CN104233515A - 一种聚乙烯醇纤维废丝的回收方法 - Google Patents

一种聚乙烯醇纤维废丝的回收方法 Download PDF

Info

Publication number
CN104233515A
CN104233515A CN201410503008.XA CN201410503008A CN104233515A CN 104233515 A CN104233515 A CN 104233515A CN 201410503008 A CN201410503008 A CN 201410503008A CN 104233515 A CN104233515 A CN 104233515A
Authority
CN
China
Prior art keywords
polyvinyl alcohol
vinal
waste silk
waste
alcohol fibers
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410503008.XA
Other languages
English (en)
Other versions
CN104233515B (zh
Inventor
吴福胜
高祖安
田宗杰
王平林
姜家保
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Wanwei Updated High Tech Material Industry Co Ltd
Original Assignee
Anhui Wanwei Updated High Tech Material Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Wanwei Updated High Tech Material Industry Co Ltd filed Critical Anhui Wanwei Updated High Tech Material Industry Co Ltd
Priority to CN201410503008.XA priority Critical patent/CN104233515B/zh
Publication of CN104233515A publication Critical patent/CN104233515A/zh
Application granted granted Critical
Publication of CN104233515B publication Critical patent/CN104233515B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚乙烯醇纤维废丝的回收方法，其特征在于：首先清理聚乙烯醇纤维废丝中的杂物，获得待回收聚乙烯醇纤维废丝；向废丝溶解机中注入温水，然后添加醋酸和硼酸，搅拌至溶解；将待回收聚乙烯醇纤维废丝投加到废丝溶解机中，加温搅拌至待回收聚乙烯醇纤维废丝溶解，获得聚乙烯醇废丝溶液，对其进行过滤，即得回收聚乙烯醇溶液。通过本发明的方法，可以将聚乙烯醇纤维废丝转换为聚乙烯醇溶液，该聚乙烯醇溶液可回用至聚乙烯醇纤维的生产中，使其得到充分有效的利用，节省了原料，降低了聚乙烯醇纤维的生产成本。

