CN102336533A - 一种明矾石混凝土膨胀剂 - Google Patents

一种明矾石混凝土膨胀剂 Download PDF

Info

Publication number
CN102336533A
CN102336533A CN2011101763478A CN201110176347A CN102336533A CN 102336533 A CN102336533 A CN 102336533A CN 2011101763478 A CN2011101763478 A CN 2011101763478A CN 201110176347 A CN201110176347 A CN 201110176347A CN 102336533 A CN102336533 A CN 102336533A
Authority
CN
China
Prior art keywords
alunite
concrete
natural
expanding agent
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011101763478A
Other languages
English (en)
Inventor
金树青
沈熙佐
项炳泉
金骥
倪朝民
许衡宇
徐有前
金鑫
Original Assignee
金树青
沈熙佐
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 金树青, 沈熙佐 filed Critical 金树青
Priority to CN2011101763478A priority Critical patent/CN102336533A/zh
Publication of CN102336533A publication Critical patent/CN102336533A/zh
Pending legal-status Critical Current

Abstract

一种明矾石混凝土膨胀剂,属混凝土外加剂技术领域。其目的是提供一种既能充份利用地方资源,又能符合我国现行膨胀剂标准要求的明矾石混凝土膨胀剂。其原料组分及其重量百分比为:铵明矾8~15%,天然明矾石10~15%,天然无水石膏或二水石膏75~79%;上述天然明矾石、天然石膏经粉磨均匀后与铵明矾粉混合搅拌均匀制得。降低了明矾石混凝土膨胀剂中的含碱量,提前产生了限制膨胀率,增强了膨胀性能,提高了抗压强度,其理化性能达到和超过现行膨胀剂标准的要求,具有很高的经济效益和社会效益。

Description

一种明矾石混凝土膨胀剂
技术领域
[0001] 本发明涉及一种在硫铝酸钙类混凝土膨胀剂掺活化剂的明矾石混凝土膨胀剂,具体的说是一种在老配方基础上予以改进的明矾石混凝土膨胀剂,属混凝土外加剂技术领域。
背景技术
[0002] 众所周知,普通混凝土由于收缩开裂,往往发生渗漏,降低了它的使用功能和耐久性。在水泥中内掺入不含钠盐、不易引起混凝土碱骨料反应的硫铝酸钙类混凝土膨胀剂,拌制成补偿收缩混凝土,做混凝土结构自防水,延长后浇缝间距,防止大体积混凝土和高强度混凝土温差裂缝的出现,大大提高混凝土结构的抗裂防水能力。
[0003] 上世纪七十年代,安徽省建科所金树青等科技人员与庐江县水泥厂研制成功的JEA混凝土膨胀剂,是我国硫铝酸钙的第一代混凝土膨胀剂,是利用天然、不需煅烧的明矾石和石膏,粉磨而成,它的掺量按混凝土水泥重量的12-17%,膨胀剂中的含碱量为 1. 1-2.2%。中国专利ZL94120191. 0公开的系列低碱明矾石膨胀剂,在上述明矾石膨胀剂的组分中减少明矾石掺量,增加部分含碱量低的工业废渣,使明矾石膨胀剂中的含碱量降低为1.08-1. 37%,掺量降低为7-9%。由于我国第一部混凝土外加剂应用规程GBJ 119-88和混凝土膨胀剂标准JC476-92对混凝土膨胀剂中的含碱量没有规定,因此,明矾石混凝土膨胀剂在在国内外建筑工程中得到推广应用。为防止混凝土碱集料反应的危害, 日本在凝土膨胀剂标准JISA : 1997中规定:膨胀剂中的含碱量不大于0. 75 %。为与国际接轨,防止混凝土碱集料反应,1998年后,我国对混凝土膨胀剂中钾、钠作出规定:总碱量 K2OXO. 658+Na20 要求;^ 0. 75% (JC476-1998 标准)。中国专利 ZL98U6823. 4 公开的低碱低掺量混凝土膨胀剂,其含碱量小于0. 6%,但它用的原材料是价格较贵的铝粉和氧化钙或碳化钙及矾泥,没有利用不需煅烧的天然明矾石资源。本发明借鉴上述两专利的优缺点,采用明矾做明矾石膨胀剂的活化剂。明矾有两种:钾明矾和铵明矾,由于钾明矾中钾、钠含量大,与铵明矾相比,总碱量要大近1.7倍(见表一),且价格也比铵明矾贵。试验表明:用等量掺量配制明矾石膨胀剂,钾明矾碱含量超标(见表二)。
[0004] 表一:明矾石、石膏、铵明石、钾明矾的总碱量
[0005]
材料名称 含总碱量 K2OXO. 658+N320天然明矾石 2. 97%天然石膏 0. 163%铵明石 1. 95%钾明矾 3. 2%[0006] 表二 :铵明矾和钾明矾做活化剂,等量掺量配制JEA明矾石混凝土膨胀剂的总碱量含量试验:
[0007]
Figure CN102336533AD00041
发明内容
[0008] 本发明的目的在于提供一种既能充份利用地方资源,又能符合我国现行膨胀剂标准要求的明矾石混凝土膨胀剂。
[0009] 其技术方案是:一种明矾石混凝土膨胀剂,其特征在于其原料组分及其重量百分比为:铵明矾8〜15%,天然明矾石10〜15%,天然无水石膏或二水石膏75〜79% ;
[0010] 上述天然明矾石、天然无水石膏或二水石膏经粉磨均勻后与铵明矾粉混合搅拌均勻制得(商品名JEA新型明矾石膨胀剂)。
[0011] 其技术效果是:本发明的明矾石混凝土膨胀剂,在我国第一代硫铝酸钙类明矾石混凝土膨胀剂充份利用国内安徽、四川、山东等地不需煅烧的天然明矾石和石膏矿产资源的基础上,加以改进,按比例掺入活化剂铵明矾,降低了明矾石混凝土膨胀剂中的含碱量, 提前产生了限制膨胀率,增强了膨胀性能,提高了抗压强度,其理化性能达到和超过现行膨胀剂标准的要求(见表三),具有很高的经济效益和社会效益。
[0012] 表三:总碱量,限制膨胀率和抗压强度(用42. 5P0普硅水泥掺量9% )
[0013]
Figure CN102336533AD00042
具体实施方式:
[0014] 实施例1。取天然明矾石100kg,天然无水石膏750kg,经粉磨均勻,细度达到膨胀剂标准后,再与通过20目过筛铵明矾粉150kg混合搅拌均勻,即得JEA新型明矾石膨胀剂 (商品名)。
[0015] 实施例2。取天然明矾石130kg,天然无水石膏790kg,经粉磨均勻,细度达到膨胀剂标准后,再与通过20目过筛铵明矾粉80kg混合搅拌均勻,即得JEA新型明矾石膨胀剂 (商品名)。
[0016] 实施例3。取天然明矾石150kg,天然二水石膏750kg,经粉磨均勻,细度达到膨胀剂标准后,再与通过20目过筛铵明矾粉IOOkg混合搅拌均勻,即得JEA新型明矾石膨胀剂 (商品名)。

Claims (1)

1. 一种明矾石混凝土膨胀剂,其特征在于其原料组分及其重量百分比为:铵明矾8〜 15%,天然明矾石10〜15%,天然无水石膏或二水石膏75〜79% ;上述天然明矾石、天然无水石膏或二水石膏经粉磨均勻后与铵明矾粉混合搅拌均勻制得。
CN2011101763478A 2011-06-28 2011-06-28 一种明矾石混凝土膨胀剂 Pending CN102336533A (zh)