CN104194640B - 松香增粘树脂的制备方法 - Google Patents

松香增粘树脂的制备方法 Download PDF

Info

Publication number
CN104194640B
CN104194640B CN201410386069.2A CN201410386069A CN104194640B CN 104194640 B CN104194640 B CN 104194640B CN 201410386069 A CN201410386069 A CN 201410386069A CN 104194640 B CN104194640 B CN 104194640B
Authority
CN
China
Prior art keywords
reactor
rosin
tackifying resin
temperature
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410386069.2A
Other languages
English (en)
Other versions
CN104194640A (zh
Inventor
黄桂彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Zhongchang Resin Co Ltd
Original Assignee
Guangxi Zhongchang Resin Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Zhongchang Resin Co Ltd filed Critical Guangxi Zhongchang Resin Co Ltd
Priority to CN201410386069.2A priority Critical patent/CN104194640B/zh
Publication of CN104194640A publication Critical patent/CN104194640A/zh
Application granted granted Critical
Publication of CN104194640B publication Critical patent/CN104194640B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种松香增粘树脂的制备方法，涉及松香加工技术领域，该方法在惰性气体条件下，将马尾松松香投入反应釜中加热熔解，釜内温度升至140℃时，向反应釜内加入丙烯酸、脂肪酸搅拌，在20分钟-40分钟内升温至200℃时，向反应釜加入季戊四醇搅拌均匀，在温度为200℃-250℃下保温3-8小时后，除去低沸点物质，降温出料。本方法制得的树脂产品具有较高软化点，色泽浅，酸值小，产品性能稳定。

Description

松香增粘树脂的制备方法
技术领域
本发明涉及松香加工技术领域，尤其是一种松香增粘树脂的制备方法。
背景技术
松香增粘树脂是对松香进行改性后得到的产品，它被广泛应用于胶粘剂、油墨、涂料等行业，现有的松香增粘树脂的软化点较高，色泽容易变深，产品性能不稳定，会出现黏性下降和粘接失效等问题。
发明内容
本发明的目的是提供一种松香增粘树脂的制备方法，这种方法可以解决现有松香增粘树脂存在软化点高、色泽深和产品性能不稳定的问题。
为了解决上述问题，本发明采用的技术方案是：这种松香增粘树脂的制备方法包括以下步骤：在惰性气体条件下，将马尾松松香投入反应釜中加热熔解，釜内温度升至140℃时，向反应釜内加入丙烯酸、脂肪酸搅拌，在20分钟-40分钟内升温至200℃时，向反应釜加入季戊四醇搅拌均匀，在温度为200℃-250℃下保温3-8小时后，除去低沸点物质，降温出料。
上述松香增粘树脂的制备方法的技术方案中，更具体的技术方案还可以是：在降温出料之前，于200℃-230℃的温度条件下，向反应釜内加入抗氧剂搅拌。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：制得的树脂产品具有较高软化点，色泽浅，酸值小，产品性能稳定。
具体实施方式
下面结合实施例对本发明作进一步详述：
实施例1
本实施例的松香增粘树脂的制备方法是：
在惰性气体条件下，将100克马尾松松香投入反应釜中加热熔解，釜内温度升至140℃时，向反应釜内加入12克丙烯酸、30克脂肪酸搅拌，在20分钟内升温至200℃时，向反应釜加入25克季戊四醇搅拌均匀，在温度为200℃下保温8小时后，除去低沸点物质，在200℃的温度条件下，向反应釜内加入2.5克抗氧剂搅拌，降温出料。
本实施例得到的松香增粘树脂的色号为5号，软化点为99℃，酸值为19。
实施例2
本实施例的松香增粘树脂的制备方法是：
在惰性气体条件下，将100克马尾松松香投入反应釜中加热熔解，釜内温度升至140℃时，向反应釜内加入10克丙烯酸、35克脂肪酸搅拌，在30分钟内升温至200℃时，向反应釜加入22克季戊四醇搅拌均匀，在温度为230℃下保温6小时后，除去低沸点物质，在210℃的温度条件下，向反应釜内加入2.2克抗氧剂搅拌，降温出料。
本实施例得到的松香增粘树脂的色号为5号，软化点为101℃，酸值为18.5。
实施例3
本实施例的松香增粘树脂的制备方法是：
在惰性气体条件下，将100克马尾松松香投入反应釜中加热熔解，釜内温度升至140℃时，向反应釜内加入15克丙烯酸、32克脂肪酸搅拌，在40分钟内升温至200℃时，向反应釜加入22克季戊四醇搅拌均匀，在温度为250℃下保温3小时后，除去低沸点物质，在230℃的温度条件下，向反应釜内加入2.5克抗氧剂搅拌，降温出料。
本实施例得到的松香增粘树脂的色号为4号，软化点为103℃，酸值为18。

Claims (2)

1.一种松香增粘树脂的制备方法，其特征在于包括以下步骤：在惰性气体条件下，将马尾松松香投入反应釜中加热熔解，釜内温度升至140℃时，向反应釜内加入丙烯酸、脂肪酸搅拌，在20分钟-40分钟内升温至200℃时，向反应釜加入季戊四醇搅拌均匀，在温度为200℃-250℃下保温3-8小时后，除去低沸点物质，降温出料。
2.根据权利要求1所述的松香增粘树脂的制备方法，其特征在于：在降温出料之前，于200℃-230℃的温度条件下，向反应釜内加入抗氧剂搅拌。
CN201410386069.2A 2014-08-07 2014-08-07 松香增粘树脂的制备方法 Active CN104194640B (zh)