CN102660185A - Alkyd resin paint, preparation method and construction method - Google Patents
Alkyd resin paint, preparation method and construction method Download PDFInfo
- Publication number
- CN102660185A CN102660185A CN2012101198167A CN201210119816A CN102660185A CN 102660185 A CN102660185 A CN 102660185A CN 2012101198167 A CN2012101198167 A CN 2012101198167A CN 201210119816 A CN201210119816 A CN 201210119816A CN 102660185 A CN102660185 A CN 102660185A
- Authority
- CN
- China
- Prior art keywords
- alkyd varnish
- solvent
- alkyd resin
- synolac
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses alkyd resin paint which comprises, by mass, 250-300 parts of alkyd resin, 30-40 parts of wetting dispersant reagent, 300-500 parts of inert fillers and 30-50 parts of anti-settling agent. The alkyd resin paint has strong decorating effect and can be matched with different colors so that the texture with different colors of the alkyd resin paint can be produced according to the requirements and the alkyd resin paint endows different effects on office desks, conference tables, clothes cabinets, cupboards, doors and windows. In addition, after wood is filled first, the follow-up paint using amount and the construction time are reduced. The overall cost is effectively reduced.
Description
Technical field
The present invention relates to a kind of alkyd varnish and preparation method and constructional method.
Background technology
The present finishing of furniture such as some desks, conference table, wardrobe, cabinet, door and window is all hoped to save cost, beautifies furniture and is embodied the texture of timber itself again, and people's life is more got close to nature, and makes household warmth more.This invention gives wood furniture colorful, motley style, and has saved the consumption and the man-hour of paint.Saved resource greatly.Wiping the furniture of alkyd varnish of the present invention also give people pleasing feeling of freshness more.Furniture decoration on the market at present, people are remarkable to hanker after pure white, black or these single form or styles such as colourless, more hopes bright in luster, various informative.
Summary of the invention
The purpose of this invention is to provide a kind of alkyd varnish.
The technical scheme that the present invention taked is:
A kind of alkyd varnish comprises the raw material of following mass parts: the anti-settling agent of the wetting dispersing agent of the Synolac of 250-300 part, 30-40 part, the physique filler of 300-500 part, 30-50 part.
The solid content of described Synolac is 80-95%.
Described physique filler comprises 800-2000 purpose permanent white, lime carbonate, Magnesium Silicate q-agent, mica powder, zeyssatite.
Described anti-settling agent comprises organobentonite, polyamide wax pulp, aerosil.
A kind of preparation method of alkyd varnish may further comprise the steps: 1) Synolac is added dispersion tank, add wetting dispersing agent and solvent, be uniformly dispersed;
2) add anti-settling agent, solvent again, be uniformly dispersed, transfer viscosity to get final product with solvent oil at last.
Step 2) in solvent for use and the step 1) mass ratio of solvent for use be 0.5-1.5:1.
A kind of constructional method of alkyd varnish may further comprise the steps: Dicoration base material is carried out surface treatment, be coated with one deck alkyd varnish more on it.
Surface treatment to Dicoration base material comprises common treatment processs such as scrubbing, finishing, polishing.
The method of coating comprises conventional coating processes such as roller coat, spraying.
After alkyd varnish is applied to base material, also can further be coated with and plants priming paint or finish paint.
The invention has the beneficial effects as follows: the decorative effect of alkyd varnish of the present invention is strong, its adjustable different color, thus can make the texture of different color according to demand, thus give desk, conference table, wardrobe, cabinet, the different effect of door and window.
Embodiment
A kind of alkyd varnish is made up of the raw material of following mass parts: the anti-settling agent of the wetting dispersing agent of the Synolac of 250-300 part, 30-40 part, the physique filler of 300-500 part, 30-50 part, the solvent of 80-120 part, the solvent oil of 100-150 part, the coating toner of 0-50 part.
The solid content of described Synolac is 80-95%.
Described physique filler comprises 800-2000 purpose permanent white, lime carbonate, Magnesium Silicate q-agent, mica powder, zeyssatite, transparent powder.
Described anti-settling agent comprises organobentonite, polyamide wax pulp, aerosil.
A kind of preparation method of alkyd varnish may further comprise the steps:
1) Synolac is added dispersion tank, add wetting dispersing agent and solvent, be uniformly dispersed;
2) add anti-settling agent, solvent again, be uniformly dispersed, transfer viscosity to get final product with solvent oil at last.
Step 2) in solvent for use and the step 1) mass ratio of solvent for use be 0.5-1.5:1.
Described solvent comprises YLENE, pimelinketone.
