CN104371517A - Alkyd resin primer and preparation method thereof - Google Patents
Alkyd resin primer and preparation method thereof Download PDFInfo
- Publication number
- CN104371517A CN104371517A CN201410619461.7A CN201410619461A CN104371517A CN 104371517 A CN104371517 A CN 104371517A CN 201410619461 A CN201410619461 A CN 201410619461A CN 104371517 A CN104371517 A CN 104371517A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- added
- alkyd resin
- neutralizing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an alkyd resin primer, relating to the technical field of building and decoration materials. The alkyd resin primer consists of the following raw materials in parts by weight: 15-25 parts of iron oxide red, 4-8 parts of an anti-rust pigment, 15-25 parts of a filling material, 35-45 parts of waterborne alkyd resin, 6-8 parts of mixed additives, 20-30 parts of deionized water and 4-6 parts of a PH value neutralizing agent. The alkyd resin primer disclosed by the invention has the beneficial effects that the alkyd resin primer is convenient and simple to prepare, easily-available in raw material, less in equipment investment and convenient to operate; and the prepared alkyd resin primer is environment-friendly and pollution-free, is high in purity, strong in adhesion and significant in use effect, and is safe and reliable.
Description
Technical field
The present invention relates to technical field of construction and decoration materials, be specifically related to a kind of alkyd primer and preparation method thereof.
Background technology
Coating is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes, comprises more scientific and technological composition, be widely used in modern science and technology and industrial circle.But paint has some habitual addresses of blurting out still to remain, as emulsion paint, priming paint, finish paint etc.Generally speaking, coating is exactly the material that can be coated in coated article part surface and can form the continuous film of firm attachment.It both can be inorganic, as electro-coppering, and electronickelling, electro-galvanizing etc.Also can be organic, as most organic polymer material, organic polymer material constitutes current Coating Market major portion, that paints is of a great variety, the paint that different fields uses, and kind is also not quite similar, resin paint is that relative usage paints more widely, throughput requirements is larger, but floor paint technical recipe is on the market still relatively traditional, can not meet the demand of current market.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of nontoxic, environment protection health, simple alkyd primer of preparation technology and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of alkyd primer, is characterized in that, be made up of the raw material of following component:
Iron oxide red 15-25 part, rust-stabilising pigment 4-8 part, stopping composition 15-25 part, aqueous alkide resin 35-45 part, mixed aid 6-8 part, deionized water 20-30 part, pH value neutralizing agent 4-6 part.
The preferred component of each raw material is:
Iron oxide red 20 parts, rust-stabilising pigment 6 parts, stopping composition 20 parts, aqueous alkide resin 40 parts, mixed aid 7 parts, deionized water 25 parts, pH value neutralizing agent 5 parts.
The raw material that described mixed aid comprises has: tripoly phosphate sodium STPP 2-4 part, silicone oil 1-3 part, polyacrylic ester 3-5 part, polydimethylsiloxane 1-3 part, zinc chloride 4-6 part, water 15-25 part;
Preparation method is: select a stirring tank, is added successively in still by above raw material, stirs post-heating to after 30-50 DEG C, after then adopting sand mill to carry out sand milling.
Described pH neutralizing agent is ammoniacal liquor, and described stopping composition is talcum powder.
Another object of the present invention prepares the preparation method of alkyd primer of the present invention, it is characterized in that: comprise following processing step,
A, select the Scattered Kettle of a cleaning, the deionized water in raw material is added wherein, then adds mixed aid, constantly stir and disperse;
B, the Scattered Kettle pH value neutralizing agent in raw material added in step a, adjust ph is after 8, continues dispersion 20-40min;
C, after above-mentioned steps b dispersion terminates, the stopping composition in raw material is added wherein, after stirring, adds the aqueous alkide resin of formula ratio 60% in raw material again, control rotating speed 800-100r/min and stir 15-20min;
D, until step c reaction terminate after, all materials are all added in sand mill and carry out sand milling until after particle fineness≤40um, aqueous alkide resin remaining in raw material and iron oxide red are added wherein, stirs, packaging put in storage.
The invention has the beneficial effects as follows: the present invention is simply easy to prepare, raw material is easy to get, and facility investment is few, convenient operation, the alkyd primer of preparation, and environment friendly and pollution-free, purity is high, strong adhesion, and result of use is obvious, safe and reliable.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of alkyd primer, is made up of the raw material of following component:
Iron oxide red 15kg, rust-stabilising pigment 4kg, talcum powder 15kg, aqueous alkide resin 35kg, mixed aid 6kg, deionized water 20kg, ammoniacal liquor 4kg.
