CN106752445A - A kind of interiro wall latex paint and preparation method thereof - Google Patents
A kind of interiro wall latex paint and preparation method thereof Download PDFInfo
- Publication number
- CN106752445A CN106752445A CN201611152481.3A CN201611152481A CN106752445A CN 106752445 A CN106752445 A CN 106752445A CN 201611152481 A CN201611152481 A CN 201611152481A CN 106752445 A CN106752445 A CN 106752445A
- Authority
- CN
- China
- Prior art keywords
- latex paint
- wall latex
- interiro wall
- sagging
- aluminium powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of interiro wall latex paint and preparation method thereof, the interiro wall latex paint is made up of following raw material：Fluorocarbon resin, sagging inhibitor, anti-sagging agent, levelling agent, cellulose, dibutyl tin dilaurate, butyl acetate, dimethylbenzene, aluminium powder intermixture and flatting silica.The preparation method of the interiro wall latex paint is including getting the raw materials ready, pre-processing, premix is let down.The interiro wall latex paint that the present invention is obtained, its raw material is arranged in pairs or groups by selected various Material claddings, and component and its weight proportion are determined by multinomial experiment, and VOC content is that 0, harmful substance contents are low, health environment-friendly；Superfine aluminium power is with the addition of in the interiro wall latex paint formula that the present invention is provided, film forming back reflection light is gorgeous in riotous profusion；The interiro wall latex paint resistance to soiling that the present invention is obtained is good, easily clean, gloss is high, sense of touch is fine and smooth, strong covering power；The preparation method of the interiro wall latex paint that the present invention is provided is simple to operate, prepare convenient, low for equipment requirements, low cost, it is adaptable to industrialization large-scale production.
Description
Technical field
The invention belongs to building coating field, and in particular to a kind of interiro wall latex paint and preparation method thereof.
Background technology
With enriching constantly for people's material life, to residential location, the finishing requirement of working environment is also continuous for people
Improve, meanwhile, the also also more and more higher of the requirement to emulsion paint.Emulsion paint is being commonly called as latex paint, is born in twentieth century seven
Next period in the ten's, is the major class synthetic resin emulsion coating with acrylate copolymer emulsion as representative.Emulsion paint is moisture
Property coating is dissipated, it is that, with synthetic resin emulsion as base-material, filler is by the painting that adds various auxiliary agents to refine after grinding distribution
Material.Emulsion paint possesses many merits different from traditional wall covering, is such as easy to brush, dries that rapid, paint film is water-fast, anti-scratch
Washing property is good etc..In China, people are traditionally base-material synthetic resin emulsion, with water as decentralized medium, add pigment, filler
（Also known as extender pigment）And auxiliary agent, through the coating that certain technical process is made, it is called emulsion paint, also it is latex paint.
Interiro wall latex paint, with high molecular synthetic resin as main film forming substance, it is necessary to which it is diluent to use organic solvent, should
Coating is made of certain pigment, filler and the blended grinding of auxiliary agent, is a kind of volatile paint, and price is than water-soluble interior wall
Emulsion paint and water soluble paint will height.Interiro wall latex paint is one of indoor wall, ceiling primary decoration material, and feature is decoration effect
Really good, easy construction, environmental pollution is small, low cost, there is good weatherability and stain resistance, have preferable thickness, gloss,
Water resistance, alkali resistance, using extremely wide.But in the prior art, there is certain, such as color and luster list in interiro wall latex paint
One, tinting strength, tinting power is poor；Resistance to soiling is poor, is difficult to clean；Noxious material is more, the problems such as not environmentally friendly enough, there is larger room for improvement.
The content of the invention
Shortcoming it is an object of the invention to overcome prior art, there is provided a kind of interiro wall latex paint, the emulsion paint has ring
Protect, color is high, resistance to soiling is good, easily clean, strong covering power the advantages of.
