CN104250677B - 热成形且加压淬火的纵梁 - Google Patents
热成形且加压淬火的纵梁 Download PDFInfo
- Publication number
- CN104250677B CN104250677B CN201410283021.9A CN201410283021A CN104250677B CN 104250677 B CN104250677 B CN 104250677B CN 201410283021 A CN201410283021 A CN 201410283021A CN 104250677 B CN104250677 B CN 104250677B
- Authority
- CN
- China
- Prior art keywords
- region
- longeron
- class
- longeron according
- kind region
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种热成形且加压淬火的纵梁。该纵梁通过热成形以及加压淬火制成,该纵梁(1)在加压淬火之后具有至少两个不同强度的区域。第一类区域(2)具有主要为贝氏体的组织,第二类区域(3)具有主要为马氏体的组织,在第一类区域(2)和第二类区域(3)之间的过渡区域(4)小于30mm,所述第一类区域(2)构造在纵梁(1)的、在碰撞情况下应受到特别强的变形和/或应通过变形卸除碰撞能量的区域中,所述第一类区域(2)具有10~30%之间的延伸性能A50,在过渡区域(4)中的屈服极限和/或抗拉强度以每10mm大于100N/mm2的梯度递减或递增,所述第二类区域(3)具有大于1000N/mm2的强度。
Description
本申请是申请号为201110310458.3、申请日为2011年10月14日、发明名称为“热成形且加压淬火的纵梁及其制造方法”的发明专利申请的分案申请。
技术领域
本发明涉及一种通过热成形以及加压淬火制造的纵梁。
背景技术
在汽车制造中,基于法律的和针对制造商的规定,对汽车安全性的要求越来越高。同时,汽车制造商还致力于在燃料消耗以及CO2排放最小化的同时减小汽车车身自重。这在低自重和高抗弯和抗扭刚度以及高碰撞安全性之间构成矛盾。
一种途径例如是使用轻金属材料、尤其是铝合金,或使用例如由金属合金以及纤维复合材料或塑料构成的混合结构方式的车身。但上述两种方案均造成高材料成本,这又在汽车制造中提高了制造成本。
但金属合金、尤其是钢材料始终是用于车身制造、尤其是白车身制造的优选材料。此外,通过持续的发展,钢材料在当今仍然被当作高科技材料,其通过各种不同的方法途径能够在有利制造性、良好碰撞安全性和长寿命之间形成良好的折衷。
例如DE 10 2005 054 847 B3公开了热成形的且加压淬火的构件,其从模具中取出和在调节到钢的高强度机械特性之后进行有针对性的热处理。尤其对在碰撞情况下受到轴向载荷的结构和/或安全构件而言,按照上述方式制造的构件一方面应为高强度,另一方面应在碰撞情况下形成褶皱,从而能有针对性地卸除碰撞能量。
根据现有技术,热处理通常在320~400℃之间的温度范围中进行并且几乎不改变在热成形和加压淬火过程中调节出的包括强度值在内的材料特性,但却同时提高了材料的延展性,从而可在碰撞情况下很好地形成褶皱。
但附加的热处理又引起较高的制造费用,因为用于大规模生产开始时的工具成本大大增加。
发明内容
因此,本发明的任务是提供一种用于设置在汽车上的纵梁,其相对于现有技术具有较低的制造成本,同时可在纵梁内部符合目的地调节出材料特性。
