CN104403436A - Fluorocarbon exterior wall emulsion paint and preparation method thereof - Google Patents
Fluorocarbon exterior wall emulsion paint and preparation method thereof Download PDFInfo
- Publication number
- CN104403436A CN104403436A CN201410621315.8A CN201410621315A CN104403436A CN 104403436 A CN104403436 A CN 104403436A CN 201410621315 A CN201410621315 A CN 201410621315A CN 104403436 A CN104403436 A CN 104403436A
- Authority
- CN
- China
- Prior art keywords
- agent
- parts
- exterior wall
- fluorocarbon
- aluminium powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fluorocarbon exterior wall emulsion paint and relates to the technical field of building decoration materials. The paint is composed of the following raw materials in parts by weight: 55 to 65 parts of fluorocarbon resin, 0.3 to 0.5 part of dispersant, 15 to 25 parts of cellulose acetate butyrate, 6 to 8 parts of aluminum powder, 0.3 to 0.5 part of leveling agent, 0.3 to 0.5 part of aluminum powder orienting agent, 1.0 to 2.0 parts of rheological anti-settling agent, and 10 to 20 parts of mixed solvent. The preparation method has the advantages of simpleness, easily-available raw materials, little equipment investment, and convenient operation, and the prepared fluorocarbon exterior wall emulsion paint has the advantages of environment-friendliness, no pollution, high purity, good using effect, strong high temperature resistant performance, safety, and reliability.
Description
Technical field
The present invention relates to technical field of construction and decoration materials, be specifically related to a kind of fluorocarbon exterior wall emulsion paint and preparation method thereof.
Background technology
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.Paint is the call in ancient times; Coating, is modern civilization address, comprises more scientific and technological composition, be widely used in modern science and technology and industrial circle.But paint has some habitual addresses of blurting out still to remain, as emulsion paint, priming paint, finish paint etc.Generally speaking, coating is exactly the material that can be coated in coated article part surface and can form the continuous film of firm attachment.It both can be inorganic, as electro-coppering, and electronickelling, electro-galvanizing etc.Also can be organic, as most organic polymer material, organic polymer material constitutes current Coating Market major portion, that paints is of a great variety, the paint that different fields uses, and kind is also not quite similar, current emulsion paint is on the market in use particularly extensive, deeply use by all kinds of industry, but the technical recipe of emulsion paint still relatively tradition, can not the demand of the current market of compound.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of asepsis environment-protecting, simple fluorocarbon exterior wall emulsion paint of preparation technology and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of fluorocarbon exterior wall emulsion paint, is characterized in that, be made up of the raw material of following component:
Fluorocarbon resin 55-65 part, dispersion agent 0.3-0.5 part, cellulose acetate butyrate 15-25 part, aluminium powder 6-8 part, flow agent 0.3-0.5 part, aluminium powder directing agent 0.3-0.5 part, stream become anti-settling agent 1.0-2.0 part, mixed solvent 10-20 part.
The preferred component of each raw material is:
Fluorocarbon resin 60 parts, dispersion agent 0.4 part, cellulose acetate butyrate 20 parts, aluminium powder 7 parts, flow agent 0.4 part, aluminium powder directing agent 0.4 part, stream become anti-settling agent 1.5 parts, mixed solvent 15 parts.
Described dispersion agent is tripoly phosphate sodium STPP, and described flow agent is polydimethylsiloxane.
Described mixed solvent is the mixture of gained after the direct mix and blend of sterilant, defoamer and pH value regulator; Described sterilant: defoamer: pH value regulator is 2:3:1
Another object of the present invention prepares the preparation method of fluorocarbon exterior wall emulsion paint of the present invention, it is characterized in that: comprise following processing step,
A, the reactor selecting an agitator is set, after the aluminium powder in raw material, dispersion agent, aluminium powder directing agent and mixed solvent added entering according to formula ratio, after carrying out stirrings 30min according to the rotating speed of 100-300r/min, again after immersion 3-5h, for subsequent use;
B, select the sand mill of a cleaning, the fluorocarbon resin in raw material, cellulose acetate butyrate, flow agent and stream are become anti-settling agent and all adds wherein, after high speed dispersion 20min, add the aluminium powder after soaking in step a, after dispersion 10-20min, filter and package.