It is another object of the present invention to provide the preparation method of this kind of interiro wall latex paint, the method is simple to operate, system
Standby convenient, low cost is suitable to industrialization large-scale production.
The present invention is achieved through the following technical solutions：A kind of interiro wall latex paint, it is prepared by the raw material of following weight portion
Form：
Fluorocarbon resin：30~50；Sagging inhibitor：8~20；Anti-sagging agent：1~3；
Levelling agent：0.1~0.3；Cellulose：18~30；Dibutyl tin dilaurate：0.1~0.3；
Butyl acetate：0.25~0.42；Dimethylbenzene：2~5；Aluminium powder intermixture：5~15；
Flatting silica：0.003~0.01.
Preferably, it is prepared from by the raw material of following weight portion：
Dispersant： 48.76；Sagging inhibitor： 13.8；Anti-sagging agent： 1.84；
Levelling agent： 0.184；Cellulose： 23.92；Catalyst： 0.184；
Butyl acetate： 0.362；Dimethylbenzene： 2.994；Aluminium powder intermixture：8；
Flatting silica： 0.006.
Further, the fluorocarbon resin is WF-Q212 fluorocarbon resins.
Further, the sagging inhibitor is DISPARLON 4200-10.
Further, the anti-sagging agent is DISPARLON 6900-20X.
Further, the levelling agent is BYK-323.
Further, the cellulose is any one in cellulose acetate butyrate ester or CAB 381-0.5.
Further, the aluminium powder intermixture is the mixing of aluminium powder and high boiling aromatic hydrocarbons, and aluminium powder and high boiling aromatic hydrocarbons
Mass ratio is 1.5~2.5:1.
Further, the flatting silica is the mixing of amorphous silica and microcrystalline wax.
A kind of preparation method of interiro wall latex paint, it is comprised the following steps：
S1. get the raw materials ready：Weigh each raw material by above-mentioned formula rate, and butyl acetate be divided into two parts of A, B, and volume ratio be 10~
15:1, it is standby；
S2. pre-process：It is 50% that A parts of butyl acetate is diluted into mass percent concentration, adds fluorocarbon resin, obtains pretreatment
Fluorocarbon resin；It is 95% that B parts of butyl acetate is diluted into mass percent concentration, adds dibutyl tin dilaurate, obtains pretreatment
The fourth tin of dilaurate two；
S3. premix：It is made up of following sub-step：
S31. the fluorocarbon resin of pretreatment is first added in dispersion machine, sagging inhibitor is added under the stirring condition of 500~550rpm
And anti-sagging agent, the rotating speed of dispersion machine is adjusted to 900~950rpm, it is stirred well to content fineness≤15 μm；
S32. the rotating speed of adjustment dispersion machine is 500~550rpm, sequentially adds levelling agent, cellulose, the tin dilaurate of pretreatment
Two fourth tin and dimethylbenzene, then improve dispersing speed to 900~950rpm, are sufficiently stirred for 10~20min；
S4. it is let down：Adjustment dispersing speed adds aluminium powder intermixture and flatting silica to 500~550rpm, it is sufficiently stirred for 5~
10min, keeps rotating speed constant, and viscosity and proportion are adjusted with water, lifts three times up and down, stirs 10~15min, that is, obtain interior wall breast
Shellac varnish.
