CN105315860A - Water-based alkyd paint for door and preparing method thereof - Google Patents
Water-based alkyd paint for door and preparing method thereof Download PDFInfo
- Publication number
- CN105315860A CN105315860A CN201510837046.3A CN201510837046A CN105315860A CN 105315860 A CN105315860 A CN 105315860A CN 201510837046 A CN201510837046 A CN 201510837046A CN 105315860 A CN105315860 A CN 105315860A
- Authority
- CN
- China
- Prior art keywords
- parts
- synolac
- mill base
- alkyd paint
- door use
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Water-based alkyd paint for a door is prepared from 30-50 parts of alkyd resin, 15-20 parts of nitrocotton, 3-6 parts of benzoic acid, 2-4 parts of calcium naphthenate, 3-4 parts of lithopone, 5-8 parts of bentonite, 2-5 parts of dioctyl stearate, 50-70 parts of ethyl alcohol, 15-20 parts of ethyl acetate, 4-5 parts of butyl acetate, 10-15 parts of deionized water and 2-8 parts of isobutyl alcohol. A preparing method is simple in process, and the water-based alkyd paint is high in adhesive force and resistant to ageing.
Description
Technical field
The present invention relates to technical field of coatings, particularly a kind of door use alkyd paint and preparation method thereof.
Background technology
In current door processing industry, the technical recipe for the alkyd paint of door external coating is more complicated, and production difficulty is high, surface effect and sticking power poor.
For the problems referred to above, the invention provides a kind of door use alkyd paint and preparation method thereof, technique is simple, and product strong adhesion is ageing-resistant.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of door use alkyd paint and preparation method thereof.Effectively can solve existing door use alkyd paint technique more complicated, production difficulty is high, surface effect and the poor problem of sticking power.
A kind of door use alkyd paint, it is characterized in that, by weight, it is made up of following component:
Synolac 30-50 part, nitro-cotton 15-20 part, phenylformic acid 3-6 part, calcium naphthenate 2-4 part, zinc sulfide white 3-4 part, wilkinite 5-8 part, stearic acid dioctyl ester 2-5 part, ethanol 50-70 part, ethyl acetate 15-20 part, butylacetate 4-5 part, deionized water 10-15 part, isopropylcarbinol 2-8 part.
Further, described Synolac adopts one or several the arbitrary proportion mixture in 100A Synolac, 3355 Synolac.
Further, described door use alkyd paint also comprises color material 1-3 part.
Present invention also offers the preparation method of described door use alkyd paint:
1. take wilkinite and ethyl acetate by formula, at use stirrer moderate-speed mixer 15min after mixing, form native cream;
2. by formula take 50% of Synolac liquid measure, mix with the native cream 1. produced to step, and add by fill a prescription take 50% of deionized water liquid measure, then start stirrer, moderate-speed mixer 30min;
3. the mill base that 2. step produces is added shredder and start grinding, regulate mill base flow, control grinding temperature not higher than 60 DEG C, after fineness is up to standard, with by the residue Synolac taken of filling a prescription, the mill base in shredder is ejected;
4. mill base step 3. produced is introduced in paint mixing tank and is stirred, and then adds by other components taken of filling a prescription, moderate-speed mixer 30min;
5. mill base specification 80 mesh filter screen step 4. produced filters, packaging; Packaging temp is no more than 45 DEG C.
Beneficial effect of the present invention is, provides a kind of door use alkyd paint and preparation method thereof technique simple, product strong adhesion, ageing-resistant.
Embodiment
Be further described the specific embodiment of the present invention below in conjunction with embodiment, following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
Embodiment 1
The concrete technical scheme of the present invention is as follows:
A kind of door use alkyd paint, it is characterized in that, by weight, it is made up of following component:
100A Synolac 40 parts, nitro-cotton 17 parts, 4 parts, phenylformic acid, calcium naphthenate 2 parts, 3 parts, zinc sulfide white, wilkinite 7 parts, stearic acid dioctyl ester 3 parts, ethanol 55 parts, ethyl acetate 19 parts, butylacetate 5 parts, deionized water 13 parts, isopropylcarbinol 7 parts.
Present invention also offers the preparation method of described door use alkyd paint:
1. take wilkinite and ethyl acetate by formula, at use stirrer moderate-speed mixer 15min after mixing, form native cream;
2. by formula take 50% of 100A Synolac liquid measure, mix with the native cream 1. produced to step, and add by fill a prescription take 50% of deionized water liquid measure, then start stirrer, moderate-speed mixer 30min;
3. the mill base that 2. step produces is added shredder and start grinding, regulate mill base flow, control grinding temperature not higher than 60 DEG C, after fineness is up to standard, with by the residue Synolac taken of filling a prescription, the mill base in shredder is ejected;
4. mill base step 3. produced is introduced in paint mixing tank and is stirred, and then adds by other components taken of filling a prescription, moderate-speed mixer 30min;
5. mill base specification 80 mesh filter screen step 4. produced filters, packaging; Packaging temp is no more than 45 DEG C.