上述任务根据本发明借助一种纵梁得以解决,其通过热成形以及加压淬火制成,该纵梁在加压淬火之后具有至少两个不同强度的区域,其中,第一类区域具有主要为贝氏体的组织,第二类区域具有主要为马氏体的组织,在第一类区域和第二类区域之间的过渡区域小于30mm,所述第一类区域构造在纵梁的、在碰撞情况下应受到特别强的变形和/或应通过变形卸除碰撞能量的区域中,所述第一类区域具有10~30%之间的延伸性能A50,在过渡区域中的屈服极限和/或抗拉强度以每10mm大于100N/mm2的梯度递减或递增,所述第二类区域具有大于1000N/mm2的强度。
在本申请中还包括一种用于制造纵梁的方法,其中,纵梁具有至少两个不同硬度的区域,所述方法具有下述方法特征:提供可淬火的金属板坯或者说半成品,将该金属板坯或者说半成品至少加热到奥氏体化温度;中间冷却金属板坯或者说半成品的第一类区域,冷却速度选择得大于该金属板坯或者说半成品的材料的下临界冷却速度;在加压淬火工具中将金属板坯或者说半成品热成形且加压淬火成纵梁。
按本发明的纵梁通过热成形以及加压淬火来制造,其中,纵梁通过本来的制造过程,即在加压淬火之后,具有至少两个不同强度的区域。第一类区域主要具有贝氏体组织并且第二类区域主要具有马氏体组织,在两类区域之间构造过渡区域,该过渡区域在小于30mm的距离上延伸。
过渡区域构造得小于30mm并且尤其是小于20mm。通过极小的过渡区域在本发明的范畴中可以在一个制造步骤中、即在制造方法本身中有针对性地对构件进行调节,使得在考虑到出现的制造误差的情况下,在有利制造性的同时可靠地形成要求的碰撞特性。
有利地在根据本发明的纵梁中可过程安全且有针对性地在预先定义的第一类和第二类区域中形成一定的材料特性。在由高强度的可淬火的钢构成的金属板坯或预成形坯料或者说半成品的热成形和加压淬火期间将第一类区域中间冷却,使得第一类区域和第二类区域有针对性地形成不同的强度、硬度和延展特性。与第二类区域相反,在第一类区域中产生趋于延展性的材料组织。两类区域彼此间的过渡区域趋于明确限定。由此在很大程度上降低或避免了制造误差。通过第一类区域中主要为贝氏体的组织产生具有延展的材料特性的区域。
第一类区域利于希望的变形,使得在碰撞情况下在此可形成褶皱亦或压缩,而不形成裂纹或发生断裂。由此在强度仍高的同时提升了根据本发明的纵梁的能量吸收性能。因此,在安装了根据本发明的纵梁的汽车中大量能量被吸收,使得碰撞的动能可转化为变形能量,同时保持汽车车身其余部分的高刚度。
此外可想到将纵梁用作发动机支座亦或用于后备箱区域中。此处在必要时需要比在乘客车厢本身的区域中更高的能量吸收性能。通过有针对性地形成第一类区域和第二类区域例如能够在根据本发明的纵梁中形成第一类区域和第二类区域在纵梁的长度上沿车辆方向的依次排列,其优点在于纵梁在碰撞情况下能够呈手风琴状地折叠。
本发明的纵梁在汽车车身中例如横向地设置在前侧和/或后侧,以便有针对性地拦截冲撞的物体或另一汽车。纵梁在此应这样尽可能地拦截冲撞到汽车上的物体或被汽车撞上的固定物体,使得纵梁尽可能小地变形以便吸收能量且有针对性地防止物体侵入汽车本身中。
因此,在根据本发明的纵梁中,能量吸收性能整体上提高,这又使汽车车身的整体能量吸收性能得到提高,同时保持高刚度。而且在较高延展性的区域中可基于例如较薄的壁厚而实现材料节省,这又降低了汽车车身的整体重量。因此,在安装了根据本发明的纵梁的汽车中大量能量被吸收,使得冲撞的动能转化为变形能量,同时至少保持乘客车厢的高刚度亦或乘客车厢和由此车身的提高的刚度。
