CN107619626A - A kind of aqueous high-temperature-resistant high humidity inorganic coating and preparation method thereof - Google Patents
A kind of aqueous high-temperature-resistant high humidity inorganic coating and preparation method thereof Download PDFInfo
- Publication number
- CN107619626A CN107619626A CN201710719637.XA CN201710719637A CN107619626A CN 107619626 A CN107619626 A CN 107619626A CN 201710719637 A CN201710719637 A CN 201710719637A CN 107619626 A CN107619626 A CN 107619626A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- inorganic
- temperature
- water
- high humidity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of aqueous high-temperature-resistant high humidity inorganic coating and preparation method thereof, including following raw material components and percentage by weight:Cellulose 0.2 1%;Inorganic silicic acid potassium 10 20%;Inorganic Ludox 5 20%;Fluorine carbon emulsion 10 20%;Water-based cosolvent 1 5%;Aqueous wetting agent 0.1 0.5%;Aqueous dispersion 0.5 1.5%;Aqueous defoamer 0.1 1.5%;Pigment 10 20%;Filler 15 30%;Film forming accelerating 1 2.5%;Water-based thickener 0.1 0.5%;Water surplus.The aqueous high-temperature-resistant high humidity inorganic coating that the present invention obtains can bottom, face it is general, repeat spraying or brush, grinability and fillibility are good, and richness and gloss can adjust;Paint film alcohol resistance can be good, and it is without exception to be soaked in 60min in the ethanol water that mass concentration is 75%;The alkali resistance of paint film, acid-proof.
Description
Technical field
The present invention relates to inorganic coating technical field, specifically discloses a kind of aqueous high-temperature-resistant high humidity inorganic coating and its system
Preparation Method.
Background technology
Inorganic coating, refer to inorganic silicate inner-outer wall surface and use coating, inner-outer wall coating decoration can not only be made more attractive,
And permanent chemical bond can occur with mineral surfaces.Its service life is 5-10 times of general organic coating, or even longer.
Outer wall coating can be made, and climate does not influence with Drought-wet change.
In Chinese architecture coating market now, aqueous inorganic paint occupation rate less than 5%, this with America and Europe more than 90% city
Field popularity rate difference is far-reaching.And and for example this is big for the scale of construction of Chinese architecture coating, for environmental angle, inorganic coating but also with
The incomparable inherent advantage of organic coating.
" it is economical, efficiently, energy-conservation, ecology " form the basic principle that human development follows jointly.World in recent years
In the range of have also been proposed the general principle of sustainable development, this is all by as promoting and promote the very strong driving force that inorganic coating develops.
In fact, the development of inorganic coating has been subjected to most attention, Japan and some countries of Europe also propose " coating is inorganization "
Viewpoint.These will all indicate that this inorganic coating possesses very big advantages for development and potentiality.
It is seldom currently used for the selected water-base resin under the conditions of hot and humid and emulsion kind.And quality also it is irregular not
Together;Its alternative species of auxiliary agent and color stuffing with paint is also few.Based on some of the above reason, water-based common coating
Performance still has certain gap compared with solvent based coating, and it is in drying time, hardness, richness, water resistance, heat resistance and resistance to strong
Sour highly basic etc. is nothing like the solvent based coating of same type.This is determined by water-based system own characteristic.
Common organic high temperature-resistant high humidity coating is in construction work, basic unit-brushing primer (1 time)-organic high temperature-resistant of polishing
High humidity coating (1-2 times) is, it is necessary to two or more coating.The aqueous high-temperature-resistant high humidity inorganic coating need to have concurrently priming paint and
The advantages of finish paint, direct two edge forming, so as to save cost, production efficiency is improved again.
The content of the invention
It is an object of the invention to overcome the defects of existing, there is provided a kind of aqueous high-temperature-resistant high humidity inorganic coating and its preparation
Method, the aqueous high-temperature-resistant high humidity inorganic coating can bottom, face it is general, repeat spraying or brush, grinability and fillibility are good, rich
Full scale and gloss can adjust;Paint film alcohol resistance and resistance to sulfuric acid excellent.
