CN105315849A - Epoxy finish paint for door and preparing method thereof - Google Patents
Epoxy finish paint for door and preparing method thereof Download PDFInfo
- Publication number
- CN105315849A CN105315849A CN201510837066.0A CN201510837066A CN105315849A CN 105315849 A CN105315849 A CN 105315849A CN 201510837066 A CN201510837066 A CN 201510837066A CN 105315849 A CN105315849 A CN 105315849A
- Authority
- CN
- China
- Prior art keywords
- parts
- mill base
- door
- epoxy
- prescription
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Epoxy finish paint for a door is prepared from 40-60 parts of epoxy resin, 7-9 parts of chlorinated paraffin, 2-4 parts of calcium stearate, 3-4 parts of barium sulfate, 5-8 parts of bentonite, 4-6 parts of kaolin, 2-5 parts of dioctyl stearate, 10-15 parts of cyclohexanone, 50-70 parts of solvent oil 200#, 15-20 parts of xylene, 4-5 parts of ethyl acetate, 3-6 parts of ethyl alcohol and 2-8 parts of butanol. A preparing method is simple in process, and the epoxy finish paint is high in adhesive force and resistant to ageing.
Description
Technical field
The present invention relates to technical field of coatings, particularly a kind of door epoxy finish and preparation method thereof.
Background technology
In current door processing industry, the technical recipe for the epoxy finish of door external coating is more complicated, and production difficulty is high, surface effect and sticking power poor.
For the problems referred to above, the invention provides a kind of door epoxy finish and preparation method thereof, technique is simple, and product strong adhesion is ageing-resistant.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of door epoxy finish and preparation method thereof.Effectively can solve existing door epoxy finish technique more complicated, production difficulty is high, surface effect and the poor problem of sticking power.
A kind of door epoxy finish, it is characterized in that, by weight, it is made up of following component: epoxy resin 40-60 part, clorafin 7-9 part, calcium stearate 2-4 part, barium sulfate 3-4 part, wilkinite 5-8 part, kaolin 4-6 part, stearic acid dioctyl ester 2-5 part, pimelinketone 10-15 part, 200# solvent oil 50-70 part, dimethylbenzene 15-20 part, ethyl acetate 4-5 part, ethanol 3-6 part, butanols 2-8 part.
Further, described door epoxy finish also comprises color material 1-3 part.
Present invention also offers the preparation method of described door epoxy finish:
1. take 50% of epoxy resin liquid measure by formula, add and stir by the fill a prescription clorafin that takes and calcium stearate, moderate-speed mixer 15min in stirrer;
2. add the color material, barium sulfate, wilkinite, the kaolin that take by filling a prescription in the mill base 1. produced to step and take 50% of 200# solvent oil liquid measure by formula, tank limit powder is scraped with shovel, without thick precipitation powder at the bottom of tank, moderate-speed mixer 30min in stirrer;
3. mill base shredder step 2. produced starts grinding, regulates mill base flow, controls grinding temperature and is not less than 38 DEG C, after fineness is up to standard, the mill base in shredder is ejected with by the remaining epoxy taken of filling a prescription;
4. mill base step 3. produced is introduced in paint mixing tank, then adds by other components taken of filling a prescription, moderate-speed mixer 30min in stirrer;
5. mill base specification 120 mesh filter screen step 4. produced filters, packaging.
Beneficial effect of the present invention is, provides a kind of door epoxy finish and preparation method thereof technique simple, product strong adhesion, ageing-resistant.
Embodiment
Be further described the specific embodiment of the present invention below in conjunction with embodiment, following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
Embodiment 1
The concrete technical scheme of the present invention is as follows:
A kind of door epoxy finish, it is characterized in that, by weight, it is made up of following component: epoxy resin 40 parts, clorafin 7 parts, calcium stearate 2 parts, 3 parts, barium sulfate, wilkinite 5 parts, kaolin 4 parts, stearic acid dioctyl ester 2 parts, pimelinketone 10 parts, 200# solvent oil 50 parts, dimethylbenzene 15 parts, ethyl acetate 4 parts, ethanol 3 parts, 2 parts, butanols.
Present invention also offers the preparation method of described door epoxy finish:
1. take 50% of epoxy resin liquid measure by formula, add and stir by the fill a prescription clorafin that takes and calcium stearate, moderate-speed mixer 15min in stirrer;
2. add the color material, barium sulfate, wilkinite, the kaolin that take by filling a prescription in the mill base 1. produced to step and take 50% of 200# solvent oil liquid measure by formula, tank limit powder is scraped with shovel, without thick precipitation powder at the bottom of tank, moderate-speed mixer 30min in stirrer;
3. mill base shredder step 2. produced starts grinding, regulates mill base flow, controls grinding temperature and is not less than 38 DEG C, after fineness is up to standard, the mill base in shredder is ejected with by the remaining epoxy taken of filling a prescription;
4. mill base step 3. produced is introduced in paint mixing tank, then adds by other components taken of filling a prescription, moderate-speed mixer 30min in stirrer;
5. mill base specification 120 mesh filter screen step 4. produced filters, packaging.
