CN109554006A - A kind of preparation method with A grades of fire-proof function interior wall inorganic environment-friendly coating - Google Patents
A kind of preparation method with A grades of fire-proof function interior wall inorganic environment-friendly coating Download PDFInfo
- Publication number
- CN109554006A CN109554006A CN201811360064.7A CN201811360064A CN109554006A CN 109554006 A CN109554006 A CN 109554006A CN 201811360064 A CN201811360064 A CN 201811360064A CN 109554006 A CN109554006 A CN 109554006A
- Authority
- CN
- China
- Prior art keywords
- fire
- grades
- interior wall
- solution
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods with A grades of fire-proof function interior wall inorganic environment-friendly coating.For the present invention mainly with inorganic silicic acid lithium, silica solution is main film forming matter, titanium dioxide, talcum powder, the heat proof materials such as kaolin are as pigments and fillers, and magnesium hydroxide is as fire retardant, with dispersing agent, defoaming agent, wetting agent, thickener etc. collectively constitute, the coating category ordor removing environment-friendly type coating, Diamond Search content, it is water-fast, mildew resistant moistureproof performance is good, have the inorganic interior wall functional coating of A grades of fire-protection ratings.
Description
Technical field
The present invention relates to interior wall fireproofing inorganic environmental protection coating material preparation methods.
Background technique
With the development of social economy and being constantly progressive for scientific level, people increasingly focus on indoor environmental quality, are good for
Kang Huanbao, the inorganic coating of fire safety are just gradually approved and are used by market and client.
Interior decoration traditional at present uses emulsion paint substantially, and environmental protection and performance can satisfy daily required.But it is some to want
Higher client's household or such as market, hotel public place are asked, may require that in addition to product quality and environmental protection, it is also contemplated that one
Critically important fire safety factor.Selection has the environmental protection coating material of fire-proof function
Product of the present invention is used using inorganic material as main film forming matter, is provided by using inorganic silicic acid lithium solution preferable resistance to
It cleans, outside water resistance, it is often more important that excellent fire protecting performance is provided, while selecting the pigments and fillers with certain fire resistance,
Using modified magnesium hydroxide as fire retardant, and reduce the smog generated in burning.And it is inorganic to add a small amount of elastic emulsion improvement
The risk of the firmly possible cracking phenomena of coating paint film.Addition stabilizer mainly improves the stability of modified magnesium hydroxide and system.Body
It is the addition of organic solvent-free, the almost nil interior wall inorganic coating of VOC content.
Summary of the invention
1, the present invention selects the environment protection elastic lotion of low film formation temperature, can not have to addition coalescing agent.
2, after elastic emulsion is added, addition potassium methyl silicate is adjusted the system after lotion is added and is in alkaline shape
State, prevention lotion are reacted with subsequent alkaline silicate potassium solution and silica solution, it is ensured that the stability under storing does not occur obvious
Rear thickening behavior.
3, before adding silica solution and lithium metasilicate solution, it is necessary to stirring first be added to stabilizer and add after five minutes.
4, silicon sol solution is added in the present invention, can preferably improves the storage stability of finished product paint.
5, the thickener that adds selects the alkali soluble of hydrophobically modified to rise thickener in the present invention.
Specific embodiment:
More detailed elaboration is carried out to the present invention below, in order to be understood by industry field technical staff, thus to the present invention
Protection scope be bound.
Embodiment one,
It is as follows for the preparation ratio of each section in the present invention:
Deionized water 27%
Dispersing agent 0.4%
Wetting agent 0.3%
Hydroxyethylmethylcellulose .0.3%
Defoaming agent 0.4%
Titanium dioxide 15%
Kaolin 12%
Talcum powder 8%
Modified magnesium hydroxide 3%
Ordor removing lotion 3%
Stabilizer 0.2%
Methane-siliconic acid potassium solution 0.1%
Silica solution 5%
Lithium metasilicate solution 25%
Defoaming agent 0.4%
Thickener 0.2%
Production explanation: 1, deionized water, dispersing agent, wetting agent low speed 300-500 are weighed and turns stirring 3 minutes in advance, adds hydroxyl second
Defoaming agent is added in ylmethyl cellulose, stirring after five minutes.2, turn that titanium dioxide, kaolin, talcum is added in middling speed 800-1000
Powder and modified magnesium hydroxide, high speed dispersion 30-40 minutes.3, lotion is added, is in alkali with methane-siliconic acid potassium solution regulation system
Character state.4, lithium metasilicate solution, defoaming agent, thickener are added.5, the thickener added is slowly added to after need to being diluted with water.