In order to realize the above object the present invention is by realizing including following technical scheme:A kind of aqueous high-temperature-resistant high humidity
Inorganic coating, including following raw material components and percentage by weight:
Preferably, the percentage by weight of the cellulose is 0.3-0.7%.
Preferably, the percentage by weight of the inorganic silicic acid potassium is 11-14%.
Preferably, the percentage by weight of the inorganic Ludox is 10-14%.
Preferably, the percentage by weight of the fluorine carbon emulsion is 10-14%.
Preferably, the percentage by weight of the water-based cosolvent is 1.2-2%.
Preferably, the percentage by weight of the aqueous wetting agent is 0.1-0.3%.
Preferably, the percentage by weight of the aqueous dispersion is 0.8-1.3%.
Preferably, the percentage by weight of the aqueous defoamer is 0.2-0.5%.
Preferably, the percentage by weight of the pigment is 16-18%.
Preferably, the percentage by weight of the filler is 20-25%.
Preferably, the percentage by weight of the film forming accelerating is 1.2-1.8%.
Preferably, the percentage by weight of the water-based thickener is 0.2-0.6%.
Preferably, the percentage by weight of the water is 15-35%.
Preferably, the cellulose is hydroxyethyl cellulose or ethylhydroxyethylcellulose.
Preferably, mole proportion of the inorganic silicic acid potassium is more than 6.
The too high rock-steady structure that can destroy inorganic Ludox of solution alkaline of low mole of inorganic silicic acid potassium, can make inorganic silicon molten
Glue becomes gel or solid and separated out, and can also destroy the pH value of system, so as to occur shedding, the problems such as poor water resistance.The present invention
Requirement of the high molar ratio amount more than 6 is met using inorganic silicic acid potassium, its alkalescence is low, and water resistance is preferable.
Preferably, the particle diameter of the inorganic Ludox is less than 100nm, SiO in the inorganic Ludox2Content is more than
30%.
It is highly preferred that the model of inorganic Ludox profit difficult to understand or the section CB102 of resistance to Europe.Inorganic silicon on open market is molten
Glue be quartz sand do raw material with highly basic NaOH go dissolving react, big 100nm-1 μm of particle diameter, Na can be generated2O content is more than 1.0%
Ludox, this inorganic Ludox easily produces autohemagglutination, storage and poor compatibility.The present invention is prepared inorganic using silicon dissolution method
Ludox, silicon dissolution method are with inorganic or organic alkali as a catalyst, are reacted with elemental silicon and pure water to prepare Ludox, Ludox
Uniform particle sizes, it is easily controllable.
Preferably, the solid content of the fluorine carbon emulsion is 40-50%, and Oil repellent is 10-14% in the fluorine carbon emulsion.
Preferably, the water-based cosolvent is ethylene glycol phenyl ether or medical grade propylene glycol.
It is highly preferred that the model Tao Shi EPH-6 of the ethylene glycol phenyl ether.
Preferably, the filler includes the one or more in barium sulfate, calcium carbonate, calcium silicates, mica powder and talcum powder.
It is highly preferred that the filler by barium sulfate, mica powder and talcum powder according to weight ratio (10-15):(4-6):(4-6)
Combine.
Preferably, the aqueous wetting agent is any one in organic-silicon-modified wetting agent and acrylic acid modified wetting agent
Kind or two kinds.
It is highly preferred that the model BD-109 or CF-10 of the aqueous wetting agent.
Preferably, the aqueous dispersion is ammonium polyacrylate dipersant.
It is highly preferred that model the Tao Shi CA-2500 or Sheng Nuopuke 5027 of the aqueous dispersion.
Preferably, the aqueous defoamer is modified any one in defoamer selected from organosilicon, mineral oil or polyethers.
It is highly preferred that the model of the aqueous defoamer is selected from 2134, A10, SN-321C or SN-NXZ.
Preferably, the pigment is selected from any one of titanium dioxide, iron oxide red, iron oxide yellow and iron oxide black.
