CN103449765A - 一种防腐蚀加气砖的制备方法 - Google Patents

一种防腐蚀加气砖的制备方法 Download PDF

Info

Publication number
CN103449765A
CN103449765A CN2013103276682A CN201310327668A CN103449765A CN 103449765 A CN103449765 A CN 103449765A CN 2013103276682 A CN2013103276682 A CN 2013103276682A CN 201310327668 A CN201310327668 A CN 201310327668A CN 103449765 A CN103449765 A CN 103449765A
Authority
CN
China
Prior art keywords
parts
hour
preparation
sodium
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103276682A
Other languages
English (en)
Inventor
潘逸东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2013103276682A priority Critical patent/CN103449765A/zh
Publication of CN103449765A publication Critical patent/CN103449765A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防腐蚀加气砖的制备方法，所需原料重量份配比为：中药粉1-2，玻璃废渣12-14、硼砂1-2、尼龙纤维1-2、沥青2-4、生石灰10-15、甲基硅醇钠1-2、水泥20-25，亚硝酸钠0.3-0.8、苯甲酸特丁1-2、三乙醇胺0.2-0.4、纳米沸石粉2-4、仲烷基磺酸钠0.06-0.1、十二烷基硫酸钠1-3，铝粉0.03-0.04，菜籽饼粉0.002-0.004。

Description

一种防腐蚀加气砖的制备方法
技术领域
本发明涉及加气砖领域，确切地说是一种防腐蚀加气砖的制备方法。
背景技术
    加气砖，是通过高温蒸压设备工艺生产的加气混凝土砌块。“加气砖”可以理解为一个简化的或是一个通用的名称。其涵盖的产品范围应该要大一点，即采用包括蒸压在内的其他各种工艺生产的砖品。
以前建筑市场所用的墙体材料主要是红砖，现在许多先进地区已经全面禁止红砖使用。
现有加气砖发展技术缓慢，无法满足多元化的市场需求。
发明内容
本发明的目的在于提供一种防腐蚀加气砖的制备方法。
上述目的通过以下方案实现：
一种防腐蚀加气砖的制备方法，其特征在于：所需原料重量份配比为：中药粉1-2，玻璃废渣12-14、硼砂1-2、尼龙纤维1-2、沥青2-4、生石灰10-15、甲基硅醇钠1-2、水泥20-25，亚硝酸钠0.3-0.8、苯甲酸特丁1-2、三乙醇胺0.2-0.4、纳米沸石粉2-4、仲烷基磺酸钠0.06-0.1、十二烷基硫酸钠1-3，铝粉0.03-0.04,菜籽饼粉0.002-0.004；
制备方法为：
（1)取2-4份五倍子、3-5份地肤子、1-2份山姜花、3-5份黄连、1-2份板蓝根混匀后，烤干后，磨粉，得中药粉备用；
（2）按重量份取玻璃废渣，破碎，过100-200目筛，于700-800℃下煅烧1-2小时后，降温至800-900℃，保温1-2小时，取出，于浓度为8-10%的氢氟酸溶液中浸泡9-12小时，取出，混合搅拌，使其充分混合均匀后，再加入中药粉，混匀，然后再与其余物料混匀后，三辊研磨机研磨1-2小时后，再加入适量水，浇筑入模成型，预养，脱模，切割，得砌块坯；
　（3）将砌块坯放入反应釜中按照常规工艺蒸压养护后，入库成品即得。所述的蒸压养护工艺的时长为10-15小时，温度为175-185℃，压力为1-1.5MPa。
本发明的有益效果为：本发明所指的加气砖防腐蚀效果显著，强度高，使用方便，中药粉的加入，杀菌效果显著。
具体实施方式
一种防腐蚀加气砖的制备方法，所需原料重量份配比为：中药粉1，玻璃废渣14、硼砂1、尼龙纤维2、沥青4、生石灰10、甲基硅醇钠2、水泥23，亚硝酸钠0.3、苯甲酸特丁2、三乙醇胺0.4、纳米沸石粉3、仲烷基磺酸钠0.08、十二烷基硫酸钠2，铝粉0.04,菜籽饼粉0.004；
制备方法为：
（1)取3份五倍子、5份地肤子、1份山姜花、3份黄连、1.3份板蓝根混匀后，烤干后，磨粉，得中药粉备用；
（2）按重量份取玻璃废渣，破碎，过200目筛，于800℃下煅烧2小时后，降温至900℃，保温2小时，取出，于浓度为8%的氢氟酸溶液中浸泡12小时，取出，混合搅拌，使其充分混合均匀后，再加入中药粉，混匀，然后再与其余物料混匀后，三辊研磨机研磨2小时后，再加入适量水，浇筑入模成型，预养，脱模，切割，得砌块坯；
　（3）将砌块坯放入反应釜中按照常规工艺蒸压养护后，入库成品即得。
所述的蒸压养护工艺的时长为13小时，温度为185℃，压力为1.5MPa。
本砌块的平均容重590kg/m3,保温性能好,抗腐蚀性能好，寿命长，平均值抗压强度为10.2MPa。

Claims (2)

1.一种防腐蚀加气砖的制备方法，其特征在于：所需原料重量份配比为：中药粉1-2，玻璃废渣12-14、硼砂1-2、尼龙纤维1-2、沥青2-4、生石灰10-15、甲基硅醇钠1-2、水泥20-25，亚硝酸钠0.3-0.8、苯甲酸特丁1-2、三乙醇胺0.2-0.4、纳米沸石粉2-4、仲烷基磺酸钠0.06-0.1、十二烷基硫酸钠1-3，铝粉0.03-0.04,菜籽饼粉0.002-0.004；
制备方法为：
（1）取2-4份五倍子、3-5份地肤子、1-2份山姜花、3-5份黄连、1-2份板蓝根混匀后，烤干后，磨粉，得中药粉备用；
按重量份取玻璃废渣，破碎，过100-200目筛，于700-800℃下煅烧1-2小时后，降温至800-900℃，保温1-2小时，取出，于浓度为8-10%的氢氟酸溶液中浸泡9-12小时，取出，混合搅拌，使其充分混合均匀后，再加入中药粉，混匀，然后再与其余物料混匀后，三辊研磨机研磨1-2小时后，再加入适量水，浇筑入模成型，预养，脱模，切割，得砌块坯；
　（3）将砌块坯放入反应釜中按照常规工艺蒸压养护后，入库成品即得。
2.根据权利要求1所述的一种防腐蚀加气砖的制备方法，其特征在于：
所述的蒸压养护工艺的时长为10-15小时，温度为175-185℃，压力为1-1.5MPa。
CN2013103276682A 2013-07-31 2013-07-31 一种防腐蚀加气砖的制备方法 Pending CN103449765A (zh)