根据本发明的纵梁的另一优点在于,通过有针对性地在根据本发明的热成形和加压淬火之后构造为第二类区域的区域避免不希望的屈服。第二类区域的高硬度由此避免在特定区域中出现不希望的变形。
在结合高硬度的情况下同样也避免了材料基于高持续负荷振动和/或震动而减弱。纵梁的其余组成部分、即第二区域主要具有强度值特别高的马氏体组织,由此足够满足构件的最低要求的强度和碰撞特性。
按本发明制造的纵梁因此可相对于借助现有技术中已知的制造方法制造的构件低成本地制造,因为仅需一个成形和加压淬火过程来形成要求的最重要的构件特性。通过形成主要是马氏体的组织和主要由贝氏体组织构成的中间组织,在此允许在构件的明确限定的区域中特别不易产生缺陷地、有针对性地形成要求的材料特性。
按本发明,具有马氏体组织作为主要组织成分的第二类区域的特点在于,马氏体组织大于50%、尤其是大于80%、优选大于90%并且特别优选大于95%,其它组织成分小于50%、优选小于30%,并且尤其是小于15%。
马氏体组织的高抗扭刚度和抗弯刚度确保本发明纵梁的高硬度,这例如在倾翻的情况下或类似的碰撞作用下尽可能好地维持乘客车厢并且由此尽可能好地保护乘客。
但在本发明的范畴中,在第二类区域中也可以存在贝氏体作为其它组织成分。
在本发明的范畴中,第一类区域具有贝氏体作为主要组织成分,其它组织成分小于50%、优选小于30%、尤其是小于15%。在此例如存在由贝氏体与铁素体和/或珠光体构成的混合组织。在本发明的范畴中,必要时在第一类区域中也可存在马氏体作为组织成分。
作为替换方案,第一类区域在此至少部分地被第二类区域包围、特别优选第一类区域被第二类区域完全包围。在用于例如碰撞吸能盒的连接点的区域中,第一区域优选被第二区域完全包围。由于按本发明的特别小的过渡区域在构件方向上仍得到刚度,由此基本上不产生例如以不希望的理论弯折点形式的薄弱部位。但第一类区域也可构造成延展性的,以便最大程度地避免裂纹形成。通过第一类区域的延展性最大程度地避免了连接纵梁或其它耦联部件的连接处因为受到例如偏置碰撞而断裂。
为此特别优选将第一类区域构造成点状、优选具有小于40mm、尤其是小于20mm并且特别优选小于10mm的直径。
在本发明的范畴中,所述第一类区域可构造成用于其它构件在纵梁上的耦联点。
在本发明的范畴中,所述第一类区域可以比第二类区域具有提高的壁厚。
在本发明的范畴中,在第一类区域中也可形成贯穿部。这表示,在成形过程和/或加压淬火过程期间可同时形成贯穿部、或特别优选可以在加压淬火过程结束之后形成贯穿部。在此,由于延展性较高,形成对冲孔或冲压工具而言较小的工具磨损,或者说在无裂纹产生的情况下可以形成贯穿部。
在本发明的范畴中有利地规定:将边缘区域、尤其是凹部和法兰构造为第一类区域,由此可有效地避免从边缘开始裂开。在加压淬火后进行机械加工如调整的区域也适合构造为第一类区域。
此外在本发明的范畴中,第一类区域还可设置为用于形成切边的区域。为了在热成形和加压淬火后例如以简单的切割或者说分割方法有利地进行冷裁切,在此准备该材料的对切割或者说分割工具来说磨损小的初始状态。在高的公差要求下,构件的进一步加工例如裁切在此可特别完好、精确且低成本地进行。尤其是无需使用激光对通常来说坚硬的构件边缘进行切割。此外可以特别有利地构造环绕的、窄的且接近最终轮廓的第二类区域。同时大大降低由硬的组织中的局部应力引起的迟后形成裂纹的危险。
在本发明的范畴中,第一类区域具有10~30%之间、优选14~20%之间、尤其优选12~20%之间并且尤其是12~16%之间、特别优选14~16%之间的延展能力A50由此在确保足够的延展性的同时也确保足够高的强度,从而在碰撞情况下可避免裂纹形成和由此各个汽车结构元件的断裂。
