CN104108954B - Method for enabling porcelain body surface to have painting effect on rice paper - Google Patents
Method for enabling porcelain body surface to have painting effect on rice paper Download PDFInfo
- Publication number
- CN104108954B CN104108954B CN201410334096.5A CN201410334096A CN104108954B CN 104108954 B CN104108954 B CN 104108954B CN 201410334096 A CN201410334096 A CN 201410334096A CN 104108954 B CN104108954 B CN 104108954B
- Authority
- CN
- China
- Prior art keywords
- body surface
- porcelain body
- rice paper
- white
- painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a method for enabling a porcelain body surface to have painting effect on rice paper, which comprises the following steps: mixing low-temperature white glaze, peach gum and alum, adding water, carrying out ball milling to obtain a pulp, spraying on the porcelain body surface with a spray gun, naturally drying in air to form a mixed glaze layer on the porcelain body surface like a piece of rice paper, and painting or writing on the porcelain body surface. A new calligrapher or painter tester can immediately feel like painting on rice paper when painting on porcelain, so that painting on the porcelain becomes easier.
Description
Technical field
The invention belongs to art ceramic products manufacture technology field, be specifically related to a kind of novel method being used in painting arts of ceramic product and making.In artistic work making processes, the method can make porcelain body surface have and make paintbrush sense and blotting effect on rice paper.
Background technology
Traditional Ceramic Painting, overall point two kinds: over-glaze decoration, under glazed.Under glazed directly draws or execute ground-coat enamel to draw on mud embryo again, burns till (bule and white porcelain is main representative) by more than 1300 degrees Celsius high temperature.Over-glaze decoration is exactly draw a picture on burned ceramic whiteware tire surface, burns till by 780 degrees centigrade furnace temperature, as traditional decoration, powder enamel, colour enamels, new coloured silk etc.
But due to traditional Ceramic Painting technique, grasp and get up to have certain technical difficulty, also there is certain drawback.Such as bule and white porcelain is drawn a picture on mud embryo, and brush drawing is got on, and idiosome can absorb water too fast, lacks the effect of that rhythm on rice paper, and draw a picture on ceramic whiteware tire surface, do not absorb water again or the possibility of oil suction at all.
For adapting to the artist of a lot of new contact Ceramic Painting, find rapidly painting and calligraphy also simple approach as rice paper on pottery, applicant is according to the water-intake rate of life, mature rice paper and its paper surface tactile sensation, develop traditional Chinese painting on Xuan paper method on a cotton up to, the method can make porcelain body surface have and make paintbrush sense and blotting effect on rice paper.
Summary of the invention
The object of this invention is to provide a kind of method making porcelain body surface have effect of drawing a picture on rice paper, the method makes painting and calligraphy on pottery also simple as on rice paper.
In order to realize object of the present invention, the technical scheme adopted is: a kind of method making porcelain body surface have effect of drawing a picture on rice paper, comprises the steps:
1) provide a kind of pottery white tire;
2) use: low temperature white glaze: peach gum: alum, the ratio batching of=100g:6 ~ 6.5g:3.5 ~ 4g, thin up, through ball mill ball milling 10 ~ 20 minutes, crosses 200 mesh sieves, makes mixed slurry;
3) with spray gun by above-mentioned 2) mixed slurry made is sprayed on porcelain body surface, after natural air drying, forms the thick mixing glaze layer of 0.3 ~ 1.3mm on porcelain body surface.
Described low temperature white glaze is a kind of ceramic glaze, can easily buy in ceramic raw material market, and its firing temperature is usually between 760 DEG C ~ 800 DEG C.
Described peach gum is the resin be secreted in the bark such as peach or mountain peach, through water logging, washes away impurity, dries the flour after rear grinding, and its major ingredient is semi-lactosi, rhamnosyl, α-glucose aldehydic acid etc., on sale on market.In the present invention, the add-on of peach gum is to the texture on mixing glaze layer surface and water-intake rate important, and along with peach gum add-on reduces, the pigment diffuse speed on mixing glaze layer surface is accelerated.Change according to the ratio of peach gum and mix adjustable birth a surname of change of glaze layer thickness or the pen sense effect of ripe a surname.
