CN103964783A - 一种保温隔声砂浆 - Google Patents

一种保温隔声砂浆 Download PDF

Info

Publication number
CN103964783A
CN103964783A CN201410189100.3A CN201410189100A CN103964783A CN 103964783 A CN103964783 A CN 103964783A CN 201410189100 A CN201410189100 A CN 201410189100A CN 103964783 A CN103964783 A CN 103964783A
Authority
CN
China
Prior art keywords
insulating
heat insulating
sound
mortar
adopting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410189100.3A
Other languages
English (en)
Other versions
CN103964783B (zh
Inventor
丁光亚
胡保永
张波
卢小运
胡秀青
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wenzhou University
Original Assignee
Wenzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wenzhou University filed Critical Wenzhou University
Priority to CN201410189100.3A priority Critical patent/CN103964783B/zh
Publication of CN103964783A publication Critical patent/CN103964783A/zh
Application granted granted Critical
Publication of CN103964783B publication Critical patent/CN103964783B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种保温隔声砂浆,本发明在原有砂浆的基础上添加漂珠、橡胶粉、粉煤灰和减水剂,按一定的配比混合均匀而制成的具有保温隔声性能的复合砂浆。本发明大大提高了楼地面的保温隔声性能,降低成本。除此之外,在原有砂浆的基础上加入漂珠、橡胶粉等工业废料,促进了废料的循环使用,具有良好的经济效益和社会效益。

Description

一种保温隔声砂浆
技术领域
本发明涉及一种保温隔声砂浆,适用于楼面板地砖或者木地板之间的垫层进行处理,以及楼面板下层即为天棚装饰进行处理等,属于土木建筑材料技术领域。
背景技术
建筑空间内的保温性能直接关系到室内环境的热稳定性和舒适性,对降低建筑能耗起着至关重要的作用。上个世纪八九十年代的老房子没有有效的保温、隔声措施,住户们一直对楼层间传递的噪声怨言不断。而近些年来建造的住宅,采取了一定的措施。墙面的隔声通过混凝土这种混合材料来隔绝空气声。保温方式主要是外墙外保温,内墙内保温以及墙体自保温。窗户的保温性能使用中空玻璃得到一定改善。但是楼地面的保温隔声依然没有引起足够的重视,作为围护结构的重要部分,这对减少热量散失有很大的改善空间。同时随着人们生活水平的提高,对住宅保温隔声也有了更高的要求。
另外,从做法上看,目前已有的墙面保温是附加保温层。这种方法虽然可以达到一定的效果,但各种高效保温材料价格较高,而且其生产加工过程中也会大量消耗各种能源。建筑节能不应当只着眼于建筑建成后在使用过程中的能耗,还应当从整体系统的观念出发,关注建筑全寿命周期的能源消耗。从这个角度出发,楼地面的新型保温砂浆就不但要有出色的保温隔热性能,其加工生产过程也应当简单易行,节省能源,减少成本。
因此,为改变以上现状,工艺简单又经济有效的保温隔声砂浆的研制刻不容缓。要研制和使用各种各样的保温、隔声和阻尼减振材料来提高室内环境的热稳定性,控制室内噪声污染。主要从以下方面:控制上、下层传来的噪声、隔绝房间里的能量传到上、下层去等。可以预见这种保温隔声砂浆将具有一定的市场前景。
发明内容
本发明所要解决的技术问题是提供一种保温隔声砂浆,该砂浆对楼地面的保温和隔声性能有一定提高,且兼具保温隔热性能和隔绝固体撞击声功能,可以简化施工、提高效率。
为此,本发明提供的保温隔声砂浆,由水泥、细砂、漂珠、橡胶粉、粉煤灰和减水剂混合而成。
在上述技术方案中水泥、细砂、漂珠、橡胶粉、粉煤灰和减水剂的最佳质量比依次为1 : 5.9882 : 0.3569 : 0.3569 : 0.1765 : 0.0863。
本发明的有益效果:这种新型保温隔声砂浆的施工方法与传统的水泥砂浆相比,仅需要在水泥、细砂的基础上加上不同配合比例的橡胶粉、漂珠、粉煤灰和减水剂等材料,并均匀搅拌,工艺简单方便。同时,面对不同的室内环境要求,可以通过改变橡胶粉和漂珠的比例,来调节导热系数。可以有效提高楼地面的保温隔声性能,减少热量的散失,改善热工性能,控制噪声传播,弥补普通水泥砂浆的缺陷;除此之外,在使用过程中,该保温砂浆无污染,对人体不会造成伤害,是一种绿色环保材料。
具体实施方式
本发明提供的保温隔声砂浆,由水泥、细砂、漂珠、橡胶粉、粉煤灰和减水剂混合而成,所述水泥、细砂、漂珠、橡胶粉、粉煤灰和减水剂的最佳质量比依次为1 : 5.9882 : 0.3569 : 0.3569 : 0.1765 : 0.0863。其中所采用水泥是标号32.5的硅酸盐水泥;所采用的橡胶粉是废旧轮胎经过加工处理,形成的橡胶制品粉末,呈黑色装颗粒,是在自然条件下难以降解的高分子弹性材料,不溶于水且是憎水物质,不易腐烂,有良好的隔声效果;所采用的漂珠是电厂燃烧煤以后的产物,漂珠为外表呈光滑的珠形颗粒,颜色呈灰白色,堆积密度为440kg/m3,抗压强度在3~5MPa,导热系数为0.011-0.063W/m.k,粒径为40-80目,漂珠具有重量轻,耐火度高,导电系数低,无毒等特点,同时漂珠中空结构特点决定了它具有良好的吸音隔声性能,所以在保温隔声方面可以有很大的应用;所采用的粉煤灰是煤燃烧后的烟气中收集下来的细灰。是燃煤类工厂排出的主要固体废弃物,在砂浆中掺加粉煤灰能节约水泥和细骨料;改善砂浆拌合物的和易性;减少热能膨胀性、水化热;减少用水量等;所采用的减水剂是BC-2型高效减水剂,由黄酸甲醛缩合物及早强剂等原料复合而成,属于阴离子型表面活性剂。对水泥具有湿润,扩散作用,从而可大幅度降低砂浆的用水量,提高强度改善砂浆的活易性,节约水泥。
本发明提供的保温隔声砂浆的技术经济性明显优于传统保温砂浆。同时,可为废旧工业品的治理与资源化利用开辟一条切实可行的新途径,将会带来巨大的节能环保效益,推动各类技术和政策的发展。另外,创造性地采用新型建材往往可以变废为宝,减少污染和能源浪费,从而达到一举多得的效果。另外对此种砂浆的各方面性能进行检测,从而为理论研究和生产应用提供可靠的依据。此外,通过本课题的研究,为进一步优化保温隔声砂浆技术提供参考,为建筑市场建筑节能事业的发展提供必要的技术资料,为国家建筑节能的普及实施提供技术支持。
下面提供两个实验案例以验证其技术效果:
实施例1
采用常规砂浆试验尺寸,试样尺寸为70.7mm×70.7mm×70.7mm。搅拌好的砂浆注入试模中,砂浆面高于试模3~5mm,振动捣实后,刮平表面。试块成型后在20℃养护24h脱模,继续养护,至28天龄期测试砂浆固化体的无侧限抗压强度。
实施例2
采用试样尺寸为400mm×400mm×40mm. 搅拌好的砂浆注入试模中,砂浆面高于试模3~5mm,振动捣实后,刮平表面。试块成型后在20℃养护24h脱模,继续养护。至28天龄期测试砂浆试块的导热系数和隔声性能。
试样的配合比(见表1)和各组试验样品的性能(见表2)分别如下:
表1 砂浆试配过程各组分重量配比
表2 各组试验样品的性能
各物质的用量允许误差如表3所示:
表3拌合砂浆计量允许偏差
通过以上测定的数据显示,可以选择配比为1 : 5.9882 : 0.3569 : 0.3569 : 0.1765 : 0.0863的试验组作为我们抹面砂浆,此配合比的强度为1.83MPa,导热系数为0.256W/ (m·K),隔声量为48.70 dB,既满足强度要求又满足保温隔声所达到的效果,此配比为最佳配合比。
同时由上述实例可见,可以通过改变橡胶粉和漂珠的比例来调节抗压强度,导热系数及隔声性能指标。综合分析,橡胶粉的加入量增大,导热系数较小,但是其强度也随之减少;漂珠的加入量增大,隔声性能增强,但强度也随之减小。在应用时可以根据实际工程来选择合适的配合比,进行指导工程应用。