此外特别优选第一类区域具有500~1000N/mm2之间、优选550~800N/mm2之间的抗拉强度。第一类区域具有200~800N/mm2之间、优选250~600N/mm2之间、特别优选250~500N/mm2、极其优选300~500N/mm2之间的屈服极限。
在第二类区域和第一类区域之间优选屈服极限和/或抗拉强度以每10mm大于100N/mm2、优选大于200N/mm2并且尤其是大于400N/mm2的梯度递减或递增。这表示,屈服极限和/或抗拉强度从第一类区域朝第二类区域的方向每10mm增加大于100N/mm2。
优选第二类区域具有大于1000N/mm2、尤其是大于1200N/mm2并且特别优选大于1400N/mm2的强度。
在本发明的范畴中,可以使用拼焊板或连续变截面辊轧板用于制造纵梁。
按本发明的用于制造热成形且加压淬火的纵梁的方法,其中,纵梁具有至少两个不同强度的区域,规定下述方法特征:提供可淬火的金属板坯或者说半成品,将其至少加热到奥氏体化温度;中间冷却金属板坯或者说半成品的第一类区域,将冷却速度选择得大于该金属板坯或者说半成品的材料的形成贝氏体的下临界冷却速度;在加压淬火工具中将金属板坯或者说半成品热成形且加压淬火为纵梁。
通过本发明的方法,在时间控制和/或温度控制下产生中间阶段组织。该中间阶段组织尤其是在金属板坯的第一类区域中通过中间冷却产生。在本发明的范畴中这样选择中间冷却的冷却速度,使其大于金属板坯的材料形成贝氏体的下临界冷却速度。即冷却速度大于形成贝氏体的下临界冷却速度。尤其是冷却在加压淬火后应该较软的区域,也就是说具有较大延展性的区域。
在本发明的范畴中,原则上构件也可冷预成形为半成品。因此至少部分地预成形由可淬火的金属板坯构成的构件。优选预成形至少匹配最终形状的80%。在冷预成形过程——其例如在室温中进行——之后,接着至少加热到奥氏体化温度、即加热到超过AC3温度。紧接着至少部分地中间冷却第一类区域以及进行本发明方法的后续步骤。
中间冷却的冷却过程在此在将可淬火的金属板坯加热到奥氏体化温度之后进行,但在本发明的范畴中该冷却过程也可在热成形和加压淬火之前或期间进行。尤其当中间冷却的冷却过程在加压淬火期间进行时,在加压工具中设置相应的元件,它们可实现相应的冷却和相应的冷却速度。
如果中间冷却在热成形和加压淬火之前进行,则可以理解生产线带有加热到超过奥氏体化温度的金属板坯的相应的中间转送器。
冷却本身例如可通过自由对流或强制对流、冷却辊、双面或单面的具有绝热支垫的退火板或通过加载冷却介质如水或通过其它相应的冷却装置来进行。在此,冷却既可在固定安装的中间站进行,又可在生产周期中可动的冷却单元中进行。优选冷却速度在中间冷却时处于200K/s(开尔文/秒)~5K/s之间。特别优选设置50K/s的冷却速度。冷却在此优选直接开始于从炉中取出后。由此在第一区域中产生550~900MPa之间的强度值。优选产生大致为700MPa的强度值。
尤其是将第二类区域——金属板坯的不属于第一类区域的任意区域——保持得高于奥氏体化温度。这表示,在金属板坯被至少加热到奥氏体化温度之后保持在相应的高于奥氏体化温度的温度上。这例如可主动地通过外界热源亦或消极地通过相应的绝热来实现。但也可考虑保持高于温度AC1。由此与从AC3的成形相比出现一定的强度损失,但这在多数情况下并不要紧。
在外界热源的情况下,第二类区域中的温度尤其可通过红外灯、加热螺旋管、多孔燃烧器、绝热板或类似的外界热源来保持。在本发明的范畴中,也可选择明显高于奥氏体化温度的温度,由此在加热到高于奥氏体化温度的过程结束后直至加压淬火过程开始之间的时间以及在此进行的冷却这样彼此协调,使得在加压淬火过程开始时第二类区域始终具有至少高于奥氏体化温度的温度。
