CN104058681A - 抗裂保温砂浆 - Google Patents

抗裂保温砂浆 Download PDF

Info

Publication number
CN104058681A
CN104058681A CN201410230235.XA CN201410230235A CN104058681A CN 104058681 A CN104058681 A CN 104058681A CN 201410230235 A CN201410230235 A CN 201410230235A CN 104058681 A CN104058681 A CN 104058681A
Authority
CN
China
Prior art keywords
parts
thermal insulating
powder
insulating mortar
resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410230235.XA
Other languages
English (en)
Other versions
CN104058681B (zh
Inventor
王长富
毛东超
王玉童
刘伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Original Assignee
ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd filed Critical ANHUI FUYANG FULONG BUILDING MATERIALS Co Ltd
Priority to CN201410230235.XA priority Critical patent/CN104058681B/zh
Publication of CN104058681A publication Critical patent/CN104058681A/zh
Application granted granted Critical
Publication of CN104058681B publication Critical patent/CN104058681B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗裂保温砂浆，其由下列重量份的原料组成：普通硅酸盐水泥40-60、莫来砂20-30、聚丙烯短切纤维1.5-2.5、钢渣粉4-6、聚苯乙烯泡沫颗粒10-15、膨胀珍珠岩5-10、羟丙基甲基纤维素0.5-1、可再分散性乳胶粉3-5、聚乙烯醇4-6、石棉粉3-7、硅藻土4-8、玉米芯粉2.5-4.5、新戊二醇3-6、木质素磺酸钠2-3、复合填料4-6；本发明保温砂浆具有较高的粘结强度高和抗压强度，抗裂性能优异，解决了传统的保温砂浆易空鼓开裂的缺点；同时还具有优良的保温隔热性、耐水性、耐候性、耐酸碱腐蚀性、耐冻融、抗老化、防霉防火等性能，施工性能好，绿色环保，安全可靠，具有极大的市场空间和发展前景。

Description

抗裂保温砂浆
技术领域
本发明涉及一种抗裂保温砂浆，属于建筑材料领域。
背景技术
保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业搅拌混合而制成的一种预拌干粉砂浆，用于构筑建筑表面保温层的一种建筑材料。随着低碳环保和建筑节能的不断推广以及人们对居住环境舒适性需求的不断提高，保温砂浆越来越受到人们的广泛重视，近年来我国保温砂浆的研究较多，在实际工程中已有很多应用，但与发达国家相比，现有市场上的保温砂浆还存在着强度低，凝固后容易开裂，影响整体美观和保温效果。
发明内容
本发明的目的在于针对现有技术的不足，提供一种强度高、保温隔热性好、施工性能好的抗裂保温砂浆，能有效防止出现开裂现象。
本发明采用的技术方案如下：
一种抗裂保温砂浆，由下列重量份的原料组成：普通硅酸盐水泥40-60、莫来砂20-30、聚丙烯短切纤维1.5-2.5、钢渣粉4-6、聚苯乙烯泡沫颗粒10-15、膨胀珍珠岩5-10、羟丙基甲基纤维素0.5-1、可再分散性乳胶粉3-5、聚乙烯醇4-6、石棉粉3-7、硅藻土4-8、玉米芯粉2.5-4.5、新戊二醇3-6、木质素磺酸钠2-3、复合填料4-6；
所述复合填料的制备方法如下：
（a）称取以下重量份的原料：海泡石10-15、蛭石5-10、页岩20-30、煤矸石8-12、高岭土10-15、硼泥5-10、乙烯基三(β-甲氧基乙氧基)硅烷1-2、纸浆废液25-35、草木灰4-8、纳米硅溶胶15-20、三聚磷酸钠3-6、司盘80 0.5-1、柠檬酸1-2、糖钙2-4、纳米氮化硅3-5、玉石粉4-6、椰子油脂肪酸二乙醇酰胺2-3；
（b）将页岩、煤矸石、高岭土和硼泥混合均匀，粉碎过100-150目筛，然后加入纸浆废液、柠檬酸和三聚磷酸钠，湿法球磨20-30min，造粒，控制粒径为0.3-0.4mm,110-120℃下烘干，再于1150-1250℃下高温焙烧1-2h，冷却至室温待用；
（c）将海泡石和蛭石混合均匀后于660-720℃温度下煅烧2-3h，冷却至室温后置于浓度为10-15%的盐酸溶液，水浴加热至70-80℃，保温30-50min，过滤，用蒸馏水将滤渣洗涤至中性，烘干，粉碎过200-300目筛，然后加入乙烯基三(β-甲氧基乙氧基)硅烷、椰子油脂肪酸二乙醇酰胺、糖钙、纳米氮化硅和玉石粉，高速混合20-30min，待用；
（d）取纳米硅溶胶和司盘80搅拌均匀，加入步骤（b）制得的颗粒，高速搅拌5-10min，再加入草木灰和步骤（c）制得的混合料，高速搅拌10-15min，烘干即可。
使用方法：将上述原料混合均匀，然后按重量比1∶1.2-1.5的比例将砂浆干粉与水搅拌均匀后即可使用。
本发明的有益效果：
本发明保温砂浆与传统保温砂浆相比较，具有较高的粘结强度高和抗压强度，抗裂性能优异，解决了传统的保温砂浆易空鼓开裂的缺点；同时还具有优良的保温隔热性、耐水性、耐候性、耐酸碱腐蚀性、耐冻融、抗老化、防霉防火等性能，该保温砂浆施工性能好，绿色环保，安全可靠，具有极大的市场空间和发展前景。
具体实施方式
一种抗裂保温砂浆，由下列重量（kg）的原料组成：普通硅酸盐水泥50、莫来砂25、聚丙烯短切纤维2、钢渣粉5、聚苯乙烯泡沫颗粒10、膨胀珍珠岩8、羟丙基甲基纤维素0.8、可再分散性乳胶粉4、聚乙烯醇5、石棉粉4、硅藻土6、玉米芯粉3、新戊二醇4、木质素磺酸钠2、复合填料5；
所述复合填料的制备方法如下：
（a）称取以下重量份的原料：海泡石10、蛭石10、页岩25、煤矸石10、高岭土12、硼泥8、乙烯基三(β-甲氧基乙氧基)硅烷1.5、纸浆废液30、草木灰6、纳米硅溶胶18、三聚磷酸钠4、司盘80 0.7、柠檬酸1.5、糖钙3、纳米氮化硅4、玉石粉5、椰子油脂肪酸二乙醇酰胺2；
（b）将页岩、煤矸石、高岭土和硼泥混合均匀，粉碎过50目筛，然后加入纸浆废液、柠檬酸和三聚磷酸钠，湿法球磨30min，造粒，控制粒径为0.3mm,115℃下烘干，再于1180℃下高温焙烧2h，冷却至室温待用；
（c）将海泡石和蛭石混合均匀后于680℃温度下煅烧3h，冷却至室温后置于浓度为15%的盐酸溶液，水浴加热至80℃，保温30min，过滤，用蒸馏水将滤渣洗涤至中性，烘干，粉碎过250目筛，然后加入乙烯基三(β-甲氧基乙氧基)硅烷、椰子油脂肪酸二乙醇酰胺、糖钙、纳米氮化硅和玉石粉，高速混合25min，待用；
（d）取纳米硅溶胶和司盘80搅拌均匀，加入步骤（b）制得的颗粒，高速搅拌6min，再加入草木灰和步骤（c）制得的混合料，高速搅拌10min，烘干即可。
将上述原料混合均匀，然后按重量比1∶1.4的比例将砂浆干粉与水搅拌均匀后即可使用。
本实施例生产出来的保温砂浆的性能参数见下表。
项目 计量单位 实测值
导热系数 W/（m·k） 0.042
28d抗压强度 kPa 424
线性收缩率 % 0.18
软化系数 — 0.86
抗裂性 — 5mmm以下无裂纹