Preferably, the model section rope 290 of the film forming accelerating.
Preferably, the water-based thickener is in association type polyurethanes thickener and hydroxyethylcellulose thickener
It is one or two kinds of.
It is highly preferred that the model SHIN-ETSU HANTOTAI HS30000 of the water-based thickener, sub- bodyguard orchid 250HBR, Tao Shi RM-3030 or
Ai Dike 450VF.
The present invention discloses a kind of method for preparing aqueous high-temperature-resistant high humidity inorganic coating as described above, including following step
Suddenly:
1) water is put into mixer in advance, then adds the cellulose, the aqueous dispersion and described water-based
Defoamer, low speed are uniformly dispersed;
2) the water-based cosolvent and the aqueous wetting agent are added, is uniformly dispersed at a high speed;
3) filler and the pigment are added, is uniformly dispersed at a high speed, is filtered, obtains slurry mix semi-finished product;
4) the inorganic silicic acid potassium, the inorganic Ludox and fluorine carbon breast at low speeds, are added while stirring
Liquid, is slow added into the film forming accelerating, then adds the water-based thickener, stirs, and it is high to obtain aqueous high-temperature-resistant
Wet inorganic coating.
In summary, the present invention provides a kind of aqueous high-temperature-resistant high humidity inorganic coating and preparation method thereof, and of the invention has
Beneficial effect:
The aqueous high-temperature-resistant high humidity inorganic coating that the present invention obtains can bottom, face it is general, repeat spraying or brush, grinability
Good with fillibility, richness and gloss can adjust;Paint film alcohol resistance can be good, is soaked in the ethanol water that mass concentration is 75%
Middle 60min is without exception;Paint film is placed in mass concentration as 48h in 10% aqueous sulfuric acid, the difference such as coating bubble-free comes off;Paint film
Mass concentration is placed in as 20% NaOH aqueous solution 144h, the difference such as coating bubble-free comes off;Paint film is placed in 100 DEG C of boiling 24h,
Coating does not occur bubble and the difference such as come off.The present invention obtains the burst size of methanal of aqueous high-temperature-resistant high humidity inorganic coating than general water
Property coating is lower, and the present invention prepares aqueous high-temperature-resistant high humidity inorganic coating and is sprayed on inner-outer wall base material, meet it is safe and environment-friendly,
Power conservation requirement and be advantageous to health of human body, spray efficiency is high, and cost is low, is adapted to industrialized production.
Embodiment
The present invention is expanded on further with reference to embodiment.It should be understood that embodiment is merely to illustrate the present invention, and it is unrestricted
The scope of the present invention.
It is the proportioning of each raw material components in embodiment 1~8 in table 1, the content of each raw material components is parts by weight in table.
The weight proportion of each raw material components in the embodiment 1~8 of table 1
Embodiment 1
1) 150kg water is put into mixer in advance, then adds 4kg hydroxyethyl cellulose (model 250HBR) and 10kg
Aqueous dispersion (model C A2500) and 3kg aqueous defoamers (model BASF2134), mixing speed is adjusted to 300r/min,
The scattered 5min of mixing;
2) the water-based cosolvents of 15kg (EPH-6) and 1.5kg aqueous wetting agents (model BD-109) are added, by mixing speed liter
To 1300r/min, disperse 10min at a high speed;
3) 10kg water is added, then adds 170kg titanium dioxides and 125kg calcium silicates (1250 mesh), at a high speed scattered 5min,
Then 50kg mica powders and 50kg talcum powder are added while stirring, at a high speed scattered 35min, detection fineness, cleannes, that is, starched
Expect mixture semi-finished product;
4) by adjustment of rotational speed to 300r/min, 125kg fluorine carbon emulsions (model DF01) and 125kg are sequentially added while stirring
Inorganic Ludox, 15kg film forming acceleratings (model OE300) stirring 12min is slow added into, then adds 5kg water-based thickeners
(model 450VF) adjusts viscosity, adds 140kg water, is eventually adding 1.5kg preservatives (model LX300) and stirs, and obtains water
Property high-temp resisting high-humidity resisting inorganic coating.
