CN104191852B - A kind of ink-jet canvas and preparation method thereof - Google Patents
A kind of ink-jet canvas and preparation method thereof Download PDFInfo
- Publication number
- CN104191852B CN104191852B CN201410438828.5A CN201410438828A CN104191852B CN 104191852 B CN104191852 B CN 104191852B CN 201410438828 A CN201410438828 A CN 201410438828A CN 104191852 B CN104191852 B CN 104191852B
- Authority
- CN
- China
- Prior art keywords
- parts
- canvas
- ink
- coat
- jet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of ink-jet canvas, described canvas sequentially consists of base material, priming coat and finishing coat, described priming coat is by filler 35 ~ 45 parts, polyvinyl alcohol 1 ~ 3 part, binding agent 30 ~ 40 parts, auxiliary agent 0.5 ~ 2 part, 10 ~ 30 parts of water composition, described finishing coat is by silica 10 ~ 15 part, polyvinyl alcohol 1 ~ 3 part, adhesive specially 30 ~ 40 parts, auxiliary agent 0.5 ~ 2 part, antiseepage agent 1 ~ 5 part, 30 ~ 50 parts of water composition.The latex used in disclosed ink-jet canvas, with Latex ink has preferable matching and binding strength, and when using Latex ink jet to print, ink low-temperature setting is on finishing coat, it is possible to obtain preferably color fastness；Additionally with the addition of antiseepage agent simultaneously in topcoating, be possible to prevent ink imbibition, make pattern edge become apparent from, color representation power is more preferable.
Description
Technical field
The present invention relates to color inkjet printing medium field, particularly relate to a kind of ink-jet canvas and preparation method thereof.
Background technology
Inkjet technology is by the printing of inkjet printer a kind of new digital imaging technique on ink-absorbing medium by digitized image, has operating procedure simple, without advantages such as plate-making, non-pollution discharge, great personalizations.And ink-jet canvas is as a kind of functional type print media being rich in artistic characteristics, it is widely used in image description dossal, decoration painting, oil painting product imitated etc..Particularly oil painting product is imitated, and owing to famous-object oil painting selling at exorbitant prices allows vast majority of people hang back, and the art atmosphere band of famous-object oil painting is entered ten million average family by the birth of ink-jet canvas.
Hewlett-Packard Corporation develops a kind of novel ink-jet ink Latex ink, this ink environmental protection, imaging is lasting, equipment fanout free region, represent one of the inkjet printing direction in future, but its supporting painting canvas class ink-jet bears medium, in addition to the ink-jet canvas of the original-pack production of Hewlett-Packard Corporation, ink-jet canvas based on the exploitation of Latex ink is the most less on the market, and specific aim and the suitability are the most poor.
Summary of the invention
Goal of the invention: the invention reside in the defect overcome in background technology, it is provided that a kind of ink-jet canvas for Latex ink and preparation method thereof, it is with strong points, and the suitability is high.
Technical scheme: a kind of ink-jet canvas, described canvas sequentially consists of base material, priming coat and finishing coat, described priming coat is by filler 35 ~ 45 parts, polyvinyl alcohol 1 ~ 3 part, binding agent 30 ~ 40 parts, auxiliary agent 0.5 ~ 2 part, 10 ~ 30 parts of water composition, described finishing coat is by silica 10 ~ 15 part, polyvinyl alcohol 1 ~ 3 part, adhesive specially 30 ~ 40 parts, auxiliary agent 0.5 ~ 2 part, antiseepage agent 1 ~ 5 part, 30 ~ 50 parts of water composition.
Described filler is one or more in lithopone, Pulvis Talci, Kaolin, calcium carbonate, and fineness 800 ~ 1250 mesh.
Described adhesive specially is Vinyl Acetate-Acrylate Copolymer Water-Borne Emulsion, and Tg is-20 DEG C.
Described silicon dioxide is pore type precipitated silica, and particle diameter is 2-10um, and pore volume is 100-300ml/g.
Described polyvinyl alcohol is domestic 1788 types, a kind of or mixing in 1799 types.
