CN104387856A - Novel environment-friendly internal wall latex paint and preparation method thereof - Google Patents
Novel environment-friendly internal wall latex paint and preparation method thereof Download PDFInfo
- Publication number
- CN104387856A CN104387856A CN201410619769.1A CN201410619769A CN104387856A CN 104387856 A CN104387856 A CN 104387856A CN 201410619769 A CN201410619769 A CN 201410619769A CN 104387856 A CN104387856 A CN 104387856A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- novel environment
- latex paint
- wall latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a novel environment-friendly internal wall latex paint, relating to the technical field of architectural decoration materials. The novel environment-friendly internal wall latex paint is composed of the following raw materials: 350-360 parts of deionized water, 2-4 parts of hydroxyethyl cellulose, 8-12 parts of dispersing agent, 2-6 parts of defoaming agent, 2-4 parts of pH value regulator, 20-30 parts of propanediol, 160-180 parts of titanium white, 120-160 parts of calcium carbonate, 50-70 parts of talcum powder, 40-50 parts of aluminum silicate, 17-19 parts of styrene-acrylic emulsion, 2-4 parts of thickener, 1-2 parts of leveling agent and 1-3 parts of bactericide. The method has the advantages of convenient and simple preparation process, accessible raw materials and low equipment investment, and is convenient for operation; and the prepared novel environment-friendly internal wall latex paint has the advantages of environmental protection, no pollution, high purity, favorable use effect, favorable high temperature resistance and high safety and reliability.
Description
Technical field
The present invention relates to technical field of construction and decoration materials, be specifically related to a kind of novel environment friendly interiro wall latex paint and preparation method thereof.
Background technology
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.Paint is the call in ancient times; Coating, is modern civilization address, comprises more scientific and technological composition, be widely used in modern science and technology and industrial circle.But paint has some habitual addresses of blurting out still to remain, as emulsion paint, priming paint, finish paint etc.Generally speaking, coating is exactly the material that can be coated in coated article part surface and can form the continuous film of firm attachment.It both can be inorganic, as electro-coppering, and electronickelling, electro-galvanizing etc.Also can be organic, as most organic polymer material, organic polymer material constitutes current Coating Market major portion, that paints is of a great variety, the paint that different fields uses, and kind is also not quite similar, current emulsion paint is on the market in use particularly extensive, deeply use by all kinds of industry, but the technical recipe of emulsion paint still relatively tradition, can not the demand of the current market of compound.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of asepsis environment-protecting, simple novel environment friendly interiro wall latex paint of preparation technology and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of novel environment friendly interiro wall latex paint, is characterized in that, be made up of the raw material of following component:
Deionized water 350-360 part, Natvosol 2-4 part, dispersion agent 8-12 part, defoamer 2-6 part, pH value regulator 2-4 part, propylene glycol 20-30 part, titanium dioxide 160-180 part, calcium carbonate 120-160 part, talcum powder 50-70 part, pure aluminium silicate 40-50 part, benzene emulsion 17-19 part, thickening material 2-4 part, flow agent 1-2 part, sterilant 1-3 part.
The preferred component of each raw material is: deionized water 355 parts, Natvosol 3 parts, dispersion agent 10 parts, defoamer 4 parts, pH value regulator 3 parts, propylene glycol 25 parts, titanium dioxide 170 parts, 140 parts, calcium carbonate, talcum powder 60 parts, pure aluminium silicate 45 parts, benzene emulsion 18 parts, thickening material 3 parts, flow agent 1.5 parts, 2 parts, sterilant.
Described dispersion agent is tripoly phosphate sodium STPP, and described defoamer is silicone oil, and described pH value regulator is ammoniacal liquor, and described thickening material is polyacrylic ester, and described flow agent is polydimethylsiloxane, and described sterilant is zinc chloride.
Another object of the present invention prepares the preparation method of novel environment friendly interiro wall latex paint of the present invention, it is characterized in that: comprise following processing step,
A, select the paint mixing tank of a cleaning, the deionized water in raw material is added wherein according to 85% of formula ratio, under constantly stirring, adds the Natvosol in raw material, continue stirring reaction 70-80min;
B, until above-mentioned steps a reaction terminate after, the defoamer of the pH value regulator in raw material, dispersion agent, 50% formula ratio and sterilant are all added wherein, stir;
C, after above-mentioned steps b stirs, add wherein by the titanium dioxide in raw material, calcium carbonate, talcum powder and pure aluminium silicate, control rotating speed is 300-400r/min, after stirring reaction 30min, add 5% of propylene glycol in raw material and formula ratio deionized water, again stir;
D, after above-mentioned steps c stirring reaction terminates, the benzene emulsion in raw material is added wherein, then defoamer remaining in raw material is added after entering, stirring reaction 30min again;
After the reaction of e, steps d terminates, add thickening material, flow agent and the remaining deionized water in raw material, after stirring 20min, filter and package.
The invention has the beneficial effects as follows: the present invention is simply easy to prepare, raw material is easy to get, and facility investment is few, convenient operation, the novel environment friendly interiro wall latex paint of preparation, and environment friendly and pollution-free, purity is high, and result of use is good, and high thermal resistance is strong, safe and reliable.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of novel environment friendly interiro wall latex paint, is made up of the raw material of following component:
Deionized water 350kg, Natvosol 2kg, tripoly phosphate sodium STPP 8kg, silicone oil 2kg, ammoniacal liquor 2kg, propylene glycol 20kg, titanium dioxide 160kg, calcium carbonate 120kg, talcum powder 50kg, pure aluminium silicate 40kg, benzene emulsion 17kg, polyacrylic ester 2kg, polydimethylsiloxane 1kg, zinc chloride 1kg.