The present invention has advantages below：
1. the interiro wall latex paint that the present invention is obtained, its raw material is arranged in pairs or groups by selected various Material claddings, is determined by multinomial experiment
Component and its weight proportion, VOC content are that 0, soluble chromium is less than 60mg/kg, and dissoluble lead is less than 90 mg/kg, soluble cadmium
Less than 75 mg/kg, soluble mercury is less than 60mg/kg, health environment-friendly；
2. superfine aluminium power with the addition of in the interiro wall latex paint formula that the present invention is provided, and film forming back reflection light is gorgeous in riotous profusion, and can
Allotment different colours (such as local tyrant's gold, rose gold), meets the demand of different crowd according to demand；
3. the present invention is obtained interiro wall latex paint Solid content ＞ 50%, have excellent weather resistance：Abrasion resistance 10000 times, and resistance to soiling
It is good, easily clean；
4. the interiro wall latex paint gloss that the present invention is obtained is high, there is fabulous decorative effect；Fineness≤15 μm, sense of touch is fine and smooth；Contrast
Rate 95%, strong covering power can cover wall defect, and whole structure flat smooth is the ideal material of indoor wall decoration；
5. the preparation method of the interiro wall latex paint that the present invention is provided is simple to operate, prepare convenient, low for equipment requirements, low cost,
Mass produced suitable for industrialization.
Specific embodiment
With reference to embodiment, the present invention will be further described, and protection scope of the present invention is not limited to following institute
State：
Embodiment 1：A kind of interiro wall latex paint, it is prepared from by the raw material of following weight portion：
Fluorocarbon resin：30；Sagging inhibitor：8；Anti-sagging agent： 1；
Levelling agent：0.1；Cellulose： 18；Dibutyl tin dilaurate： 0.1；
Butyl acetate：0.25；Dimethylbenzene： 2；Aluminium powder intermixture： 5；
Flatting silica：0.003.
Wherein, the fluorocarbon resin is WF-Q212 fluorocarbon resins；The sagging inhibitor is DISPARLON 4200-10；Institute
Anti-sagging agent is stated for DISPARLON 6900-20X；The levelling agent is BYK-323；The cellulose is cellulose acetate-butyrate
Ester；The aluminium powder intermixture is the mixing of aluminium powder and high boiling aromatic hydrocarbons, and aluminium powder and the mass ratio of high boiling aromatic hydrocarbons are 1.5:1；
The flatting silica is the mixing of amorphous silica and microcrystalline wax.
The preparation method of above-mentioned interiro wall latex paint, it is comprised the following steps：
S1. get the raw materials ready：Each raw material is weighed by above-mentioned formula rate, and butyl acetate is divided into two parts of A, B, and volume ratio is 10:1,
It is standby；
S2. pre-process：It is 50% that A parts of butyl acetate is diluted into mass percent concentration, adds fluorocarbon resin, obtains pretreatment
Fluorocarbon resin；It is 95% that B parts of butyl acetate is diluted into mass percent concentration, adds dibutyl tin dilaurate, obtains pretreatment
The fourth tin of dilaurate two；
S3. premix：It is made up of following sub-step：
S31. the fluorocarbon resin of pretreatment is first added in dispersion machine, sagging inhibitor and anti-stream is added under the stirring condition of 500rpm
Agent is hung, the rotating speed of dispersion machine is adjusted to 900rpm, content fineness≤15 μm are stirred well to；
S32. the rotating speed of adjustment dispersion machine is 500rpm, sequentially adds levelling agent, cellulose, the dibutyl tin dilaurate of pretreatment
And dimethylbenzene, dispersing speed is then improved to 900rpm, it is sufficiently stirred for 10~20min；
S4. it is let down：Adjustment dispersing speed adds aluminium powder intermixture and flatting silica to 500rpm, is sufficiently stirred for 50min, keeps
Rotating speed is constant, and viscosity and proportion are adjusted with water, lifts three times up and down, stirs 10min, that is, obtain interiro wall latex paint.
Embodiment 2：A kind of interiro wall latex paint, it is prepared from by the raw material of following weight portion：
Fluorocarbon resin： 50；Sagging inhibitor： 20；Anti-sagging agent： 3；
Levelling agent： 0.3；Cellulose： 30；Dibutyl tin dilaurate： 0.3；
Butyl acetate： 0.42；Dimethylbenzene： 5；Aluminium powder intermixture： 15；
Flatting silica：0.01.
