CN104151791B - 一种耐高温水解pbt材料 - Google Patents

一种耐高温水解pbt材料 Download PDF

Info

Publication number
CN104151791B
CN104151791B CN201410361751.6A CN201410361751A CN104151791B CN 104151791 B CN104151791 B CN 104151791B CN 201410361751 A CN201410361751 A CN 201410361751A CN 104151791 B CN104151791 B CN 104151791B
Authority
CN
China
Prior art keywords
high temperature
temperature resistant
glass fibre
mixing
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410361751.6A
Other languages
English (en)
Other versions
CN104151791A (zh
Inventor
孟勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan maintenance Plastic Co.,Ltd.
Guangdong Gaohang Intellectual Property Operation Co ltd
Original Assignee
CHUZHOU YOUSHENG HIGH POLYMER MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHUZHOU YOUSHENG HIGH POLYMER MATERIAL Co Ltd filed Critical CHUZHOU YOUSHENG HIGH POLYMER MATERIAL Co Ltd
Priority to CN201410361751.6A priority Critical patent/CN104151791B/zh
Publication of CN104151791A publication Critical patent/CN104151791A/zh
Application granted granted Critical
Publication of CN104151791B publication Critical patent/CN104151791B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐高温水解PBT材料，它是由下述重量份的原料组成的：聚对苯二甲酸丁二醇酯81‑90、薄荷素油1‑2、环己六醇2‑3、亚磷酸双酚A酯1‑2、十六烷基三甲基氯化铵1‑2、蜂胶2‑3、聚偏二氟乙烯2‑4、玻璃纤维10‑20、邻苯二甲酸二甲酯4‑6、二月桂酸二丁基锡0.8‑1、2‑硫醇基苯骈咪唑1‑2、加工助剂2‑3，本发明的PBT材料中加入的玻璃纤维可以有效的降低粘度，增强各组分的水分散性，使得成品具有优良的耐高温水解性能，加入的加工助剂可以有效的改善各物料间的相容性，提高成品的稳定性，提高整体性能。

Description

一种耐高温水解PBT材料
技术领域
本发明主要涉及材料领域，尤其涉及一种耐高温水解PBT材料。
背景技术
聚对苯二甲酸丁二醇酯，耐候性、吸水率低，仅为0.1％，在潮湿环境中仍保持各种物性(包括电性能)，电绝缘性，但体积电阻、介电损耗大。耐热水、碱类、酸类、油类、但易受卤化烃侵蚀，耐水解性差，低温下可迅速结晶，成型性良好。缺点是缺口冲击强度低，成型收缩率大。故大部分采用玻璃纤维增强或无机填充改性，其拉伸强度、弯曲强度可提高一倍以上，热变形温度也大幅提高。可以在140℃下长期工作，玻纤增强后制品纵、横向收缩率不一致，易使制品发生翘曲。
PBT结晶速度快，最适宜加工方法为注塑，其他方法还有挤出、吹塑、涂覆和各种二次加工成型，成型前需预干燥，水分含量要降至0.02％。
PBT(增强、改性PBT)主要用于汽车、电子电器、工业机械和聚合物合金、共混工业。如作为汽车中的分配器、车体部件、点火器线圈骨架、绝缘盖、排气系统零部件、摩托车点火器、电子电器工业中如电视机的偏转线圈，显像管和电位器支架，伴音输出变压器骨架，适配器骨架，开关接插件、电风扇、电冰箱、洗衣机电机端盖、轴套。
另外还有运输机械零件，缝纫机和纺织机械零件、钟表外壳、镜筒、电熨斗罩、水银灯罩、烘烤炉部件、电动工具零件、屏蔽套。
发明内容
本发明目的就是提供一种耐高温水解PBT材料。
本发明是通过以下技术方案实现的：
一种耐高温水解PBT材料，它是由下述重量份的原料组成的：
聚对苯二甲酸丁二醇酯81-90、薄荷素油1-2、环己六醇2-3、亚磷酸双酚A酯1-2、十六烷基三甲基氯化铵1-2、蜂胶2-3、聚偏二氟乙烯2-4、玻璃纤维10-20、邻苯二甲酸二甲酯4-6、二月桂酸二丁基锡0.8-1、2-硫醇基苯骈咪唑1-2、加工助剂2-3；
所述的玻璃纤维为单丝直径是5-10微米的E-CR玻璃纤维；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙1-2、罗望子胶2-3、硅酮母粒1-2、癸二酸二辛酯2-3、牡蛎壳粉2-3、钨酸铵0.1-0.3、8-羟基喹啉0.2-0.4、聚二甲基硅氧烷1-2；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在50-60℃下加热混合2-4分钟，加入聚二甲基硅氧烷，200-300转/分搅拌分散7-10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂。
一种耐高温水解PBT材料的制备方法，其特征在于包括以下步骤：
将玻璃纤维、亚磷酸双酚A酯混合，在70-80℃下搅拌混合5-8分钟，加入邻苯二甲酸二甲酯、薄荷素油，搅拌混合至常温；
将十六烷基三甲基氯化铵加入环己六醇中，加入蜂胶，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述耐高温水解PBT材料。
本发明的优点是：
本发明的PBT材料中加入的玻璃纤维可以有效的降低粘度，增强各组分的水分散性，使得成品具有优良的耐高温水解性能，加入的加工助剂可以有效的改善各物料间的相容性，提高成品的稳定性，提高整体性能。
具体实施方式
实施例1
一种耐高温水解PBT材料，它是由下述重量份(公斤)的原料组成的：
聚对苯二甲酸丁二醇酯90、薄荷素油2、环己六醇2、亚磷酸双酚A酯2、十六烷基三甲基氯化铵1、蜂胶3、聚偏二氟乙烯2、玻璃纤维20、邻苯二甲酸二甲酯5、二月桂酸二丁基锡0.8、2-硫醇基苯骈咪唑2、加工助剂3；
所述的玻璃纤维为单丝直径是5-10微米的E-CR玻璃纤维；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙2、罗望子胶3、硅酮母粒2、癸二酸二辛酯2、牡蛎壳粉2、钨酸铵0.3、8-羟基喹啉0.4、聚二甲基硅氧烷2；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在60℃下加热混合4分钟，加入聚二甲基硅氧烷，300转/分搅拌分散10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂。
一种耐高温水解PBT材料的制备方法，包括以下步骤：
将玻璃纤维、亚磷酸双酚A酯混合，在80℃下搅拌混合5分钟，加入邻苯二甲酸二甲酯、薄荷素油，搅拌混合至常温；
将十六烷基三甲基氯化铵加入环己六醇中，加入蜂胶，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述耐高温水解PBT材料。
本实施方法中所得的耐高温水解PBT材料的具体性能为：
拉伸强度为93MPa；
缺口冲击强度(KJ/m2)9.94；
垂直燃烧(1.6mm)FV-O。