Embodiment 2
1) 150kg water is put into mixer in advance, then adds 4kg hydroxyethyl cellulose (model 250HBR) and 10kg
Aqueous dispersion (model C A2500) and 3kg aqueous defoamers (model BASF2134), mixing speed is adjusted to 300r/min,
The scattered 5min of mixing;
2) after adding the water-based cosolvents of 15kg (EPH-6) and 1.5kg aqueous wetting agents (model BD-109), by mixing speed
1300r/min is risen to, at a high speed scattered 10min;
3) 10kg water is added, 170kg titanium dioxides is then added and 125kg calcium carbonate (1250 mesh, Guangdong Jiangling) is high afterwards
The scattered 5min of speed, then adds 50kg talcum powder and 50kg mica powders when stirring, at a high speed scattered 35min, detection fineness, cleannes,
Obtain slurry mix semi-finished product;
4) by adjustment of rotational speed to 300r/min, 125kg fluorine carbon emulsions (model DF01) and 125kg are sequentially added while stirring
Inorganic silicic acid potassium (model G730), be then slow added into 15kg film forming acceleratings (model OE300) stirring 10min, finally
5kg water-based thickeners (model 450VF) adjustment viscosity is added, 140kg water is added, is eventually adding 1.5kg preservatives (LX300) and stirs
Mix uniformly, obtain aqueous high-temperature-resistant high humidity inorganic coating.
Embodiment 3
1) 150kg water is put into mixer in advance, then adds 4kg hydroxyethyl celluloses (model 250HBR) and 10kg water
Property dispersant (model C A2500) and 3kg aqueous defoamers (model BASF2134), mixing speed is adjusted to 300r/min, mixed
Close scattered 5min;
2) after adding the water-based cosolvents of 17.5kg (EPH-6) and 1.5kg aqueous wetting agents (model BD-109), by stirring speed
Degree rises to 1200r/min, at a high speed scattered 10min;
3) 10kg water is added, then adds 170kg titanium dioxides and 125kg barium sulfate (1250 mesh), at a high speed scattered 5min,
Then add 50kg talcum powder and 50kg mica powders when stirring, at a high speed scattered 30min, detection fineness, cleannes, that is, obtain slurry and mix
Compound semi-finished product;
4) by adjustment of rotational speed to 300r/min, 125kg fluorine carbon emulsions (model DF01), 100kg are sequentially added while stirring
Inorganic Ludox and 125kg inorganic silicic acid potassium, be then slow added into 15kg film forming acceleratings (model OE300) stirring
12min, 2.5kg water-based thickeners (model 450VF) adjustment viscosity is eventually adding, 40kg water is added, is eventually adding 1.5kg anti-corrosions
Agent (model LX300) stirs, and obtains aqueous high-temperature-resistant high humidity inorganic coating.
Embodiment 4
1) 150kg water is put into mixer in advance, then adds 4kg hydroxyethyl cellulose (model 250HBR) and 10kg
Aqueous dispersion (model C A2500) and 3kg aqueous defoamers (model BASF2134), mixing speed is adjusted to 300r/min,
The scattered 5min of mixing;
2) after adding the water-based cosolvents of 15kg (EPH-6) and 1.5kg aqueous wetting agents (model BD-109), by mixing speed
1300r/min is risen to, at a high speed scattered 10min;
3) 10kg water is added, it is scattered at a high speed after then adding 170kg titanium dioxides and 125kg barium sulfate (1250 mesh)
5min, 50kg mica powders and 50kg talcum powder are then added when stirring, at a high speed scattered 30min, detection fineness, cleannes, that is, obtained
Obtain slurry mix semi-finished product;
4) by adjustment of rotational speed to 300r/min, sequentially add while stirring 125kg styrene-acrylic emulsions (model RS-309) and
125kg inorganic silicic acid potassium, 15kg film forming acceleratings (model OE300) stirring 12min is slow added into, it is water-based then to add 5kg
Thickener (model 450VF) adjusts viscosity, adds 140kg water, is eventually adding 1.5kg preservatives (model LX300) and stirs,
Obtain aqueous high-temperature-resistant high humidity inorganic coating.