Description

一种聚乙烯醇纤维废丝的回收方法
技术领域
本发明涉及聚乙烯醇纤维技术领域，更具体的说，涉及一种用于聚乙烯醇纤维废丝的回收方法。
背景技术
聚乙烯醇纤维是一种用途广泛的有机合成纤维材料，因其具有良好的强度、模量、抗酸碱、易溶解等优良性能，可用于混凝土增强、造纸、纺织、医学等领域。
聚乙烯醇纤维是由聚乙烯醇通过溶解、过滤、脱泡、纺丝、凝固、热处理等工艺制造而成，现多采用凝胶纺丝工艺。
聚乙烯醇纤维在生产过程中会产生一定数量的聚乙烯醇纤维废丝，目前这些聚乙烯醇纤维废丝基本是作为不合格的聚乙烯醇低价处理给黏胶生产企业，造成了原料的浪费，无形中增加了聚乙烯纤维的生产成本。
因此，提供一种聚乙烯醇纤维废丝的回收方法，以降低聚乙烯醇纤维的生产成本是本领域技术人员亟待解决的问题。
发明内容
本发明是为避免上述现有技术所存在的不足之处，提供一种聚乙烯醇纤维废丝的回收方法，将其回用至聚乙烯醇纤维的生产中，以降低聚乙烯醇纤维的生产成本。
为实现上述目的，本发明提供如下技术方案：
本发明聚乙烯醇纤维废丝的回收方法，其特点在于包括如下步骤：
(1)清理聚乙烯醇纤维废丝中的杂物，获得待回收聚乙烯醇纤维废丝；
(2)向废丝溶解机中注入温水，然后添加醋酸和硼酸，搅拌至溶解；
(3)将待回收聚乙烯醇纤维废丝投加到所述废丝溶解机中，加温至98℃，然后搅拌至待回收聚乙烯醇纤维废丝溶解，获得聚乙烯醇废丝溶液；
(4)过滤所述聚乙烯醇废丝溶液中未溶解的固体颗粒物，即得回收聚乙烯醇溶液。
本发明聚乙烯醇纤维废丝的回收方法，其特点也在于：
步骤(2)中温水与醋酸、硼酸的用量比为1100L：1L：2.1Kg；
步骤(3)中待回收聚乙烯醇纤维废丝与步骤(2)中温水的用量比为3～8Kg:22L。
步骤(2)所述温水的温度是40～60℃。
与已有技术相比，本发明的有益效果体现在：
本发明聚乙烯醇纤维废丝的回收方法，包括清理步骤、溶解步骤和过滤步骤，通过本发明的方法，可以将聚乙烯醇纤维废丝转换为聚乙烯醇溶液，该聚乙烯醇溶液可回用至聚乙烯醇纤维的生产中，使其得到充分有效的利用，节省了原料，降低了聚乙烯醇纤维的生产成本。
具体实施方式
下面对本发明的较佳实例进行阐述，以使本发明的优点和特征能更易于被本技术领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本实施例聚乙烯醇纤维废丝的回收方法，具体步骤为：
(1)清理聚乙烯醇纤维废丝中的杂物，包括烧焦丝、尘土等获得待回收聚乙烯醇纤维废丝；
(2)向废丝溶解机中注入50℃温水5500L，然后添加醋酸5L和硼酸10.5Kg，搅拌至溶解；
(3)将1250Kg待回收聚乙烯醇纤维废丝投加到废丝溶解机中，加温至98℃，然后搅拌至待回收聚乙烯醇纤维废丝溶解，获得聚乙烯醇废丝溶液；
(4)使用板框式过滤机过滤聚乙烯醇废丝溶液中未溶解的固体颗粒物，即得回收聚乙烯醇溶液。
所获得的回收聚乙烯醇溶液可重新用于聚乙烯醇纤维的生产，具体方式为：
在回收步骤完成步骤(3)时，取样聚乙烯醇废丝溶液并检测其质量浓度，若浓度不低于15％，则合格，在完成步骤(4)的过滤后，可直接加入至生产聚乙烯醇纤维的聚乙烯醇溶液中，且加入量不超过新聚乙烯醇溶液的10％；若浓度低于15％，则先不进行步骤(4)，而是向其中再投加待回收聚乙烯醇纤维废丝，继续步骤(3)，直至所得聚乙烯醇废丝溶液满足浓度要求。
通过本发明的方法可以将聚乙烯醇纤维废丝转换为聚乙烯醇溶液，该聚乙烯醇溶液回用至聚乙烯醇纤维的生产中，使其得到充分有效的利用，节省了原料，降低了聚乙烯醇纤维的生产成本。
以上所述仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。

Claims (3)

1.一种聚乙烯醇纤维废丝的回收方法，其特征在于包括如下步骤：
(1)清理聚乙烯醇纤维废丝中的杂物，获得待回收聚乙烯醇纤维废丝；
(2)向废丝溶解机中注入温水，然后添加醋酸和硼酸，搅拌至溶解；
(3)将待回收聚乙烯醇纤维废丝投加到所述废丝溶解机中，加温至98℃，然后搅拌至所述待回收聚乙烯醇纤维废丝溶解，获得聚乙烯醇废丝溶液；
(4)过滤所述聚乙烯醇废丝溶液中未溶解的固体颗粒物，即得回收聚乙烯醇溶液。
2.根据权利要求1所述的聚乙烯醇纤维废丝的回收方法，其特征在于：
步骤(2)中温水与醋酸、硼酸的用量比为1100L：1L：2.1Kg；
步骤(3)中待回收聚乙烯醇纤维废丝与步骤(2)中温水的用量比为3～8Kg:22L。
3.根据权利要求1或2所述的聚乙烯醇纤维废丝的回收方法，其特征在于：
步骤(2)所述温水的温度是40～60℃。
CN201410503008.XA 2014-09-26 2014-09-26 一种聚乙烯醇纤维废丝的回收方法 Active CN104233515B (zh)