Claims (11)

1.一种保温隔声砂浆,其特征在于:由水泥、细砂、漂珠、橡胶粉、粉煤灰和减水剂混合而成。
2.根据权利要求1所述的保温隔声砂浆,其特征是:所述水泥、细砂、漂珠、橡胶粉、粉煤灰和减水剂的最佳质量比依次为1 : 5.9882 : 0.3569 : 0.3569 : 0.1765 : 0.0863。
3.根据权利要求1或2所述的保温隔声砂浆,其特征在于:所采用水泥是标号32.5的硅酸盐水泥。
4.根据权利要求1或2所述的保温隔声砂浆,其特征在于:所采用的橡胶粉是废旧轮胎经过加工处理,形成的橡胶制品粉末。
5.根据权利要求1或2所述的保温隔声砂浆,其特征在于:所采用的漂珠是电厂燃烧煤以后的产物,漂珠为外表呈光滑的珠形颗粒,颜色呈灰白色,堆积密度为440kg/m3,抗压强度在3~5MPa,导热系数为0.011-0.063W/m.k,粒径为40-80目。
6.根据权利要求3所述的保温隔声砂浆,其特征在于:所采用的漂珠是电厂燃烧煤以后的产物,漂珠为外表呈光滑的珠形颗粒,颜色呈灰白色,堆积密度为440kg/m3,抗压强度在3~5MPa,导热系数为0.011-0.063W/m.k,粒径为40-80目。
7.根据权利要求1或2所述的保温隔声砂浆,其特征在于:所采用的粉煤灰是煤燃烧后的烟气中收集下来的细灰。
8.根据权利要求3所述的保温隔声砂浆,其特征在于:所采用的粉煤灰是煤燃烧后的烟气中收集下来的细灰。
9.根据权利要求4所述的保温隔声砂浆,其特征在于:所采用的粉煤灰是煤燃烧后的烟气中收集下来的细灰。
10.根据权利要求5所述的保温隔声砂浆,其特征在于:所采用的粉煤灰是煤燃烧后的烟气中收集下来的细灰。
11.根据权利要求1或2所述的保温隔声砂浆,其特征在于:所采用的减水剂是BC-2型高效减水剂,由黄酸甲醛缩合物及早强剂等原料复合而成,属于阴离子型表面活性剂。
CN201410189100.3A 2014-05-07 2014-05-07 一种保温隔声砂浆 Expired - Fee Related CN103964783B (zh)