在本发明的另一种有利的方案中,在中间冷却第一类区域时选择能够获得贝氏体组织的冷却速度,优选冷却到700~400℃之间、优选650~450℃之间并且尤其是650~500℃之间的温度,也优选优选冷却到600~400℃之间、尤其是500℃的温度。在大于相应使用的材料的下临界冷却速度的冷却速度、但高于马氏体起始温度的情况下,在等温保持冷却温度时形成所谓的贝氏体,也被称为中间组织亦或中间阶段。
与现有技术中所公开的形成珠光体或铁素体(珠光体主要通过直接从奥氏体中扩散而形成)的方法相反,在贝氏体中间阶段中由于冷却较快而显著增大了碳在奥氏体中扩散的难度。在大多从晶界开始的贝氏体形成时,小的奥氏体区域转化为畸变的α晶格。因为α晶格中的扩散速度要比γ晶格中大很多,所以在该含过饱和碳的α固溶体中出现小的渗碳体颗粒,冷却越快,渗碳体颗粒越细小。在此产生大致针状结构的贝氏体组织。在此由于硬度随颗粒细度的增加而增大形成颗粒状结构的碳化物。此外,贝氏体组织又区分为上贝氏体和下贝氏体,在上贝氏体中,碳化物结合成较大的缺陷,而在下贝氏体中,碳化物极其细微地分布。
在本发明方法的一种优选的方案中,第一类区域在预定的时间上保持中间冷却的冷却温度、优选大致等温地保持温度。通过该方案可根据时间准确产生具有所要求或者说希望的强度值的贝氏体中间组织。在该方案中,中间冷却主要在第一类区域的材料组织转化为奥氏体亦或直接转化为中间组织的温度上进行。从该冷却温度起,材料组织通过保持等温一段特定的时间进行进一步转化。在奥氏体组织的情况下,材料转化为贝氏体组织。当材料通过选择冷却速度直接被冷却为中间阶段时,则在此已经产生奥氏体和贝氏体的混合组织。通过保持该冷却温度,在一段特定的时间上保持纯贝氏体转化组织范围。第一类区域保持在该温度上的时间越长,则该组织的贝氏体成分越高。
在另一种优选的方案中,冷却到冷却温度的中间组织区域在加压淬火工具本身中由贝氏体组织转化阶段进一步被淬火,使得在第一类区域中产生由马氏体和贝氏体构成的中间组织或由马氏体、贝氏体以及铁素体和/或珠光体构成的混合组织。通过将第一类区域淬火——该区域中的组织具有中间阶段,剩余奥氏体成分在加压淬火时转化为马氏体成分。由此在第一类区域中产生马氏体-贝氏体混合组织。贝氏体成分与马氏体成分的比值在此和第一区域在开始加压淬火过程之前保持在中间阶段中的持续时间有关。
在一种特别优选的方案中,第一类区域这样在一定的时间范围上保持等温,以便使第一类区域完全转化为贝氏体。由此产生与铁素体-珠光体组织相比强度更高的材料组织。尤其是由此可有针对性地避免使延展性最小的珠光体组织。
在本发明的一种特别优选的方案中,中间冷却时的冷却速度选择得大于所使用材料的上临界冷却速度。由此可有针对性地产生奥氏体区域,其接下来在预规定的时间上保持、优选等温保持在一定的温度水平上,使得组织在该保持时间上有针对性地转化为贝氏体。根据所用的保持时间在此可产生部分贝氏体的奥氏体的组织或只有贝氏体的组织。在贝氏体-奥氏体组织的情况下,其通过接下来的加压淬火过程转化为贝氏体-马氏体组织。
在本发明的范畴中,在铁素体和珠光体温度以下保持大致等温是指,主要在700℃、尤其是在600℃、特别优选550℃以下、但在马氏体起始温度以上。在较长时间范围上保持等温可导致温度例如从500℃下降到400℃,但这在本发明的范畴中仍能被看作大致等温。特别优选第一类区域在1~80s的时间范围中保持等温。特别优选将15s设置为保持时间。但这根据具体所用的材料合金来选择。