Claims (1)

1.一种耐高温水解PBT材料，其特征在于它是由下述重量份的原料组成的：
聚对苯二甲酸丁二醇酯81-90、薄荷素油1-2、环己六醇2-3、亚磷酸双酚A 酯1-2、十六烷基三甲基氯化铵1-2、蜂胶2-3、聚偏二氟乙烯2-4、玻璃纤维10-20、邻苯二甲酸二甲酯4-6、二月桂酸二丁基锡0.8-1、2-硫醇基苯骈咪唑1-2、加工助剂2-3；
所述的玻璃纤维为单丝直径是5-10微米的E-CR玻璃纤维；
所述的加工助剂是由下述重量份的原料组成的：
硅酸三钙1-2、罗望子胶2-3、硅酮母粒1-2、癸二酸二辛酯2-3、牡蛎壳粉2-3、钨酸铵0.1-0.3、8-羟基喹啉0.2-0.4、聚二甲基硅氧烷1-2；
将牡蛎壳粉、硅酮母粒混合，搅拌均匀后加入癸二酸二辛酯，在50-60℃下加热混合2-4分钟，加入聚二甲基硅氧烷，200-300转/分搅拌分散7-10分钟，得预混料；
将硅酸三钙与钨酸铵混合球磨，加入上述预混料和剩余各原料，搅拌均匀，得所述加工助剂；
所述耐高温水解PBT材料的制备方法包括以下步骤：
将玻璃纤维、亚磷酸双酚A酯混合，在70-80℃下搅拌混合5-8分钟，加入邻苯二甲酸二甲酯、薄荷素油，搅拌混合至常温；
将十六烷基三甲基氯化铵加入环己六醇中，加入蜂胶，搅拌均匀；
将上述处理后的各原料与剩余各原料混合，高速搅拌均匀，送入双螺杆挤出机挤出，经过拉条、冷却、切粒、干燥处理，即得所述耐高温水解pbt材料。
CN201410361751.6A 2014-07-28 2014-07-28 一种耐高温水解pbt材料 Expired - Fee Related CN104151791B (zh)