Claims (1)

1.一种抗裂保温砂浆，其特征在于，由下列重量份的原料组成：普通硅酸盐水泥40-60、莫来砂20-30、聚丙烯短切纤维1.5-2.5、钢渣粉4-6、聚苯乙烯泡沫颗粒10-15、膨胀珍珠岩5-10、羟丙基甲基纤维素0.5-1、可再分散性乳胶粉3-5、聚乙烯醇4-6、石棉粉3-7、硅藻土4-8、玉米芯粉2.5-4.5、新戊二醇3-6、木质素磺酸钠2-3、复合填料4-6；
所述复合填料的制备方法如下：
（a）称取以下重量份的原料：海泡石10-15、蛭石5-10、页岩20-30、煤矸石8-12、高岭土10-15、硼泥5-10、乙烯基三(β-甲氧基乙氧基)硅烷1-2、纸浆废液25-35、草木灰4-8、纳米硅溶胶15-20、三聚磷酸钠3-6、司盘80 0.5-1、柠檬酸1-2、糖钙2-4、纳米氮化硅3-5、玉石粉4-6、椰子油脂肪酸二乙醇酰胺2-3；
（b）将页岩、煤矸石、高岭土和硼泥混合均匀，粉碎过100-150目筛，然后加入纸浆废液、柠檬酸和三聚磷酸钠，湿法球磨20-30min，造粒，控制粒径为0.3-0.4mm,110-120℃下烘干，再于1150-1250℃下高温焙烧1-2h，冷却至室温待用；
（c）将海泡石和蛭石混合均匀后于660-720℃温度下煅烧2-3h，冷却至室温后置于浓度为10-15%的盐酸溶液，水浴加热至70-80℃，保温30-50min，过滤，用蒸馏水将滤渣洗涤至中性，烘干，粉碎过200-300目筛，然后加入乙烯基三(β-甲氧基乙氧基)硅烷、椰子油脂肪酸二乙醇酰胺、糖钙、纳米氮化硅和玉石粉，高速混合20-30min，待用；
（d）取纳米硅溶胶和司盘80搅拌均匀，加入步骤（b）制得的颗粒，高速搅拌5-10min，再加入草木灰和步骤（c）制得的混合料，高速搅拌10-15min，烘干即可。
CN201410230235.XA 2014-05-28 2014-05-28 抗裂保温砂浆 Active CN104058681B (zh)