在本发明方法的另一种优选的方案中,第一类区域的中间冷却在加压淬火工具中进行,优选通过设置在加压淬火工具中的冷却板进行。由此减少了周期和制造成本。尤其是可仅在两个工具步骤中制造具有不同强度区域的汽车构件。首先在炉具中加热并且紧接着仅在一个工具中合并进行中间冷却、热成形和加压淬火。
为本来的加压淬火过程的冷却速度选择至少25K/s的冷却速度。特别优选大于27K/s。但尤其是为本来的加压淬火过程选择更高的冷却速度。加压淬火过程尤其在第一类区域和第二类区域中以相同的冷却速度主要取决于加压淬火工具和工件之间局部的温度梯度来进行。但由于加压淬火过程开始时两类区域中存在不同的温度,所以第一类和第二类区域的冷却速度也可略微不同。
在本发明的方法中特别优选使用可淬火的钢,该钢属于微合金调制钢。其特别是具有下列合金元素作为成分(质量百分比):
在本发明的范畴中,特别优选第一类区域的中间冷却借助集成有冷却板的工具进行。冷却板在此具有600℃以下的固有温度,但该固有温度相对于大于900℃的AC3温度较低。第一类区域可借助冷却板来冷却并且在必要时也可在一段时间上保持等温。这种冷却板例如可基于电热器或通过在背面用烧嘴加热或用热油加热到要求的温度。
在另一种方案中,中间冷却也可通过基本上冷的冷却板进行。所述板的温度大大低于400℃,优选在-100℃~+100℃之间、特别优选在-10℃~+25℃之间。但借助冷的冷却板仅能有限地执行等温保持时间。特别优选将两类冷却板例如也集成到热成形和加压工具中,使得在本来的用炉具加热之后的整个过程仅在一个工具中进行。但在本发明的范畴中,用于实施中间冷却的冷却板也可安装在附加的工具中,由此过程的进行是从加热炉经中间冷却再到本来的热成形和加压淬火工具。该方案的优点在于可将该单独的工具构造为基本上平面的工具,其具有基本上平面的加热板或冷却板。
附图说明
本发明的其它优点、特征、特性和方面由后续说明示意性地给出。这有利于简单地理解本发明。附图如下:
图1示出按本发明的具有第一类区域、过渡区域和第二类区域的纵梁的局部图;
图2示出按本发明的纵梁;
图3示出用于实施本发明方法的ZTU图(时间-温度转化图);
图4示出根据本发明的纵梁组件。
具体实施方式
附图中为相同或相似部件使用相同附图标记,尽管出于简化原因省略了重复的说明。
图1示出纵梁1的局部。在此从周围可看出,在第二类区域3中构造按本发明的第一类区域2。在第一类区域2和第二类区域3之间设置过渡区域4。在第一类区域2中形成趋于延展性的材料组织,在第二类区域3中形成硬的材料组织。在本发明的范畴中,过渡区域4大致具有宽度a,其与第一类区域2相比特别小。
图2示出根据本发明的纵梁1。纵梁1具有加强筋5,空隙6和凹坑7。此外,根据本发明的纵梁1在其边缘区域中具有接合法兰8。加强筋5、空隙6、凹坑7和接合法兰8分别根据要求构造为第一类区域,纵梁1的其余区域相反构造为第二区域。
图3示出示例性的钢的ZTU图,其不限制本发明的范围。图中示出在冷却速度下随温度在材料中产生的不同组织结构。在视图下部区域中示出马氏体形成。在其上方,即在视图中部区域中示出贝氏体形成,并且在贝氏体上方示出珠光体形成或者说铁素体形成。
在此所示的实施例中,示出三条用于不同冷却过程的曲线。曲线K1示出用于按本发明的第一区域的温度曲线,该第一区域首先被加热到超过AC3温度的温度。从该温度起以一定的冷却速度冷却到约520℃的中间温度,该冷却速度在该情况下大于图中所示材料的形成贝氏体的上临界冷却速度oK。在达到中间冷却的约520℃的冷却温度时,第一区域在时间段t1上基本上等温保持在一定的温度上,该温度在此例如由于热辐射、对流或传热形式的散热从约520℃下降到约480℃。因此在中间冷却的时间点Z1上产生奥氏体组织并且在时间点P1上(在第一种方案中的加压淬火的起点)产生贝氏体-奥氏体混合组织。
