CN104058682A - 一种抗菌加气砖 - Google Patents

一种抗菌加气砖 Download PDF

Info

Publication number
CN104058682A
CN104058682A CN201410231241.7A CN201410231241A CN104058682A CN 104058682 A CN104058682 A CN 104058682A CN 201410231241 A CN201410231241 A CN 201410231241A CN 104058682 A CN104058682 A CN 104058682A
Authority
CN
China
Prior art keywords
parts
antibacterial
coal ash
mucine
xylo
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410231241.7A
Other languages
English (en)
Inventor
张思坦
张绪庆
胡星
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU EAST CHINA GYPSUM Co Ltd
Original Assignee
BENGBU EAST CHINA GYPSUM Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU EAST CHINA GYPSUM Co Ltd filed Critical BENGBU EAST CHINA GYPSUM Co Ltd
Priority to CN201410231241.7A priority Critical patent/CN104058682A/zh
Publication of CN104058682A publication Critical patent/CN104058682A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗菌加气砖，其是由下述重量份的原料制得：硅酸盐水泥15-25、脱硫石膏18-22、煤灰渣4-6，淀粉1-2，铝粉0.1-0.2、羧甲基纤维素钠1-2、苯丙乳液3-5，四氧化三铁0.1-0.2、硬脂酸1-2、淤泥4-8、锰渣12-15、三乙醇胺1-2、乙二醇1-3，木质素磺酸钙1-2，助剂3-6；本发明抗菌性能优异，同时抗裂性能相对较高,满足常规加气砖性能要求。

Description

一种抗菌加气砖
技术领域
本发明涉及加气砖领域，确切地说是一种抗菌加气砖。
背景技术
加气砖，指的是通过高温蒸压设备工艺生产的加气混凝土砌块，现有加气砖品种单一，性能差，无法满足日益增加的市场需求。
发明内容
本发明的目的在于提供一种抗菌加气砖。
上述目的通过以下方案实现：
一种抗菌加气砖，其特征在于：其是由下述重量份的原料制得：
硅酸盐水泥15-25、脱硫石膏18-22、煤灰渣4-6，淀粉1-2，铝粉0.1-0.2、羧甲基纤维素钠1-2、苯丙乳液3-5，四氧化三铁0.1-0.2、硬脂酸1-2、淤泥4-8、锰渣12-15、三乙醇胺1-2、乙二醇1-3，木质素磺酸钙1-2，助剂3-6；
所述的助剂由下述重量份的原料制得：膨润土10-15，煤灰渣6-8、钢渣5-8、凹凸棒土15-18、醋酸钠1-2、氧化铜1-2、明胶 0.2-0.4，氯化石蜡 2.8-3.3、异构醇聚氧乙烯醚 0.2-0.4、硅烷偶联剂KH550 2-4；
所述的助剂的制备方法为：
取煤灰渣、钢渣混匀后，破碎，所得粉料于720-800℃下于煅烧2-4小时，再取出冷却，与凹凸棒土、明胶以及适量水混匀后，研磨30-50分钟，取出加12-18%的氢氧化钠溶液调PH为8-8.5，再加入膨润土，研磨浆料至400-500目后，再加盐酸溶液调为中性，喷雾干燥，所得粉末与其它剩余原料混合，混合均匀即得。
所述的一种抗菌加气砖，其特征在于：
制备方法为：
（1）将除水泥、铝粉、羧甲基纤维素钠以外的其它原料混匀，加入适量水，在30-35℃下搅拌均匀后，再加入水泥、铝粉、羧甲基纤维素钠，搅拌均匀，得混合水泥浆料；
（2）将混合水泥浆料浇筑入模成型，后在35-42℃下预养3-4小时，脱模，切割，蒸压养护后，即得。
本发明的有益效果为：本发明抗菌性能优异，同时抗裂性能相对较高,,满足常规加气砖性能要求。
具体实施方式
一种抗菌加气砖，其是由下述重量kg的原料制得：
硅酸盐水泥25、脱硫石膏22、煤灰渣4，淀粉1，铝粉0.2、羧甲基纤维素钠2、苯丙乳液3，四氧化三铁0.2、硬脂酸1、淤泥8、锰渣15、三乙醇胺1、乙二醇3，木质素磺酸钙2，助剂6；
所述的助剂由下述重量kg的原料制得：膨润土15，煤灰渣8、钢渣5、凹凸棒土18、醋酸钠2、氧化铜1、明胶 0.4，氯化石蜡 3.3、异构醇聚氧乙烯醚 0.4、硅烷偶联剂KH550 3；
所述的助剂的制备方法为：
取煤灰渣、钢渣混匀后，破碎，所得粉料于800℃下于煅烧4小时，再取出冷却，与凹凸棒土、明胶以及适量水混匀后，研磨40分钟，取出加12%的氢氧化钠溶液调PH为8，再加入膨润土，研磨浆料至500目后，再加盐酸溶液调为中性，喷雾干燥，所得粉末与其它剩余原料混合，混合均匀即得。
所述的一种抗菌加气砖，
制备方法为：
（1）将除水泥、铝粉、羧甲基纤维素钠以外的其它原料混匀，加入适量水，在35℃下搅拌均匀后，再加入水泥、铝粉、羧甲基纤维素钠，搅拌均匀，得混合水泥浆料；
（2）将混合水泥浆料浇筑入模成型，后在38℃下预养4小时，脱模，切割，蒸压养护后，即得。
本实施例所得加气砖的平均容重为660kg/m3,保温性能好，平均值抗压强度为8.2MPa。

Claims (2)

1.一种抗菌加气砖，其特征在于：其是由下述重量份的原料制得：
硅酸盐水泥15-25、脱硫石膏18-22、煤灰渣4-6，淀粉1-2，铝粉0.1-0.2、羧甲基纤维素钠1-2、苯丙乳液3-5，四氧化三铁0.1-0.2、硬脂酸1-2、淤泥4-8、锰渣12-15、三乙醇胺1-2、乙二醇1-3，木质素磺酸钙1-2，助剂3-6；
所述的助剂由下述重量份的原料制得：膨润土10-15，煤灰渣6-8、钢渣5-8、凹凸棒土15-18、醋酸钠1-2、氧化铜1-2、明胶 0.2-0.4，氯化石蜡 2.8-3.3、异构醇聚氧乙烯醚 0.2-0.4、硅烷偶联剂KH550 2-4；
所述的助剂的制备方法为：
取煤灰渣、钢渣混匀后，破碎，所得粉料于720-800℃下于煅烧2-4小时，再取出冷却，与凹凸棒土、明胶以及适量水混匀后，研磨30-50分钟，取出加12-18%的氢氧化钠溶液调PH为8-8.5，再加入膨润土，研磨浆料至400-500目后，再加盐酸溶液调为中性，喷雾干燥，所得粉末与其它剩余原料混合，混合均匀即得。
2.根据权利要求1所述的一种抗菌加气砖，其特征在于：
制备方法为：
（1）将除水泥、铝粉、羧甲基纤维素钠以外的其它原料混匀，加入适量水，在30-35℃下搅拌均匀后，再加入水泥、铝粉、羧甲基纤维素钠，搅拌均匀，得混合水泥浆料；
（2）将混合水泥浆料浇筑入模成型，后在35-42℃下预养3-4小时，脱模，切割，蒸压养护后，即得。
CN201410231241.7A 2014-05-29 2014-05-29 一种抗菌加气砖 Pending CN104058682A (zh)