CN102220078A - Orangefigured paint, preparation method and construction process thereof - Google Patents
Orangefigured paint, preparation method and construction process thereof Download PDFInfo
- Publication number
- CN102220078A CN102220078A CN2011101195785A CN201110119578A CN102220078A CN 102220078 A CN102220078 A CN 102220078A CN 2011101195785 A CN2011101195785 A CN 2011101195785A CN 201110119578 A CN201110119578 A CN 201110119578A CN 102220078 A CN102220078 A CN 102220078A
- Authority
- CN
- China
- Prior art keywords
- mill base
- agent
- tangerine line
- percent
- line effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides orangefigured paint, a preparation method and a construction process thereof. The orangefigured paint comprises the following components in percentage by weight: 30.0 to 40.0 percent of thermosetting acrylic resin, 5.0 to 15.0 percent of synthetic fatty acid resin, 0.01 to 0.05 percent of curing agent, 0 to 0.01 percent of defoaming agent, 0.3 to 1.2 percent of orangefiguring agent, 1.0 to 2.0 percent of antiflooding wetting dispersant, 0 to 10.0 percent of dimethylbenzene, 0 to 10.0 percent of trimethylbenzene, 0 to 5 percent of cyclohexanone and 20 to 50 percent of color paste. The orangefigured paint can form beautiful patterns, has high decorative performance, and has high weather resistance, high chemical resistance, high water resistance, high impact resistance and high wear resistance; the orangefigured paint also has high mechanical performance and high gasoline resistance, high engine oil resistant and high aging resistance; the cost of the paint is low, and the construction of the paint is convenient; and the paint can be widely used for indoor furniture decoration, indoor decoration and artwork surface decoration and can be used for machine tool, printing and dyeing machines, textile machines, plastic machines, safes, appliances and instruments, medical appliances, motors, electric tools, antitheft doors and other large machines.
Description
Technical field
The present invention relates to a kind of paint vehicle, relate in particular to a kind of tangerine line effect lacquer and preparation method thereof and construction technology.
Background technology
Tangerine line coating is a kind of as novelty finish, has unique tangerine line effect, attractive in appearance and ornamental height.And paint film is tough and tensile, good luster, and not efflorescence has certain help to covering coarse surface, is applicable to various surface decorations.At present, most tangerine line coating on the market is easily aging under the irradiation of sunlight, weathering resistance is also poor, fades easily etc., and when being used for the decoration of equipment appearances such as lathe, dyeing machine, textile manufacturing machine, be subjected to the corrosion of gasoline or machine oil etc. easily and variable color or come off, outward appearance is influenced.
Summary of the invention
A purpose of the present invention is, a kind of tangerine line effect lacquer is provided, and has excellent mechanical property after the film forming, and has good anti-gasoline, anti-machine oil and ageing-resistant performance, and decorative pattern is attractive in appearance, ornamental height.
Another object of the present invention is to provide the preparation method of above-mentioned tangerine line effect lacquer, technology is simple.
Another purpose of the present invention is to provide a kind of construction technology of above-mentioned tangerine line effect lacquer, easy construction, and performance is good.
For achieving the above object, the invention provides a kind of tangerine line effect lacquer, it comprises that component and weight percent thereof are as follows: thermosetting acrylic resin 30.0-40.0%, synthetic fat acid resin 5.0-15.0%, stiffening agent 0.01-0.05%, defoamer 0-0.01%, tangerine line agent 0.3-1.2%, anti-loose colour wetting dispersing agent 1.0-2.0%, dimethylbenzene 0-10.0%, trimethylbenzene 0-10.0%, pimelinketone 0-5%, and mill base 20-50%.
Described stiffening agent is a dilaurate tin, and defoamer is a modified polyorganosiloxane, and anti-loose colour wetting dispersing agent is the mixing solutions of unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane copolymer.
Described mill base is at least a in titanium dioxide mill base, permanent bordeaux mill base, iron oxide yellow mill base, red iron oxide mill base, phthalocyanine blue mill base, carbon black color paste, the permanent violet mill base.
