丁二酸或乙二酸。
4.根据权利要求1所述的铈-镍-磷合金电镀液，其特征在于，所述光亮剂为糖精、甲醛、二甲基己炔醇中一种或至少2种的混合物。
5.根据权利要求1所述的铈-镍-磷合金电镀液，其特征在于，所述铈-镍-磷合金电镀液的PH值为2～4。
6.根据权利要求1所述的铈-镍-磷合金电镀液，其特征在于，所述铈-镍-磷合金电镀液工作温度60～70℃。
7.一种制备权利要求1所述铈-镍-磷合金电镀液的方法，其特征在于，包括以下步骤：
(1)向去离子水中加入有机羧酸10～25g、亚磷酸30～80g、硼酸10～20g、镍盐60～160g搅拌溶解制成混合液；
(2)向该混合液中加入氧化铈0.05～1g和光亮剂3～8g搅拌溶解，再加入余量的去离子水至总体积为1L，得到铈-镍-磷合金电镀液。
8.根据权利要求7所述的制备方法，其特征在于，步骤(2)中氧化铈先酸化处理，再加入到混合液中。
CN201410569006.0A 2014-10-22 2014-10-22 一种铈-镍-磷合金电镀液及其制备方法 Pending CN104264198A (zh)