CN103898798B - 涂布纸 - Google Patents
涂布纸 Download PDFInfo
- Publication number
- CN103898798B CN103898798B CN201210570345.1A CN201210570345A CN103898798B CN 103898798 B CN103898798 B CN 103898798B CN 201210570345 A CN201210570345 A CN 201210570345A CN 103898798 B CN103898798 B CN 103898798B
- Authority
- CN
- China
- Prior art keywords
- paper
- coating
- pulp
- mass parts
- antiseptic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种涂布纸,其包括原纸、及形成于原纸单面或双面的至少一涂层,该涂布纸的最外表的涂层为一抗菌涂层,该抗菌涂层中含有抗菌剂及载体,且该抗菌剂负载在载体上,该载体为多孔材料或微胶囊中的一种或两种。本发明在涂布涂料中加入负载于载体上的抗菌剂,抗菌剂利用率高,制得的涂布纸具有良好的抗菌效果。
Description
技术领域
本发明涉及一种涂布纸,尤其涉及一种具有抗菌功能的涂布纸。
背景技术
纸产品是生活中不可缺的包装材料。在食品、医疗和卫生领域,有必要使用具有抗菌能力的纸产品。现有技术对原纸抗菌的处理主要通过抄造时向纸浆配料添加抗菌材料而得以实现,然而,由于原纸抄造涉及搅拌、上网、脱水、成型、烘干等较为复杂的步骤,一部分抗菌材料必然会随白水流失,导致抗菌材料利用效率较低。现有技术对涂布纸抗菌的的处理主要通过涂布含有抗菌材料的涂料,然而,在涂料中应用纳米银或季铵类、壳聚糖等抗菌剂容易引起涂料系统颗粒的团聚、絮凝,造成分散困难,无法获得较高的涂料固含,制得的涂料在循环使用过程中无法保证足够的涂料物性的稳定性,也不能获得稳定均匀的涂层结构。
发明内容
有鉴于此,有必要提供一种涂布纸,其抗菌效果良好,且抗菌材料利用率高。
一种涂布纸,其包括原纸、及形成于原纸单面或双面的至少一涂层,该涂布纸的最外表的涂层为一抗菌涂层,该抗菌涂层中含有抗菌剂及载体,且该抗菌剂负载在载体上,该载体为多孔材料或微胶囊中的一种或两种。
本发明在涂布涂料中加入负载于载体上的抗菌剂,抗菌剂利用率高,制得的涂布纸具有良好的抗菌效果。
具体实施方式
本发明的涂布纸包括原纸、及形成于原纸单面或双面的至少一涂层,且该涂布纸的最外表的涂层为一抗菌涂层。该涂布纸还可选择性地在涂布涂层前在原纸表面涂布表胶层。
为进一步加强涂布纸的抗菌性,抄造该原纸的浆料中还可添加竹浆,其中竹浆占浆料总质量的10%-30%。该浆料中还含有漂白阔叶木浆和漂白针叶木浆,其中漂白阔叶木浆与漂白针叶木浆的质量比为50-85:5-10。竹浆中含有具有抗菌效果的“竹琨”,从而赋予原纸一定的抗菌效果,此外由于抗菌材料以纤维形式存在,在原纸抄造过程中也几乎没有损失。此外,竹浆的加入也可以减少一部分针叶木浆料的使用量,节约了原纸制造阶段的成本。
