CN104261779B - 一种环保墙体保温材料及其制备方法 - Google Patents

一种环保墙体保温材料及其制备方法 Download PDF

Info

Publication number
CN104261779B
CN104261779B CN201410436210.5A CN201410436210A CN104261779B CN 104261779 B CN104261779 B CN 104261779B CN 201410436210 A CN201410436210 A CN 201410436210A CN 104261779 B CN104261779 B CN 104261779B
Authority
CN
China
Prior art keywords
fluorgypsum
insulation material
thermal insulation
environment protection
protection wall
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410436210.5A
Other languages
English (en)
Other versions
CN104261779A (zh
Inventor
李根固
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Huiming Construction Group Co Ltd
Original Assignee
Anhui Huiming Construction Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Huiming Construction Group Co Ltd filed Critical Anhui Huiming Construction Group Co Ltd
Priority to CN201410436210.5A priority Critical patent/CN104261779B/zh
Publication of CN104261779A publication Critical patent/CN104261779A/zh
Application granted granted Critical
Publication of CN104261779B publication Critical patent/CN104261779B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保墙体保温材料，其是由下述重量份的原料制得：改性氟石膏1530，元明粉25，偏硅酸钠13，麦饭石粉2030，玻璃微珠1020，硅酸盐水泥80100，牛脂胺聚氧乙烯醚12，膨胀蛭石6080，磺酸乙基纤维素13，苯丙乳液1015，皂苷12；本发明的墙体保温材料合理回收利用工业废料氟石膏，既能达到预期的保温效果，又符合节能减排的要求，经济效益和环境效益高。

Description

一种环保墙体保温材料及其制备方法
技术领域
本发明涉及建筑材料领域，具体涉及一种环保墙体保温材料及其制备方法。
背景技术
墙体保温材料作为影响建筑节能一个重要因素，其开发与应用已经越来越受到世界各国的普遍重视。合理开发墙体保温材料，既能大量节约墙体材料，提高墙体保温性能，又能达到节约资源，减少环境污染的目的。
氟石膏是用硫酸与氟石制取氟化氢的副产品，产量非常可观。目前多数氟石膏稍加处理后就作为固体废弃物堆存，不仅占用土地，还对生态环境产生一定的危害。因此，合理回收利用氟石膏具有重大意义。氟石膏成分复杂，且具有易吸水等特性，因此氟石膏用作建材需结合改性剂、添加剂对其性能进行改善。
发明内容
本发明的目的是提供一种环保墙体保温材料。
本发明是通过以下技术方案实现的：
一种环保墙体保温材料，其是由下述重量份的原料制得：
改性氟石膏15-30，元明粉2-5，偏硅酸钠1-3，麦饭石粉20-30，玻璃微珠10-20，硅酸盐水泥80-100，牛脂胺聚氧乙烯醚1-2，膨胀蛭石60-80，磺酸乙基纤维素1-3，苯丙乳液10-15，皂苷1-2；
改性氟石膏由下列重量份的原料制成：
氟石膏20-40，三乙醇胺2-4，酒石酸1-3，酒石酸氢钾2-4，十六烷基三甲基溴化铵0.5-1，生石灰10-15；
改性氟石膏的制备方法是：
将氟石膏200-300℃处理1-2h，洗涤过滤后烘干，加入生石灰，混合均匀后600-800℃煅烧3-5h，加入适量水，200-300r/min搅拌15-30min，过滤后洗涤至pH中性，加入三乙醇胺、十六烷基三甲基溴化铵、酒石酸和酒石酸氢钾，加热至75-85℃，200-300r/min搅拌1-2h，真空干燥后研磨，过100-200目筛，即得；一种环保墙体保温材料的制备方法，包括以下步骤：
(1)将苯丙乳液、皂苷和牛脂胺聚氧乙烯醚混合后40-60℃、800-1000r/min搅拌15-30min，喷雾干燥后得活性粉体；
(2)将元明粉、麦饭石粉和磺酸乙基纤维素混合后200-300℃处理1-2h，研磨均匀，过200-300目筛，与活性粉体以及其余原料混合，200-300r/min搅拌1-2h，分装后即得。
本发明的优点是：
1.通过调整配方以及改性，使工业废料氟石膏得到合理利用，节能减排，经济效益和环境效益高；
2.防水性能强，耐火、耐腐蚀性好；
3.和易性优良，便于施工、维护。
具体实施方式
本发明非限定实施例如下：
实施例1
一种环保墙体保温材料，由下列重量(kg)的组分原料制备而成：
改性氟石膏25，元明粉4，偏硅酸钠2，麦饭石粉25，玻璃微珠15，硅酸盐水泥90，牛脂胺聚氧乙烯醚1.5，膨胀蛭石70，磺酸乙基纤维素2，苯丙乳液12，皂苷1.5；
其中，改性氟石膏由下列重量(kg)的原料制成：
氟石膏30，三乙醇胺3，酒石酸2，酒石酸氢钾3，十六烷基三甲基溴化铵0.6，生石灰12；
改性氟石膏的制备方法：
将氟石膏250℃处理1h，洗涤过滤后烘干，加入生石灰，混合均匀后700℃煅烧4h，加入适量水，200r/min搅拌15min，过滤后洗涤至pH中性，加入三乙醇胺、十六烷基三甲基溴化铵、酒石酸和酒石酸氢钾，加热至80℃，200r/min搅拌2h，真空干燥后研磨，过100目筛，即得。
环保墙体保温材料的制备方法包括以下步骤：
(1)将苯丙乳液、皂苷和牛脂胺聚氧乙烯醚混合后60℃、800r/min搅拌15min，喷雾干燥后得活性粉体；
(2)将元明粉、麦饭石粉和磺酸乙基纤维素混合后200℃处理2h，研磨均匀，过200目筛，与活性粉体以及其余原料混合，200r/min搅拌2h，分装后即得。实施例为干粉材料，使用时需在施工现场加水调制成料浆，即可施工。
依据DB34/T1279-2010标准进行产品性能测试，上述实施的测试结果如下：
表观干密度(kg/m3)：268；
体积收缩率(％)：0.12；
抗压强度(MPa)：0.92；
粘结强度(KPa)：98；
导热系数(w/m﹒k)：0.049；
软化系数：0.81。

