CN100336767C - 一种自密实高强砂浆 - Google Patents
一种自密实高强砂浆 Download PDFInfo
- Publication number
- CN100336767C CN100336767C CNB2006100272020A CN200610027202A CN100336767C CN 100336767 C CN100336767 C CN 100336767C CN B2006100272020 A CNB2006100272020 A CN B2006100272020A CN 200610027202 A CN200610027202 A CN 200610027202A CN 100336767 C CN100336767 C CN 100336767C
- Authority
- CN
- China
- Prior art keywords
- cement
- present
- mortar
- high strength
- strength mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于建筑材料技术领域,具体涉及一种自密实高强砂浆。由水泥、石粉、硅灰、膨胀剂、减水剂按一定配比组合而成。所述水泥为硅酸盐水泥或普通硅酸盐之一种,石粉为双飞粉,减水剂为聚羧酸盐减水剂。本发明通过采用新型减水剂,使得砂浆的流动度经时损失很小,2小时内的流动度基本保持不变,28d抗压强度高达70~90MPa以上,提高了施工的便利性。本发明用硅酸盐水泥或普通硅酸盐水泥和黄砂配制了高强度砂浆,大大降低了生产成本,便于大量使用。本发明制备方法简单、应用广泛。
Description
技术领域
本发明属于建筑材料技术领域,具体涉及一种自密实高强砂浆,可以用作灌浆料。
背景技术
近年来,密筋配置的钢筋混凝土结构的应用越来越多,由于钢筋间距很小,浇筑这样的混凝土结构不便于振捣,需要使用有自密实功能的混凝土,因此,全世界自密实混凝土的应用增长迅速。在钢混结构连续桥梁的剪力钉预留孔处,钢筋与剪力钉交织,钢筋间距更小,最小钢筋间距可能不到15mm。按照钢筋混凝土对骨料最大粒径小于最小钢筋间距3/4的要求(可以振捣的情况),最大骨料粒径应该小于11mm。在钢筋间距这样小、不能振捣的情况下,直接使用无粗骨料的自密实砂浆更为合适。
自密实砂浆也可以称之为灌浆料,灌浆料在工业设备安装的二次灌浆中已经有广泛的应用。但是,这些灌浆料往往使用特殊水泥和特殊细骨料,价格比较贵;另一方面,这些灌浆料往往流动度损失很快,要求随拌随用,更不适合较大批量的混合和输送。
发明内容
本发明的目的在于提出一种具有补偿收缩或微膨胀功能,而且价格低廉的砂浆,可以用于钢混桥梁预留孔浇筑的自密实高强砂浆。
本发明提出的自密实高强砂浆,由水泥、石粉、硅灰、膨胀剂、黄砂、减水剂和水组成,各组分的重量百分比为:
组分 重量百分比
水泥 20%~30%
石粉 8%~12%
硅灰 1.2%~2.1%
UEA膨胀剂 2%~4.5%
直径为2.5mm黄砂 32%~48%
减水剂 0.50%~0.84%
水 6.8%~13.6%,
其总量满足100%。
本发明中,所述水泥为硅酸盐水泥或普通硅酸盐水泥之一种。
本发明中,所述石粉为双飞粉,或称为重质碳酸钙,或称为方解石粉,细度为300目。
本发明中,所述减水剂为聚羧酸盐减水剂。
本发明的制备方法可以分为以下2种:
(1)临时配制法:按比例准确称取原料,将减水剂与水混合备用,将黄砂、水泥、石粉、硅灰和UEA膨胀剂加入混合机,干搅拌1-3分钟,然后将掺有减水剂的水加入到搅拌机内,搅拌2~4分钟,即得所需产品。临时配制法适合于大批量使用的情形,既可以现场配制,也可以通过工厂配制后运往工地使用(运输距离小于1小时)。
(2)预制干混砂浆法:按比例准确称取原料,将黄砂需经过干燥处理,然后将黄砂、水泥、石粉、硅灰和UEA膨胀剂加入混合机中,搅拌10~20分钟,制成干混料,按照一定规格进行定量包装,包装须具有防潮功能。在使用现场,将干混料、水、减水剂按比例混合搅拌机中,用电动搅拌机混合均匀,即得所需产品。
本发明相对于市场的灌浆料,价格低廉,使用方便,便于较大批量混合、输送;如果需要,也可以做成双包装预混料,在现场拌合以后在使用。
本发明经有关部门检测,(参见JGJ56-84“混凝土减水剂质量标准和试验方法”中的附录B水泥净浆流动度测定方法),其流动度大于20cm,2小时内流动度基本没有损失,28d抗压强度高达70~90MPa以上的自密实砂浆。
本发明具有如下的优点:
1、由于本发明的自密实砂浆具有较高的流动性,无需振捣,可直接浇筑成型,而且流动度经时损失小(2小时内的流动度基本保持不变),砂浆强度高达70~90MPa,特别适合于密配筋的钢筋混凝土结构。
