CN104084527A - 一种铬铁矿/膨胀蛭石复合的醇基铸造涂料及其制作方法 - Google Patents

一种铬铁矿/膨胀蛭石复合的醇基铸造涂料及其制作方法 Download PDF

Info

Publication number
CN104084527A
CN104084527A CN201410266567.3A CN201410266567A CN104084527A CN 104084527 A CN104084527 A CN 104084527A CN 201410266567 A CN201410266567 A CN 201410266567A CN 104084527 A CN104084527 A CN 104084527A
Authority
CN
China
Prior art keywords
parts
alcohol
hour
add
chromite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410266567.3A
Other languages
English (en)
Inventor
黄浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Hongkun Auto Parts Co Ltd
Original Assignee
Wuhu Hongkun Auto Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Hongkun Auto Parts Co Ltd filed Critical Wuhu Hongkun Auto Parts Co Ltd
Priority to CN201410266567.3A priority Critical patent/CN104084527A/zh
Publication of CN104084527A publication Critical patent/CN104084527A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铬铁矿/膨胀蛭石复合的醇基铸造涂料，其特征在于，由下列重量份的原料制成：铬铁矿65-85、硅藻土15-20、钙石粉4-9、膨胀蛭石1-3、乙基纤维素0.5-0.7、硅油1-2、氯化钙0.3-0.7、碳酸锂0.3-0.5、三乙烯四胺1.1-2.3、偏苯三酸酐0.6-2.1、核桃壳13-16、酚醛树脂3-5、六亚甲基四胺2-6、乙醇40-60、助剂3-6；本发明的涂料具有强度高、悬浮性好、易剥离等优点；本发明制备方法工艺简单，原料价格低廉、来源广泛，具有良好的应用前景。

Description

一种铬铁矿/膨胀蛭石复合的醇基铸造涂料及其制作方法
技术领域
本发明涉及铸造涂料领域，具体涉及一种铬铁矿/膨胀蛭石复合的醇基铸造涂料及其制作方法。
背景技术
铸造涂料是指用来涂敷在型腔或砂芯表面，以改变其表面耐火度、化学稳定性、抗金属冲刷性、抗粘砂性等性能的铸造辅助材料，它是由多种性质不同的材料组成的分散系，其组成主要包括耐火材料、悬浮剂、载体、粘结剂及特殊添加剂等组成。作用于铸件时要求涂料有良好的工艺性能、工作性能、质量稳定性以及施涂重现性，一方面可以起到隔热，均衡温度，免除金属液的冲击腐蚀性的目的，另一方面可以防止铸件产品因局部冷却过快而造成的开裂、砂眼、白口铁形成等缺陷。铸造涂料种类繁多，大体可以分为两类：水基涂料和醇基涂料。其中醇基涂料在涂覆后经点燃既可固化，不需烘干，能缩短生产周期，简化工艺，减少烘干设备投资，是被铸造界广为使用的一种快干涂料，已广泛应用于钢、铁、有色铸件的生产中。
然而现有技术中醇基铸造涂料有诸多缺陷，比如：悬浮稳定性较差、在长途运输和存放过程中易分层、耐高温性能较差、硬度低、化学稳定性差、抗金属冲刷性能低、抗粘砂性弱等，使得醇基铸造涂料功能单一，无法满足大规模的工业化生产。
发明内容
本发明的目的就是提供一种铬铁矿/膨胀蛭石复合的醇基铸造涂料及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种铬铁矿/膨胀蛭石复合的醇基铸造涂料，其特征在于，由下列重量份的原料制成：铬铁矿65-85、硅藻土15-20、钙石粉4-9、膨胀蛭石1-3、乙基纤维素0.5-0.7、硅油1-2、氯化钙0.3-0.7、碳酸锂0.3-0.5、三乙烯四胺1.1-2.3、偏苯三酸酐0.6-2.1、核桃壳13-16、酚醛树脂3-5、六亚甲基四胺2-6、乙醇40-60、助剂3-6。
所述的助剂由下列重量份原料制成：贝壳20-25、海泡石35-45、锆英石55-75、硅烷偶联剂KH-5701.4-4.6、二甲基硅油0.4-0.7、二茂铁 1.2-3.2、氧化铁粉2-5、煤焦油3-5、木质素磺酸钙0.3-0.6、纳米碳化硅粉0.1-0.3、碳酸钙2.3-4.7、聚乙烯醇5-7、适量水，其制备方法是将贝壳、海泡石、锆英石放入煅烧炉中在550-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入氧化铁粉、木质素磺酸钙研磨，喷雾干燥制得干燥粉；将二甲基硅油、二茂铁加入到硅烷偶联剂KH-570中搅拌至溶解，加入纳米碳化硅粉、煤焦油、碳酸钙继续搅拌10-20分钟，制得浆体；将上述制得的干燥粉和浆体混合搅拌20-40分钟，再加入其他剩余成分加水研磨造粒，烘干即得。
所述的一种铬铁矿/膨胀蛭石复合的醇基铸造涂料的制备方法，其特征在于包括以下步骤：
（1）将核桃壳放入炭化炉中在410-540℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒硅油搅拌混匀，制得改性的核桃壳粉；
（2）将上述步骤制得的改性核桃壳粉与钙石粉、硅藻土、1/4重量的乙醇一起搅拌成浆并加热至140-160℃，加入三乙烯四胺、偏苯三酸酐保持温度研磨1-2小时，冷却至50-60℃加入碳酸锂研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将膨胀蛭石放入煅烧炉中于530-650℃下煅烧处理1-3小时，取出冷却至室温粉碎，与1/5重量的乙醇搅拌均匀，静置10-12小时，然后加入乙基纤维素、酚醛树脂、六亚甲基四胺加热至70-80℃搅拌30-40分钟；
（4）将铬铁矿投入反应釜中，加入氯化钙和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、助剂，同时将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
本发明有以下有益效果：本发明的涂料具有强度高、悬浮性好、易剥离等优点；本发明制备方法工艺简单，原料价格低廉、来源广泛，具有良好的应用前景。
具体实施方式
所述的一种铬铁矿/膨胀蛭石复合的醇基铸造涂料，其特征在于，由下列重量份的原料制成：铬铁矿69、硅藻土17、钙石粉4、膨胀蛭石1、乙基纤维素0.5、硅油1、氯化钙0.3、碳酸锂0.3、三乙烯四胺1.5、偏苯三酸酐0.6、核桃壳13、酚醛树脂3、六亚甲基四胺2、乙醇40、助剂3。
所述的助剂由下列重量份原料制成：贝壳23、海泡石39、锆英石57、硅烷偶联剂KH-5703.4、二甲基硅油0.4、二茂铁 3.2、氧化铁粉2、煤焦油3、木质素磺酸钙0.3、纳米碳化硅粉0.3、碳酸钙2.3、聚乙烯醇5、适量水，其制备方法是将贝壳、海泡石、锆英石放入煅烧炉中在550-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入氧化铁粉、木质素磺酸钙研磨，喷雾干燥制得干燥粉；将二甲基硅油、二茂铁加入到硅烷偶联剂KH-570中搅拌至溶解，加入纳米碳化硅粉、煤焦油、碳酸钙继续搅拌10-20分钟，制得浆体；将上述制得的干燥粉和浆体混合搅拌20-40分钟，再加入其他剩余成分加水研磨造粒，烘干即得。
制作方法包括以下步骤：
（1）将核桃壳放入炭化炉中在410-540℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒硅油搅拌混匀，制得改性的核桃壳粉；
（2）将上述步骤制得的改性核桃壳粉与钙石粉、硅藻土、1/4重量的乙醇一起搅拌成浆并加热至140-160℃，加入三乙烯四胺、偏苯三酸酐保持温度研磨1-2小时，冷却至50-60℃加入碳酸锂研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将膨胀蛭石放入煅烧炉中于530-650℃下煅烧处理1-3小时，取出冷却至室温粉碎，与1/5重量的乙醇搅拌均匀，静置10-12小时，然后加入乙基纤维素、酚醛树脂、六亚甲基四胺加热至70-80℃搅拌30-40分钟；
（4）将铬铁矿投入反应釜中，加入氯化钙和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、助剂，同时将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
通过上述实施例加工得到的铸造涂料的技术指标如下：
（1）固含量：28.98%；
（2）涂层耐磨性：0.513；
（3）放置24小时涂料悬浮率：99.05%；
（4）涂敷、烘干、冷却后涂层外观：无裂纹、无起泡和肉眼可见的针孔的均匀涂层。