Wherein, the fluorocarbon resin is WF-Q212 fluorocarbon resins；The sagging inhibitor is DISPARLON 4200-10；Institute
Anti-sagging agent is stated for DISPARLON 6900-20X；The levelling agent is BYK-323；The cellulose is CAB 381-0.5；Institute
It is aluminium powder and the mixing of high boiling aromatic hydrocarbons to state aluminium powder intermixture, and aluminium powder and the mass ratio of high boiling aromatic hydrocarbons are 1.5~2.5:1；
The flatting silica is the mixing of amorphous silica and microcrystalline wax.
The preparation method of above-mentioned interiro wall latex paint, it is comprised the following steps：
S1. get the raw materials ready：Each raw material is weighed by above-mentioned formula rate, and butyl acetate is divided into two parts of A, B, and volume ratio is 15:1,
It is standby；
S2. pre-process：It is 50% that A parts of butyl acetate is diluted into mass percent concentration, adds fluorocarbon resin, obtains pretreatment
Fluorocarbon resin；It is 95% that B parts of butyl acetate is diluted into mass percent concentration, adds dibutyl tin dilaurate, obtains pretreatment
The fourth tin of dilaurate two；
S3. premix：It is made up of following sub-step：
S31. the fluorocarbon resin of pretreatment is first added in dispersion machine, sagging inhibitor and anti-stream is added under the stirring condition of 550rpm
Agent is hung, the rotating speed of dispersion machine is adjusted to 950rpm, content fineness≤15 μm are stirred well to；
S32. the rotating speed of adjustment dispersion machine is 550rpm, sequentially adds levelling agent, cellulose, the dibutyl tin dilaurate of pretreatment
And dimethylbenzene, dispersing speed is then improved to 950rpm, it is sufficiently stirred for 20min；
S4. it is let down：Adjustment dispersing speed adds aluminium powder intermixture and flatting silica to 550rpm, is sufficiently stirred for 10min, keeps
Rotating speed is constant, and viscosity and proportion are adjusted with water, lifts three times up and down, stirs 15min, that is, obtain interiro wall latex paint.
Embodiment 3：A kind of interiro wall latex paint, it is prepared from by the raw material of following weight portion：
Dispersant：48.76；Sagging inhibitor： 13.8；Anti-sagging agent： 1.84；
Levelling agent：0.184；Cellulose： 23.92；Catalyst： 0.184；
Butyl acetate：0.362；Dimethylbenzene： 2.994；Aluminium powder intermixture：8；
Flatting silica：0.006.
Wherein, the fluorocarbon resin is WF-Q212 fluorocarbon resins；The sagging inhibitor is DISPARLON 4200-10；Institute
Anti-sagging agent is stated for DISPARLON 6900-20X；The levelling agent is BYK-323；The cellulose is cellulose acetate-butyrate
Ester；The aluminium powder intermixture is the mixing of aluminium powder and high boiling aromatic hydrocarbons, and aluminium powder and the mass ratio of high boiling aromatic hydrocarbons are 1.8:1；
The flatting silica is the mixing of amorphous silica and microcrystalline wax.
The preparation method of above-mentioned interiro wall latex paint, it is comprised the following steps：
S1. get the raw materials ready：Each raw material is weighed by above-mentioned formula rate, and butyl acetate is divided into two parts of A, B, and volume ratio is 12:1,
It is standby；
S2. pre-process：It is 50% that A parts of butyl acetate is diluted into mass percent concentration, adds fluorocarbon resin, obtains pretreatment
Fluorocarbon resin；It is 95% that B parts of butyl acetate is diluted into mass percent concentration, adds dibutyl tin dilaurate, obtains pretreatment
The fourth tin of dilaurate two；
S3. premix：It is made up of following sub-step：
S31. the fluorocarbon resin of pretreatment is first added in dispersion machine, sagging inhibitor and anti-stream is added under the stirring condition of 520rpm
Agent is hung, the rotating speed of dispersion machine is adjusted to 910rpm, content fineness≤15 μm are stirred well to；
S32. the rotating speed of adjustment dispersion machine is 520rpm, sequentially adds levelling agent, cellulose, the dibutyl tin dilaurate of pretreatment
And dimethylbenzene, dispersing speed is then improved to 910rpm, it is sufficiently stirred for 13min；
S4. it is let down：Adjustment dispersing speed adds aluminium powder intermixture and flatting silica to 520rpm, is sufficiently stirred for 6min, keeps turning
Speed is constant, and viscosity and proportion are adjusted with water, lifts three times up and down, stirs 13min, that is, obtain interiro wall latex paint.