2、由于本发明采用了硅酸盐水泥和普通硅酸盐水泥以及普通的黄砂,大大降低了砂浆的成本。
3、由于本发明的原材料全部采用大量生产的市售成品,所以原材料易得,适合于广泛应用。
具体实施方式
以下结合实施例对本发明的技术方案作进一步描述。所有试样成型都没有插实或振捣,只需刮平表面即可。
实施例1:使用普通硅酸盐水泥配制的自密实高强砂浆。原材料及规格见表1,材料配比及性能见表2。
表1
材料 | 规格或牌号 | 来源 |
水泥 | PO42.5普硅硅酸盐水泥 | 上海海豹水泥集团 |
硅灰 | EM920U | 埃肯国际贸易上海有限公司 |
石粉 | 双飞粉,冰封牌 | 长兴李家巷丰华微粉厂 |
膨胀剂 | UEA | 上海纽曼新型建材厂 |
黄砂 | 过2.5mm筛 | 普通黄砂 |
减水剂 | PC新型混凝土高效减水剂;pH值中性;固含量40%;粘度(涂-4杯)40s | 上海澳申建筑化学科技有限公司 |
表2 使用普通硅酸盐水泥配制的自密实高强砂浆及其比较例
项目 | 配比1 | 比较例 | |
材料用量重量百分比% | 水泥 | 22.3 | 25 |
石粉 | 12 | 0 | |
硅灰 | 1.2 | 0 | |
UEA膨胀剂 | 3 | 0 | |
黄砂 | 48 | 75 | |
减水剂 | 0.5 | 0 | |
水 | 13 | 12.5 | |
性能 | 流动度(2小时)/cm | 22(21) | 跳桌流动度16 |
抗压强度/MPa | 71 | 54 | |
抗折强度/ | 12 | 9 | |
28d尺寸变化率/% | 0.01 | 0.01 |
实施例2:使用硅酸盐水泥配制的自密实高强砂浆,所用材料规格及生产厂家见表3,材料配比和性能见表4。
表3
材料 | 规格或牌号 | 来源 |
水泥 | PII 52.5R | 嘉新京阳水泥 |
硅灰 | EM920U | 埃肯国际贸易上海有限公司 |
石粉 | 双飞粉 | 上海石粉厂 |
膨胀剂 | UEA | 上海纽曼新型建材厂 |
黄砂 | 过2.5mm筛 | 普通黄砂 |
减水剂 | GLENIUM SP-8CN | 上海麦斯特建材有限公司 |
表4 使用硅酸盐水泥配制的自密实高强砂浆及其比较例
项目 | 配比2 | 比较例 | |
材料用量重量百分比% | 水泥 | 30 | 25 |
石粉 | 12 | 0 | |
硅灰 | 2 | 0 | |
UEA膨胀剂 | 3 | 0 | |
黄砂 | 40.59 | 75 | |
减水剂 | 0.81 | 0 | |
水 | 11.6 | 12.5 | |
性能 | 流动度(2小时)/cm | 21(21) | 跳桌流动度16 |
抗压强度/MPa | 85 | 58 | |
抗折强度/ | 13 | 10 | |
28d尺寸变化率/% | 0.02 | 0.01 |
实施例3:使用普通硅酸盐水泥,按照预制干混砂浆法配制自密实高强砂浆。原材料规格见表5,干粉配比见表6。
表5
材料 | 规格或牌号 | 来源 |
水泥 | PO42.5 | 上海水泥厂 |
硅灰 | EM920U | 埃肯国际贸易上海有限公司 |
石粉 | 双飞粉 | 上海石粉厂 |
膨胀剂 | UEA | 上海华联外加剂厂 |
黄砂 | 过2.5mm筛 | 普通黄砂,烘干 |
减水剂 | GLENIUM SP-8CN | 上海麦斯特建材有限公司 |
表6 使用硅酸盐水泥配制的自密实高强砂浆的干粉配比
材料 | 用量重量百分比% | 备注 |
水泥 | 30 | 所有干燥组分预先混合均匀成为干粉 |
石粉 | 12 | |
硅灰 | 2.1 | |
UEA膨胀剂 | 4.5 | |
黄砂 | 38.9 |
水 | 10.4 | |
减水剂 | 0.84 |
将干粉、水、减水剂加入搅拌机中,用电动搅拌机混合均匀,然后浇筑试样。砂浆性能见表7。
表7
性能项目 | 数值 |
流动度(2小时)/cm | 23(22) |
抗压强度/MPa | 92 |
抗折强度/ | 13.5 |
28d尺寸变化率/% | 0.02 |
Claims (4)
1、一种自密实高强砂浆,其特征在于由水泥、石粉、硅灰、膨胀剂、黄砂、减水剂和水组成,各组分的重量百分比为:
组分 重量百分比
水泥 20%~30%
石粉 8%~12%
硅灰 1.2%~2.1%
UEA膨胀剂 2%~4.5%
直径为2.5mm黄砂 32%~48%
减水剂 0.50%~0.84%
水 6.8%~13.6%,
其总量满足100%。
2、根据权利要求1所述的自密实高强砂浆,其特征在于所述水泥为硅酸盐水泥或普通硅酸盐水泥之一种。
3、根据权利要求1所述的自密实高强砂浆,其特征在于所述石粉为双飞粉,细度为300目。
4、根据权利要求1所述的自密实高强砂浆,其特征在于所述减水剂为聚羧酸盐减水剂。