CN102409375A - 一种镍磷合金电镀液及其使用方法 - Google Patents
一种镍磷合金电镀液及其使用方法 Download PDFInfo
- Publication number
- CN102409375A CN102409375A CN2011103928742A CN201110392874A CN102409375A CN 102409375 A CN102409375 A CN 102409375A CN 2011103928742 A CN2011103928742 A CN 2011103928742A CN 201110392874 A CN201110392874 A CN 201110392874A CN 102409375 A CN102409375 A CN 102409375A
- Authority
- CN
- China
- Prior art keywords
- nickel
- electroplating
- phosphorus alloy
- electroplating solution
- salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种镍磷合金电镀液,包括以下浓度的成分:200-250g/L的硫酸镍、35-45g/L的氯化镍、38-42g/L的硼酸、50-70g/L的次磷酸钠、34-47g/L的氟化氢铵、1-2g/L的稀土可溶盐,0.08-0.12g/L的表面活性剂。使用本发明的电镀液中添加了一定量的稀土元素,能够显著改善镀液的性能,如提高电流效率,分散能力,能够提高电沉积过程的阴极极化度,最后得到的镀层致密,均匀,结合力良好,硬度高,耐蚀性能优良。
Description
技术领域
本发明涉及一种镍磷合金电镀液及其使用方法。
背景技术
中国的液压活塞杆多用镀铬进行防腐处理,行业电镀企业基本按国家标准GBll379-89《金属覆盖层工程用铬电镀层》及GB/T12611-90《金属零件镀覆前质量控制技术要求》标准规定执行,然而,在极端条件下,现有技术生产的镀铬活塞杆防锈蚀能力较差,同时,生产的液压活塞杆表面粗度较大。
发明内容
本发明的目的是提供一种镍磷合金电镀液及其使用方法。
本发明所采取的技术方案是:
一种镍磷合金电镀液,包括以下浓度的成分:200-250g/L的硫酸镍、35-45g/L的氯化镍、38-42g/L的硼酸、50-70g/L的次磷酸钠、34-47g/L的氟化氢铵、1-2g/L的稀土可溶盐, 0.08-0.12g/L的表面活性剂。
一种镍磷合金电镀液,包括以下浓度的成分:200-230g/L的硫酸镍、35-45g/L的氯化镍、38-42g/L的硼酸、62-70g/L的次磷酸钠、34-47g/L的氟化氢铵、1-2g/L的稀土可溶盐, 0.08-0.12g/L的表面活性剂。
所述的表面活性剂为十二烷基苯磺酸钠、十二烷基醚硫酸钠、烷基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚中的一种。
一种镍磷合金电镀液的使用方法,调节电镀液的pH至2.0-3.5,再把电镀液加热到60-75℃,将作为阴极的工件放入其中,阳极为镍金属,阴极的电流密度为1-2A/dm2。
本发明的有益效果是:使用本发明的电镀液中添加了一定量的稀土元素,能够显著改善镀液的性能,如提高电流效率,分散能力,能够提高电沉积过程的阴极极化度,最后得到的镀层致密,均匀,结合力良好,硬度高,耐蚀性能优良。
具体实施方式
下面结合具体实施例对本发明做进一步的说明:
实施例1:
一种镍磷合金电镀液,包括以下浓度的成分:200g/L的硫酸镍(即1L的电镀液中,硫酸镍的质量为200g)、35g/L的氯化镍、38g/L的硼酸、62g/L的次磷酸钠、34g/L的氟化氢铵,1.0g/L的铈可溶盐、0.08g/L的十二烷基醚硫酸钠。
电镀液的溶剂为水。
施镀时,用10%的稀硫酸调节电镀液的pH至2,再把电镀液加热到60℃,将作为阴极的液压活塞杆工件放入其中,阳极为镍金属,阴极的电流密度为1A/dm2。
实施例2:
一种镍磷合金电镀液,包括以下浓度的成分:210g/L的硫酸镍、40g/L的氯化镍、42g/L的硼酸、64g/L的次磷酸钠、41g/L的氟化氢铵,1.5g/L的镧可溶盐、0.12g/L的十二烷基苯磺酸钠。
施镀时,用7%的稀硫酸调节电镀液的pH至3.0,再把电镀液加热到70℃,将作为阴极的液压活塞杆工件放入其中,阳极为镍金属,阴极的电流密度为2A/dm2。
实施例3:
一种镍磷合金电镀液,包括以下浓度的成分:230g/L的硫酸镍、45g/L的氯化镍、41g/L的硼酸、70g/L的次磷酸钠、47g/L的氟化氢铵、2.0g/L的铈可溶盐、0.09g/L的壬基酚聚氧乙烯醚。
施镀时,用5%的稀硫酸调节电镀液的pH至3.2,再把电镀液加热到75℃,将作为阴极液压活塞杆工件放入其中,阳极为镍金属,阴极的电流密度为1.6A/dm2。
经测试,实施例1-3得到的工件的镀层的显微硬度为HV 600-700,用5%NaCl溶液(pH=7)浸泡200小时,表面无锈点,实施例1-3的电镀液的电流效率η分别为52%、55%、52%,沉积速度在0.3-0.35μm/min,镀层的磷含量分别为12%、10%、12%。
实施例1-3中,施镀完镍磷合金的工件上可以按照常规工艺再进行镀铬处理。
将实施例1-3经过施镀的工件进行热震试验(测试标准:GB5270-85),热震试验的温度按照钢基体金属(本发明中的工件基体为45G钢)对应的300℃进行,最后发现镀层均没有起泡,脱落现象,说明镀层的结合力较好。
Claims (4)
1.一种镍磷合金电镀液,其特征在于:包括以下浓度的成分:200-250g/L的硫酸镍、35-45g/L的氯化镍、38-42g/L的硼酸、50-70g/L的次磷酸钠、34-47g/L的氟化氢铵、1-2g/L的稀土可溶盐, 0.08-0.12g/L的表面活性剂。
2.根据权利要求1所述的一种镍磷合金电镀液,其特征在于:包括以下浓度的成分:200-230g/L的硫酸镍、35-45g/L的氯化镍、38-42g/L的硼酸、62-70g/L的次磷酸钠、34-47g/L的氟化氢铵、1-2g/L的稀土可溶盐, 0.08-0.12g/L的表面活性剂。
3.根据权利要求1所述的一种镍磷合金电镀液,其特征在于:所述的表面活性剂为十二烷基苯磺酸钠、十二烷基醚硫酸钠、烷基酚聚氧乙烯醚、脂肪醇聚氧乙烯醚中的一种。
4.一种如权利要求1所述的镍磷合金电镀液的使用方法,其特征在于:调节电镀液的pH至2.0-3.5,再把电镀液加热到60-75℃,将作为阴极的工件放入其中,阳极为镍金属,阴极的电流密度为1-2A/dm2。