The mixing glaze layer thickness that the present invention is formed can be grasped by the water suction speed needed for expert of calligraphy and painting, and along with the increase of mixing glaze layer thickness, its absorption speed is accelerated.Can according to the manufacturability of product and painting and calligraphy needs, gauge control is better at 0.3 ~ 1.3mm.
The present invention is approximately identical with the quality of batching for the water yield of diluting, so that meet spray gun service requirements.
In the present invention, described low temperature white glaze can also transparent glase fired at lower temperature+glass white substitute, and the quality proportioning of the mixture of transparent glase fired at lower temperature and glass white is: 65 ~ 75:25 ~ 35, can realize object of the present invention.Described transparent glase fired at lower temperature is a kind of glaze conventional in Production of Ceramics, and its firing temperature is usually between 750 DEG C ~ 850 DEG C, on sale on market.Glass white is a kind of conventional beramic color, and the glass white selected should be consistent with the firing temperature of transparent glase fired at lower temperature.
The present invention owing to the addition of appropriate peach gum and alum in mixed slurry, make air-dry after mixing glaze layer in oxide particle be uniformly dispersed, bulk appropriateness, water-intake rate is moderate.After aforesaid method process, mixing glaze layer will as covered a porcelain body snow-white rice paper on the surface, writing brush is taken to draw a picture with beramic color above or write calligraphy again, have that the rhythm effect as write rapidly on rice paper, allow painting and calligraphy person just like the sensation of drawing a picture of writing on rice paper, be particularly suitable for the ink charm drawing freehand brushwork in traditional Chinese painting.
Draw a picture above-mentioned and/or ceramic kiln-firing after calligraphy, firing temperature is consistent with the firing temperature of described low temperature white glaze or transparent.The ceramic burnt out has between over-glaze decoration and under glazed effect unique between the two.
Embodiment
Embodiment 1
1. select the white tire of the pottery of high-quality;
2. use: low temperature white glaze: peach gum: alum: water=500g:30g:20:500 g dilution proportion;
3. make a call to 15 minutes through high speed ball mill;
4. filter through 200 mesh sieve holes;
5. be sprayed on porcelain body surface with K3 spray gun, after natural air drying, form the mixing glaze layer that 1.3mm is thick;
Painting and calligraphy person is with beramic color water transfer or adjust oil to carry out drawing a picture or writing calligraphy on its surface, just like the sensation of drawing a picture of writing on raw rice paper.
Embodiment 2
1. select the white tire of the pottery of high-quality;
2. use: low temperature white glaze: peach gum: alum: water=500g:32.5g:17.5g:500g dilution proportion;
3. make a call to 15 minutes through high speed ball mill;
4. filter through 200 mesh sieve holes;
5. be sprayed on porcelain body surface with K3 spray gun, after natural air drying, form the mixing glaze layer that 0.3mm is thick;
Painting and calligraphy person is with beramic color water transfer or adjust oil to carry out drawing a picture or writing calligraphy on its surface, just like the sensation of drawing a picture of writing on mature rice paper.
Embodiment 3
1. select the white tire of the pottery of high-quality;
2. use: transparent glase fired at lower temperature+glass white: peach gum: alum: water=700g:300g:65g:35g:1000g dilution proportion; (because the firing temperature of beramic color glass white and transparent glase fired at lower temperature has a variety of, so select two kinds of glaze must at equal firing range).
3. beat thin to 15 minutes through high speed ball mill;
4. be filtered to container through 200 mesh sieve holes again;
5. even in porcelain body surface with the spray of K3 spray gun, after natural air drying, form the mixing glaze layer that 0.3mm is thick.
Painting and calligraphy person is with beramic color water transfer or adjust oil to carry out drawing a picture or writing calligraphy on its surface, just like the sensation of drawing a picture of writing on mature rice paper.