接下来在第一种方案中从时间点P1开始通过加压淬火过程进行淬火,使得第一区域中的贝氏体-奥氏体混合组织转化为贝氏体-马氏体混合组织。与此并行地,按本发明的第二区域从高于AC3的温度起通过加压淬火进行淬火,从而直接由奥氏体组织产生马氏体组织,为整体概况性起见在此并未详细示出这点。
本发明方法的第二种方案借助第一区域的根据曲线2的冷却过程来示出。曲线2的冷却过程类似于曲线K1的冷却过程,其中从时间点Z2(与Z1相同)起,冷却温度保持更长的时间,使得加压淬火过程开始于时间点P2,因而时间间隔t2大于t1。第一区域中的组织在时间点P2上完全转化为贝氏体并且因此在时间点P2后不再通过冷却速度进行进一步的组织转化。
在本发明的第三种方案中,根据曲线3从高于AC3温度的温度选择一定的冷却速度,使得在中间冷却的冷却过程中直接转化为贝氏体中间组织。在此在第一区域中产生奥氏体-贝氏体中间组织,由此在时间点P3上进行加压淬火过程时在第一区域中该贝氏体-奥氏体混合组织转化为贝氏体-马氏体混合组织。在根据曲线2和3的方案中,第二区域——其在中间冷却期间始终保持在AC3温度之上——通过在加压淬火过程期间的冷却从奥氏体直接转化为马氏体。在根据曲线3的方案中,按本发明总是选择大于相应所用材料的下临界冷却速度uK的温度。
图4示出纵梁组件9,其由纵梁1以及热处理的构件10构成。纵梁1在此在中部区域中构造为第二类区域以及在外部区域中构造为第一类区域。纵梁1和该构件分别在其两个侧面区域通过接合法兰8彼此耦联。纵梁1本身的接合法兰8在此构造为具有更加延展的材料特性的第一类区域。因此在例如受到碰撞发生变形的情况下通过纵梁1本身保证基本刚度。基于更加延展的材料特性避免断裂。这两个构件在耦联位置11中彼此连接。
附图标记列表
1 纵梁
2 第一类区域
3 第二类区域
4 过渡区域
5 加强筋
6 空隙
7 凹坑
8 接合法兰
9 纵梁组件
10 热处理的构件
11 耦联位置
a 宽度
P1 加压淬火起始时间点
P2 加压淬火起始时间点
P3 加压淬火起始时间点
oK 上临界冷却速度
uK 下临界冷却速度
t1 中间冷却温度的保持时间
t2 中间冷却温度的保持时间
Z1 中间冷却的时间点
Z2 中间冷却的时间点
Z3 中间冷却的时间点
K1 曲线1
K2 曲线2
K3 曲线3
Claims (34)
1.纵梁,其通过热成形以及加压淬火制成,该纵梁(1)在加压淬火之后具有至少两个不同强度的区域,其特征在于,第一类区域(2)具有主要为贝氏体的组织,第二类区域(3)具有主要为马氏体的组织,在第一类区域(2)和第二类区域(3)之间的过渡区域(4)小于30mm,所述第一类区域(2)构造在纵梁(1)的、在碰撞情况下应受到特别强的变形和/或应通过变形卸除碰撞能量的区域中,所述第一类区域(2)具有10~30%之间的延伸性能A50,在过渡区域(4)中的屈服极限和/或抗拉强度以每10mm大于100N/mm2的梯度递减或递增,所述第二类区域(3)具有大于1000N/mm2的强度。
2.根据权利要求1所述的纵梁,其特征在于,所述过渡区域(4)小于20mm。
3.根据权利要求1所述的纵梁,其特征在于,第一类区域和第二类区域在纵梁的长度上沿车辆方向依次排列,使得纵梁在碰撞情况下能够呈手风琴状地折叠。
4.根据权利要求2所述的纵梁,其特征在于,第一类区域和第二类区域在纵梁的长度上沿车辆方向依次排列,使得纵梁在碰撞情况下能够呈手风琴状地折叠。
5.根据权利要求1至4之一所述的纵梁,其特征在于,所述第二类区域(3)具有马氏体组织作为主要组织成分,其它组织成分小于50%。
