CN104140646B - 一种无卤抗氧化pbt材料 - Google Patents
一种无卤抗氧化pbt材料 Download PDFInfo
- Publication number
- CN104140646B CN104140646B CN201410340750.3A CN201410340750A CN104140646B CN 104140646 B CN104140646 B CN 104140646B CN 201410340750 A CN201410340750 A CN 201410340750A CN 104140646 B CN104140646 B CN 104140646B
- Authority
- CN
- China
- Prior art keywords
- pbt
- raw material
- oxidant
- halogen
- silicone polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种无卤抗氧化pbt材料，它是由下述重量份的原料组成的：聚对苯二甲酸丁二醇酯93-100、聚二甲基硅氧烷1-2、二氯异氰尿酸钠0.1-0.4、三丁基三氯化锡0.4-1、8-羟基喹啉铜1-2、聚乙烯醇缩丁醛酯2-3、三乙二醇二异辛酸酯2-4、焦亚硫酸钠1-2、抗氧剂1010？0.2-1、二甲基乙醇胺1-2、沉淀硫酸钡3-4、马来酸酐1-2、加工助剂1-2，本发明的pbt材料，机械强度高和热变形系数小，在高温下机械强度降低不大，性能与同类材料相比更高，抗氧化性好，耐候性强，适用范围广，使用寿命长。
Description
技术领域
本发明主要涉及材料领域，尤其涉及一种无卤抗氧化pbt材料。
背景技术
聚对苯二甲酸丁二醇酯，耐候性、吸水率低，仅为0.1%，在潮湿环境中仍保持各种物性（包括电性能），电绝缘性，但体积电阻、介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。缺点是缺口冲击强度低，成型收缩率大。故大部分采用玻璃纤维增强或无机填充改性，其拉伸强度、弯曲强度可提高一倍以上，热变形温度也大幅提高。可以在140℃下长期工作，玻纤增强后制品纵、横向收缩率不一致，易使制品发生翘曲。
PBT结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02%。
PBT（增强、改性PBT）主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套。
另外还有运输机械零件，缝纫机和纺织机械零件、钟表外壳、镜筒、电熨斗罩、水银灯罩、烘烤炉部件、电动工具零件、屏蔽套。
发明内容
本发明目的就是提供一种无卤抗氧化pbt材料。
本发明是通过以下技术方案实现的：
一种无卤抗氧化pbt材料，它是由下述重量份的原料组成的：
聚对苯二甲酸丁二醇酯93-100、聚二甲基硅氧烷1-2、二氯异氰尿酸钠0.1-0.4、三丁基三氯化锡0.4-1、8-羟基喹啉铜1-2、聚乙烯醇缩丁醛酯2-3、三乙二醇二异辛酸酯2-4、焦亚硫酸钠1-2、抗氧剂10100.2-1、二甲基乙醇胺1-2、沉淀硫酸钡3-4、马来酸酐1-2、加工助剂1-2；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙1-2、罗望子胶2-3、硅酮母粒1-2、癸二酸二辛酯2-3、牡蛎壳粉2-3、钨酸铵0.1-0.3、8-羟基喹啉0.2-0.4、聚二甲基硅氧烷1-2；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在50-60℃下加热混合2-4分钟，加入聚二甲基硅氧烷，200-300转/分搅拌分散7-10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂。
一种无卤抗氧化pbt材料的制备方法，其特征在于包括以下步骤：
将沉淀硫酸钡、聚乙烯醇缩丁醛酯、马来酸酐混合，在40-50℃下搅拌混合2-5分钟，加入聚二甲基硅氧烷，100-200转/分搅拌分散3-6分钟，加入二甲基乙醇胺，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述无卤抗氧化pbt材料。
本发明的优点是：
本发明的pbt材料，机械强度高和热变形系数小，在高温下机械强度降低不大，性能与同类材料相比更高，抗氧化性好，耐候性强，适用范围广，使用寿命长。
具体实施方式
实施例1
一种无卤抗氧化pbt材料，它是由下述重量份（公斤）的原料组成的：
聚对苯二甲酸丁二醇酯100、聚二甲基硅氧烷1、二氯异氰尿酸钠0.1、三丁基三氯化锡0.4、8-羟基喹啉铜1、聚乙烯醇缩丁醛酯2、三乙二醇二异辛酸酯2、焦亚硫酸钠1、抗氧剂10100.2、二甲基乙醇胺2、沉淀硫酸钡4、马来酸酐2、加工助剂1；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙1、罗望子胶3、硅酮母粒1、癸二酸二辛酯2、牡蛎壳粉2-3、钨酸铵0.3、8-羟基喹啉0.4、聚二甲基硅氧烷1；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在60℃下加热混合4分钟，加入聚二甲基硅氧烷，300转/分搅拌分散10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂。
一种无卤抗氧化pbt材料的制备方法，包括以下步骤：
将沉淀硫酸钡、聚乙烯醇缩丁醛酯、马来酸酐混合，在50℃下搅拌混合5分钟，加入聚二甲基硅氧烷，200转/分搅拌分散6分钟，加入二甲基乙醇胺，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述无卤抗氧化pbt材料。
本实施方法中所得的无卤抗氧化pbt材料的具体性能为：
拉伸强度为96MPa；
缺口冲击强度（KJ/m2）9.82；
垂直燃烧(1.6mm)FV-O。
Claims (2)
1.一种无卤抗氧化pbt材料，其特征在于它是由下述重量份的原料组成的：
聚对苯二甲酸丁二醇酯93-100、聚二甲基硅氧烷1-2、二氯异氰尿酸钠0.1-0.4、三丁基三氯化锡0.4-1、8-羟基喹啉铜1-2、聚乙烯醇缩丁醛酯2-3、三乙二醇二异辛酸酯2-4、焦亚硫酸钠1-2、抗氧剂10100.2-1、二甲基乙醇胺1-2、沉淀硫酸钡3-4、马来酸酐1-2、加工助剂1-2；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙1-2、罗望子胶2-3、硅酮母粒1-2、癸二酸二辛酯2-3、牡蛎壳粉2-3、钨酸铵0.1-0.3、8-羟基喹啉0.2-0.4、聚二甲基硅氧烷1-2；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在50-60℃下加热混合2-4分钟，加入聚二甲基硅氧烷，200-300转/分搅拌分散7-10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂。
2.一种如权利要求1所述的无卤抗氧化pbt材料的制备方法，其特征在于包括以下步骤：
将沉淀硫酸钡、聚乙烯醇缩丁醛酯、马来酸酐混合，在40-50℃下搅拌混合2-5分钟，加入聚二甲基硅氧烷，100-200转/分搅拌分散3-6分钟，加入二甲基乙醇胺，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述无卤抗氧化pbt材料。