抄造原纸的浆料中还添加有常规的填料、阳离子聚合电解质、内部施胶剂及阴离子保留助剂,然后搅拌、上网、形成湿纸幅,压榨、烘干后,形成所述原纸。按占纸浆总重量比例计算,添加的填料占纸浆总重量的1%-20%,阳离子聚合电解质占纸浆总重量的0.25%-5%,内部施胶剂占纸浆总重量的1%-2.5%,阴离子保留助剂占纸浆总重量的0.1%-2%。
该抗菌涂层中含有抗菌剂、纸张涂料常规使用的颜料、胶乳及其他的的辅助添加剂。
该抗菌涂层采用抗菌涂料涂布制得。该抗菌涂料中含有抗菌剂及载体,且该抗菌剂负载在载体上。该抗菌涂料中含有100质量份颜料、0.02-0.2质量份抗菌剂,4-10质量份胶乳,及其他辅助添加剂为选择性添加或不添加,其他辅助添加剂具体包括2-8质量份淀粉、0.2-1.0质量份的耐水化剂、0.4-1.0质量份的润滑剂、0.05-0.2质量份的消泡剂,0.05-0.15质量份的分散剂。抗菌涂料的单面涂布量为2-10g/m2。其中,抗菌涂料中含有颜料、胶乳和各种辅助添加剂均为造纸涂料使用的常规的成分,在本发明中将不进行详述。
本发明使用的抗菌剂可为无机抗菌材料,具体为铜族元素(如铜、银、金)的纳米或胶体颗粒、二氧化钛、氧化锌、氧化铜、磷酸二氢铵、碳酸锂中的一种或多种的组合。该抗菌剂也可为有机抗菌材料,具体为酰基苯胺类、咪唑类、噻唑类、异噻唑酮衍生物、季铵盐类、双呱类、酚类的一种或多种的组合。
该载体可为多孔材料或微胶囊中的一种或两种。该多孔材料可为氟石或硅胶。其中,纳米金、银或铜与载体的重量比例为1:10-10:1。其余的抗菌剂与载体的比例无特殊要求。
本发明提供一种负载于硅胶上的胶体银抗菌剂的制备方法的示例,具体包括如下步骤:(1)将500ml去离子水加热至沸腾,加入100mg硝酸银;向上述硝酸银溶液中加入10ml的柠檬酸钠溶液(质量百分浓度为2%),搅拌30分钟后自然冷却至室温即制成胶体银溶液。该胶体银溶液呈黄绿色,其银纳米粒子的粒径为10-300纳米。(2)配制100ml 0.5%氨的乙醇溶液,取2ml氨的乙醇溶液加入20ml上述胶体银溶液,搅拌5分钟。继续加入0.2ml正硅酸乙酯,高速(800RPM以上)搅拌30分钟后静置一定时间,得到一种负载于硅胶上的胶体银抗菌剂。
本发明在涂布涂料中加入负载于载体上的抗菌剂,抗菌剂利用率高,制得的涂布纸具有良好的抗菌效果。
下面通过实施例来对本发明进行具体说明。
实施例1-5
原纸的制备:将5%漂白针叶木浆,85%漂白阔叶木浆,10%竹浆进行混合配制浆料,并加入相对原纸重量20%的重质碳酸钙,5%阳离子淀粉、2.5%烷基烯酮二聚体类施胶剂。经搅拌、上网抄造、烘干后,得到定量为80g/m2的原纸A。
负载在载体上的抗菌剂的制备:将500ml去离子水加热至沸腾,加入100mg硝酸银。向上述硝酸银溶液中加入10ml 2%柠檬酸钠溶液,搅拌30分钟后自然冷却至室温,配制成胶体银溶液。配制100ml0.5%氨的乙醇溶液,取2ml氨的乙醇溶液加入20ml上述胶体银溶液,搅拌5分钟。继续加入0.2ml正硅酸乙酯,高速搅拌30分钟后隔夜静置。得到一种负载于硅胶上的胶体银抗菌剂B。
3组抗菌涂料的制备:对应3组抗菌涂料分别取100份重质碳酸钙颜料,加入6份胶乳,5份淀粉、0.6份的耐水化剂、0.6份的润滑剂、0.1份的消泡剂,0.1份的分散剂,并加入上述步骤制得的抗菌剂B分散均匀,3组抗菌涂料分别添加0.02份、0.12份及0.2份的抗菌剂B。