Claims (2)

1.一种环保墙体保温材料，其特征在于，其是由下述重量份的原料制得：改性氟石膏15-30，元明粉2-5，偏硅酸钠1-3，麦饭石粉20-30，玻璃微珠10-20，硅酸盐水泥80-100，牛脂胺聚氧乙烯醚1-2，膨胀蛭石60-80，磺酸乙基纤维素1-3，苯丙乳液10-15，皂苷1-2；所述改性氟石膏由下列重量份的原料制成：氟石膏20-40，三乙醇胺2-4，酒石酸1-3，酒石酸氢钾2-4，十六烷基三甲基溴化铵0.5-1，生石灰10-15；所述改性氟石膏的制备方法是：将氟石膏200-300℃处理1-2h，洗涤过滤后烘干，加入生石灰，混合均匀后600-800℃煅烧3-5h，加入适量水，200-300r/min搅拌15-30min，过滤后洗涤至pH中性，加入三乙醇胺、十六烷基三甲基溴化铵、酒石酸和酒石酸氢钾，加热至75-85℃，200-300r/min搅拌1-2h，真空干燥后研磨，过100-200目筛，即得。
2.根据权利要求1所述的一种环保墙体保温材料的制备方法，其特征在于，包括以下步骤：
（1）将苯丙乳液、皂苷和牛脂胺聚氧乙烯醚混合后40-60℃、800-1000r/min搅拌15-30min，喷雾干燥后得活性粉体；
（2）将元明粉、麦饭石粉和磺酸乙基纤维素混合后200-300℃处理1-2h，研磨均匀，过200-300目筛，与活性粉体以及其余原料混合，200-300r/min搅拌1-2h，分装后即得。
CN201410436210.5A 2014-08-29 2014-08-29 一种环保墙体保温材料及其制备方法 Expired - Fee Related CN104261779B (zh)