CN104191852A - Ink-jet oil painting canvas and manufacturing method thereof - Google Patents
Ink-jet oil painting canvas and manufacturing method thereof Download PDFInfo
- Publication number
- CN104191852A CN104191852A CN201410438828.5A CN201410438828A CN104191852A CN 104191852 A CN104191852 A CN 104191852A CN 201410438828 A CN201410438828 A CN 201410438828A CN 104191852 A CN104191852 A CN 104191852A
- Authority
- CN
- China
- Prior art keywords
- ink
- parts
- canvas
- jet
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an ink-jet oil painting canvas. The oil painting canvas comprises a base material, a bottom coating layer and a surface coating layer from bottom to top in sequence, wherein the bottom coating layer comprises the following components in parts by weight: 35-45 parts of filler, 1-3 parts of polyvinyl alcohol, 30-40 parts of a bonding agent, 0.5-2 parts of an additive and 10-30 parts of water; the surface coating layer comprises the following components in parts by weight: 10-15 parts of silicon dioxide, 1-3 parts of polyvinyl alcohol, 30-40 parts of a special bonding agent, 0.5-2 parts of an additive, 1-5 parts of an anti-bleeding agent, and 30-50 parts of water. The ink-jet oil painting canvas disclosed by the invention has the advantages that the matching and the bonding strength of the ink-jet oil painting canvas with latex used in Latex ink are good, and when the Latex ink is used for ink-jet printing, the ink can be cured on the surface coating layer at low temperature, and high color fastness can be obtained; simultaneously, the extra anti-bleeding agent is added into the surface coating layer, so that the bleeding of ink can be prevented, the edges of a painting are clear and the color expressiveness is excellent.
Description
Technical field
The present invention relates to color inkjet printing medium field, relate in particular to a kind of ink-jet canvas and preparation method thereof.
Background technology
Inkjet technology be by digitized image by printing of inkjet printer a kind of new digital imaging technique on ink-absorbing medium, have operating procedure simple, without plate-making, non-pollution discharge, have the advantages such as personalized.And ink-jet canvas is as a kind of functional form print media that is rich in artistic characteristics, be widely used in image description dossal, decoration painting, oil painting product imitated etc.Particularly oil painting product is imitated, and because the selling at exorbitant prices of famous-object oil painting allows most people hang back, and the birth of ink-jet canvas has entered ten million average family by the art atmosphere band of famous-object oil painting.
Hewlett-Packard Corporation has developed a kind of novel ink-jet ink Latex ink, this ink environmental protection, imaging is lasting, equipment is without injury, representing one of following inkjet printing direction, but medium is born in its supporting painting canvas class ink-jet, except the ink-jet canvas of the original-pack production of Hewlett-Packard Corporation, ink-jet canvas based on the exploitation of Latex ink is also less on the market, and specific aim and applicability are also poor.
Summary of the invention
Goal of the invention: the invention reside in the defect overcoming in background technology, a kind of ink-jet canvas for Latex ink and preparation method thereof is provided, it is with strong points, and applicability is high.
Technical scheme: a kind of ink-jet canvas, described canvas is followed successively by base material from bottom to up, priming coat and finishing coat, described priming coat is by 35 ~ 45 parts of fillers, 1 ~ 3 part of polyvinyl alcohol, 30 ~ 40 parts, adhesive, 0.5 ~ 2 part of auxiliary agent, 10 ~ 30 parts of compositions of water, described finishing coat is by 0 ~ 15 part of silica 1,1 ~ 3 part of polyvinyl alcohol, 30 ~ 40 parts of adhesive speciallies, 0.5 ~ 2 part of auxiliary agent, 1 ~ 5 part of antiseepage agent, 30 ~ 50 parts of compositions of water.
Described filler is one or more in lithopone, talcum powder, kaolin, calcium carbonate, and fineness 800 ~ 1250 orders.
Described adhesive specially is Vinyl Acetate-Acrylate Copolymer Water-Borne Emulsion, and Tg is-20 ℃.
Described silica is pore type precipitated silica, and particle diameter is 2-10um, and pore volume is 100-300ml/g.
Described polyvinyl alcohol is domestic 1788 types, a kind of or mixing in 1799 types.
Described adhesive is water-and acrylate emulsion.
Described auxiliary agent is brightening agent, defoamer, levelling agent, anticorrisive agent.
Described base material can be purified cotton cloth or chemical fiber fabric or the blended union of the two, grammes per square metre 150-200gsm.