Simultaneously, the invention provides a kind of preparation method of above-mentioned tangerine line effect lacquer, it comprises the steps:
Step 1 takes by weighing each component by weight percentage: thermosetting acrylic resin 30.0-40.0%, synthetic fat acid resin 5.0-15.0%, stiffening agent 0.01-0.05%, defoamer 0-0.01%, tangerine line agent 0.3-1.2%, anti-loose colour wetting dispersing agent 1.0-2.0%, dimethylbenzene 0-10.0%, trimethylbenzene 0-10.0%, pimelinketone 0-5%, and mill base 20-50%;
Step 2 drops into thermosetting acrylic resin, synthetic fat acid resin, stiffening agent, defoamer, the agent of tangerine line, dimethylbenzene, trimethylbenzene and pimelinketone in the dispersion cylinder successively, disperses 30-40 minute with high speed dispersor;
Step 3 will prevent that loose colour wetting dispersing agent, mill base drop in the above-mentioned dispersion cylinder, disperse 30-40 minute with high speed dispersor, filter.
Described stiffening agent is a dilaurate tin, and defoamer is a modified polyorganosiloxane, and anti-loose colour wetting dispersing agent is the mixing solutions of unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane copolymer; Described mill base is at least a in titanium dioxide mill base, permanent bordeaux mill base, iron oxide yellow mill base, red iron oxide mill base, phthalocyanine blue mill base, carbon black color paste, the permanent violet mill base.
The rotating speed of described high speed dispersor is 1500 rev/mins.
The present invention also provides a kind of construction technology of above-mentioned tangerine line effect lacquer, comprises the steps:
Step 1 is carried out dedusting, oil removing to substrate surface;
Step 2, tangerine line effect lacquer is pressed 4-5 with solidifying agent: 1 proportioning, being diluted to viscosity with thinner is 16-20 second, afterwards it is sprayed on the ground, levelling 5-10 minute, forms first and film on ground;
Step 3, tangerine line effect lacquer and solidifying agent press 4-5: 1 proportioning, being diluted to viscosity with thinner is 30-40 second, afterwards it is sprayed on first of ground films, levelling 5-10 minute, to carry out afterwards from doing or putting into baking oven and toast, formation second is filmed.
Described solidifying agent comprises that component and weight percent thereof are as follows: isocyanate curing agent 70.0-80.0% and N-BUTYL ACETATE 20.0-30.0%; Its preparation method is: add isocyanate curing agent and N-BUTYL ACETATE by weight percentage successively in producing cylinder, disperseed 15-20 minute with the low speed of dispersion machine with 300 rev/mins, filter with 300 order filtering nets the back, promptly.
Described thinner comprises that component and weight percent thereof are as follows: toluene 30.0-50.0%, vinyl acetic monomer 20.0-40.0%, N-BUTYL ACETATE 10.0-30.0% and trimethylbenzene 0-5.0%; Its preparation method is: add each component by weight percentage successively in producing cylinder, disperseed 15-20 minute with the low speed of dispersion machine with 300 rev/mins, filter with 300 order filtering nets then, promptly.
Storing temperature described in the step 3 is 75-100 ℃, and storing time is 30-40 minute; Described air-drying time is 24-48 hour; Described viscosity 16-20 second and 30-40 all are at 25 ℃ down with the data that are coated with-4 glasss of measurements seconds.
Beneficial effect of the present invention: tangerine line effect lacquer of the present invention, decorative pattern is attractive in appearance, ornamental height, not only has excellent weathering resistance, favorable chemical resistance, water tolerance, shock-resistance and wear resistance also have excellent mechanical property, good anti-gasoline, anti-machine oil and ageing-resistant performance; Cost is low, easy construction can be widely used on indoor furniture, indoor decoration, handicraft surface decoration and the heavy mechanical equipments such as lathe, dyeing machine, textile manufacturing machine, molding machine, strong box, instrument, medical machinery, motor, power tool and antitheft door.