Embodiment two,
It is as follows for the preparation ratio of each section in the present invention:
Deionized water 17%
Dispersing agent 0.8%
Wetting agent 0.1%
Hydroxyethylmethylcellulose 0.1%
Defoaming agent 0.15%
Titanium dioxide 20%
Kaolin 5%
Talcum powder 4%
Modified magnesium hydroxide 8%
Ordor removing lotion 8%
Stabilizer 0.8%
Methane-siliconic acid potassium solution 0.4%
Silica solution 15%
Lithium metasilicate solution 20%
Defoaming agent 0.1%
Thickener 1%
Production explanation: 1, deionized water, dispersing agent, wetting agent low speed 300-500 are weighed and turns stirring 3 minutes in advance, adds hydroxyl second
Defoaming agent is added in ylmethyl cellulose, stirring after five minutes.2, turn that titanium dioxide, kaolin, talcum is added in middling speed 800-1000
Powder and modified magnesium hydroxide, high speed dispersion 30-40 minutes.3, lotion is added, is in alkali with methane-siliconic acid potassium solution regulation system
Character state.4, lithium metasilicate solution, defoaming agent, thickener are added.5, the thickener added is slowly added to after need to being diluted with water.
Embodiment three,
It is as follows for the preparation ratio of each section in the present invention:
Deionized water 18%
Dispersing agent 0.6%
Wetting agent 0.2%
Hydroxyethylmethylcellulose 0.3%
Defoaming agent 0.3%
Titanium dioxide 22%
Kaolin 6%
Talcum powder 5%
Modified magnesium hydroxide 4%
Ordor removing lotion 5%
Stabilizer 0.4%
Methane-siliconic acid potassium solution 0.3%
Silica solution 7%
Lithium metasilicate solution 30%
Defoaming agent 0.2%
Thickener 0.7%
Production explanation: 1, deionized water, dispersing agent, wetting agent low speed 300-500 are weighed and turns stirring 3 minutes in advance, adds hydroxyl second
Defoaming agent is added in ylmethyl cellulose, stirring after five minutes.2, turn that titanium dioxide, kaolin, talcum is added in middling speed 800-1000
Powder and modified magnesium hydroxide, high speed dispersion 30-40 minutes.3, lotion is added, is in alkali with methane-siliconic acid potassium solution regulation system
Character state.4, lithium metasilicate solution, defoaming agent, thickener are added.5, the thickener added is slowly added to after need to being diluted with water.
The present invention is not limited to the above embodiments, can be implemented described in the content of present invention and has the good result.
Claims (5)
1. a kind of preparation method with A grades of fire-proof function interior wall inorganic environment-friendly coating
Deionized water 17-27%
Dispersing agent 0.4-0.8%
Wetting agent 0.1-0.3%
Hydroxyethylmethylcellulose 0.1-0.3%
Defoaming agent 0.15-0.4%
Titanium dioxide 15-22%
Kaolin 5-12%
Talcum powder 4-8%
Modified magnesium hydroxide 3-8%
Elastic emulsion 3-8%
Stabilizer 0.2-0.8%
Methane-siliconic acid potassium solution 0.1-0.4%
Silica solution 5-15%
Lithium metasilicate solution 20-30%
Defoaming agent 0.1-0.4%
Thickener 0.2-1%.
2. being free of APEO according to the method described in claim 1, the wetting agent has to comply with environmental requirement.
3. according to the method described in claim 1, the silica sol modulus is greater than 2.5;Lithium metasilicate solution production modulus is greater than
3.0。
4. according to the method described in claim 1, must assure that slurry is in alkaline state after addition methane-siliconic acid potassium solution.
5. according to the method described in claim 1, modified magnesium hydroxide need to be with partial size less than 40 microns.