Embodiment 4
1. select the white tire of the pottery of high-quality;
2. use: transparent glase fired at lower temperature: glass white: peach gum: alum: water=750g:250g:60g:40g:1000 g dilution proportion;
3. beat thin to 15 minutes through high speed ball mill;
4. be filtered to container through 200 mesh sieve holes again;
5. even in porcelain body surface with the spray of K3 spray gun, after natural air drying, form the mixing glaze layer that 1.0mm is thick.
Painting and calligraphy person is with beramic color water transfer or adjust oil to carry out drawing a picture or writing calligraphy on its surface, just like the sensation of drawing a picture of writing on raw rice paper.
Embodiment 5
1. select the white tire of the pottery of high-quality;
2. use: transparent glase fired at lower temperature: glass white: peach gum: alum: water=650g:350g:60g:40g:1000 g dilution proportion;
3. beat thin to 15 minutes through high speed ball mill;
4. be filtered to container through 200 mesh sieve holes again;
5. even in porcelain body surface with the spray of K3 spray gun, after natural air drying, form the mixing glaze layer that 0.5mm is thick.
Painting and calligraphy person is with beramic color water transfer or adjust oil to carry out drawing a picture or writing calligraphy on its surface, just like the sensation of drawing a picture of writing on mature rice paper.
Because after glaze spraying is air-dry, the porcelain body of above-mentioned each example example surface can as the snow-white smooth rice paper of covering one, and water-intake rate is also as good as with rice paper, and this allows the expert of calligraphy and painting of any new examination pen, can find the pen and ink sensation of ceramic drawing as rice-paper painting at once.
After method process described in the various embodiments described above, after reentering klining one-tenth, its goods have between over-glaze decoration and under glazed effect unique between the two, attempt by numerous expert of calligraphy and painting and praise highly, unanimously think that this invention is a large innovation achievement of Jing Dezhen technology in producing porcelain.
Claims (4)
1. make porcelain body surface have a method for effect of drawing a picture on rice paper, comprise the steps:
1) provide a kind of pottery white tire;
2) use: low temperature white glaze: peach gum: the ratio batching of alum=100g:6 ~ 6.5g:3.5 ~ 4g, thin up, through ball mill ball milling 10 ~ 20 minutes, crosses 200 mesh sieves, makes mixed slurry;
3) with spray gun by above-mentioned 2) mixed slurry made is sprayed on porcelain body surface, after natural air drying, forms the thick mixing glaze layer of 0.3 ~ 1.3mm on porcelain body surface.
2. make porcelain body surface have the method for effect of drawing a picture on rice paper as claimed in claim 1, it is characterized in that: described step 2) in, use: low temperature white glaze: peach gum: alum: water=500g:30g:20g:500ml dilution proportion is prepared burden; Form the mixing glaze layer of 1.3mm thickness on porcelain body surface after air-dry.
3. make porcelain body surface have a method for effect of drawing a picture on rice paper, comprise the steps:
1) provide a kind of pottery white tire;
2) use: the mixture of transparent glase fired at lower temperature and glass white: peach gum: the ratio batching of alum=100g:6 ~ 6.5g:3.5 ~ 4g, thin up, through ball mill ball milling 10 ~ 20 minutes, crosses 200 mesh sieves, makes mixed slurry; The quality proportioning of the mixture of described transparent glase fired at lower temperature and glass white is: 65 ~ 75:25 ~ 35, and described glass white and transparent glase fired at lower temperature have identical firing range;
3) with spray gun by above-mentioned 2) mixed slurry made is sprayed on porcelain body surface, after natural air drying, forms the thick mixing glaze layer of 0.3 ~ 1.3mm on porcelain body surface.
4. make porcelain body surface have the method for effect of drawing a picture on rice paper as claimed in claim 3, it is characterized in that: described step 2) in, use: transparent glase fired at lower temperature: glass white: peach gum: alum: water=700g:300g:65g:35g:1000g dilution proportion is prepared burden; Form on porcelain body surface the mixing glaze layer that thickness is 0.3mm after air-dry.