Embodiment
The invention provides a kind of tangerine line effect lacquer, it comprises that component and weight percent thereof are as follows:
Thermosetting acrylic resin 30.0-40.0%;
Synthetic fat acid resin 5.0-15.0%;
Stiffening agent 0.01-0.05%;
Defoamer 0-0.01%;
Tangerine line agent 0.3-1.2%;
Anti-loose colour wetting dispersing agent 1.0-2.0%;
Dimethylbenzene 0-10.0%;
Trimethylbenzene 0-10.0%;
Pimelinketone 0-5%; And
Mill base 20-50%.
Wherein, thermosetting acrylic resin and synthetic fat acid resin are matrix resin, as the film forming matter of this paint vehicle.Described stiffening agent is a dilaurate tin, and defoamer is a modified polyorganosiloxane, and anti-loose colour wetting dispersing agent is the mixing solutions of unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane copolymer, plays dispersion, anti-loose colour effect.The agent of described tangerine line is the high molecular polymer that contains multiple specific functional groups, the mechanism that this tangerine line agent produces is: coating is when levelling, because the surface tension that the surface tension of tangerine line agent is filmed less than normal coating, the tangerine line agent that is scattered in the each point of filming has changed the local tension force of filming, the little place of surface tension produces a pit everywhere, and final film coated surface is " recessed " shape and distributes and present tangerine line effect.The film coated surface decorative pattern is uneven, and not only the stereoscopic sense is strong, and the mechanical property excellence, and lines reappears stable.According to different lines sizes, select suitable tangerine line agent kind and consumption.
Described mill base is at least a in titanium dioxide mill base, permanent bordeaux mill base, iron oxide yellow mill base, red iron oxide mill base, phthalocyanine blue mill base, carbon black color paste, the permanent violet mill base.Described tangerine line effect lacquer is to arrange in pairs or groups mutually by the mill base of different colours to reconcile into different form and aspect, the content of mill base in whole paint vehicle system should be in certain proportional range simultaneously, if mill base is then resin content minimizing relatively too much, then influence the film-forming properties of tangerine line effect lacquer; Mill base is hiding lack then very little, influences the aesthetic property of tangerine line effect lacquer.And mill base is mainly allocated by raw materials such as toner, dispersion agents and is formed, the used toner of modulation mill base requires to have enough opacifying powers and color development power, and select corresponding dispersion agent allotment for use according to the difference of mill base kind, with the mill base that acquisition has suitable fineness (fineness≤15 μ m), just can obtain the preferable tangerine line effect lacquer of effect.When coating of the present invention uses, carry out proportioning, be diluted to proper viscosity, spray again by thinner with solidifying agent.
The preparation method of above-mentioned tangerine line effect lacquer, it comprises the steps:
Step 1 takes by weighing each component by weight percentage: thermosetting acrylic resin 30.0-40.0%, synthetic fat acid resin 5.0-15.0%, stiffening agent 0.01-0.05%, defoamer 0-0.01%, tangerine line agent 0.3-1.2%, anti-loose colour wetting dispersing agent 1.0-2.0%, dimethylbenzene 0-10.0%, trimethylbenzene 0-10.0%, pimelinketone 0-5%, and mill base 20-50%.
Step 2, thermosetting acrylic resin, synthetic fat acid resin, stiffening agent, defoamer, the agent of tangerine line, dimethylbenzene, trimethylbenzene and pimelinketone are dropped in the dispersion cylinder successively, by dimethylbenzene, trimethylbenzene, pimelinketone etc. other components are dissolved, disperseed 30-40 minute with the rotating speed of high speed dispersor with 1500 rev/mins.
Step 3 will prevent that loose colour wetting dispersing agent, mill base drop in the above-mentioned dispersion cylinder, disperse 30-40 minute with the rotating speed of high speed dispersor with 1500 rev/mins, form the paint vehicle of homogeneous, filter.
The construction technology of above-mentioned tangerine line effect lacquer, it comprises the steps:
Step 1 is carried out dedusting, oil removing to substrate surface; Described ground is furniture, artwork, various device or the various decorative cover etc. for the treatment of.Also comprise substrate surface is polished, polish, be beneficial to adhering to of follow-up lacquer as adopting sand paper.