Embodiment 5
1) 150kg water is put into mixer in advance, then adds 4kg hydroxyethyl celluloses (model 250HBR) and 10kg water
Property dispersant (model C A2500) and 3kg aqueous defoamers (model BASF2134), mixing speed is adjusted to 400r/min, mixed
Close scattered 6min;
2) after adding the water-based cosolvents of 15kg (EPH-6) and 1.5kg aqueous wetting agents (model BD-109), by mixing speed
1200r/min is risen to, at a high speed scattered 10min;
3) 10kg water is added, it is scattered at a high speed after then adding 170kg titanium dioxides and 125kg calcium silicates (1250 mesh)
5min, 50kg mica powders and 50kg talcum powder are then added when stirring, at a high speed scattered 30min, detection fineness, cleannes, that is, obtained
Obtain slurry mix semi-finished product;
4) by adjustment of rotational speed to 300r/min, 125kg styrene-acrylic emulsions (model RS-309) are sequentially added while stirring,
The inorganic Ludox of 125kg, 15kg film forming acceleratings (model OE300) stirring 10min is slow added into, then adds water-based thickening
Agent (model 450VF) adjusts viscosity, adds 140kg water, is eventually adding 1.5kg preservatives (model LX300) and stirs, and obtains
Aqueous high-temperature-resistant high humidity inorganic coating.
Embodiment 6
1) 150kg water is put into mixer in advance, then adds 4kg hydroxyethyl celluloses (model 250HBR) and 10kg water
Property dispersant (model C A2500) and 3kg aqueous defoamers (model BASF2134), mixing speed is adjusted to 300r/min, mixed
Close scattered 7min;
2) after adding the water-based cosolvents of 15kg (EPH-6) and 1.5kg aqueous wetting agents (model BD-109), by mixing speed
1300r/min is risen to, at a high speed scattered 10min;
3) 10kg water is added, the barium sulfate (1250 mesh) for then adding 170kg titanium dioxides and 125kg is scattered at a high speed afterwards
5min, 50kg mica powders and 50kg talcum powder are then added when stirring, at a high speed scattered 35min, detection fineness, cleannes, that is, obtained
Obtain slurry mix semi-finished product;
4) by adjustment of rotational speed to 300r/min, sequentially added in Jiao Bian 125kg acrylic emulsions (model RS-706) and
The inorganic Ludox of 125kg, 15kg film forming acceleratings (model OE300) stirring 12min is slow added into, it is water-based then to add 5kg
Thickener (model 450VF) adjusts viscosity, adds 140kg water, is eventually adding 1.5kg preservatives (model LX300) and stirs,
Obtain aqueous high-temperature-resistant high humidity inorganic coating.
Embodiment 7
1) 150kg water is put into mixer in advance, then adds 4kg hydroxyethyl celluloses (model 250HBR) and 10kg water
Property dispersant (model C A2500) and 3kg aqueous defoamers (model BASF2134), mixing speed is adjusted to 300r/min, mixed
Close scattered 7min;
2) after adding the water-based cosolvents of 15kg (EPH-6) and 1.5kg aqueous wetting agents (model BD-109), by mixing speed
1300r/min is risen to, at a high speed scattered 10min;
3) 10kg water is added, then adds 170kg titanium dioxides and 125kg calcium carbonate (1250 mesh, Guangdong Jiangling) afterwards at a high speed
Scattered 5min, 50kg mica powders and 50kg talcum powder are then added when stirring, at a high speed scattered 25min, detection fineness, cleannes,
Obtain slurry mix semi-finished product;
4) by adjustment of rotational speed to 300r/min, 125kg acrylic emulsions (model RS-706) and 125kg are added while stirring
Inorganic silicic acid potassium, 15kg film forming acceleratings (model OE300) stirring 12min is slow added into, then adds 5kg water-based thickeners
(model 450VF) adjusts viscosity, adds 140kg water, is eventually adding 1.5kg preservatives (model LX300) and stirs, and obtains water
Property high-temp resisting high-humidity resisting inorganic coating.
