CN104004395A - UV roller coat elastic under-coating paint used for wood veneer and preparing method and construction process of UV roller coat elastic under-coating paint - Google Patents

UV roller coat elastic under-coating paint used for wood veneer and preparing method and construction process of UV roller coat elastic under-coating paint Download PDF

Info

Publication number
CN104004395A
CN104004395A CN201410269690.0A CN201410269690A CN104004395A CN 104004395 A CN104004395 A CN 104004395A CN 201410269690 A CN201410269690 A CN 201410269690A CN 104004395 A CN104004395 A CN 104004395A
Authority
CN
China
Prior art keywords
roller coat
coating
elasticity
wooden skin
skin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410269690.0A
Other languages
Chinese (zh)
Other versions
CN104004395B (en
Inventor
周伟建
刘化春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG MAYDOS BUILDING MATERIALS CO Ltd
Original Assignee
GUANGDONG MAYDOS BUILDING MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG MAYDOS BUILDING MATERIALS CO Ltd filed Critical GUANGDONG MAYDOS BUILDING MATERIALS CO Ltd
Priority to CN201410269690.0A priority Critical patent/CN104004395B/en
Publication of CN104004395A publication Critical patent/CN104004395A/en
Application granted granted Critical
Publication of CN104004395B publication Critical patent/CN104004395B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses UV roller coat elastic under-coating paint used for wood veneer and a preparing method and construction process of the UV roller coat elastic under-coating paint. The paint comprises, by weight, 10-35% of monomer, 42-70% of UV elastic resin, 5-8% of photoinitiator, 5-15% of filling powder, 0.4-0.5% of addition agents, and 0.1-0.3% of anti-settling agents. The monomer is one of or a mixture of more than two of isobornyl acrylate, ethoxylation nonylphenol acrylate (4), propoxylated neopentyl glycol di-acrylate and trimethylolpropane acrylate. After the wood veneer is coated with the elastic under-coating paint through an automatic roller coating line , the reality of natural wood veneer and the surface effect of a traditional paint process are achieved, a paint film has good elasticity, the wood veneer is tough and can be folded at will like paper and the paint film cannot break.