The raw material that described mixed aid comprises has: tripoly phosphate sodium STPP 2kg, silicone oil 1kg, polyacrylic ester 3kg, polydimethylsiloxane 1kg, zinc chloride 4kg, water 15kg;
Preparation method is: select a stirring tank, is added successively in still by above raw material, stirs post-heating to after 30-50 DEG C, after then adopting sand mill to carry out sand milling.
A, select the Scattered Kettle of a cleaning, the deionized water in raw material is added wherein, then adds mixed aid, constantly stir and disperse;
B, the Scattered Kettle pH value neutralizing agent in raw material added in step a, adjust ph is after 8, continues dispersion 20-40min;
C, after above-mentioned steps b dispersion terminates, the stopping composition in raw material is added wherein, after stirring, adds the aqueous alkide resin of formula ratio 60% in raw material again, control rotating speed 800-100r/min and stir 15-20min;
D, until step c reaction terminate after, all materials are all added in sand mill and carry out sand milling until after particle fineness≤40um, aqueous alkide resin remaining in raw material and iron oxide red are added wherein, stirs, packaging put in storage.
Embodiment 2
A kind of alkyd primer, is made up of the raw material of following component:
Iron oxide red 20kg, rust-stabilising pigment 6kg, stopping composition 20kg, aqueous alkide resin 40kg, mixed aid 7kg, deionized water 25kg, pH value neutralizing agent 5kg.
The raw material that described mixed aid comprises has: tripoly phosphate sodium STPP 3kg, silicone oil 2kg, polyacrylic ester 4kg, polydimethylsiloxane 2kg, zinc chloride 5kg, water 20kg;
Preparation method is: select a stirring tank, is added successively in still by above raw material, stirs post-heating to after 30-50 DEG C, after then adopting sand mill to carry out sand milling.
A, select the Scattered Kettle of a cleaning, the deionized water in raw material is added wherein, then adds mixed aid, constantly stir and disperse;
B, the Scattered Kettle pH value neutralizing agent in raw material added in step a, adjust ph is after 8, continues dispersion 20-40min;
C, after above-mentioned steps b dispersion terminates, the stopping composition in raw material is added wherein, after stirring, adds the aqueous alkide resin of formula ratio 60% in raw material again, control rotating speed 800-100r/min and stir 15-20min;
D, until step c reaction terminate after, all materials are all added in sand mill and carry out sand milling until after particle fineness≤40um, aqueous alkide resin remaining in raw material and iron oxide red are added wherein, stirs, packaging put in storage.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (5)
1. an alkyd primer, is characterized in that, is made up of the raw material of following component:
Iron oxide red 15-25 part, rust-stabilising pigment 4-8 part, stopping composition 15-25 part, aqueous alkide resin 35-45 part, mixed aid 6-8 part, deionized water 20-30 part, pH value neutralizing agent 4-6 part.
2. alkyd primer according to claim 1, is characterized in that: the preferred component of each raw material is: iron oxide red 20 parts, rust-stabilising pigment 6 parts, stopping composition 20 parts, aqueous alkide resin 40 parts, mixed aid 7 parts, deionized water 25 parts, pH value neutralizing agent 5 parts.
3. alkyd primer according to claim 1, it is characterized in that: the raw material that described mixed aid comprises has: tripoly phosphate sodium STPP 2-4 part, silicone oil 1-3 part, polyacrylic ester 3-5 part, polydimethylsiloxane 1-3 part, zinc chloride 4-6 part, water 15-25 part;
Preparation method is: select a stirring tank, is added successively in still by above raw material, stirs post-heating to after 30-50 DEG C, after then adopting sand mill to carry out sand milling.
4. alkyd primer according to claim 1, is characterized in that: described pH neutralizing agent is ammoniacal liquor, and described stopping composition is talcum powder.
5. the alkyd primer of preparation described in claim 1 or 2, is characterized in that: comprise the following steps,
A, select the Scattered Kettle of a cleaning, the deionized water in raw material is added wherein, then adds mixed aid, constantly stir and disperse;
B, the Scattered Kettle pH value neutralizing agent in raw material added in step a, adjust ph is after 8, continues dispersion 20-40min;
C, after above-mentioned steps b dispersion terminates, the stopping composition in raw material is added wherein, after stirring, adds the aqueous alkide resin of formula ratio 60% in raw material again, control rotating speed 800-100r/min and stir 15-20min;
D, until step c reaction terminate after, all materials are all added in sand mill and carry out sand milling until after particle fineness≤40um, aqueous alkide resin remaining in raw material and iron oxide red are added wherein, stirs, packaging put in storage.