Embodiment 4：A kind of interiro wall latex paint, it is prepared from by the raw material of following weight portion：
Fluorocarbon resin：40；Sagging inhibitor：18；Anti-sagging agent： 2.5；
Levelling agent：0.25；Cellulose：25；Dibutyl tin dilaurate： 0.264；
Butyl acetate：0.41；Dimethylbenzene：4.52；Aluminium powder intermixture： 12；
Flatting silica：0.007.
Wherein, the fluorocarbon resin is WF-Q212 fluorocarbon resins；The sagging inhibitor is DISPARLON 4200-10；Institute
Anti-sagging agent is stated for DISPARLON 6900-20X；The levelling agent is BYK-323；The cellulose is CAB 381-0.5；Institute
It is aluminium powder and the mixing of high boiling aromatic hydrocarbons to state aluminium powder intermixture, and aluminium powder and the mass ratio of high boiling aromatic hydrocarbons are 2.2:1；It is described to disappear
Light powder is the mixing of amorphous silica and microcrystalline wax.
The preparation method of above-mentioned interiro wall latex paint, it is comprised the following steps：
S1. get the raw materials ready：Each raw material is weighed by above-mentioned formula rate, and butyl acetate is divided into two parts of A, B, and volume ratio is 14:1,
It is standby；
S2. pre-process：It is 50% that A parts of butyl acetate is diluted into mass percent concentration, adds fluorocarbon resin, obtains pretreatment
Fluorocarbon resin；It is 95% that B parts of butyl acetate is diluted into mass percent concentration, adds dibutyl tin dilaurate, obtains pretreatment
The fourth tin of dilaurate two；
S3. premix：It is made up of following sub-step：
S31. the fluorocarbon resin of pretreatment is first added in dispersion machine, sagging inhibitor and anti-stream is added under the stirring condition of 535rpm
Agent is hung, the rotating speed of dispersion machine is adjusted to 945rpm, content fineness≤15 μm are stirred well to；
S32. the rotating speed of adjustment dispersion machine is 535rpm, sequentially adds levelling agent, cellulose, the dibutyl tin dilaurate of pretreatment
And dimethylbenzene, dispersing speed is then improved to 945rpm, it is sufficiently stirred for 18min；
S4. it is let down：Adjustment dispersing speed adds aluminium powder intermixture and flatting silica to 535rpm, is sufficiently stirred for 8min, keeps turning
Speed is constant, and viscosity and proportion are adjusted with water, lifts three times up and down, stirs 14min, that is, obtain interiro wall latex paint.
Interiro wall latex paint obtained in above-described embodiment 1-4 is carried out into performance test, experimental result is as follows：Viscosity 105/KU,
It is easy to construction；Solid content ＞ 50%, have excellent weather resistance：Abrasion resistance 10000 times, and resistance to soiling is good, easily cleans；VOC content be 0,
Soluble chromium is less than 60mg/kg, and dissoluble lead is less than 90 mg/kg, and soluble cadmium is less than 75 mg/kg, and soluble mercury is less than
60mg/kg, health environment-friendly；Gloss/60 ° are 10 °, and fineness≤15 μm, sense of touch is fine and smooth, contrast ratio 95%；Strong covering power, can cover
Wall defect.Whole structure flat smooth, is the ideal material of indoor wall decoration.
