CN104014703A - C12MoV扭转辊锻造工艺 - Google Patents

C12MoV扭转辊锻造工艺 Download PDF

Info

Publication number
CN104014703A
CN104014703A CN201410268157.2A CN201410268157A CN104014703A CN 104014703 A CN104014703 A CN 104014703A CN 201410268157 A CN201410268157 A CN 201410268157A CN 104014703 A CN104014703 A CN 104014703A
Authority
CN
China
Prior art keywords
forging
temperature
hours
controlled
forging process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410268157.2A
Other languages
English (en)
Inventor
吕美莲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Auspicious Outstanding Co Ltd Of Forging Of Anhui Province
Original Assignee
Auspicious Outstanding Co Ltd Of Forging Of Anhui Province
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Auspicious Outstanding Co Ltd Of Forging Of Anhui Province filed Critical Auspicious Outstanding Co Ltd Of Forging Of Anhui Province
Priority to CN201410268157.2A priority Critical patent/CN104014703A/zh
Publication of CN104014703A publication Critical patent/CN104014703A/zh
Pending legal-status Critical Current

Abstract

本发明公开了C12MoV扭转辊锻造工艺，选用近似转动辊锻圆进行模具锻造，(1)加热采用低温进炉，在600℃充分预热保温3小时，然后控制升温速度在60℃/h，升温到800℃后保温3小时，再升温，升温控制速度在80℃/h，升温到1180—1200℃保温4—5小时，加热过程中要不断翻转材料，防止材料过热，锻造时要轻锤慢打，反复鐓拔，将材料心部组织击碎，始锻温度控制在1060-1080℃，终锻温度为900-850℃，两火成型，锻造比＞3锻后采用快冷到700℃然后坑冷或砂冷。本发明克服了现有技术的不足，通过合理设计工艺控制参数，锻造时工件心部不会产生裂纹，心部偏析和网状碳化物能击碎，提高锻造产品品质。

Description

C12MoV扭转辊锻造工艺
技术领域
本发明涉及锻造技术领域，具体属于C12MoV扭转辊锻造工艺。
背景技术
C12MoV是模具钢，含C、Cr高，塑性差，导热性差，加热过程中温度控制不当，容易发生过热、过烧缺陷。同时由于钢锭心部存在偏析和网状碳化物，锻造时心部容易产生裂纹，要求加热时有足够的保温时间，便于锻造时将心部偏析和网状碳化物能击碎。
发明内容
本发明的目的是提供了C12MoV扭转辊锻造工艺，克服了现有技术的不足，通过合理设计工艺控制参数，锻造时工件心部不会产生裂纹，心部偏析和网状碳化物能击碎，提高锻造产品品质。
本发明采用的技术方案如下：
C12MoV扭转辊锻造工艺，选用近似转动辊锻圆进行模具锻造，(1)加热采用低温进炉，在600℃充分预热保温3小时，然后控制升温速度在60℃/h，升温到800℃后保温3小时，再升温，升温控制速度在80℃/h，升温到1180—1200℃保温4—5小时，加热过程中要不断翻转材料，防止材料过热，锻造时要轻锤慢打，反复鐓拔，将材料心部组织击碎，始锻温度控制在1060-1080℃，终锻温度为900-850℃，两火成型，锻造比＞3锻后采用快冷到700℃然后坑冷或砂冷。
与已有技术相比，本发明的有益效果如下：
本发明通过合理设计工艺控制参数，锻造时工件心部不会产生裂纹，心部偏析和网状碳化物能击碎，提高锻造产品品质。
附图说明
图1为本发明的加热工艺流程图。
具体实施方式
参见附图，C12MoV扭转辊锻造工艺，选用近似转动辊锻圆进行模具锻造，(1)加热采用低温进炉，在600℃充分预热保温3小时，然后控制升温速度在60℃/h，升温到800℃后保温3小时，再升温，升温控制速度在80℃/h，升温到1180—1200℃保温4—5小时，加热过程中要不断翻转材料，防止材料过热，锻造时要轻锤慢打，反复鐓拔，将材料心部组织击碎，始锻温度控制在1060-1080℃，终锻温度为900-850℃，两火成型，锻造比＞3锻后采用快冷到700℃然后坑冷或砂冷。

Claims (1)

1.C12MoV扭转辊锻造工艺，其特征在于：选用近似转动辊锻圆进行模具锻造，(1)加热采用低温进炉，在600℃充分预热保温3小时，然后控制升温速度在60℃/h，升温到800℃后保温3小时，再升温，升温控制速度在80℃/h，升温到1180—1200℃保温4—5小时，加热过程中要不断翻转材料，防止材料过热，锻造时要轻锤慢打，反复鐓拔，将材料心部组织击碎，始锻温度控制在1060-1080℃，终锻温度为900-850℃，两火成型，锻造比＞3锻后采用快冷到700℃然后坑冷或砂冷。
CN201410268157.2A 2014-06-16 2014-06-16 C12MoV扭转辊锻造工艺 Pending CN104014703A (zh)