Embodiment 2
The concrete technical scheme of the present invention is as follows:
A kind of door epoxy finish, it is characterized in that, by weight, it is made up of following component: epoxy resin 55 parts, clorafin 8 parts, calcium stearate 3 parts, 4 parts, barium sulfate, wilkinite 7 parts, kaolin 56 parts, stearic acid dioctyl ester 3 parts, pimelinketone 12 parts, 200# solvent oil 60 parts, dimethylbenzene 17 parts, ethyl acetate 4 parts, ethanol 6 parts, 3 parts, butanols, 2 parts, color material.
Present invention also offers the preparation method of described door epoxy finish:
1. take 50% of epoxy resin liquid measure by formula, add and stir by the fill a prescription clorafin that takes and calcium stearate, moderate-speed mixer 15min in stirrer;
2. add the color material, barium sulfate, wilkinite, the kaolin that take by filling a prescription in the mill base 1. produced to step and take 50% of 200# solvent oil liquid measure by formula, tank limit powder is scraped with shovel, without thick precipitation powder at the bottom of tank, moderate-speed mixer 30min in stirrer;
3. mill base shredder step 2. produced starts grinding, regulates mill base flow, controls grinding temperature and is not less than 38 DEG C, after fineness is up to standard, the mill base in shredder is ejected with by the remaining epoxy taken of filling a prescription;
4. mill base step 3. produced is introduced in paint mixing tank, then adds by other components taken of filling a prescription, moderate-speed mixer 30min in stirrer;
5. mill base specification 120 mesh filter screen step 4. produced filters, packaging.
Embodiment 3
The concrete technical scheme of the present invention is as follows:
A kind of door epoxy finish, it is characterized in that, by weight, it is made up of following component: epoxy resin 45 parts, clorafin 7 parts, calcium stearate 4 parts, 3 parts, barium sulfate, wilkinite 6 parts, kaolin 5 parts, stearic acid dioctyl ester 4 parts, pimelinketone 11 parts, 200# solvent oil 55 parts, dimethylbenzene 15 parts, ethyl acetate 4 parts, ethanol 7 parts, 7 parts, butanols, 3 parts, color material.
Present invention also offers the preparation method of described door epoxy finish:
1. take 50% of epoxy resin liquid measure by formula, add and stir by the fill a prescription clorafin that takes and calcium stearate, moderate-speed mixer 15min in stirrer;
2. add the color material, barium sulfate, wilkinite, the kaolin that take by filling a prescription in the mill base 1. produced to step and take 50% of 200# solvent oil liquid measure by formula, tank limit powder is scraped with shovel, without thick precipitation powder at the bottom of tank, moderate-speed mixer 30min in stirrer;
3. mill base shredder step 2. produced starts grinding, regulates mill base flow, controls grinding temperature and is not less than 38 DEG C, after fineness is up to standard, the mill base in shredder is ejected with by the remaining epoxy taken of filling a prescription;
4. mill base step 3. produced is introduced in paint mixing tank, then adds by other components taken of filling a prescription, moderate-speed mixer 30min in stirrer;
5. mill base specification 120 mesh filter screen step 4. produced filters, packaging.
The above is only preferred embodiments of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. a door epoxy finish, it is characterized in that, by weight, it is made up of following component: epoxy resin 40-60 part, clorafin 7-9 part, calcium stearate 2-4 part, barium sulfate 3-4 part, wilkinite 5-8 part, kaolin 4-6 part, stearic acid dioctyl ester 2-5 part, pimelinketone 10-15 part, 200# solvent oil 50-70 part, dimethylbenzene 15-20 part, ethyl acetate 4-5 part, ethanol 3-6 part, butanols 2-8 part.
2. a kind of door epoxy finish as claimed in claim 1, is characterized in that, describedly also comprises color material 1-3 part.
3. a kind of door epoxy finish as claimed in claim 1 or 2, is characterized in that, the preparation method of described door epoxy finish is as follows:
1. take 50% of epoxy resin liquid measure by formula, add and stir by the fill a prescription clorafin that takes and calcium stearate, moderate-speed mixer 15min in stirrer;
2. add the color material, barium sulfate, wilkinite, the kaolin that take by filling a prescription in the mill base 1. produced to step and take 50% of 200# solvent oil liquid measure by formula, tank limit powder is scraped with shovel, without thick precipitation powder at the bottom of tank, moderate-speed mixer 30min in stirrer;
3. mill base shredder step 2. produced starts grinding, regulates mill base flow, controls grinding temperature and is not less than 38 DEG C, after fineness is up to standard, the mill base in shredder is ejected with by the remaining epoxy taken of filling a prescription;
4. mill base step 3. produced is introduced in paint mixing tank, then adds by other components taken of filling a prescription, moderate-speed mixer 30min in stirrer;
5. mill base specification 120 mesh filter screen step 4. produced filters, packaging.