The invention has the beneficial effects as follows: the present invention is simply easy to prepare, raw material is easy to get, and facility investment is few, convenient operation, the fluorocarbon exterior wall emulsion paint of preparation, and environment friendly and pollution-free, purity is high, and result of use is good, and high thermal resistance is strong, safe and reliable.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of fluorocarbon exterior wall emulsion paint, is made up of the raw material of following component:
Fluorocarbon resin 55kg, tripoly phosphate sodium STPP 0.3kg, cellulose acetate butyrate 15kg, aluminium powder 6kg, polydimethylsiloxane 0.3kg, aluminium powder directing agent 0.3kg, stream become anti-settling agent 1.0kg, mixed solvent 10kg.
Described mixed solvent is the mixture of gained after the direct mix and blend of sterilant, defoamer and pH value regulator; Described sterilant: defoamer: pH value regulator is 2:3:1
Prepare the method for fluorocarbon exterior wall emulsion paint of the present invention, comprise following processing step:
A, the reactor selecting an agitator is set, after the aluminium powder in raw material, tripoly phosphate sodium STPP, aluminium powder directing agent and mixed solvent added entering according to formula ratio, after carrying out stirrings 30min according to the rotating speed of 100-300r/min, again after immersion 3-5h, for subsequent use;
B, select the sand mill of a cleaning, fluorocarbon resin in raw material, cellulose acetate butyrate, polydimethylsiloxane and stream are become anti-settling agent all add wherein, after high speed dispersion 20min, add the aluminium powder after soaking in step a, after dispersion 10-20min, filter and package.
Embodiment 2
A kind of fluorocarbon exterior wall emulsion paint, is made up of the raw material of following component:
Fluorocarbon resin 60kg, tripoly phosphate sodium STPP 0.4kg, cellulose acetate butyrate 20kg, aluminium powder 7kg, polydimethylsiloxane 0.4kg, aluminium powder directing agent 0.4kg, stream become anti-settling agent 1.5kg, mixed solvent 15kg.
Described mixed solvent is the mixture of gained after the direct mix and blend of sterilant, defoamer and pH value regulator; Described sterilant: defoamer: pH value regulator is 2:3:1
Prepare the method for fluorocarbon exterior wall emulsion paint of the present invention, comprise following processing step:
A, the reactor selecting an agitator is set, after the aluminium powder in raw material, tripoly phosphate sodium STPP, aluminium powder directing agent and mixed solvent added entering according to formula ratio, after carrying out stirrings 30min according to the rotating speed of 100-300r/min, again after immersion 3-5h, for subsequent use;
B, select the sand mill of a cleaning, fluorocarbon resin in raw material, cellulose acetate butyrate, polydimethylsiloxane and stream are become anti-settling agent all add wherein, after high speed dispersion 20min, add the aluminium powder after soaking in step a, after dispersion 10-20min, filter and package.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (5)
1. a fluorocarbon exterior wall emulsion paint, is characterized in that, is made up of the raw material of following component:
Fluorocarbon resin 55-65 part, dispersion agent 0.3-0.5 part, cellulose acetate butyrate 15-25 part, aluminium powder 6-8 part, flow agent 0.3-0.5 part, aluminium powder directing agent 0.3-0.5 part, stream become anti-settling agent 1.0-2.0 part, mixed solvent 10-20 part.
2. a kind of fluorocarbon exterior wall emulsion paint according to claim 1, is characterized in that: the preferred component of each raw material is: fluorocarbon resin 60 parts, dispersion agent 0.4 part, cellulose acetate butyrate 20 parts, aluminium powder 7 parts, flow agent 0.4 part, aluminium powder directing agent 0.4 part, stream become anti-settling agent 1.5 parts, mixed solvent 15 parts.
3. a kind of fluorocarbon exterior wall emulsion paint according to claim 1, it is characterized in that: described dispersion agent is tripoly phosphate sodium STPP, described flow agent is polydimethylsiloxane.
4. a kind of fluorocarbon exterior wall emulsion paint according to claim 1, is characterized in that: described mixed solvent is the mixture of gained after the direct mix and blend of sterilant, defoamer and pH value regulator; Described sterilant: defoamer: pH value regulator is 2:3:1.
5. the fluorocarbon exterior wall emulsion paint of preparation described in claim 1 or 2, is characterized in that: comprise the following steps,
A, the reactor selecting an agitator is set, after the aluminium powder in raw material, dispersion agent, aluminium powder directing agent and mixed solvent added entering according to formula ratio, after carrying out stirrings 30min according to the rotating speed of 100-300r/min, again after immersion 3-5h, for subsequent use;
B, select the sand mill of a cleaning, the fluorocarbon resin in raw material, cellulose acetate butyrate, flow agent and stream are become anti-settling agent and all adds wherein, after high speed dispersion 20min, add the aluminium powder after soaking in step a, after dispersion 10-20min, filter and package.