Claims (2)

1.一种铬铁矿/膨胀蛭石复合的醇基铸造涂料，其特征在于，由下列重量份的原料制成：铬铁矿65-85、硅藻土15-20、钙石粉4-9、膨胀蛭石1-3、乙基纤维素0.5-0.7、硅油1-2、氯化钙0.3-0.7、碳酸锂0.3-0.5、三乙烯四胺1.1-2.3、偏苯三酸酐0.6-2.1、核桃壳13-16、酚醛树脂3-5、六亚甲基四胺2-6、乙醇40-60、助剂3-6；所述的助剂由下列重量份原料制成：贝壳20-25、海泡石35-45、锆英石55-75、硅烷偶联剂KH-5701.4-4.6、二甲基硅油0.4-0.7、二茂铁 1.2-3.2、氧化铁粉2-5、煤焦油3-5、木质素磺酸钙0.3-0.6、纳米碳化硅粉0.1-0.3、碳酸钙2.3-4.7、聚乙烯醇5-7、适量水，其制备方法是将贝壳、海泡石、锆英石放入煅烧炉中在550-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入氧化铁粉、木质素磺酸钙研磨，喷雾干燥制得干燥粉；将二甲基硅油、二茂铁加入到硅烷偶联剂KH-570中搅拌至溶解，加入纳米碳化硅粉、煤焦油、碳酸钙继续搅拌10-20分钟，制得浆体；将上述制得的干燥粉和浆体混合搅拌20-40分钟，再加入其他剩余成分加水研磨造粒，烘干即得。
2.根据权利要求1所述的一种铬铁矿/膨胀蛭石复合的醇基铸造涂料的制作方法，其特征在于包括以下步骤：
（1）将核桃壳放入炭化炉中在410-540℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒硅油搅拌混匀，制得改性的核桃壳粉；
（2）将上述步骤制得的改性核桃壳粉与钙石粉、硅藻土、1/4重量的乙醇一起搅拌成浆并加热至140-160℃，加入三乙烯四胺、偏苯三酸酐保持温度研磨1-2小时，冷却至50-60℃加入碳酸锂研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将膨胀蛭石放入煅烧炉中于530-650℃下煅烧处理1-3小时，取出冷却至室温粉碎，与1/5重量的乙醇搅拌均匀，静置10-12小时，然后加入乙基纤维素、酚醛树脂、六亚甲基四胺加热至70-80℃搅拌30-40分钟；
（4）将铬铁矿投入反应釜中，加入氯化钙和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、助剂，同时将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
CN201410266567.3A 2014-06-16 2014-06-16 一种铬铁矿/膨胀蛭石复合的醇基铸造涂料及其制作方法 Pending CN104084527A (zh)