Embodiment 2
The concrete technical scheme of the present invention is as follows:
A kind of door use alkyd paint, it is characterized in that, by weight, it is made up of following component:
3355 Synolac 45 parts, nitro-cotton 16 parts, 5 parts, phenylformic acid, calcium naphthenate 3 parts, 3 parts, zinc sulfide white, wilkinite 6 parts, stearic acid dioctyl ester 3 parts, ethanol 53 parts, ethyl acetate 13 parts, butylacetate 4 parts, deionized water 10 parts, isopropylcarbinol 3 parts, 2 parts, color material.
Present invention also offers the preparation method of described door use alkyd paint:
1. take wilkinite and ethyl acetate by formula, at use stirrer moderate-speed mixer 15min after mixing, form native cream;
2. by formula take 50% of 3355 Synolac liquid measures, mix with the native cream 1. produced to step, and add by fill a prescription take 50% of deionized water liquid measure, then start stirrer, moderate-speed mixer 30min;
3. the mill base that 2. step produces is added shredder and start grinding, regulate mill base flow, control grinding temperature not higher than 60 DEG C, after fineness is up to standard, with by the residue Synolac taken of filling a prescription, the mill base in shredder is ejected;
4. mill base step 3. produced is introduced in paint mixing tank and is stirred, and then adds by other components taken of filling a prescription, moderate-speed mixer 30min;
5. mill base specification 80 mesh filter screen step 4. produced filters, packaging; Packaging temp is no more than 45 DEG C.
Embodiment 3
The concrete technical scheme of the present invention is as follows:
A kind of door use alkyd paint, it is characterized in that, by weight, it is made up of following component:
100A Synolac 20 parts, 3355 Synolac 26 parts, nitro-cotton 16 parts, 5 parts, phenylformic acid, calcium naphthenate 3 parts, 3 parts, zinc sulfide white, wilkinite 6 parts, stearic acid dioctyl ester 3 parts, ethanol 53 parts, ethyl acetate 13 parts, butylacetate 4 parts, deionized water 10 parts, isopropylcarbinol 3 parts, 3 parts, color material.
Present invention also offers the preparation method of described door use alkyd paint:
1. take wilkinite and ethyl acetate by formula, at use stirrer moderate-speed mixer 15min after mixing, form native cream;
2. by formula take 100A Synolac liquid measure 50% and 3355 Synolac liquid measure 50%, mix with the native cream 1. produced to step, and add by fill a prescription take 50% of deionized water liquid measure, then start stirrer, moderate-speed mixer 30min;
3. the mill base that 2. step produces is added shredder and start grinding, regulate mill base flow, control grinding temperature not higher than 60 DEG C, after fineness is up to standard, with by the residue Synolac taken of filling a prescription, the mill base in shredder is ejected;
4. mill base step 3. produced is introduced in paint mixing tank and is stirred, and then adds by other components taken of filling a prescription, moderate-speed mixer 30min;
5. mill base specification 80 mesh filter screen step 4. produced filters, packaging; Packaging temp is no more than 45 DEG C.
The above is only preferred embodiments of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. a door use alkyd paint, is characterized in that, by weight, it is made up of following component:
Synolac 30-50 part, nitro-cotton 15-20 part, phenylformic acid 3-6 part, calcium naphthenate 2-4 part, zinc sulfide white 3-4 part, wilkinite 5-8 part, stearic acid dioctyl ester 2-5 part, ethanol 50-70 part, ethyl acetate 15-20 part, butylacetate 4-5 part, deionized water 10-15 part, isopropylcarbinol 2-8 part.
2. a kind of door use alkyd paint as claimed in claim 1, is characterized in that, described Synolac adopts one or several the arbitrary proportion mixture in 100A Synolac, 3355 Synolac.
3. a kind of door use alkyd paint as claimed in claim 1, is characterized in that, describedly also comprises color material 1-3 part.
4. a kind of door use alkyd paint as claimed in claim 1 or 2, is characterized in that, the preparation method of described door use alkyd paint is as follows:
1. take wilkinite and ethyl acetate by formula, at use stirrer moderate-speed mixer 15min after mixing, form native cream;
2. by formula take 50% of Synolac liquid measure, mix with the native cream 1. produced to step, and add by fill a prescription take 50% of deionized water liquid measure, then start stirrer, moderate-speed mixer 30min;
3. the mill base that 2. step produces is added shredder and start grinding, regulate mill base flow, control grinding temperature not higher than 60 DEG C, after fineness is up to standard, with by the residue Synolac taken of filling a prescription, the mill base in shredder is ejected;
4. mill base step 3. produced is introduced in paint mixing tank and is stirred, and then adds by other components taken of filling a prescription, moderate-speed mixer 30min;
5. mill base specification 80 mesh filter screen step 4. produced filters, packaging; Packaging temp is no more than 45 DEG C.