CN104109446A - 一种新型耐高温绝缘涂料 - Google Patents
一种新型耐高温绝缘涂料 Download PDFInfo
- Publication number
- CN104109446A CN104109446A CN201410304053.2A CN201410304053A CN104109446A CN 104109446 A CN104109446 A CN 104109446A CN 201410304053 A CN201410304053 A CN 201410304053A CN 104109446 A CN104109446 A CN 104109446A
- Authority
- CN
- China
- Prior art keywords
- parts
- high temperature
- resistant insulation
- insulation material
- novel high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种新型耐高温绝缘涂料，由以下重量份的组分构成：有机硅改性环氧树脂40-50份，氧化硅20-30份，云母粉15-30份，阻燃剂10-15份，三氧化二锑20-30份，改性膨润土6-8份，增韧剂6-8份，固化剂10-15份，聚硅氧烷8-10份，消泡剂3-5份。适应性强，在高温、腐蚀等苛刻环境条件下也具备良好绝缘性能，耐候性、抗老化性能优良，对各种金属基材均具有良好的附着力，固含量高，干燥固化时体积收缩率低。
Description
技术领域
本发明涉及涂料技术领域，具体涉及一种新型耐高温绝缘涂料。
背景技术
随着科技工业的发展，我们对绝缘材料的性能要求越来越高，开发性能优异的H级、C 级、户外，以及能应用于高温、潮湿、严寒、大温差、强辐照、腐蚀性、油污、盐雾等苛刻环境条件的高压绝缘材料，是电工电气新材料领域的一个世界性课题。所以材料不但要在一般环境下具有良好的耐击穿性能，而且在高温和腐蚀环境中也应具备良好的绝缘性能。
发明内容
本发明的目的是解决现有的技术缺陷，提供一种新型耐高温绝缘涂料，具有稳定性好、耐高温和耐腐蚀的特点。
本发明所采用的技术方案是：一种新型耐高温绝缘涂料，由以下重量份的组分构成 ：有机硅改性环氧树脂40-50份，氧化硅20-30份，云母粉15-30份，阻燃剂10-15份，三氧化二锑20-30份，改性膨润土6-8份，增韧剂6-8份，固化剂10-15份，聚硅氧烷8-10份，消泡剂3-5份。
上述聚硅氧烷是经过聚醚改性的。
本发明的有益效果是：适应性强，在高温、腐蚀等苛刻环境条件下也具备良好绝缘性能，耐候性、抗老化性能优良，对各种金属基材均具有良好的附着力，固含量高，干燥固化时体积收缩率低。采用聚硅氧烷作为流平剂，可以促使涂料在干燥成膜过程中形成一个平整、光滑、均匀的涂膜。
具体实施方式
下面结合具体实施例来对本发明作进一步的描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
一种新型耐高温绝缘涂料，由以下重量份的组分构成 ：有机硅改性环氧树脂40份，氧化硅20份，云母粉15份，阻燃剂10份，三氧化二锑20份，改性膨润土6份，增韧剂6份，固化剂10份，经过聚醚改性的聚硅氧烷8份，消泡剂3份。
实施例2
一种新型耐高温绝缘涂料，由以下重量份的组分构成 ：有机硅改性环氧树脂45份，氧化硅25份，云母粉20份，阻燃剂13份，三氧化二锑25份，改性膨润土7份，增韧剂7份，固化剂13份，经过聚醚改性的聚硅氧烷9份，消泡剂4份。
实施例3
一种新型耐高温绝缘涂料，由以下重量份的组分构成 ：有机硅改性环氧树脂50份，氧化硅30份，云母粉30份，阻燃剂15份，三氧化二锑30份，改性膨润土8份，增韧剂8份，固化剂15份，经过聚醚改性的聚硅氧烷10份，消泡剂5份。
上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进，这些改进也应视为本发明的保护范围。
Claims (2)
1.一种新型耐高温绝缘涂料，其特征在于，由以下重量份的组分构成 ：有机硅改性环氧树脂40-50份，氧化硅20-30份，云母粉15-30份，阻燃剂10-15份，三氧化二锑20-30 份，改性膨润土6-8份，增韧剂6-8份，固化剂10-15份，聚硅氧烷8-10份，消泡剂3-5份。
2.根据权利要求1所述的一种新型耐高温绝缘涂料，其特征在于：所述聚硅氧烷是经过聚醚改性的。