Below in conjunction with specific embodiment the present invention is done further explanation:
Embodiment 1:
A kind of alkyd varnish, its prescription is formed like following table 1:
The preparation method of corresponding alkyd varnish is:
1) Synolac being taken by weighing input disperses to stir behind adding YLENE and the wetting dispersing agent in the cylinder;
2) speed with 600-800r/min adds organobentonite and aerosil while stirring; Add the back and disperse 5-10min with the stirring velocity of 1000-1200r/min;
3) talcum powder that takes by weighing, transparent powder, mica powder added under condition of stirring disperse in the cylinder, clean casing wall and disperse axle, disperse 20-25min with the stirring velocity of 1200-1500r/min with pimelinketone, to fineness be 60 microns;
4) transfer viscosity to get final product with the S-100 solvent oil at last.
Embodiment 2:
A kind of alkyd varnish, its prescription is formed like following table 2:
The preparation method of corresponding alkyd varnish is:
1) Synolac being taken by weighing input disperses to stir behind adding YLENE and the wetting dispersing agent in the cylinder;
2) speed with 600-800r/min adds organobentonite and polyamide wax pulp while stirring; Add the back and disperse 5-10min with the stirring velocity of 1000-1200r/min;
3) permanent white that takes by weighing, transparent powder, zeyssatite added under condition of stirring disperse in the cylinder, clean casing wall and disperse axle, disperse 20-25min with the stirring velocity of 1200-1500r/min with pimelinketone, to fineness be 60 microns;
4) transfer viscosity to get final product with the S-150 solvent oil at last.
Embodiment 3:
A kind of alkyd varnish, its prescription is formed like following table 3:
The preparation method of corresponding alkyd varnish is:
1) Synolac being taken by weighing input disperses to stir behind adding YLENE and the wetting dispersing agent in the cylinder;
2) speed with 600-800r/min adds organobentonite while stirring; Add the back and disperse 5-10min with the stirring velocity of 1000-1200r/min;
3) permanent white that takes by weighing, transparent powder, zeyssatite added under condition of stirring disperse in the cylinder, clean casing wall and disperse axle, disperse 20-25min with the stirring velocity of 1200-1500r/min with pimelinketone, to fineness be 60 microns;
4) transfer viscosity to get final product with the S-150 solvent oil at last.
Embodiment 4:
A kind of alkyd varnish, its prescription is formed like following table 4:
The preparation method of corresponding alkyd varnish is:
1) Synolac being taken by weighing input disperses to stir behind adding YLENE and the wetting dispersing agent in the cylinder;
2) speed with 600-800r/min adds aerosil while stirring; Add the back and disperse 5-10min with the stirring velocity of 1000-1200r/min;
3) permanent white that takes by weighing, transparent powder, zeyssatite added under condition of stirring disperse in the cylinder, clean casing wall and disperse axle, disperse 20-25min with the stirring velocity of 1200-1500r/min with pimelinketone, to fineness be 60 microns;
4) transfer viscosity to get final product with the S-200 solvent oil at last.
Like following table is the correlated performance of the alkyd varnish of embodiment 1-4 gained:
Claims (7)
1. an alkyd varnish is characterized in that: the raw material that comprises following mass parts: the anti-settling agent of the wetting dispersing agent of the Synolac of 250-300 part, 30-40 part, the physique filler of 300-500 part, 30-50 part.
2. a kind of alkyd varnish according to claim 1 is characterized in that: the solid content of described Synolac is 80-95%.
3. a kind of alkyd varnish according to claim 1 is characterized in that: described physique filler comprises 800-2000 purpose permanent white, lime carbonate, Magnesium Silicate q-agent, mica powder, zeyssatite.
4. a kind of alkyd varnish according to claim 1 is characterized in that: described anti-settling agent comprises organobentonite, polyamide wax pulp, aerosil.
5. the preparation method of the described a kind of alkyd varnish of claim 1 is characterized in that: may further comprise the steps:
1) Synolac is added dispersion tank, add wetting dispersing agent and solvent, be uniformly dispersed;
2) add anti-settling agent, solvent again, be uniformly dispersed, transfer viscosity to get final product with solvent oil at last.
6. the preparation method of a kind of alkyd varnish according to claim 5 is characterized in that: step 2) in solvent for use and the step 1) mass ratio of solvent for use be 0.5-1.5:1.
7. the constructional method of the described a kind of alkyd varnish of claim 1 is characterized in that: may further comprise the steps: Dicoration base material is carried out surface treatment, be coated with the described alkyd varnish of one deck claim 1 more on it.