CN103881446A - Quick-drying type furniture varnish - Google Patents
Quick-drying type furniture varnish Download PDFInfo
- Publication number
- CN103881446A CN103881446A CN201310554893.XA CN201310554893A CN103881446A CN 103881446 A CN103881446 A CN 103881446A CN 201310554893 A CN201310554893 A CN 201310554893A CN 103881446 A CN103881446 A CN 103881446A
- Authority
- CN
- China
- Prior art keywords
- parts
- quick
- type furniture
- varnish
- furniture varnish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to quick-drying type furniture varnish. The quick-drying type furniture varnish comprises the following components in parts by weight: 17-22 parts of basic alkyd resin, 9-14 parts of polycarbonate resin, 17-22 parts of polyphenylene ether resin, 12-16 parts of polysulfone resin, 2-8 parts of styrene, 1-5 parts of an initiator, 20-40 parts of varnish naphtha, 15-30 parts of butanol, 7-12 parts of methyl ethyl ketone, 6-13 parts of a thinner, 2-7 parts of calcium plumbate and 1-3 parts of basic lead silico-chromate. The quick-drying type furniture varnish provided by the invention is easily available in raw materials and low in cost, has the advantages of no toxicity, no pollution, environmental protection and the like, and has hardness, water resistance and gasoline resistance. As the basic alkyd resin is added into the quick-drying type furniture varnish, the drying speed is high when the quick-drying type furniture varnish is used for coating of home furnishing.
Description
Technical field
The present invention relates to a kind of varnish, particularly a kind of quick-dry type furniture varnish.
Background technology
Varnish (English name: varnish) is not containing the transparent of pigment or with light flaxen coating, good luster, and film forming is fast, and purposes is wide.Main component is resin and solvent or resin, oil and solvent.Be applied to after body surface, form the film with protection, decoration and property, the dry rear smooth film that forms, shows the original decorative pattern of object plane.
Existing varnish function singleness, the making raw material that varnish is general is not easy to obtain, and raw material production cost is high, and the dry speed of general varnish is slow, can not meet people's demand.
Summary of the invention
The object of this invention is to provide the quick-dry type furniture varnish that a kind of result of use is good.
For achieving the above object, the present invention is achieved by the following technical solutions: a kind of quick-dry type furniture varnish, the parts by weight of its each component are: 17～22 parts of basic alkyds, 9～14 parts of polycarbonate resins, 17～22 parts of polyphenylene oxide resins, 12～16 parts of polysulfone resins, 2～8 parts of vinylbenzene, 1～5 part of initiator, 20～40 parts of varnish makers' and painters' naphtha, 15～30 parts, butanols, 7～12 parts of methylethylketones, 6～13 parts of solvent or diluents, 2～7 parts of calcium plumbites, 1～3 part of basic lead chromate silicate.
Further, described basic alkyd is during take tung oil as conjugated double bond source, and the content of tung oil is advisable with 12～17%, during take cis-butenedioic anhydride as conjugated double bond source, the content of tung oil is advisable with 1～2%, and its oil content is 50～65% to be advisable, gelation constant is 1.02～1.07, and molecular weight is 7000～10000.
Further, described initiator is ammonium persulphate or Potassium Persulphate.
Further, described solvent or diluent is selected polyurethane paint solvent, or the mixture that mixes according to 1:1 of pimelinketone, butanone.
The invention has the beneficial effects as follows: the invention provides a kind of quick-dry type furniture varnish, raw material is easy to get, with low cost, there is the advantages such as nontoxic, pollution-free, environmental protection, and it also has hardness, water tolerance, petrol-resistance energy, owing to wherein adding basic alkyd, for the application of household, rate of drying is fast.
Embodiment
For understanding better the present invention; below by three embodiment, the present invention is done to further concrete elaboration; but unintelligible is limitation of the invention; the foregoing invention content of some nonessential improvement and adjustment do according to to(for) those skilled in the art, be also considered as dropping in protection scope of the present invention.
Embodiment 1
A kind of quick-dry type furniture varnish of the present embodiment, the parts by weight of its each component are: 21 parts of basic alkyds, 10 parts of polycarbonate resins, 21 parts of polyphenylene oxide resins, 15 parts of polysulfone resins, 5 parts of vinylbenzene, 3 parts of initiators, 35 parts of varnish makers' and painters' naphtha, 23 parts, butanols, 11 parts of methylethylketones, 9 parts of solvent or diluents, 6 parts of calcium plumbites, 2 parts of basic lead chromate silicates.
