CN104085028B - 竹片二次碳化工艺 - Google Patents
竹片二次碳化工艺 Download PDFInfo
- Publication number
- CN104085028B CN104085028B CN201410304867.6A CN201410304867A CN104085028B CN 104085028 B CN104085028 B CN 104085028B CN 201410304867 A CN201410304867 A CN 201410304867A CN 104085028 B CN104085028 B CN 104085028B
- Authority
- CN
- China
- Prior art keywords
- bamboo chip
- carbonization
- bamboo
- hours
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种竹片二次碳化工艺，包括以下步骤：步骤一：将破片后得到的竹片放入碳化炉中，进行一次碳化，温度控制在120℃～140℃，时间在2～3小时；步骤二：待一次碳化后的竹片完全冷却后，进行二次碳化，二次碳化先将竹片在110℃～125℃的高温下进行碳化，时间为2～2.5小时，然后升温至130～135℃，时间为1～1.5小时。本发明通过采用二次碳化工艺，使竹材中的有机物如糖、淀粉、蛋白质等在高温、高湿的环境下分解，使真菌等虫类失去营养来源，同时又将附着在竹材中的虫卵及真菌杀死，保证了竹片的加工质量以及延长了产品寿命；另外由于采用二次碳化，使不同竹龄和不同部位的竹片颜色趋于一致，减小了色差，增加了地板的美观性。
Description
技术领域
本发明涉及竹木综合处理技术领域，特别涉及一种竹片二次碳化工艺。
背景技术
竹子作为一种常见的植物，在工业应用中具有非常广阔的应用价值，特别是将竹子进行处理后，可以制成家具、地板、用具等多种产品，相对于木制品来说具有价格低廉、重量较轻、材料来源广泛等多重优点，碳化是竹制品加工中一个非常重要的环节，但是在现有技术中一般只有一次碳化，通过一次碳化处理后的竹片虽然也能满足加工要求，但是总体而言，还是存在竹片表面物理性质不稳定的问题。
发明内容
有鉴于此，本发明的目的是提供一种竹片二次碳化工艺，能够进一步稳定竹片表面的物理性质，同时加剧了竹片内部有机物如糖、淀粉、蛋白质等在高温、高湿的环境下分解，保证了竹片的加工质量。
本发明的目的是通过以下技术方案实现的：
本发明的竹片二次碳化工艺，包括以下步骤：
步骤一：将经过粗铣后的竹片进行蒸煮；
步骤二：将经过步骤一处理过的竹片放入碳化炉中，进行一次碳化，温度控制在120℃～140℃，时间在2～3小时；
步骤三：待一次碳化后的竹片完全冷却后，进行二次碳化，二次碳化先将竹片在110℃～125℃的高温下进行碳化，时间为2～2.5小时，然后升温至130～135℃，时间为1～1.5小时。
进一步，所述步骤一中，所述蒸煮是将竹片放入60℃～80℃的热水容器中进行静置，时间为5～10min，然后将容器中的水进行加热至沸腾状态，并保持5～8小时；
进一步，在步骤一中，在进行蒸煮环节之前，将竹片置于浓度为75％的乙醇溶液中进行浸泡，时间为10～30min。
进一步，步骤二与步骤三的碳化过程中，湿度保持在75％～85％。
本发明的有益效果是：
本发明通过采用二次碳化工艺，使竹材中的有机物如糖、淀粉、蛋白质等在高温、高湿的环境下分解，使真菌等虫类失去营养来源，同时又将附着在竹材中的虫卵及真菌杀死，保证了竹片的加工质量以及延长了产品寿命；另外由于采用二次碳化，使不同竹龄和不同部位的竹片颜色趋于一致，减小了色差，增加了地板的美观性。
本发明的其他优点、目标和特征在某种程度上将在随后的说明书中进行阐述，并且在某种程度上，基于对下文的考察研究对本领域技术人员而言将是显而易见的，或者可以从本发明的实践中得到教导。本发明的目标和其他优点可以通过下面的说明书和权利要求书来实现和获得。
具体实施方式
以下将参照附图，对本发明的优选实施例进行详细的描述。应当理解，优选实施例仅为了说明本发明，而不是为了限制本发明的保护范围。
实施例一
本实施例的竹片二次碳化工艺，包括以下步骤：
步骤一：将破片后得到的竹片放入碳化炉中，进行一次碳化，温度控制在120℃，时间在3小时；
步骤二：待一次碳化后的竹片完全冷却后，进行二次碳化，二次碳化先将竹片在110℃的高温下进行碳化，时间为2.5小时，然后升温至130℃，时间为1.5小时。
本实施例中，步骤一与步骤二的碳化过程中，湿度保持在75％。
实施例二
本实施例中的竹片二次碳化工艺，包括以下步骤：
步骤一：将破片后得到的竹片放入碳化炉中，进行一次碳化，温度控制在140℃，时间在2小时；
步骤二：待一次碳化后的竹片完全冷却后，进行二次碳化，二次碳化先将竹片在125℃的高温下进行碳化，时间为2小时，然后升温至135℃，时间为1小时。
本实施例中，在步骤一与步骤二的碳化过程中，湿度保持在85％。
实施例三
本实施例的竹片二次碳化工艺，包括以下步骤：
步骤一：将破片后得到的竹片放入碳化炉中，进行一次碳化，温度控制在130℃，时间在2.5小时；
步骤二：待一次碳化后的竹片完全冷却后，进行二次碳化，二次碳化先将竹片在120℃的高温下进行碳化，时间为2.2小时，然后升温至132℃，时间为1.2小时。
本实施例中，在步骤一与步骤二的碳化过程中，湿度保持在80％。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (2)
1.竹片二次碳化工艺，其特征在于：包括以下步骤：
步骤一：将经过粗铣后的竹片进行蒸煮，所述蒸煮是将竹片放入60℃～80℃的热水容器中进行静置，时间为5～10min，然后将容器中的水进行加热至沸腾状态，并保持5～8小时，在进行蒸煮环节之前，将竹片置于浓度为75％的乙醇溶液中进行浸泡，时间为10～30min；
蒸煮后，将破片后得到的竹片放入碳化炉中，进行一次碳化，温度控制在120℃～140℃，时间在2～3小时；
步骤二：待一次碳化后的竹片完全冷却后，进行二次碳化，二次碳化先将竹片在110℃～125℃的高温下进行碳化，时间为2～2.5小时，然后升温至130～135℃，时间为1～1.5小时。
2.根据权利要求1所述的竹片二次碳化工艺，其特征在于：步骤一与步骤二的碳化过程中，湿度保持在75％～85％。