Prepare the method for novel environment friendly interiro wall latex paint of the present invention, comprise following processing step:
A, select the paint mixing tank of a cleaning, the deionized water in raw material is added wherein according to 85% of formula ratio, under constantly stirring, adds the Natvosol in raw material, continue stirring reaction 70-80min;
B, until above-mentioned steps a reaction terminate after, the silicone oil of the ammoniacal liquor in raw material, tripoly phosphate sodium STPP, 50% formula ratio and zinc chloride are all added wherein, stir;
C, after above-mentioned steps b stirs, add wherein by the titanium dioxide in raw material, calcium carbonate, talcum powder and pure aluminium silicate, control rotating speed is 300-400r/min, after stirring reaction 30min, add 5% of propylene glycol in raw material and formula ratio deionized water, again stir;
D, after above-mentioned steps c stirring reaction terminates, the benzene emulsion in raw material is added wherein, then silicone oil remaining in raw material is added after entering, stirring reaction 30min again;
After the reaction of e, steps d terminates, add polyacrylic ester, polydimethylsiloxane and the remaining deionized water in raw material, after stirring 20min, filter and package.
Embodiment 2
A kind of novel environment friendly interiro wall latex paint, is made up of the raw material of following component:
Deionized water 355kg, Natvosol 3kg, tripoly phosphate sodium STPP 10kg, silicone oil 4kg, ammoniacal liquor 3kg, propylene glycol 25kg, titanium dioxide 170kg, calcium carbonate 140kg, talcum powder 60kg, pure aluminium silicate 45kg, benzene emulsion 18kg, polyacrylic ester 3kg, polydimethylsiloxane 1.5kg, zinc chloride 2kg.
Prepare the method for novel environment friendly interiro wall latex paint of the present invention, comprise following processing step:
A, select the paint mixing tank of a cleaning, the deionized water in raw material is added wherein according to 85% of formula ratio, under constantly stirring, adds the Natvosol in raw material, continue stirring reaction 70-80min;
B, until above-mentioned steps a reaction terminate after, the silicone oil of the ammoniacal liquor in raw material, tripoly phosphate sodium STPP, 50% formula ratio and zinc chloride are all added wherein, stir;
C, after above-mentioned steps b stirs, add wherein by the titanium dioxide in raw material, calcium carbonate, talcum powder and pure aluminium silicate, control rotating speed is 300-400r/min, after stirring reaction 30min, add 5% of propylene glycol in raw material and formula ratio deionized water, again stir;
D, after above-mentioned steps c stirring reaction terminates, the benzene emulsion in raw material is added wherein, then silicone oil remaining in raw material is added after entering, stirring reaction 30min again;
After the reaction of e, steps d terminates, add polyacrylic ester, polydimethylsiloxane and the remaining deionized water in raw material, after stirring 20min, filter and package.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (4)
1. a novel environment friendly interiro wall latex paint, is characterized in that, is made up of the raw material of following component:
Deionized water 350-360 part, Natvosol 2-4 part, dispersion agent 8-12 part, defoamer 2-6 part, pH value regulator 2-4 part, propylene glycol 20-30 part, titanium dioxide 160-180 part, calcium carbonate 120-160 part, talcum powder 50-70 part, pure aluminium silicate 40-50 part, benzene emulsion 17-19 part, thickening material 2-4 part, flow agent 1-2 part, sterilant 1-3 part.
2. a kind of novel environment friendly interiro wall latex paint according to claim 1, is characterized in that: the preferred component of each raw material is: deionized water 355 parts, Natvosol 3 parts, dispersion agent 10 parts, defoamer 4 parts, pH value regulator 3 parts, propylene glycol 25 parts, titanium dioxide 170 parts, 140 parts, calcium carbonate, talcum powder 60 parts, pure aluminium silicate 45 parts, benzene emulsion 18 parts, thickening material 3 parts, flow agent 1.5 parts, 2 parts, sterilant.
3. a kind of novel environment friendly interiro wall latex paint according to claim 1, it is characterized in that: described dispersion agent is tripoly phosphate sodium STPP, described defoamer is silicone oil, described pH value regulator is ammoniacal liquor, described thickening material is polyacrylic ester, described flow agent is polydimethylsiloxane, and described sterilant is zinc chloride.
4. the novel environment friendly interiro wall latex paint of preparation described in claim 1 or 2, is characterized in that: comprise the following steps,
A, select the paint mixing tank of a cleaning, the deionized water in raw material is added wherein according to 85% of formula ratio, under constantly stirring, adds the Natvosol in raw material, continue stirring reaction 70-80min;
B, until above-mentioned steps a reaction terminate after, the defoamer of the pH value regulator in raw material, dispersion agent, 50% formula ratio and sterilant are all added wherein, stir;
C, after above-mentioned steps b stirs, add wherein by the titanium dioxide in raw material, calcium carbonate, talcum powder and pure aluminium silicate, control rotating speed is 300-400r/min, after stirring reaction 30min, add 5% of propylene glycol in raw material and formula ratio deionized water, again stir;
D, after above-mentioned steps c stirring reaction terminates, the benzene emulsion in raw material is added wherein, then defoamer remaining in raw material is added after entering, stirring reaction 30min again;
After the reaction of e, steps d terminates, add thickening material, flow agent and the remaining deionized water in raw material, after stirring 20min, filter and package.