Step 2, tangerine line effect lacquer is pressed 4-5 with solidifying agent: 1 proportioning, being diluted to viscosity with thinner is 16-20 second, afterwards it is sprayed on the ground, levelling 5-10 minute, forms first and film on ground.Above-mentioned viscosity number 16-20 be second 25 ℃ down with the data that are coated with-4 glasss of measurements (that is: 25 ℃, 4#).
Described tangerine line effect lacquer is by hydroxy-containing resin and isocyanate curing agent crosslinking reaction, forms acroleic acid polyurethane and film forming, so solidifying agent also needs be made into certain ratio with solvent, and the employing N-BUTYL ACETATE is that solvent carries out proportioning among the present invention.That is, described solidifying agent comprises that component and weight percent thereof are as follows: isocyanate curing agent 70.0-80.0% and N-BUTYL ACETATE 20.0-30.0%; Its preparation method is: add isocyanate curing agent and N-BUTYL ACETATE by weight percentage successively in producing cylinder, disperseed 15-20 minute with the low speed of dispersion machine with 300 rev/mins, filter with 300 order filtering nets the back, promptly.
Described thinner not only as the medium of film-forming polymer, regulate viscosity and rheological and be beneficial to the application of paint vehicle, and to film forming quality, as film performance and outward appearance material impact is arranged all by dissolve polymer.And the selection of thinner depends primarily on dissolving power, boiling point, volatility, viscosity, surface tension, flash-point, toxicity and the price etc. of solvent.Tangerine line effect lacquer of the present invention need select for use adaptive thinner could form good tangerine line effect.Described thinner comprises that component and weight percent thereof are as follows: toluene 30.0-50.0%, vinyl acetic monomer 20.0-40.0%, N-BUTYL ACETATE 10.0-30.0% and trimethylbenzene 0-5.0%; Its preparation method is: add each component by weight percentage successively in producing cylinder, disperseed 15-20 minute with the low speed of dispersion machine with 300 rev/mins, filter with 300 order filtering nets then, promptly.
Step 3, tangerine line effect lacquer is pressed 4-5 with solidifying agent: 1 proportioning, being diluted to viscosity with thinner is (25 ℃ of 30-40 seconds, 4#), afterwards it is sprayed on first of ground films, levelling 5-10 minute, carries out 24-48 hour afterwards from doing or put into 75-100 ℃ of baking oven baking/30-40 minute, form second and film, thus the construction technology of finishing.Described solidifying agent and thinner are described with above-mentioned step.Have tangerine line effect by the substrate surface after the spraying film forming, attractive in appearance, have certain stereoscopic sensation.Above-mentioned viscosity number 30-40 be second 25 ℃ down with the data that are coated with-4 glasss of measurements (that is: 25 ℃, 4#).
In sum, tangerine line effect of the present invention lacquer, decorative pattern is attractive in appearance, ornamental height, the weathering resistance of tool excellence, favorable chemical resistance, water tolerance, shock-resistance and wear resistance are also had a mechanical property of excellence, good anti-gasoline, anti-machine oil and ageing-resistant performance; Cost is low, and easy construction can be widely used on indoor furniture, decoration, handicraft surface decoration and the heavy mechanical equipments such as lathe, dyeing machine, textile manufacturing machine, molding machine, strong box, instrument, medical machinery, motor, power tool and antitheft door.
The above; for the person of ordinary skill of the art; can make other various corresponding changes and distortion according to technical scheme of the present invention and technical conceive, and all these changes and distortion all should belong to the protection domain of accompanying Claim of the present invention.
Claims (10)
1. a tangerine line effect is coated with lacquer, it is characterized in that it comprises that component and weight percent thereof are as follows: thermosetting acrylic resin 30.0-40.0%, synthetic fat acid resin 5.0-15.0%, stiffening agent 0.01-0.05%, defoamer 0-0.01%, tangerine line agent 0.3-1.2%, anti-loose colour wetting dispersing agent 1.0-2.0%, dimethylbenzene 0-10.0%, trimethylbenzene 0-10.0%, pimelinketone 0-5%, and mill base 20-50%.
2. tangerine line effect lacquer as claimed in claim 1 is characterized in that described stiffening agent is a dilaurate tin, and defoamer is a modified polyorganosiloxane, and anti-loose colour wetting dispersing agent is the mixing solutions of unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane copolymer.