Embodiment 8
1) 150kg water is put into mixer in advance, then adds 4kg hydroxyethyl cellulose (model 250HBR) and 10kg
Aqueous dispersion (model C A2500) and 3kg aqueous defoamers (model BASF2134), mixing speed is adjusted to 300r/min,
The scattered 6min of mixing;
2) the water-based cosolvents of 17.5kg (EPH-6) and 1.5kg aqueous wetting agents (model BD-109) are added, by mixing speed
1200r/min is risen to, at a high speed scattered 10min;
3) 10kg water is added, then adds 170kg titanium dioxides and 125kg calcium silicates (1250 mesh), at a high speed scattered 5min,
Then 50kg mica powders and 50kg talcum powder are added when stirring, at a high speed scattered 25min, detection fineness, cleannes, that is, obtains slurry
Mixture semi-finished product;
4) by adjustment of rotational speed to 300r/min, it is inorganic that 125kg styrene-acrylic emulsions (model RS-706), 100kg are added when stirring
Ludox and 125kg inorganic silicic acid potassium, 15kg film forming acceleratings (model OE300) stirring 12min is slow added into, is then added
2.5kg water-based thickeners (model 450VF) adjust viscosity, add 40kg water, are eventually adding 1.5kg preservatives (model LX300)
Stir, obtain aqueous high-temperature-resistant high humidity inorganic coating.
Testing result:
According to examination criteria JG/T26-2002《Exterior wall inorganic architectural coatings》It is high to the aqueous high-temperature-resistant in embodiment 1~8
Wet inorganic coating is tested, the performance test results as Table 2,3, from table 2,3 as can be seen that embodiment 1~8 obtain it is water-based
The pH of high-temp resisting high-humidity resisting inorganic coating meets Testing index;The outer and no exceptions in 50 DEG C of storages a little layering in 7 days.
The aqueous high-temperature-resistant high humidity inorganic coating of embodiment 1 to 8 meets Testing index in terms of solid content, adhesive force;Paint
Film alcohol resistance can be good, and it is without exception to be soaked in 60min in the ethanol water that mass concentration is 75%;Three circulations of freeze-thaw stability
It is without exception.In water boiling resistance aspect of performance, the coating of fluorine carbon is added significantly better than phenylpropyl alcohol or the coating of acrylic acid.
Inorganic coating is equal in terms of the resistance to highly basic of the aqueous high-temperature-resistant high humidity inorganic coating of embodiment 1 to 8 is found out by table 2 and table 3
Meet the requirements.In resistance to sulfuric acid project, inorganic resin preferred sequence is followed successively by fluorine carbon>Acrylic acid>Phenylpropyl alcohol, filler preferred sequence according to
Secondary is barium sulfate>Calcium silicates>Calcium carbonate.
The burst size of methanal that the aqueous high-temperature-resistant high humidity inorganic coating of embodiment 1 to 8 is obtained is lower than general water paint,
Burst size of methanal is lower or even ND (Not detected write a Chinese character in simplified form, and are translated as not detecting).
The formula system combined in the selection of inorganic resin using fluorine carbon, inorganic Ludox and inorganic silicic acid potassium three, its
Chemical-resistance is more outstanding.
The technical performance testing result of water-based inorganic high-temperature resistant high humidity inorganic coating product in the embodiment 1 to 4 of table 2:
The technical performance testing result of water-based inorganic high-temperature resistant high humidity inorganic coating product in the embodiment 5 to 8 of table 3
By selecting the pigment of other colors, the aqueous inorganic high-temp resisting high-humidity resisting inorganic coating of different colours is prepared,
Belong to protection scope of the present invention, just do not list one by one here.
Above-mentioned aqueous high-temperature-resistant high humidity inorganic coating can be used in engineering inner-outer wall field, on engineering interior wall base material in spraying
Aqueous high-temperature-resistant high humidity inorganic coating is stated to replace the priming paint and finish paint that spray successively in the prior art, and performance is more excellent.
