CN104014725B - 一种改性猪骨型醇基铸造涂料及其制作方法 - Google Patents

一种改性猪骨型醇基铸造涂料及其制作方法 Download PDF

Info

Publication number
CN104014725B
CN104014725B CN201410194503.7A CN201410194503A CN104014725B CN 104014725 B CN104014725 B CN 104014725B CN 201410194503 A CN201410194503 A CN 201410194503A CN 104014725 B CN104014725 B CN 104014725B
Authority
CN
China
Prior art keywords
sus domestica
modified
hour
powder
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410194503.7A
Other languages
English (en)
Other versions
CN104014725A (zh
Inventor
方学军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Haimen Huaxia Li Li Network Technology Service Co., Ltd.
Original Assignee
方学军
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 方学军 filed Critical 方学军
Priority to CN201410194503.7A priority Critical patent/CN104014725B/zh
Publication of CN104014725A publication Critical patent/CN104014725A/zh
Application granted granted Critical
Publication of CN104014725B publication Critical patent/CN104014725B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种改性猪骨型醇基铸造涂料，其特征在于，由下列重量份的原料制成：高铝水泥10-14、聚乙烯醇缩丁醛0.3-0.5、烷基磺酸钠0.2-0.6、锆英粉45-60、白刚玉40-60、纳米级粘土1-3、烷基化二苯胺0.1-0.3、硝酸钠0.2-0.4、黄原胶1-2、含氢硅油1.2-3.2、猪骨12-14、酚醛树脂3-5、六亚甲基四胺1-3、乙醇40-50、助剂3-7；本发明将动物骨骼猪骨改性后添加到原料中，起到很好的悬浮效果和耐高温强度，同时综合利用其它原料相互复合制得的涂料具有耐火性好、抗粘砂能力强、刷涂性佳、流平性好等优点，解决了我国大型铸件生产企业使用的铸造涂料长期依赖进口的问题，填补了国内空白，适应性好。