6.根据权利要求5所述的纵梁,其特征在于,所述其它组织成分小于30%。
7.根据权利要求6所述的纵梁,其特征在于,所述其它组织成分小于15%。
8.根据权利要求5所述的纵梁,其特征在于,在所述第二类区域(3)中存在贝氏体作为其它组织成分。
9.根据权利要求1至4之一所述的纵梁,其特征在于,所述第一类区域(2)具有贝氏体作为主要组织成分,其它组织成分小于50%。
10.根据权利要求9所述的纵梁,其特征在于,所述其它组织成分小于30%。
11.根据权利要求10所述的纵梁,其特征在于,所述其它组织成分小于15%。
12.根据权利要求1至4之一所述的纵梁,其特征在于,所述第一类区域(2)被第二类区域(3)至少部分地包围。
13.根据权利要求12所述的纵梁,其特征在于,所述第一类区域(2)被第二类区域(3)完全包围。
14.根据权利要求1至4之一所述的纵梁,其特征在于,所述第一类区域(2)构造成点状的。
15.根据权利要求14所述的纵梁,其特征在于,所述第一类区域(2)具有小于40mm的直径。
16.根据权利要求15所述的纵梁,其特征在于,所述第一类区域(2)具有小于20mm的直径。
17.根据权利要求16所述的纵梁,其特征在于,所述第一类区域(2)具有小于10mm的直径。
18.根据权利要求1至4之一所述的纵梁,其特征在于,所述第一类区域(2)构造成用于其它构件在纵梁(1)上的耦联点。
19.根据权利要求1至4之一所述的纵梁,其特征在于,所述第一类区域(2)比第二类区域(3)具有提高的壁厚。
20.根据权利要求1至4之一所述的纵梁,其特征在于,在所述第一类区域(2)中能形成穿通部和/或在热成形之后能形成倒角。
21.根据权利要求1至4之一所述的纵梁,其特征在于,所述第一类区域(2)具有12~20%之间的延伸性能A50。
22.根据权利要求21所述的纵梁,其特征在于,所述第一类区域(2)具有12~16%之间的延伸性能A50。
23.根据权利要求22所述的纵梁,其特征在于,所述第一类区域(2)具有14~16%之间的延伸性能A50。
24.根据权利要求1至4之一所述的纵梁,其特征在于,所述第一类区域(2)具有500~1000N/mm2之间的抗拉强度。
25.根据权利要求24所述的纵梁,其特征在于,所述第一类区域(2)具有550~800N/mm2之间的抗拉强度。
26.根据权利要求1至4之一所述的纵梁,其特征在于,在过渡区域(4)中的屈服极限和/或抗拉强度以每10mm大于200N/mm2的梯度递减或递增。
27.根据权利要求26所述的纵梁,其特征在于,在过渡区域(4)中的屈服极限和/或抗拉强度以每10mm大于400N/mm2的梯度递减或递增。
28.根据权利要求1至4之一所述的纵梁,其特征在于,所述第二类区域(3)具有大于1200N/mm2的强度。
29.根据权利要求28所述的纵梁,其特征在于,所述第二类区域(3)具有大于1400N/mm2的强度。
30.根据权利要求1至4之一所述的纵梁,其特征在于,所述第一类区域(2)具有200~800N/mm2之间的屈服极限。
31.根据权利要求30所述的纵梁,其特征在于,所述第一类区域(2)具有250~600N/mm2之间的屈服极限。
32.根据权利要求31所述的纵梁,其特征在于,所述第一类区域(2)具有250~500N/mm2之间的屈服极限。
33.根据权利要求32所述的纵梁,其特征在于,所述第一类区域(2)具有300~500N/mm2之间的屈服极限。
34.根据权利要求1至4之一所述的纵梁,其特征在于,使用拼焊板或连续变截面辊轧板用于制造纵梁。