Aqueous high-temperature-resistant high humidity inorganic coating realizes that coating for internal and external wall bottom, face are general, repeats spraying or brushes, grinability and fillibility
Good, richness can adjust.Aqueous high-temperature-resistant high humidity inorganic coating is used for fresh cement, aging cement wall surface can directly construct and
It is significantly larger than the weatherability of organic exterior wall.
More than, only presently preferred embodiments of the present invention, it is not any to the present invention in form and substantial limitation, should
Point out, for those skilled in the art, on the premise of the inventive method is not departed from, can also make some
Improve and supplement, these improvement and supplement also should be regarded as protection scope of the present invention.All those skilled in the art, not
Depart from the spirit and scope of the present invention in the case of, when a little change made using disclosed above technology contents,
Modification and the equivalent variations developed, it is the equivalent embodiment of the present invention;Meanwhile all substantial technologicals according to the present invention are to above-mentioned
The variation, modification and evolution for any equivalent variations that embodiment is made, in the range of still falling within technical scheme.
Claims (10)
- A kind of 1. aqueous high-temperature-resistant high humidity inorganic coating, it is characterised in that:Including following raw material components and percentage by weight:
- 2. aqueous high-temperature-resistant high humidity inorganic coating as claimed in claim 1, it is characterised in that:The cellulose is that ethoxy is fine Dimension element or ethylhydroxyethylcellulose.
- 3. aqueous high-temperature-resistant high humidity inorganic coating as claimed in claim 1, it is characterised in that:Mole of the inorganic silicic acid potassium Proportion is more than 6.
- 4. aqueous high-temperature-resistant high humidity inorganic coating as claimed in claim 1, it is characterised in that:The particle diameter of the inorganic Ludox Less than 100nm, SiO in the inorganic Ludox2Content is more than 30%.
- 5. aqueous high-temperature-resistant high humidity inorganic coating as claimed in claim 1, it is characterised in that:The solid content of the fluorine carbon emulsion For 40-50%, Oil repellent is 10-14% in the fluorine carbon emulsion.
- 6. aqueous high-temperature-resistant high humidity inorganic coating as claimed in claim 1, it is characterised in that:The filler include barium sulfate, Any one or more in calcium carbonate, calcium silicates, mica powder and talcum powder.
- 7. aqueous high-temperature-resistant high humidity inorganic coating as claimed in claim 1, it is characterised in that:The aqueous wetting agent, which is selected from, to be had Any one in machine Si modification wetting agent and acrylic acid modified wetting agent or two kinds;And/or the one kind of the water-based thickener in association type polyurethanes thickener and hydroxyethylcellulose thickener Or two kinds;And/or the aqueous dispersion is ammonium polyacrylate dipersant.
- 8. aqueous high-temperature-resistant high humidity inorganic coating as claimed in claim 1, it is characterised in that:The aqueous defoamer, which is selected from, to be had Machine silicon, mineral oil or polyethers are modified any one in defoamer.
- 9. aqueous high-temperature-resistant high humidity inorganic coating as claimed in claim 1, it is characterised in that:The pigment be selected from titanium dioxide, Any one of iron oxide red, iron oxide yellow and iron oxide black.
- 10. a kind of method of the aqueous high-temperature-resistant high humidity inorganic coating prepared as described in claim 1 to 9 is any, its feature exist In:Comprise the following steps:1) water is put into mixer in advance, then adds the cellulose, the aqueous dispersion and the water-based defoaming Agent, low speed are uniformly dispersed;2) the water-based cosolvent and the aqueous wetting agent are added, is uniformly dispersed at a high speed;3) filler and the pigment are added, is uniformly dispersed at a high speed, is filtered, obtains slurry mix semi-finished product;4) the inorganic silicic acid potassium, the inorganic Ludox and the fluorine carbon emulsion at low speeds, are added while stirring, then The film forming accelerating is slowly added to, the water-based thickener is then added, stirs, it is inorganic to obtain aqueous high-temperature-resistant high humidity Coating.