Description

一种改性猪骨型醇基铸造涂料及其制作方法
技术领域
本发明涉及铸造涂料领域，具体涉及一种改性猪骨型醇基铸造涂料及其制作方法。
背景技术
铸造涂料是指用来涂敷在型腔或砂芯表面，以改变其表面耐火度、化学稳定性、抗金属冲刷性、抗粘砂性等性能的铸造辅助材料，它是由多种性质不同的材料组成的分散系，其组成主要包括耐火材料、悬浮剂、载体、粘结剂及特殊添加剂等组成。作用于铸件时要求涂料有良好的工艺性能、工作性能、质量稳定性以及施涂重现性，一方面可以起到隔热，均衡温度，免除金属液的冲击腐蚀性的目的，另一方面可以防止铸件产品因局部冷却过快而造成的开裂、砂眼、白口铁形成等缺陷。铸造涂料种类繁多，大体可以分为两类：水基涂料和醇基涂料。其中醇基涂料在涂覆后经点燃既可固化，不需烘干，能缩短生产周期，简化工艺，减少烘干设备投资，是被铸造界广为使用的一种快干涂料，已广泛应用于钢、铁、有色铸件的生产中。
然而现有技术中醇基铸造涂料有诸多缺陷，比如：悬浮稳定性较差、在长途运输和存放过程中易分层、耐高温性能较差、硬度低、化学稳定性差、抗金属冲刷性能低、抗粘砂性弱等，使得醇基铸造涂料功能单一，无法满足大规模的工业化生产。
发明内容
本发明的目的就是提供一种改性猪骨型醇基铸造涂料及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种改性猪骨型醇基铸造涂料，其特征在于，由下列重量份的原料制成：高铝水泥10-14、聚乙烯醇缩丁醛0.3-0.5、烷基磺酸钠0.2-0.6、锆英粉45-60、白刚玉40-60、纳米级粘土1-3、烷基化二苯胺0.1-0.3、硝酸钠0.2-0.4、黄原胶1-2、含氢硅油1.2-3.2、猪骨12-14、酚醛树脂3-5、六亚甲基四胺1-3、乙醇40-50、助剂3-7。
所述的助剂由下列重量份原料制成：猪骨25-30、累托石35-45、偏高岭土65-95、硅灰30-45、硅烷偶联剂KH-5702-6、硅溶胶0.4-0.8、纳米碳化硅粉1-3、纳米四氧化三铁1.2-3.4、当归粉0.6-1.2、羧甲基淀粉钠0.4-0.9、羧甲基纤维素4-7、适量水，其制备方法是将猪骨、累托石、偏高岭土放入煅烧炉中在560-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入纳米碳化硅粉、硅溶胶、羧甲基淀粉钠研磨，喷雾干燥制得干燥粉；取硅灰、当归粉加入硅烷偶联剂KH-570搅拌制成浆，加纳米四氧化三铁研磨20-30分钟，制得改性的硅灰；将上述制得的干燥粉、改性硅灰及其他剩余成分加水研磨造粒，烘干即得。
所述的一种改性猪骨型醇基铸造涂料的制备方法，其特征在于包括以下步骤：
（1）将猪骨放入炭化炉中在405-520℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒雾状含氢硅油搅拌混匀，制的改性猪骨粉；
（2）将上述步骤制得的改性猪骨粉与纳米级粘土、1/4重量的乙醇一起研磨并加热至120-135℃，加入聚乙烯醇缩丁醛、烷基磺酸钠保持温度搅拌1-2小时，冷却至50-60℃加入硝酸钠研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将高铝水泥、白刚玉放入煅烧炉中于530-680℃下煅烧2-4小时，取出冷却粉碎，加入1/5重量的乙醇搅拌均匀，静置10-12小时，然后加入烷基化二苯胺、酚醛树脂、六亚甲基四胺加热至70-80℃搅拌30-40分钟；
（4）将锆英粉投入反应釜中，加入黄原胶和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、助剂，同时将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
本发明有以下有益效果：本发明将动物骨骼猪骨改性后添加到原料中，起到很好的悬浮效果和耐高温强度，同时综合利用其它原料相互复合制得的涂料具有耐火性好、抗粘砂能力强、刷涂性佳、流平性好等优点，解决了我国大型铸件生产企业使用的铸造涂料长期依赖进口的问题，填补了国内空白，适应性好。
具体实施方式
所述的一种改性猪骨型醇基铸造涂料，其特征在于，由下列重量份的原料制成：高铝水泥10、聚乙烯醇缩丁醛0.3、烷基磺酸钠0.2、锆英粉60、白刚玉46、纳米级粘土1、烷基化二苯胺0.1、硝酸钠0.2、黄原胶1、含氢硅油1.2、猪骨12、酚醛树脂5、六亚甲基四胺1、乙醇40、助剂3。
所述的助剂由下列重量份原料制成：猪骨26、累托石38、偏高岭土85、硅灰30、硅烷偶联剂KH-5702、硅溶胶0.4、纳米碳化硅粉1、纳米四氧化三铁1.2、当归粉0.6、羧甲基淀粉钠0.4、羧甲基纤维素4、适量水，其制备方法是将猪骨、累托石、偏高岭土放入煅烧炉中在560-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入纳米碳化硅粉、硅溶胶、羧甲基淀粉钠研磨，喷雾干燥制得干燥粉；取硅灰、当归粉加入硅烷偶联剂KH-570搅拌制成浆，加纳米四氧化三铁研磨20-30分钟，制得改性的硅灰；将上述制得的干燥粉、改性硅灰及其他剩余成分加水研磨造粒，烘干即得。
制作方法包括以下步骤：
（1）将猪骨放入炭化炉中在405-520℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒雾状含氢硅油搅拌混匀，制的改性猪骨粉；
（2）将上述步骤制得的改性猪骨粉与纳米级粘土、1/4重量的乙醇一起研磨并加热至120-135℃，加入聚乙烯醇缩丁醛、烷基磺酸钠保持温度搅拌1-2小时，冷却至50-60℃加入硝酸钠研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将高铝水泥、白刚玉放入煅烧炉中于530-680℃下煅烧2-4小时，取出冷却粉碎，加入1/5重量的乙醇搅拌均匀，静置10-12小时，然后加入烷基化二苯胺、酚醛树脂、六亚甲基四胺加热至70-80℃搅拌30-40分钟；
（4）将锆英粉投入反应釜中，加入黄原胶和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、助剂，同时将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
通过上述实施例加工得到的铸造涂料的使用技术指标如下：
（1）涂层耐磨性：0.743；
（2）放置24小时涂料悬浮率：98%；
（3）涂料密度：1.61g/cm3；
（4）涂层的常温强度：770g/mm；
（5）经过1200℃焙烧后涂料涂层的强度：580g/mm；
（6）涂敷、烘干、冷却后涂层外观：无裂纹、无起泡和肉眼可见的针孔的均匀涂层。