Claims (10)
1. a kind of interiro wall latex paint, it is characterised in that it is prepared from by the raw material of following weight portion：
Fluorocarbon resin：30~50；Sagging inhibitor：8~20；Anti-sagging agent：1~3；
Levelling agent：0.1~0.3；Cellulose：18~30；Dibutyl tin dilaurate：0.1~0.3；
Butyl acetate：0.25~0.42；Dimethylbenzene：2~5；Aluminium powder intermixture：5~15；
Flatting silica：0.003~0.01.
2. a kind of interiro wall latex paint as claimed in claim 1, it is characterised in that it prepared by the raw material of following weight portion and
Into：
Dispersant： 48.76；Sagging inhibitor： 13.8；Anti-sagging agent： 1.84；
Levelling agent： 0.184；Cellulose： 23.92；Catalyst： 0.184；
Butyl acetate： 0.362；Dimethylbenzene： 2.994；Aluminium powder intermixture：8；
Flatting silica： 0.006.
3. a kind of interiro wall latex paint as claimed in claim 1 or 2, it is characterised in that the fluorocarbon resin is WF-Q212 fluorine carbon
Resin.
4. a kind of interiro wall latex paint as claimed in claim 1 or 2, it is characterised in that the sagging inhibitor is DISPARLON
4200-10。
5. a kind of interiro wall latex paint as claimed in claim 1 or 2, it is characterised in that the anti-sagging agent is DISPARLON
6900-20X。
6. a kind of interiro wall latex paint as claimed in claim 1 or 2, it is characterised in that the levelling agent is BYK-323.
7. a kind of interiro wall latex paint as claimed in claim 1 or 2, it is characterised in that the cellulose is cellulose acetate butyrate
Any one in plain ester or CAB 381-0.5.
8. a kind of interiro wall latex paint as claimed in claim 1 or 2, it is characterised in that the aluminium powder intermixture be aluminium powder with it is high
The mixing of boiling point aromatic hydrocarbons, and aluminium powder and the mass ratio of high boiling aromatic hydrocarbons are 1.5~2.5:1.
9. a kind of interiro wall latex paint as claimed in claim 1 or 2, it is characterised in that the flatting silica is amorphous silica
With the mixing of microcrystalline wax.
10. the preparation method of a kind of interiro wall latex paint as described in any claim in claim 1-9, it is characterised in that
It is comprised the following steps：
S1. get the raw materials ready：Weigh each raw material by above-mentioned formula rate, and butyl acetate be divided into two parts of A, B, and volume ratio be 10~
15:1, it is standby；
S2. pre-process：It is 50% that A parts of butyl acetate is diluted into mass percent concentration, adds fluorocarbon resin, obtains pretreatment
Fluorocarbon resin；It is 95% that B parts of butyl acetate is diluted into mass percent concentration, adds dibutyl tin dilaurate, obtains pretreatment
The fourth tin of dilaurate two；
S3. premix：It is made up of following sub-step：
S31. the fluorocarbon resin of pretreatment is first added in dispersion machine, sagging inhibitor is added under the stirring condition of 500~550rpm
And anti-sagging agent, the rotating speed of dispersion machine is adjusted to 900~950rpm, it is stirred well to content fineness≤15 μm；
S32. the rotating speed of adjustment dispersion machine is 500~550rpm, sequentially adds levelling agent, cellulose, the tin dilaurate of pretreatment
Two fourth tin and dimethylbenzene, then improve dispersing speed to 900~950rpm, are sufficiently stirred for 10~20min；
S4. it is let down：Adjustment dispersing speed adds aluminium powder intermixture and flatting silica to 500~550rpm, it is sufficiently stirred for 5~
10min, keeps rotating speed constant, and viscosity and proportion are adjusted with water, lifts three times up and down, stirs 10~15min, that is, obtain interior wall breast
Shellac varnish.