Described binding agent is water-and acrylate emulsion.
Described auxiliary agent is brightening agent, defoamer, levelling agent, preservative.
Described base material can be purified cotton cloth or chemical fiber fabric or the blended union of the two, grammes per square metre 150-200gsm.
The manufacture method of a kind of ink-jet canvas, specifically includes following steps:
A. base material is put into baking oven, drying and shaping 5 ~ 7min at 80 ~ 100 DEG C；
B. uniform coating base coat on the base material in described step a, dries at 100 ~ 120 DEG C, repeats coating 1 ~ 2 time, continues drying and makes semi-finished product canvas；
C. on the semi-finished product canvas of step b coating base coat, uniformly put into baking oven after coated side coating again, at 105 ~ 115 DEG C, dry 5 ~ 7min；
D. the canvas rolling after drying, cuts and packs.
Beneficial effect: disclosed ink-jet canvas, develops mainly for Latex ink, with strong points, the suitability is high.Based on Latex ink constituent and the ink-jet principle of solidification, less demanding to the absorbency bearing medium, but matching requires height, topcoating uses adhesive specially, preferable matching and binding strength is had with the latex used in Latex ink, when using Latex ink jet to print, ink low-temperature setting is on finishing coat, it is possible to obtain preferably color fastness；Additionally with the addition of antiseepage agent simultaneously in topcoating, be possible to prevent ink imbibition, make pattern edge become apparent from, color representation power is more preferable.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be described in detail.
Disclosed a kind of ink-jet canvas, described canvas sequentially consists of base material, priming coat and finishing coat, described priming coat is by filler 35 ~ 45 parts, polyvinyl alcohol 1 ~ 3 part, binding agent 30 ~ 40 parts, auxiliary agent 0.5 ~ 2 part, 10 ~ 30 parts of water composition, described finishing coat is by silica 10 ~ 15 part, polyvinyl alcohol 1 ~ 3 part, adhesive specially 30 ~ 40 parts, auxiliary agent 0.5 ~ 2 part, antiseepage agent 1 ~ 5 part, 30 ~ 50 parts of water composition.
Wherein, described filler is lithopone, Pulvis Talci, Kaolin, one or more in calcium carbonate, and fineness 800 ~ 1250 mesh, described adhesive specially is Vinyl Acetate-Acrylate Copolymer Water-Borne Emulsion, Tg is-20 DEG C, described silicon dioxide is pore type precipitated silica, particle diameter is 2-10um, pore volume is 100-300ml/g, described polyvinyl alcohol is domestic 1788 types, a kind of or mixing in 1799 types, described binding agent is water-and acrylate emulsion, described auxiliary agent is brightening agent, defoamer, levelling agent, preservative, described base material can be purified cotton cloth or chemical fiber fabric or the blended union of the two, grammes per square metre 150-200gsm.
Below for different materials and proportioning, it is illustrated with specific example.
Specific embodiment one:
Disclosed a kind of ink-jet canvas, described canvas sequentially consists of base material, priming coat and finishing coat, and its concrete manufacture method is:
A. choose terylene cloth and put into baking oven as base material, drying and shaping 5min at 80 DEG C；
B. uniform coating base coat on the base material after drying and shaping, dries at 100 DEG C, repeats 1 same drying of coating, wherein priming coat consists of Kaolin 35 parts, 1 part of polyvinyl alcohol 1799 type, 1 part of polyvinyl alcohol 1788 type, binding agent 30 parts, auxiliary agent 0.5 part, 1 part of water；
C. on the semi-finished product canvas of step b coating base coat, uniformly baking oven is put into after coated side coating again, 5min is dried at 105 DEG C, wherein finishing coat consists of silica 10 part, 1 part of polyvinyl alcohol 1799 type, 1 part of polyvinyl alcohol 1788 type, adhesive specially 30 parts, auxiliary agent 0.5 part, antiseepage agent 1 part, 30 parts of water；