A preparation method for ink-jet canvas, specifically comprises the steps:
A. base material is put into baking oven, drying and shaping 5 ~ 7min at 80 ~ 100 ℃;
B. even coating base coat on the base material in described step a is dried at 100 ~ 120 ℃, then repetitive coatings 1 ~ 2 time, continues to dry and makes semi-finished product canvas;
C. on the semi-finished product canvas of step b coating base coat, evenly after coated side coating, put into baking oven again, at 105 ~ 115 ℃, dry 5 ~ 7min;
D. by the canvas rolling after drying, cut and pack.
Beneficial effect: disclosed ink-jet canvas, mainly for Latex ink exploitation, with strong points, applicability is high.Based on Latex ink constituent and the ink-jet principle of solidification, less demanding to bearing the absorbency of medium, but it is high that matching requires, face is used adhesive specially in being coated with, there are good matching and binding strength with the latex using in Latex ink, when using Latex ink inkjet printing, ink low-temperature setting, on finishing coat, can obtain good color fastness; Face has additionally added antiseepage agent in being coated with simultaneously, can prevent ink imbibition, makes pattern edge more clear, and color representation power is also better.
The specific embodiment
Below in conjunction with specific embodiment, the present invention will be described in detail.
Disclosed a kind of ink-jet canvas, described canvas is followed successively by base material from bottom to up, priming coat and finishing coat, described priming coat is by 35 ~ 45 parts of fillers, 1 ~ 3 part of polyvinyl alcohol, 30 ~ 40 parts, adhesive, 0.5 ~ 2 part of auxiliary agent, 10 ~ 30 parts of compositions of water, described finishing coat is by 0 ~ 15 part of silica 1,1 ~ 3 part of polyvinyl alcohol, 30 ~ 40 parts of adhesive speciallies, 0.5 ~ 2 part of auxiliary agent, 1 ~ 5 part of antiseepage agent, 30 ~ 50 parts of compositions of water.
Wherein, described filler is lithopone, talcum powder, kaolin, one or more in calcium carbonate, and fineness 800 ~ 1250 orders, described adhesive specially is Vinyl Acetate-Acrylate Copolymer Water-Borne Emulsion, Tg is-20 ℃, described silica is pore type precipitated silica, particle diameter is 2-10um, pore volume is 100-300ml/g, described polyvinyl alcohol is domestic 1788 types, a kind of or mixing in 1799 types, described adhesive is water-and acrylate emulsion, described auxiliary agent is brightening agent, defoamer, levelling agent, anticorrisive agent, described base material can be purified cotton cloth or chemical fiber fabric or the blended union of the two, grammes per square metre 150-200gsm.
For different materials and proportioning, with concrete example, set forth below.
Specific embodiment one:
Disclosed a kind of ink-jet canvas, described canvas is followed successively by base material from bottom to up, priming coat and finishing coat, its concrete preparation method is:
A. choose terylene cloth and put into baking oven as base material, drying and shaping 5min at 80 ℃;
B. even coating base coat on the base material after drying and shaping is dried at 100 ℃, then 1 same oven dry of repetitive coatings, wherein priming coat consists of 35 parts of kaolin, 1 part, polyvinyl alcohol 1799 type, 1 part, polyvinyl alcohol 1788 type, 30 parts, adhesive, 0.5 part of auxiliary agent, 1 part, water;
C. on the semi-finished product canvas of step b coating base coat, evenly after coated side coating, put into baking oven again, at 105 ℃, dry 5min, wherein finishing coat consists of 0 part of silica 1,1 part, polyvinyl alcohol 1799 type, 1 part, polyvinyl alcohol 1788 type, 30 parts of adhesive speciallies, 0.5 part of auxiliary agent, 1 part of antiseepage agent, 30 parts, water;
D. by the canvas rolling after drying, cut and pack.
Specific embodiment two:
Disclosed a kind of ink-jet canvas, described canvas is followed successively by base material from bottom to up, priming coat and finishing coat, its concrete preparation method is:
A. choose purified cotton cloth and put into baking oven as base material, drying and shaping 6min at 90 ℃;
B. even coating base coat on the base material after drying and shaping is dried at 110 ℃, then 1 same oven dry of repetitive coatings, wherein priming coat consists of 40 parts of talcum powder, 1 part, polyvinyl alcohol 1799 type, 2 parts, polyvinyl alcohol 1788 type, 35 parts, adhesive, 1 part of auxiliary agent, 15 parts, water;
C. on the semi-finished product canvas of step b coating base coat, evenly after coated side coating, put into baking oven again, at 110 ℃, dry 6min, wherein finishing coat consists of 3 parts of silica 1s, 1 part, polyvinyl alcohol 1799 type, 1 part, polyvinyl alcohol 1788 type, 35 parts of adhesive speciallies, 1 part of auxiliary agent, 3 parts of antiseepage agents, 40 parts, water;
