CN103923435A - 一种改性脲甲醛树脂塑料 - Google Patents
一种改性脲甲醛树脂塑料 Download PDFInfo
- Publication number
- CN103923435A CN103923435A CN201410176641.2A CN201410176641A CN103923435A CN 103923435 A CN103923435 A CN 103923435A CN 201410176641 A CN201410176641 A CN 201410176641A CN 103923435 A CN103923435 A CN 103923435A
- Authority
- CN
- China
- Prior art keywords
- accounts
- formaldehyde resin
- urea formaldehyde
- plastic
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种改性脲甲醛树脂塑料,由脲甲醛树脂及添加剂制成,所述添加剂包括固化剂、促进剂、耐候剂、耐化学药品剂以及分散剂,所述固化剂为甲阶酚醛树脂,所述促进剂为磷酸三甲酯,所述耐候剂为四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯,所述耐化学药品剂为聚四氟乙烯,所述分散剂为氰乙基纤维素。本发明改性脲甲醛树脂塑料通过在脲甲醛树脂中添加多种添加剂,使得制得的改性脲甲醛树脂塑料具有固化方便、固化快、耐化学药品性好、耐候性好、产品质量好的特点。
Description
技术领域
本发明涉及塑料,特别是涉及一种改性脲甲醛树脂塑料。
背景技术
脲甲醛树脂尿素与甲醛反应得到的聚合物。又称脲甲醛树脂。英文缩写UF。加工成型时发生交联,制品为不溶不熔的热固性树脂。固化后的脲甲醛树脂颜色比酚醛树脂浅,呈半透明状,耐弱酸、弱碱,绝缘性能好,耐磨性极佳,价格便宜。脲甲醛树脂主要用于制造模压塑料,制造日用生活品和电器零件,还可作板材粘合剂、纸和织物的浆料、贴面板、建筑装饰板等。由于其色浅和易于着色,制品往往色彩丰富瑰丽。但是脲甲醛遇强酸、强碱易分解,耐候性较差。在固化时,往往需要通过模塑粉在30~160℃加热固化,反应较慢,效率低。
发明内容
本发明主要解决的技术问题是提供一种固化方便、固化快、耐化学药品性好、耐候性好、产品质量好的改性脲甲醛树脂塑料。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种改性脲甲醛树脂塑料,由脲甲醛树脂及添加剂制成,所述添加剂包括固化剂、促进剂、耐候剂、耐化学药品剂以及分散剂,所述固化剂为甲阶酚醛树脂,所述促进剂为磷酸三甲酯,所述耐候剂为四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯,所述耐化学药品剂为聚四氟乙烯,所述分散剂为氰乙基纤维素,所述改性脲甲醛树脂塑料各成分所占重量百分比分别为脲甲醛树脂占90.1%-94.5%,甲阶酚醛树脂占1.4%-2.3%,磷酸三甲酯占1.7%-2.6%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.1%-1.9%,聚四氟乙烯占0.8%-1.7%,氰乙基纤维素占0.5%-1.4%。
在本发明一个较佳实施例中,所述的改性脲甲醛树脂塑料各成分所占重量百分比具体为脲甲醛树脂占93.9%,甲阶酚醛树脂占1.5%,磷酸三甲酯占1.8%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.3%,聚四氟乙烯占0.9%,氰乙基纤维素占0.6%。
在本发明一个较佳实施例中,所述的改性脲甲醛树脂塑料各成分所占重量百分比具体为脲甲醛树脂占90.6%,甲阶酚醛树脂占2.2%,磷酸三甲酯占2.5%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.8%,聚四氟乙烯占1.6%,氰乙基纤维素占1.3%。
本发明的有益效果是:本发明改性脲甲醛树脂塑料通过在脲甲醛树脂中添加多种添加剂,使得制得的改性脲甲醛树脂塑料具有固化方便、固化快、耐化学药品性好、耐候性好、产品质量好的特点。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
一种改性脲甲醛树脂塑料,由脲甲醛树脂及添加剂制成,所述添加剂包括固化剂、促进剂、耐候剂、耐化学药品剂以及分散剂,所述固化剂为甲阶酚醛树脂,所述促进剂为磷酸三甲酯,所述耐候剂为四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯,所述耐化学药品剂为聚四氟乙烯,所述分散剂为氰乙基纤维素,所述改性脲甲醛树脂塑料各成分所占重量百分比分别为脲甲醛树脂占90.1%-94.5%,甲阶酚醛树脂占1.4%-2.3%,磷酸三甲酯占1.7%-2.6%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.1%-1.9%,聚四氟乙烯占0.8%-1.7%,氰乙基纤维素占0.5%-1.4%。
进一步地,所述的改性脲甲醛树脂塑料各成分所占重量百分比具体为脲甲醛树脂占93.9%,甲阶酚醛树脂占1.5%,磷酸三甲酯占1.8%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.3%,聚四氟乙烯占0.9%,氰乙基纤维素占0.6%。
进一步地,所述的改性脲甲醛树脂塑料各成分所占重量百分比具体为脲甲醛树脂占90.6%,甲阶酚醛树脂占2.2%,磷酸三甲酯占2.5%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.8%,聚四氟乙烯占1.6%,氰乙基纤维素占1.3%。
本发明改性脲甲醛树脂塑料的有益效果是:本发明改性脲甲醛树脂塑料通过在脲甲醛树脂中添加多种添加剂,使得制得的改性脲甲醛树脂塑料具有固化方便、固化快、耐化学药品性好、耐候性好、产品质量好的特点。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (3)
1.一种改性脲甲醛树脂塑料,由脲甲醛树脂及添加剂制成,其特征在于:所述添加剂包括固化剂、促进剂、耐候剂、耐化学药品剂以及分散剂,所述固化剂为甲阶酚醛树脂,所述促进剂为磷酸三甲酯,所述耐候剂为四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯,所述耐化学药品剂为聚四氟乙烯,所述分散剂为氰乙基纤维素,所述改性脲甲醛树脂塑料各成分所占重量百分比分别为脲甲醛树脂占90.1%-94.5%,甲阶酚醛树脂占1.4%-2.3%,磷酸三甲酯占1.7%-2.6%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.1%-1.9%,聚四氟乙烯占0.8%-1.7%,氰乙基纤维素占0.5%-1.4%。
2.根据权利要求1所述的改性脲甲醛树脂塑料,其特征在于,所述的改性脲甲醛树脂塑料各成分所占重量百分比具体为脲甲醛树脂占93.9%,甲阶酚醛树脂占1.5%,磷酸三甲酯占1.8%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.3%,聚四氟乙烯占0.9%,氰乙基纤维素占0.6%。
3.根据权利要求1所述的改性脲甲醛树脂塑料,其特征在于,所述的改性脲甲醛树脂塑料各成分所占重量百分比具体为脲甲醛树脂占90.6%,甲阶酚醛树脂占2.2%,磷酸三甲酯占2.5%,四[β-(3,5-二叔丁基-4羟基苯基)丙酸]季戊四醇酯占1.8%,聚四氟乙烯占1.6%,氰乙基纤维素占1.3%。