CN103897543A - Water-resistant varnish - Google Patents
Water-resistant varnish Download PDFInfo
- Publication number
- CN103897543A CN103897543A CN201310553978.6A CN201310553978A CN103897543A CN 103897543 A CN103897543 A CN 103897543A CN 201310553978 A CN201310553978 A CN 201310553978A CN 103897543 A CN103897543 A CN 103897543A
- Authority
- CN
- China
- Prior art keywords
- parts
- varnish
- resistant varnish
- water
- water resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to water-resistant varnish. The water-resistant varnish consists of the following components in parts by weight: 10-15 parts of phthalate anhydride, 13-16 parts of glycerol, 11-18 parts of pentaerythritol, 21-28 parts of alkyd resin, 22-29 parts of amino resin, 3-8 parts of triethylene tetramine, 1-5 parts of polyamide, 20-27 parts of benzoin resin, 12-19 parts of amber resin, 4-9 parts of paint thinner, 2-6 parts of curing agent and 11-16 parts of moisture proof agent. The water-resistant varnish has equivalent coating performance and construction performance to ordinary varnish. By adding the moisture proof agent, the varnish has high water resistance, and comprehensive protection and a good decorating effect can be provided for products. Moreover, the water-resistant varnish has the advantages of nontoxicity, freeness from pollution, safety and environmental friendliness.
Description
Technical field
The present invention relates to a kind of varnish, particularly a kind of water resistant varnish.
Background technology
China's furniture industry development is at present very fast, and output also constantly raises.Some family selections are bought ready-made furniture at furniture market, and some families can directly ask carpenter to make furniture, then please painter's mopping.The wood furniture no matter with what approach obtaining, all need to varnish with lacquer on its surface, plays the effect such as waterproof, mildew-resistant, can also make furniture look attractive in appearance.Some furniture intrinsic colour is just very attractive in appearance, does not need to coat coloured paint, only need to be coated with transparent varnish just passable.Nowadays the varnish of a lot of furniture uses is alkyd paint, but their dry speed is slow, and hardness is not high yet, and water resistance is not so good, and these painters' that slowed down speed of application, has affected the attractive in appearance of furniture, has also affected daily life.
Summary of the invention
The object of this invention is to provide the water resistant varnish that a kind of result of use is good.
For achieving the above object, the present invention is achieved by the following technical solutions: a kind of water resistant varnish, the parts by weight of its each component are: 10～15 parts of phthalate anhydrides, 13～16 parts of glycerol, 11～18 parts of tetramethylolmethanes, 21～28 parts of Synolac, 22～29 parts, aminoresin, 3～8 parts of triethylene tetramines, 1～5 part of polyamine, 20～27 parts of the resins of resting in peace, 12～19 parts of kochenites, 4～9 parts of solvent or diluents, 2～6 parts, solidifying agent, 11～16 parts of non-blushing thinners.
Further, described solvent or diluent is that white wine essence, white alcohol mix according to 1:2, or uses Polyester Paint solvent.
Further, described solidifying agent is by a kind of or its mixture in diethylenetriamine, triethylene tetramine, polyamine.
Further, described non-blushing thinner is that iron powder, calcium chloride, calcium carbonate mix, and blending ratio is 1:1:2.
The invention has the beneficial effects as follows: the invention provides a kind of water resistant varnish; compared with common varnish; there is equal film performance and workability; wherein add non-blushing thinner; make varnish there is stronger water repelling property; can be for product provides thorough protection and good decorative effect, and nontoxic, pollution-free, safety and environmental protection.
Embodiment
For understanding better the present invention; below by three embodiment, the present invention is done to further concrete elaboration; but unintelligible is limitation of the invention; the foregoing invention content of some nonessential improvement and adjustment do according to to(for) those skilled in the art, be also considered as dropping in protection scope of the present invention.
Embodiment 1
A kind of water resistant varnish of the present embodiment, the parts by weight of its each component are: 15 parts of phthalate anhydrides, 16 parts of glycerol, 18 parts of tetramethylolmethanes, 28 parts of Synolac, 29 parts, aminoresin, 8 parts of triethylene tetramines, 5 parts of polyamine, 27 parts of the resins of resting in peace, 19 parts of kochenites, 9 parts of solvent or diluents, 6 parts, solidifying agent, 16 parts of non-blushing thinners.
Described solvent or diluent is that white wine essence, white alcohol mix according to 1:2, or uses Polyester Paint solvent.
Described solidifying agent is by a kind of or its mixture in diethylenetriamine, triethylene tetramine, polyamine.
Described non-blushing thinner is that iron powder, calcium chloride, calcium carbonate mix, and blending ratio is 1:1:2.
Embodiment 2
A kind of water resistant varnish of the present embodiment, the parts by weight of its each component are: 10 parts of phthalate anhydrides, 13 parts of glycerol, 11 parts of tetramethylolmethanes, 21 parts of Synolac, 22 parts, aminoresin, 3 parts of triethylene tetramines, 1 part of polyamine, 20 parts of the resins of resting in peace, 12 parts of kochenites, 4 parts of solvent or diluents, 2 parts, solidifying agent, 11 parts of non-blushing thinners.
Described solvent or diluent is that white wine essence, white alcohol mix according to 1:2, or uses Polyester Paint solvent.
Described solidifying agent is by a kind of or its mixture in diethylenetriamine, triethylene tetramine, polyamine.
Described non-blushing thinner is that iron powder, calcium chloride, calcium carbonate mix, and blending ratio is 1:1:2.
Embodiment 3
A kind of water resistant varnish of the present embodiment, the parts by weight of its each component are: 14 parts of phthalate anhydrides, 15 parts of glycerol, 17 parts of tetramethylolmethanes, 25 parts of Synolac, 27 parts, aminoresin, 7 parts of triethylene tetramines, 4 parts of polyamine, 26 parts of the resins of resting in peace, 13 parts of kochenites, 5 parts of solvent or diluents, 4 parts, solidifying agent, 14 parts of non-blushing thinners.
Described solvent or diluent is that white wine essence, white alcohol mix according to 1:2, or uses Polyester Paint solvent.
Described solidifying agent is by a kind of or its mixture in diethylenetriamine, triethylene tetramine, polyamine.
Described non-blushing thinner is that iron powder, calcium chloride, calcium carbonate mix, and blending ratio is 1:1:2.
Claims (4)
1. a water resistant varnish, it is characterized in that, the parts by weight of its each component are: 10～15 parts of phthalate anhydrides, 13～16 parts of glycerol, 11～18 parts of tetramethylolmethanes, 21～28 parts of Synolac, 22～29 parts, aminoresin, 3～8 parts of triethylene tetramines, 1～5 part of polyamine, 20～27 parts of the resins of resting in peace, 12～19 parts of kochenites, 4～9 parts of solvent or diluents, 2～6 parts, solidifying agent, 11～16 parts of non-blushing thinners.
2. a kind of water resistant varnish according to claim 1, is characterized in that, described solvent or diluent is that white wine essence, white alcohol mix according to 1:2, or uses Polyester Paint solvent.
3. a kind of water resistant varnish according to claim 1, is characterized in that, described solidifying agent is by a kind of or its mixture in diethylenetriamine, triethylene tetramine, polyamine.
4. a kind of water resistant varnish according to claim 1, is characterized in that, described non-blushing thinner is that iron powder, calcium chloride, calcium carbonate mix, and blending ratio is 1:1:2.