D. by the canvas rolling after drying, cut and pack.
Specific embodiment three:
The present embodiment is that existing a kind of without fire-retardant ink-jet canvas, described canvas is followed successively by base material from bottom to up, priming coat and ink-absorbed coated layer, and its concrete preparation method is:
A. choose polyester cotton blending cloth and put into baking oven as base material, drying and shaping 7min at 100 ℃;
B. even coating base coat on the base material after drying and shaping is dried at 120 ℃, then 1 same oven dry of repetitive coatings, and wherein priming coat consists of 20 parts of kaolin, 25 parts, lithopone, 1 part, polyvinyl alcohol 1799 type, 1 part, polyvinyl alcohol 1788 type, 40 parts, adhesive, 2 parts of auxiliary agents, 30 parts, water;
C. on the semi-finished product canvas of step b coating base coat, evenly after coated side coating, put into baking oven again, at 115 ℃, dry 7min, wherein finishing coat consists of 5 parts of silica 1s, 1 part, polyvinyl alcohol 1799 type, 2 parts, polyvinyl alcohol 1788 type, 40 parts of adhesive speciallies, 2 parts of auxiliary agents, 5 parts of antiseepage agents, 50 parts, water;
D. by the canvas rolling after drying, cut and pack.
Technology contents of the present invention and technical characterictic have disclosed as above; yet those of ordinary skill in the art still may be based on enlightenment of the present invention and announcements and are done all replacement and modifications that does not deviate from spirit of the present invention; therefore; protection domain of the present invention should be not limited to the content that embodiment discloses; and should comprise various do not deviate from replacement of the present invention and modifications, and contained by present patent application claim.
Claims (9)
1. an ink-jet canvas, is characterized in that: described canvas is followed successively by base material from bottom to up priming coat and finishing coat, described priming coat is by 35 ~ 45 parts of fillers, 1 ~ 3 part of polyvinyl alcohol, 30 ~ 40 parts, adhesive, 0.5 ~ 2 part of auxiliary agent, 10 ~ 30 parts of compositions of water, described finishing coat is by 0 ~ 15 part of silica 1,1 ~ 3 part of polyvinyl alcohol, 30 ~ 40 parts of adhesive speciallies, 0.5 ~ 2 part of auxiliary agent, 1 ~ 5 part of antiseepage agent, 30 ~ 50 parts of compositions of water.
2. a kind of ink-jet canvas according to claim 1, is characterized in that: described filler is one or more in lithopone, talcum powder, kaolin, calcium carbonate, and fineness 800 ~ 1250 orders.
3. a kind of ink-jet canvas according to claim 1, is characterized in that: described adhesive specially is Vinyl Acetate-Acrylate Copolymer Water-Borne Emulsion, and Tg is-20 ℃.
4. a kind of ink-jet canvas according to claim 1, is characterized in that: described silica is pore type precipitated silica, and particle diameter is 2-10um, and pore volume is 100-300ml/g.
5. a kind of ink-jet canvas according to claim 1, is characterized in that: described polyvinyl alcohol is domestic 1788 types, a kind of or mixing in 1799 types.
6. a kind of ink-jet canvas according to claim 1, is characterized in that: described adhesive is water-and acrylate emulsion.
7. a kind of ink-jet canvas according to claim 1, is characterized in that: described auxiliary agent is brightening agent, defoamer, levelling agent, anticorrisive agent.
8. a kind of ink-jet canvas according to claim 1, is characterized in that: described base material can be purified cotton cloth or chemical fiber fabric or the blended union of the two, grammes per square metre 150-200gsm.
9. a preparation method for ink-jet canvas, is characterized in that: specifically comprise the steps:
A. base material is put into baking oven, drying and shaping 5 ~ 7min at 80 ~ 100 ℃;
B. even coating base coat on the base material in described step a is dried at 100 ~ 120 ℃, then repetitive coatings 1 ~ 2 time, continues to dry and makes semi-finished product canvas;
C. on the semi-finished product canvas of step b coating base coat, evenly after coated side coating, put into baking oven again, at 105 ~ 115 ℃, dry 5 ~ 7min;
D. by the canvas rolling after drying, cut and pack.