Claims (1)

1.一种改性猪骨型醇基铸造涂料，其特征在于，由下列重量份的原料制成：高铝水泥10-14、聚乙烯醇缩丁醛0.3-0.5、烷基磺酸钠0.2-0.6、锆英粉45-60、白刚玉40-60、纳米级粘土1-3、烷基化二苯胺0.1-0.3、硝酸钠0.2-0.4、黄原胶1-2、含氢硅油1.2-3.2、猪骨12-14、酚醛树脂3-5、六亚甲基四胺1-3、乙醇40-50、助剂3-7；所述的助剂由下列重量份原料制成：猪骨25-30、累托石35-45、偏高岭土65-95、硅灰30-45、硅烷偶联剂KH-5702-6、硅溶胶0.4-0.8、纳米碳化硅粉1-3、纳米四氧化三铁1.2-3.4、当归粉0.6-1.2、羧甲基淀粉钠0.4-0.9、羧甲基纤维素4-7、适量水，其制备方法是将猪骨、累托石、偏高岭土放入煅烧炉中在560-680℃下煅烧2-3小时，取出，放入8-12%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干粉碎，加水搅拌成浆，同时，加入纳米碳化硅粉、硅溶胶、羧甲基淀粉钠研磨，喷雾干燥制得干燥粉；取硅灰、当归粉加入硅烷偶联剂KH-570搅拌制成浆，加纳米四氧化三铁研磨20-30分钟，制得改性的硅灰；将上述制得的干燥粉、改性硅灰及其他剩余成分加水研磨造粒，烘干即得；
所述的改性猪骨型醇基铸造涂料的制作方法，包括以下步骤：
（1）将猪骨放入炭化炉中在405-520℃下煅烧处理3-4小时，取出，放入10-12%的盐酸溶液中浸泡3-6小时，过滤取出，用清水反复洗涤，烘干粉碎，喷洒雾状含氢硅油搅拌混匀，制得改性猪骨粉；
（2）将上述步骤制得的改性猪骨粉与纳米级粘土、1/4重量的乙醇一起研磨并加热至120-135℃，加入聚乙烯醇缩丁醛、烷基磺酸钠保持温度搅拌1-2小时，冷却至50-60℃加入硝酸钠研磨30-40分钟，喷雾干燥制得干燥粉；
（3）将高铝水泥、白刚玉放入煅烧炉中于530-680℃下煅烧2-4小时，取出冷却粉碎，加入1/5重量的乙醇搅拌均匀，静置10-12小时，然后加入烷基化二苯胺、酚醛树脂、六亚甲基四胺加热至70-80℃搅拌30-40分钟；
（4）将锆英粉投入反应釜中，加入黄原胶和剩余量的乙醇搅拌研磨10-15分钟，再加入步骤（2）、（3）产物、助剂，同时将反应釜温度缓慢升至75-85℃，保持温度搅拌20-40分钟，研磨直至细度达到50μm以下即可。
CN201410194503.7A 2014-05-09 2014-05-09 一种改性猪骨型醇基铸造涂料及其制作方法 Active CN104014725B (zh)