3. tangerine line effect as claimed in claim 1 lacquer is characterized in that, described mill base is at least a in titanium dioxide mill base, permanent bordeaux mill base, iron oxide yellow mill base, red iron oxide mill base, phthalocyanine blue mill base, carbon black color paste, the permanent violet mill base.
4. the preparation method of a tangerine line effect lacquer as claimed in claim 1 is characterized in that, comprises the steps:
Step 1 takes by weighing each component by weight percentage: thermosetting acrylic resin 30.0-40.0%, synthetic fat acid resin 5.0-15.0%, stiffening agent 0.01-0.05%, defoamer 0-0.01%, tangerine line agent 0.3-1.2%, anti-loose colour wetting dispersing agent 1.0-2.0%, dimethylbenzene 0-10.0%, trimethylbenzene 0-10.0%, pimelinketone 0-5%, and mill base 20-50%;
Step 2 drops into thermosetting acrylic resin, synthetic fat acid resin, stiffening agent, defoamer, the agent of tangerine line, dimethylbenzene, trimethylbenzene and pimelinketone in the dispersion cylinder successively, disperses 30-40 minute with high speed dispersor;
Step 3 will prevent that loose colour wetting dispersing agent, mill base drop in the above-mentioned dispersion cylinder, disperse 30-40 minute with high speed dispersor, filter.
5. the preparation method of tangerine line effect lacquer as claimed in claim 4, it is characterized in that, described stiffening agent is a dilaurate tin, and defoamer is a modified polyorganosiloxane, and anti-loose colour wetting dispersing agent is the mixing solutions of unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and polysiloxane copolymer; Described mill base is at least a in titanium dioxide mill base, permanent bordeaux mill base, iron oxide yellow mill base, red iron oxide mill base, phthalocyanine blue mill base, carbon black color paste, the permanent violet mill base.
6. the preparation method of tangerine line effect lacquer as claimed in claim 4 is characterized in that the rotating speed of described high speed dispersor is 1500 rev/mins.
7. the construction technology of a tangerine line effect lacquer as claimed in claim 1 is characterized in that, comprises the steps:
Step 1 is carried out dedusting, oil removing to substrate surface;
Step 2, tangerine line effect lacquer is pressed 4-5 with solidifying agent: 1 proportioning, being diluted to viscosity with thinner is 16-20 second, afterwards it is sprayed on the ground, levelling 5-10 minute, forms first and film on ground;
Step 3, tangerine line effect lacquer and solidifying agent press 4-5: 1 proportioning, being diluted to viscosity with thinner is 30-40 second, afterwards it is sprayed on first of ground films, levelling 5-10 minute, to carry out afterwards from doing or putting into baking oven and toast, formation second is filmed.
8. the construction technology of tangerine line effect as claimed in claim 7 lacquer is characterized in that, described solidifying agent comprises that component and weight percent thereof are as follows: isocyanate curing agent 70.0-80.0% and N-BUTYL ACETATE 20.0-30.0%; Its preparation method is: add isocyanate curing agent and N-BUTYL ACETATE by weight percentage successively in producing cylinder, disperseed 15-20 minute with the low speed of dispersion machine with 300 rev/mins, filter with 300 order filtering nets the back, promptly.
9. the construction technology of tangerine line effect lacquer as claimed in claim 7, it is characterized in that described thinner comprises that component and weight percent thereof are as follows: toluene 30.0-50.0%, vinyl acetic monomer 20.0-40.0%, N-BUTYL ACETATE 10.0-30.0% and trimethylbenzene 0-5.0%; Its preparation method is: add each component by weight percentage successively in producing cylinder, disperseed 15-20 minute with the low speed of dispersion machine with 300 rev/mins, filter with 300 order filtering nets then, promptly.
10. the construction technology of tangerine line effect lacquer as claimed in claim 7 is characterized in that the storing temperature described in the step 3 is 75-100 ℃, and storing time is 30-40 minute; Described air-drying time is 24-48 hour; Described viscosity 16-20 second and 30-40 all are at 25 ℃ down with the data that are coated with-4 glasss of measurements seconds.