CN104261737A - 一种掺加陶瓷废渣的湿拌砂浆及其制备方法 - Google Patents
一种掺加陶瓷废渣的湿拌砂浆及其制备方法 Download PDFInfo
- Publication number
- CN104261737A CN104261737A CN201410476238.1A CN201410476238A CN104261737A CN 104261737 A CN104261737 A CN 104261737A CN 201410476238 A CN201410476238 A CN 201410476238A CN 104261737 A CN104261737 A CN 104261737A
- Authority
- CN
- China
- Prior art keywords
- ceramic waste
- waste residue
- water
- wet
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种掺加陶瓷废渣的湿拌砂浆及其制备方法,所述掺加陶瓷废渣的湿拌砂浆,以质量百分比计,由下列组分配比组成:水泥8.2~20%,砂子65~72%,陶瓷废渣3.24~8.64%,羟乙基甲基纤维素醚0.01~0.1%,葡萄糖酸钠0~0.25%,十二烷基苯磺酸钠0.01~0.02%,水12~15%。所述掺加陶瓷废渣的湿拌砂浆的羟乙基甲基纤维素醚掺量低,成本低,实现了废物综合利用。
Description
技术领域
本发明涉及湿拌砂浆生产技术领域,尤其涉及一种掺加陶瓷废渣的湿拌砂浆及其制备方法。
背景技术
湿拌砂浆是由水泥、砂、外加剂和水,按一定比例,在搅拌站经计量、拌制后,运至使用地点,并在规定时间内使用的拌合物。陶瓷废渣是指生产陶瓷过程中打磨抛光环节中产生的废渣、经烘干筛分得到的粉末。本发明涉及掺加陶瓷废渣的湿拌砂浆及其制备方法,其特点是:在湿拌砂浆制备过程中,加入适当比例的陶瓷废渣,由于陶瓷废渣比表面积大,吸附能力与保水能力强,因此,既可以减少湿拌砂浆保水外加剂的用量,又可以对废渣进行综合利用。本发明既解决了废渣堆放场地、环境污染等问题,又生产出质量好、性能稳定的湿拌砂浆,应用于建筑工程领域,具有重要社会意义和经济效益。
发明内容
本发明的目的在于提供一种掺加陶瓷废渣、质量好、性能稳定、成本低的湿拌砂浆及其制备方法。
本发明的目的通过以下技术方案予以实现:
一种掺加陶瓷废渣的湿拌砂浆,以质量百分比计,由下列组分配比组成:
水泥 8.2~20%,
砂子 65~72%,
陶瓷废渣 3.24~8.64%,
羟乙基甲基纤维素醚 0.01~0.1%,
葡萄糖酸钠 0~0.25%,
十二烷基苯磺酸钠 0.01~0.02%,
水 12~15%。
本发明所述的掺加陶瓷废渣的湿拌砂浆,材料组成包括了水泥、砂子、陶瓷废渣、羟乙基甲基纤维素醚、葡萄糖酸钠和十二烷基苯磺酸钠。葡萄糖酸钠由于吸附作用,其分子中的羟基在水泥粒子表面阻碍水泥水化过程,使晶体相互接触受到屏蔽,使砂浆凝结时间延长。羟乙基甲基纤维素醚含有大量水化性很强的羟基,有良好的溶解性和去水化作用,可大幅度提高湿拌砂浆的保水性,并改善砂浆的工作性。陶瓷废渣具有颗粒小、比表面积大、吸附能力强等特点,在湿拌砂浆加入陶瓷废渣后,能提高砂浆的保水率,改善砂浆的工作性。表面活性剂十二烷基苯磺酸钠具有良好的引气作用,可改善砂浆的工作性能。
本发明所述掺加陶瓷废渣的湿拌砂浆的制备方法,包括如下步骤:
S1.将水注入搅拌容器中,加入葡萄糖酸钠和十二烷基苯磺酸钠,搅拌10~15min,得能延长砂浆凝结时间的有引气作用的缓凝剂;
S2.将水注入另一搅拌容器中,加入羟乙基甲基纤维素醚,搅拌10~15min,得能改善砂浆保水性添加剂;