将上述的3组抗菌涂料分别依照下表所示的涂布量分别在原纸A的一面进行刮刀式涂布,经过涂布后,纸张在130℃,170kN/m的条件下进行超级压光,得到5组涂布纸单面抗菌的铜版纸。
对比例
涂料的制备:取100份的重质碳酸钙颜料,辅助助剂加入相对颜料质量份6份胶乳,5份淀粉、0.6份耐水化剂、0.6份润滑剂、0.1份消泡剂,0.1份的分散剂,分散均匀。
取上述原纸A,取对比例的涂料对其原纸的一面进行涂布,涂布量控制在6g/m2,经过涂布后,纸张在130°C,170kN/m的条件下进行超级压光,得到铜版纸。
实施例1-5及对比例所制得的铜版纸进行抗菌测试,抗菌率的测试结果如下表所示。
抗菌测试方法简介:配制标准牛肉膏蛋白胨培养基,经灭菌操作,分别在培养皿放入试样,采用液体接种后,放入30°C培养箱,每隔24小时观察试样菌落的生长状况,测试试样未长菌面积,计算抗菌率。抗菌率=未长菌的纸页面积/纸页总面积。
从上表可知:对比例中涂布普通涂料的纸张具有一定的抗菌率,这说明原纸中的竹浆纤维发挥了抗菌效果;与对比例涂布普通涂料的纸张相比,实施例1-5涂布抗菌涂料的纸张其抗菌率大幅提升。
另外,本领域技术人员还可在本发明权利要求公开的范围和精神内做其它形式和细节上的各种修改、添加和替换。当然,这些依据本发明精神所做的各种修改、添加和替换等变化,都应包含在本发明所要求保护的范围之内。
Claims (8)
1.一种涂布纸,其包括原纸、及形成于原纸单面或双面的至少一涂层,其特征在于:该涂布纸的最外表的涂层为一抗菌涂层,该抗菌涂层中含有抗菌剂及载体,且该抗菌剂负载在载体上,该载体为微胶囊形成;该抗菌涂层还含颜料、胶乳及辅助添加剂,其中颜料100质量份、抗菌剂0.02-0.2质量份,胶乳4-10质量份,辅助添加剂包括2-8质量份淀粉、0.2-1.0质量份耐水化剂、0.4-1.0质量份润滑剂、0.05-0.2质量份消泡剂,0.05-0.15质量份分散剂。
2.如权利要求1所述的涂布纸,其特征在于:该涂布纸在涂布涂层前在原纸表面涂布表胶层。
3.如权利要求1所述的涂布纸,其特征在于:抄造该原纸的浆料中含有竹浆,其中竹浆占浆料总质量的10%-30%。
4.如权利要求3所述的涂布纸,其特征在于:抄造该原纸的浆料中还含有漂白阔叶木浆及漂白针叶木浆,其中漂白阔叶木浆与漂白针叶木浆的质量比为50-85:5-10。
5.如权利要求1所述的涂布纸,其特征在于:抄造该原纸的浆料中还添加有填料、阳离子聚合电解质、内部施胶剂及阴离子保留助剂,按占纸浆总重量比例计算,添加的填料占纸浆总重量的1%-20%,阳离子聚合电解质占纸浆总重量的0.25%-5%,内部施胶剂占纸浆总重量的1%-2.5%,阴离子保留助剂占纸浆总重量的0.1%-2%。
6.如权利要求1所述的涂布纸,其特征在于:该抗菌剂铜族元素的纳米或胶体颗粒、二氧化钛、氧化锌、氧化铜、磷酸二氢铵、碳酸锂中的一种或多种的组合。
7.如权利要求1所述的涂布纸,其特征在于:该抗菌剂为酰基苯胺类、咪唑类、噻唑类、异噻唑酮衍生物、季铵盐类、双呱类、酚类的一种或多种的组合。
8.如权利要求6所述的涂布纸,其特征在于:所述铜族元素为金、银或铜,其中纳米金、银或铜与载体的重量比例为1:10-10:1。