CN104087118A - 一种光伏支架 - Google Patents

一种光伏支架 Download PDF

Info

Publication number
CN104087118A
CN104087118A CN201410307790.8A CN201410307790A CN104087118A CN 104087118 A CN104087118 A CN 104087118A CN 201410307790 A CN201410307790 A CN 201410307790A CN 104087118 A CN104087118 A CN 104087118A
Authority
CN
China
Prior art keywords
parts
siccative
promotor
epoxy resin
solidifying agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410307790.8A
Other languages
English (en)
Inventor
高勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU DALICHENG ELECTRICAL Co Ltd
Original Assignee
JIANGSU DALICHENG ELECTRICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU DALICHENG ELECTRICAL Co Ltd filed Critical JIANGSU DALICHENG ELECTRICAL Co Ltd
Priority to CN201410307790.8A priority Critical patent/CN104087118A/zh
Publication of CN104087118A publication Critical patent/CN104087118A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种光伏支架，包括支架本体，所述支架上设有保护层，所述保护层按重量份数计含有如下组分：环氧树脂70～90份，氟碳树脂5～15份，无机填料10～40份，二甲苯10～30份、催干剂1～5份、固化剂1～5份、甘油1～5份，促进剂0.5～2份，本发明具有干燥时间短，耐老化性，抗腐蚀性优良的特点，无机填料比环氧树脂成本低，可以降低成本，并且无机填料还具有耐候性的特点，有效保证了光伏支架在恶劣环境中不被腐蚀。

Description

一种光伏支架
技术领域
本发明涉及一种支架，特别涉及一种光伏支架。 
背景技术
太阳能光伏支架，是太阳能光伏发电系统中为了摆放、安装、固定太阳能面板设计的特殊的支架，但光伏支架通常是放置在室外，经常会受到恶劣环境的影响，使得光伏支架受到腐蚀，从而影响光伏支架的使用。 
发明内容
针对上述现有技术中存在的问题，本发明提供了一种具有综合性能良好、防腐性好的一种光伏支架。 
本发明所采用的技术方案是： 
一种光伏支架包括支架本体，所述支架上设有保护层，所述保护层按重量份数计含有如下组分：环氧树脂70～90份，氟碳树脂5～15份，无机填料10～40份，二甲苯10～30份、催干剂1～5份、固化剂1～5份、甘油1～5份，促进剂0.5～2份 
所述的防腐涂料，其特征在于按重量份数计含有如下组分：环氧树脂85份，氟碳树脂7份，无机填料25份、二甲苯22份、催干剂3份、固化剂3份、甘油2份，促进剂1.5份 
所述催干剂为二月桂酸二丁基锡和环烷酸锌1.5∶2的混合物。 
所述固化剂为王基酚和多聚甲醛1∶1的混合物。 
所述无机填料为云母氧化铁。 
所述促进剂为DMP-30，EP-184，三乙醇胺的一种或几种。 
本发明的另一目的在于，提供一种防腐涂料的制备方法，其特征在于包括如下步骤： 
(1)处理无机填料，将无机填料放入％6NAOH溶液中，75℃浸泡35min，取出用清水洗至PH为中性。将其放入钛酸酯偶联剂的溶液中浸泡30min，过滤，烘干备用。 
(2)将环氧树脂85份，氟碳树脂7份在二甲苯溶液中按比例混合，备用； 
(3)加入甘油，通CO2升温到240℃，时间为2h； 
(4)降温到115℃，加入步骤(2)所述混合液，升温以除去二甲苯，在230℃恒温酯化90min； 
(5)依次加入催干剂、固化剂、促进剂即得成品。 
本发明带来的有益效果是： 
本发明具有干燥时间短，耐老化性，抗腐蚀性优良的特点，无机填料比环氧树脂成本低，可以降低成本，并且无机填料还具有耐候性的特点，有效保证了光伏支架在恶劣环境中不被腐蚀。 
具体实施方式：
下面举例对本发明作进一步说明。 
实施例1 
一种光伏支架包括支架本体，所述支架上设有保护层，所述保护层按重量份数计含有如下组分：环氧树脂70～90份，氟碳树脂5～15份，无机填料10～40份，二甲苯10～30份、催干剂1～5份、固化剂1～5份、甘油1～5份，促进剂0.5～2份 
所述的防腐涂料，其特征在于按重量份数计含有如下组分：环氧树脂85份，氟碳树脂7份，无机填料25份、二甲苯22份、催干剂3份、固化剂3份、甘油2份，促进剂1.5份 
所述催干剂为二月桂酸二丁基锡和环烷酸锌1.5∶2的混合物。 
所述固化剂为王基酚和多聚甲醛1∶1的混合物。 
所述无机填料为云母氧化铁。 
所述促进剂为DMP-30，EP-184，三乙醇胺的一种或几种。 
本发明的另一目的在于，提供一种防腐涂料的制备方法，其特征在于包括如下步骤： 
(1)处理无机填料，将无机填料放入％6NAOH溶液中，75℃浸泡35min，取出用清水洗至PH为中性。将其放入钛酸酯偶联剂的溶液中浸泡30min，过滤，烘干备用。 
(2)将环氧树脂85份，氟碳树脂7份在二甲苯溶液中按比例混合，备用； 
(3)加入甘油，通CO2升温到240℃，时间为2h； 
(4)降温到115℃，加入步骤(2)所述混合液，升温以除去二甲苯，在230℃恒温酯化90min； 
(5)依次加入催干剂、固化剂、促进剂即得成品。 
实施例2 
一种光伏支架包括支架本体，所述支架上设有保护层，所述保护层按重量份数计含有如下组分：环氧树脂82份，氟碳树脂9份，无机填料30份，二甲苯20份、催干剂2份、固化剂3份、甘油3份，促进剂1份 
所述催干剂为二月桂酸二丁基锡和环烷酸锌1.5∶2的混合物。 
所述固化剂为王基酚和多聚甲醛1∶1的混合物。 
所述无机填料为云母氧化铁。 
所述促进剂为DMP-30，EP-184，三乙醇胺的一种或几种。 
本发明的另一目的在于，提供一种防腐涂料的制备方法，其特征在于包括如下步骤： 
(1)处理无机填料，将无机填料放入％6NAOH溶液中，75℃浸泡32min，取出用清水洗至PH为中性。将其放入钛酸酯偶联剂的溶液中浸泡28min，过滤，烘干备用。 
(2)将环氧树脂82份，氟碳树脂9份在二甲苯溶液中按比例混合，备用； 
(3)加入甘油，通CO2升温到250℃，时间为2h； 
(4)降温到115℃，加入步骤(2)所述混合液，升温以除去二甲苯，在230℃恒温酯化85min； 
(5)依次加入催干剂、固化剂、促进剂即得成品。 
将配制的防腐油进行实验室综合性能评价，检测结果见表2： 
表1为研制防腐涂料的测试结果。 
检验项目 检验结果
耐酸性 不起泡，不脱落
耐碱性 不起泡，不脱落
本发明具有干燥时间短，耐老化性，抗腐蚀性优良的特点，无机填料比环氧树脂成本低，可以降低成本，并且无机填料还具有耐候性的特点，有效保证了光伏支架在恶劣环境中不被腐蚀。 
这里本发明的描述和应用是说明性的，并非想将本发明的范围限制在上述实施例中，因此，本发明不受本实施例的限制，任何采用等效替换取得的技术方案均在本发明保护的范围内。 