S3.将陶瓷废渣在105℃温度下烘干后,用200目筛子筛分;
S4.将水泥、砂子、陶瓷废渣、有引气作用的缓凝剂、保水性添加剂加水混合强制搅拌1.5~3.0min,得到性能稳定、成本低的湿拌砂浆。
与现有技术相比,本发明具有如下有益效果:
1.羟乙基甲基纤维素醚掺量低;配制湿拌砂浆的羟乙基甲基纤维素醚掺加量为0.1%以下。
2.成本低;陶瓷废渣是一种工业废渣,能部分替代羟乙基甲基纤维素醚,降低了湿拌砂浆的成本;每立方米的湿拌砂浆的成本降低5~15元。
3.实现了废物综合利用,保护环境。
具体实施方式
下面结合具体实施例对本发明作出进一步地详细阐述,但实施例并不对本发明做任何形式的限定。
实施例1
一种掺加陶瓷废渣、强度等级为M5的湿拌砂浆,以质量百分比计,由下列组分配比组成:
水泥 9.73%,
砂子 69.32%,
陶瓷废渣 8.64%,
羟乙基甲基纤维素醚 0.05%,
葡萄糖酸钠 0.25%,
十二烷基苯磺酸钠 0.01%,
水12%。
所述掺加陶瓷废渣的湿拌砂浆的制备方法,包括如下步骤:
S1.将水注入搅拌容器中,加入葡萄糖酸钠和十二烷基苯磺酸钠,搅拌10~15min,得能延长砂浆凝结时间的有引气作用的缓凝剂;
S2.将水注入另一搅拌容器中,加入羟乙基甲基纤维素醚,搅拌10~15min,得能改善砂浆保水性添加剂;
S3.将陶瓷废渣在105℃温度下烘干后,用200目筛子筛分;
S4.将水泥、砂子、陶瓷废渣、有引气作用的缓凝剂、保水性添加剂加水混合强制搅拌1.5~3.0min,得到性能稳定、成本低的湿拌砂浆。
实施例2
除了掺加陶瓷废渣的湿拌砂浆各组分百分比不同外,其他条件同实施例1;
一种掺加陶瓷废渣、强度等级为M10的湿拌砂浆,以质量百分比计,由下列组分配比组成:
水泥 11.35%,
砂子 68.21%,
陶瓷废渣 8.22%,
羟乙基甲基纤维素醚 0.1%,
葡萄糖酸钠 0.2%,
十二烷基苯磺酸钠 0.01%,
水 12%。
实施例3
除了掺加陶瓷废渣的湿拌砂浆各组分百分比不同外,其他条件同实施例1;
一种掺加陶瓷废渣、强度等级为M15的湿拌砂浆,以质量百分比计,由下列组分配比组成:
水泥 13.51%,
砂子 69.36%,
陶瓷废渣 4.86%,
羟乙基甲基纤维素醚 0.1%,
葡萄糖酸钠 0.25%,
十二烷基苯磺酸钠 0.01%,
水 12%。
实施例4
除了掺加陶瓷废渣的湿拌砂浆各组分百分比不同外,其他条件同实施例1;
一种掺加陶瓷废渣、强度等级为M20的湿拌砂浆,以质量百分比计,由下列组分配比组成:
水泥 17.72%,
砂子 66.77%,
陶瓷废渣 3.24%,
羟乙基甲基纤维素醚 0.01%,
葡萄糖酸钠 0.25%,
十二烷基苯磺酸钠 0.01%,
水 12%。
Claims (2)
1.一种掺加陶瓷废渣的湿拌砂浆,其特征在于:以质量百分比计,由下列组分配比组成:
水泥 8.2~20%,
砂子 65~72%,
陶瓷废渣 3.24~8.64%,
羟乙基甲基纤维素醚 0.01~0.1%,
葡萄糖酸钠 0~0.25%,
十二烷基苯磺酸钠 0.01~0.02%,
水 12~15%。
2.根据权利要求1所述掺加陶瓷废渣的湿拌砂浆的制备方法,其特征在于,包括如下步骤:
S1.将水注入搅拌容器中,加入葡萄糖酸钠和十二烷基苯磺酸钠,搅拌10~15min,得能延长砂浆凝结时间的有引气作用的缓凝剂;
S2.将水注入另一搅拌容器中,加入羟乙基甲基纤维素醚,搅拌10~15min,得能改善砂浆保水性添加剂;
S3.将陶瓷废渣在105℃温度下烘干后,用200目筛子筛分;
S4.将水泥、砂子、陶瓷废渣、有引气作用的缓凝剂、保水性添加剂加水混合强制搅拌1.5~3.0min,得到性能稳定、成本低的湿拌砂浆。