Described basic alkyd is during take tung oil as conjugated double bond source, and the content of tung oil is advisable with 12～17%, during take cis-butenedioic anhydride as conjugated double bond source, the content of tung oil is advisable with 1～2%, its oil content is 50～65% to be advisable, and gelation constant is 1.02～1.07, and molecular weight is 7000～10000.
Described initiator is ammonium persulphate or Potassium Persulphate.
Described solvent or diluent is selected polyurethane paint solvent, or the mixture that mixes according to 1:1 of pimelinketone, butanone.
Embodiment 2
A kind of quick-dry type furniture varnish of the present embodiment, the parts by weight of its each component are: 17 parts of basic alkyds, 9 parts of polycarbonate resins, 17 parts of polyphenylene oxide resins, 12 parts of polysulfone resins, 2 parts of vinylbenzene, 1 part of initiator, 20 parts of varnish makers' and painters' naphtha, 15 parts, butanols, 7 parts of methylethylketones, 6 parts of solvent or diluents, 2 parts of calcium plumbites, 1 part of basic lead chromate silicate.
Described basic alkyd is during take tung oil as conjugated double bond source, and the content of tung oil is advisable with 12～17%, during take cis-butenedioic anhydride as conjugated double bond source, the content of tung oil is advisable with 1～2%, its oil content is 50～65% to be advisable, and gelation constant is 1.02～1.07, and molecular weight is 7000～10000.
Described initiator is ammonium persulphate or Potassium Persulphate.
Described solvent or diluent is selected polyurethane paint solvent, or the mixture that mixes according to 1:1 of pimelinketone, butanone.
Embodiment 3
A kind of quick-dry type furniture varnish of the present embodiment, the parts by weight of its each component are: 22 parts of basic alkyds, 14 parts of polycarbonate resins, 22 parts of polyphenylene oxide resins, 16 parts of polysulfone resins, 8 parts of vinylbenzene, 5 parts of initiators, 40 parts of varnish makers' and painters' naphtha, 30 parts, butanols, 12 parts of methylethylketones, 13 parts of solvent or diluents, 7 parts of calcium plumbites, 3 parts of basic lead chromate silicates.
Described basic alkyd is during take tung oil as conjugated double bond source, and the content of tung oil is advisable with 12～17%, during take cis-butenedioic anhydride as conjugated double bond source, the content of tung oil is advisable with 1～2%, its oil content is 50～65% to be advisable, and gelation constant is 1.02～1.07, and molecular weight is 7000～10000.
Described initiator is ammonium persulphate or Potassium Persulphate.
Described solvent or diluent is selected polyurethane paint solvent, or the mixture that mixes according to 1:1 of pimelinketone, butanone.
Claims (4)
1. a quick-dry type furniture varnish, it is characterized in that, the parts by weight of its each component are: 17～22 parts of basic alkyds, 9～14 parts of polycarbonate resins, 17～22 parts of polyphenylene oxide resins, 12～16 parts of polysulfone resins, 2～8 parts of vinylbenzene, 1～5 part of initiator, 20～40 parts of varnish makers' and painters' naphtha, 15～30 parts, butanols, 7～12 parts of methylethylketones, 6～13 parts of solvent or diluents, 2～7 parts of calcium plumbites, 1～3 part of basic lead chromate silicate.
2. a kind of quick-dry type furniture varnish according to claim 1, it is characterized in that, described basic alkyd is during take tung oil as conjugated double bond source, the content of tung oil is advisable with 12～17%, during take cis-butenedioic anhydride as conjugated double bond source, the content of tung oil is advisable with 1～2%, and its oil content is 50～65% to be advisable, gelation constant is 1.02～1.07, and molecular weight is 7000～10000.
3. a kind of quick-dry type furniture varnish according to claim 1, is characterized in that, described initiator is ammonium persulphate or Potassium Persulphate.
4. a kind of quick-dry type furniture varnish according to claim 1, is characterized in that, described solvent or diluent is selected polyurethane paint solvent, or the mixture that mixes according to 1:1 of pimelinketone, butanone.