Claims (3)

1.一种光伏支架，包括支架本体，所述支架上设有保护层，其特征在于按重量份数计含有如下组分：环氧树脂70～90份，氟碳树脂5～15份，无机填料10～40份，二甲苯10～30份、催干剂1～5份、固化剂1～5份、甘油1～5份，促进剂0.5～2份。
2.如权利要求1所述的一种光伏支架,其特征在于按重量份数计含有如下组分：环氧树脂85份，氟碳树脂7份，无机填料25份、二甲苯22份、催干剂3份、固化剂3份、甘油2份，促进剂1.5份,
所述催干剂为二月桂酸二丁基锡和环烷酸锌1.5∶2的混合物, 
所述固化剂为王基酚和多聚甲醛1∶1的混合物,
所述无机填料为云母氧化铁，
所述促进剂为DMP-30，EP-184，三乙醇胺的一种或几种。
3.如权利要求1所述的一种光伏支架,其特征在于本发明的另一目的在于，提供一种防腐涂料的制备方法，包括如下步骤： 
(1) 处理无机填料，将无机填料放入％6NAOH溶液中，75℃浸泡35min，取出用清水洗至PH为中性,
将其放入钛酸酯偶联剂的溶液中浸泡30min，过滤，烘干备用,
(2)将环氧树脂85份，氟碳树脂7份在二甲苯溶液中按比例混合，备用； 
(3)加入甘油，通CO2升温到240℃，时间为2h； 
(4)降温到115℃，加入步骤(2)所述混合液，升温以除去二甲苯，在230℃恒温酯化90min；  
(5)依次加入催干剂、固化剂、促进剂即得成品。
CN201410307790.8A 2014-06-30 2014-06-30 一种光伏支架 Pending CN104087118A (zh)