D. the canvas rolling after drying, cuts and packs.
Specific embodiment two:
Disclosed a kind of ink-jet canvas, described canvas sequentially consists of base material, priming coat and finishing coat, and its concrete manufacture method is:
A. choose purified cotton cloth and put into baking oven as base material, drying and shaping 6min at 90 DEG C；
B. uniform coating base coat on the base material after drying and shaping, dries at 110 DEG C, repeats 1 same drying of coating, wherein priming coat consists of Pulvis Talci 40 parts, 1 part of polyvinyl alcohol 1799 type, 2 parts of polyvinyl alcohol 1788 type, binding agent 35 parts, auxiliary agent 1 part, 15 parts of water；
C. on the semi-finished product canvas of step b coating base coat, uniformly baking oven is put into after coated side coating again, 6min is dried at 110 DEG C, wherein finishing coat consists of silica 13 parts, 1 part of polyvinyl alcohol 1799 type, 1 part of polyvinyl alcohol 1788 type, adhesive specially 35 parts, auxiliary agent 1 part, antiseepage agent 3 parts, 40 parts of water；
D. the canvas rolling after drying, cuts and packs.
Specific embodiment three:
The present embodiment is existing one non-antiflaming ink-jet canvas, and described canvas sequentially consists of base material, priming coat and ink-absorbed coated layer, and its concrete manufacture method is:
A. choose polyester cotton blending cloth and put into baking oven as base material, drying and shaping 7min at 100 DEG C；
B. uniform coating base coat on the base material after drying and shaping, dries at 120 DEG C, repeats 1 same drying of coating, and wherein priming coat consists of Kaolin 20 parts, 25 parts of lithopone, 1 part of polyvinyl alcohol 1799 type, 1 part of polyvinyl alcohol 1788 type, binding agent 40 parts, auxiliary agent 2 parts, 30 parts of water；
C. on the semi-finished product canvas of step b coating base coat, uniformly baking oven is put into after coated side coating again, 7min is dried at 115 DEG C, wherein finishing coat consists of silica 15 parts, 1 part of polyvinyl alcohol 1799 type, 2 parts of polyvinyl alcohol 1788 type, adhesive specially 40 parts, auxiliary agent 2 parts, antiseepage agent 5 parts, 50 parts of water；
D. the canvas rolling after drying, cuts and packs.
The technology contents of the present invention and technical characteristic have revealed that as above; but those of ordinary skill in the art are still potentially based on the enlightenment of the present invention and announcement and make all replacements without departing substantially from spirit of the present invention and modification; therefore; scope should be not limited to the content disclosed in embodiment; and the various replacement without departing substantially from the present invention and modification should be included, and contained by present patent application claim.
Claims (1)
1. an ink-jet canvas, it is characterised in that: described canvas sequentially consists of base material,
Priming coat and finishing coat, described priming coat by filler 35～45 parts, polyvinyl alcohol 2～3 parts,
Binding agent 30～35 parts, auxiliary agent 0.5 part, water 10～15 parts of compositions, described finishing coat is by dioxy
SiClx 10～13 parts, polyvinyl alcohol 1～2 parts, adhesive specially 30～40 parts, auxiliary agent
0.5～2 part, antiseepage agent 1～5 parts, water 30～50 parts of compositions；
Described adhesive specially is Vinyl Acetate-Acrylate Copolymer Water-Borne Emulsion, and Tg is-20 DEG C；
Described filler is one or more in lithopone, Pulvis Talci, Kaolin, calcium carbonate, and carefully
Degree 800～1250 mesh；
Described base material is purified cotton cloth or chemical fiber fabric or the blended union of the two, grammes per square metre
150-200gsm；
The manufacture method of described ink-jet canvas, specifically includes following steps:
A. base material is put into baking oven, drying and shaping 5～7min at 80～100 DEG C；
B. uniform coating base coat on the base material in described step a, dries at 100～120 DEG C,
Repeat coating 1～2 time, continue drying and make semi-finished product canvas；
C. uniformly put into after coated side coating again on the semi-finished product canvas of step b coating base coat
Baking oven, dries 5～7min at 105～115 DEG C；
D. the canvas rolling after drying, cuts and packs.