CN104194090A - 一种耐寒的胶料的制备方法 - Google Patents

一种耐寒的胶料的制备方法 Download PDF

Info

Publication number
CN104194090A
CN104194090A CN201410471867.5A CN201410471867A CN104194090A CN 104194090 A CN104194090 A CN 104194090A CN 201410471867 A CN201410471867 A CN 201410471867A CN 104194090 A CN104194090 A CN 104194090A
Authority
CN
China
Prior art keywords
parts
cold
preparation
sizing material
resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410471867.5A
Other languages
English (en)
Other versions
CN104194090B (zh
Inventor
张勇
林木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Haida Rubber and Plastic Co Ltd
Original Assignee
Jiangyin Haida Rubber and Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Haida Rubber and Plastic Co Ltd filed Critical Jiangyin Haida Rubber and Plastic Co Ltd
Priority to CN201410471867.5A priority Critical patent/CN104194090B/zh
Publication of CN104194090A publication Critical patent/CN104194090A/zh
Application granted granted Critical
Publication of CN104194090B publication Critical patent/CN104194090B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种耐寒的胶料的制备方法，该方法包括：称取下列重量份的原料：基础胶料NBR 1704 100-200份、硫化剂5-20份、促进剂1-10份、防老剂10-20份、补强剂20-30份、增塑剂20-40份和耐寒补充剂5-20份；将上述材料在70℃密炼机中混炼3min，然后升温，混炼温度达到90℃时密炼机排料，即排出混炼胶料，保持XK-160开炼机的辊温为90℃，将上述混炼胶料加入开炼机中，待吃料完毕后，左右割刀各4次，薄通6遍后下片，胶料停放16h后在平板硫化机上硫化，在130℃下硫化20分钟，然后压制成标准实验试片，进行性能检测。经测试，本发明所述方法制得的耐寒胶料具有优良的耐寒性，其制品非常适宜在高寒地区中使用。

Description

一种耐寒的胶料的制备方法
技术领域
本发明涉及橡胶领域，具体的说，本发明涉及一种耐寒的胶料的制备方法。
背景技术
随着工业的发展，橡胶产品已经得到越来越广泛的使用，在高寒地区，由于气温极低，通常会低于零下30℃，因此胶料的耐寒性对于设备的正常使用具有显著的意义。
发明内容
本发明的目的在于提供一种耐寒的胶料的制备方法。
为了实现本发明的目的，本发明提供一种耐寒的胶料的制备方法，该方法包括：称取下列重量份的原料：基础胶料NBR 1704 100-200份、硫化剂5-20份、促进剂1-10份、防老剂10-20份、补强剂20-30份、增塑剂20-40份和耐寒补充剂5-20份；
将上述材料在70℃密炼机中混炼3min，然后升温，混炼温度达到90℃时密炼机排料，即排出混炼胶料，保持XK-160开炼机的辊温为90℃，将上述混炼胶料加入开炼机中，待吃料完毕后，左右割刀各4次，薄通6遍后下片，胶料停放16h后在平板硫化机上硫化，在130℃下硫化20分钟，然后压制成标准实验试片，进行性能检测。
优选地，本发明所述的方法称取下列重量份的原料：基础胶料NBR 1704 100份、硫化剂15份、促进剂5份、防老剂15份、补强剂30份、增塑剂30份和耐寒补充剂10份。
优选地，所述硫化剂为硫化剂DTDM。
优选地，所述促进剂为促进剂NA-22。
优选地，所述防老剂为防老剂NBC。
优选地，所述补强剂为炭黑。
优选地，所述增塑剂为癸二酸二辛酯。
优选地，所述耐寒补充剂为2-(E)-(4-甲磺酰基苯亚甲基)-6-(N-甲基-N-苯基)胺甲基环己酮。
本发明还提供2-(E)-(4-甲磺酰基苯亚甲基)-6-(N-甲基-N-苯基)胺甲基环己酮在用于耐寒胶料的耐寒补充剂中的用途。
经测试，本发明所述的耐寒胶料具有优良的耐寒性，其制品非常适宜在高寒地区中使用。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明，但这并非是对本发明的限制，本领域技术人员根据本发明的基本思想，可以做出各种修改或改进，但是只要不脱离本发明的基本思想，均在本发明的范围之内。
实施例1
称取基础胶料NBR 1704 100公斤、硫化剂DTDM 15公斤、促进剂NA-22 5公斤、防老剂NBC 15公斤、炭黑30公斤、癸二酸二辛酯30公斤和2-(E)-(4-甲磺酰基苯亚甲基)-6-(N-甲基-N-苯基)胺甲基环己酮10公斤；
将上述材料在70℃密炼机中混炼3min，然后升温，混炼温度达到90℃时密炼机排料，即排出混炼胶料，保持XK-160开炼机的辊温为90℃，将上述混炼胶料加入开炼机中，待吃料完毕后，左右割刀各4次，薄通6遍后下片，胶料停放16h后在平板硫化机上硫化，在130℃下硫化20分钟，然后压制成标准实验试片，进行性能检测。
实施例2
按照和实施例1相同的方式制备耐寒的胶料，不同之处在于不使用2-(E)-(4-甲磺酰基苯亚甲基)-6-(N-甲基-N-苯基)胺甲基环己酮。
实验例
根据GB 6034-1985《疏化橡胶压缩耐寒系数的测定》来测试试片的耐寒性。经过测定，实施例1的样品的压缩耐寒系数(-50℃)为0.42，而实施例2的样品的压缩耐寒系数(-50℃)仅为0.16，两者相比结果进行比较，差异具有统计学意义(P＜0.05)。

Claims (8)

1.一种耐寒的胶料的制备方法，该方法包括：
称取下列重量份的原料：基础胶料NBR 1704 100-200份、硫化剂5-20份、促进剂1-10份、防老剂10-20份、补强剂20-30份、增塑剂20-40份和耐寒补充剂5-20份；
将上述材料在70℃密炼机中混炼3min，然后升温，混炼温度达到90℃时密炼机排料，即排出混炼胶料，保持XK-160开炼机的辊温为90℃，将上述混炼胶料加入开炼机中，待吃料完毕后，左右割刀各4次，薄通6遍后下片，胶料停放16h后在平板硫化机上硫化，在130℃下硫化20分钟，然后压制成标准实验试片，进行性能检测。
2.根据权利要求1所述的制备方法，其特征在于，称取下列重量份的原料：基础胶料NBR 1704 100份、硫化剂15份、促进剂5份、防老剂15份、补强剂30份、增塑剂30份和耐寒补充剂10份。
3.根据权利要求2所述的制备方法，其特征在于，所述硫化剂为硫化剂DTDM。
4.根据权利要求2所述的制备方法，其特征在于，所述促进剂为促进剂NA-22。
5.根据权利要求2所述的制备方法，其特征在于，所述防老剂为防老剂NBC。
6.根据权利要求2所述的制备方法，其特征在于，所述补强剂为炭黑。
7.根据权利要求2所述的制备方法，其特征在于，所述增塑剂为癸二酸二辛酯。
8.根据权利要求2所述的制备方法，其特征在于，所述耐寒补充剂为2-(E)-(4-甲磺酰基苯亚甲基)-6-(N-甲基-N-苯基)胺甲基环己酮。
CN201410471867.5A 2014-09-16 2014-09-16 一种耐寒的胶料的制备方法 Expired - Fee Related CN104194090B (zh)