Description

UV roller coat elasticity bottom-coating and preparation method thereof and implementing process for a kind of wooden skin
Technical field
The present invention relates to a kind of UV woodwork coating, be specifically related to UV roller coat elasticity bottom-coating and preparation method thereof and implementing process for a kind of wooden skin.
Background technology
Wood skin and faced deorative industry thereof are started in the fifties in last century, through semicentennial development, have possessed suitable scale, particularly enter over 20 years, along with the leapfrogging growth of China's furniture manufacturing industry and decorations industry.Its scale is advanced by leaps and bounds especially, yet, the processing that traditional wooden skin pastes rear paint is main with traditional polyurethane coating PU solvent-borne type type paint, continuous three above the spraying paint of minimum needs, polishing, the production cycle of several days time, the profit that a large amount of recruitment demands and place take the furniture industry making sharply declines, cost constantly increases, and also exists VOC larger, and environment is had a negative impact.
Summary of the invention
Technical problem to be solved by this invention is to overcome the deficiencies in the prior art, UV roller coat elasticity bottom-coating for a kind of wooden skin is provided, wood skin is after the automatic coating line of wooden skin is covered with paint, lacquer, colour wash, etc. this elasticity bottom-coating processing, the surface effect that has the sense of reality and the traditional paint technique of natural veneer, paint film has good elasticity, wood skin is more pliable and tougher, wood micromicro is opened equally any folding and paint film does not rupture with sensitive paper, the wooden skin that these are completed to application UV elastic coating so long by paste process application in as various mouldings, Composite door pocket, Compound door leaf, edging materials etc. are above abnormal member, use this coating can effectively reduce factory cost, improve product quality, productivity effect is greatly improved.
The present invention solves this technical problem adopted technical scheme: UV roller coat elasticity bottom-coating for a kind of wooden skin, and it comprises that component and weight percent thereof are:
As preferred version, UV roller coat elasticity bottom-coating for this wood skin, it comprises that component and weight percent thereof are: monomer 10~35%, UV elastic resin 52.5~68%, light trigger 7%, powder filler 5~14.5%, anti-settling agent 0.1~0.3%.
Particularly, described monomer is iso-bornyl acrylate (IBOA), (4) ethoxylated nonylphenol acrylate, the third oxidation neopentylglycol diacrylate (NPG2PODA), the mixture of one or more in the third oxidation Viscoat 295 (TMP3POTA), its Main Function is to adjust working viscosity and adjust film performance, the preferred EM70 (IBOA) of Taiwan Changxing company, EM2071 (NP4EOA), EM2251 (NPG2PODA), EM2381 (TMP3POTA).
Particularly, described UV elastic resin, to do polyvalent alcohol by PTMG, isocyanic ester is selected TDI or IPDI, chainextender selects the synthetic elongation at break such as BDO at 300% 2 functional polyurethanes acrylic resins, preferred Japanese synthetic chemistry UV-3000B, or the 6148J-85 of Changxing, Taiwan company, or Bayer A.G's 2491 resins.
Particularly, described light trigger is the mixture of 2-hydroxy-2-methyl-1-phenyl-1-acetone (1173) and benzophenone (BP) and reactive amines (P115).Preferred BASF AG or Beijing Ying Li scientific & technical corporation or Tianjin Jiu scientific & technical corporation corresponding 1173 and BP and reactive amines (P115) product.
Particularly, described filling powder is 1250 order talcum powder, preferably Guangxi court cards talcum powder 1250 orders.
Particularly, described anti-settling agent is the hydrophilic fumed silica of median size 12 nanometers, preferably Degussa AEROSILA200.
Further, wooden skin of the present invention also comprises auxiliary agent with UV roller coat elasticity primary coat system component, and its weight percent that accounts in this formulation for coating material is 0.4~0.5%, and described auxiliary agent is at least one of dispersion agent, flow agent or defoamer.Described dispersant structure is the high molecular wetting dispersing agent of the polycarboxylic acid salts solution of polyamine acid amides, preferably Bi Ke chemistry BYK204; Described flow agent Wei Han propenyl functional group's dimethyl polysiloxane and fluorine-carbon modified polyacrylic ester, preferably the Bi Ke up-to-date BYK-UV3575 of chemical company; Described defoamer is not for containing organosilyl polymer-type defoamer, preferably the Bi Ke BYK1794 of chemical company.
For achieving the above object and solve above technical problem, the present invention also provides preparation method and the implementing process of a kind of wooden skin with UV roller coat elasticity bottom-coating.
The invention provides the preparation method of UV roller coat elasticity bottom-coating for a kind of above-mentioned wooden skin, its step is sequentially as follows:
(1) take by weight percentage each component: monomer 10~35%, UV elastic resin 42~70%, light trigger 5~8%, filling powder 5~15%, auxiliary agent 0.4~0.5%, anti-settling agent 0.1-0.3%;
(2), by described monomer and UV elastic resin, drop into and disperse, in cylinder, to use high speed dispersor high speed dispersion 10~15 minutes;
(3) drop into successively each composition in described auxiliary agent, with high speed dispersor, disperse 10~15 minutes;
(4) drop into described filling powder, with high speed dispersor, disperse 10~15 minutes;
(5) drop into described anti-settling agent, with high speed dispersor, disperse 10~15 minutes;
(6) drop into described light trigger, with high speed dispersor, disperse high speed dispersion 10~15 minutes, 100 order filter-cloth filterings, make UV roller coat elasticity bottom-coating for described wooden skin.
Particularly, the rotating speed of the high speed dispersor of described step (2) and step (3) is 1200~1500 revs/min; The rotating speed of the high speed dispersor of step (4), step (5) and step (6) is 1000~1200 revs/min.
The invention provides the implementing process of UV roller coat elasticity bottom-coating for a kind of above-mentioned wooden skin, its step is sequentially as follows:
1) by the 180 order sand paper sandings for skin of collet non-woven fabrics wood, dedusting;
2) sponge roller coat water-based bottom coloring, hairbrush swabbing, ultra red ray drying;
3) the UV bouncing putty of UV roller coat elasticity bottom-coating for roller coat wood skin, glue spread 20-25g/ ㎡, UV energy is controlled at 300mJ/cm 2, UV solidifies;
4) the UV elastic primer of UV roller coat elasticity bottom-coating for roller coat wood skin, glue spread 20-25g/ ㎡, UV energy is controlled at 300mJ/cm 2, UV solidifies;
5) by step 4) repeat to implement 2-3 time;
6) roller coat wood skin can sanding priming paint by the UV elasticity of UV roller coat elasticity bottom-coating, glue spread 20-30g/ ㎡, and UV energy is controlled at 300mJ/cm 2, UV solidifies, and 400 order sand paper sandings are standby;
7) direct roller coat UV elasticity finish paint or spray PU finish paint after cladding process.
Below in conjunction with a plurality of embodiment, the invention will be further described.
Embodiment
Embodiment 1-3
The starting material component of embodiment 1-3 and weight proportion (unit: kg) as shown in table 1.
In table, embodiment 1 is UV roller coat bouncing putty for wooden skin, and embodiment 2 is UV roller coat elastic primer for wooden skin, and embodiment 3 is that wooden skin can sanding priming paint by UV roller coat elasticity.
Wherein, UV elastic resin and monomer that the present invention adopts, filling powder, anti-precipitation powder in this coating system as film forming matter, UV elastic resin adopts and does polyvalent alcohol by PTMG, isocyanic ester is selected TDI or IPDI, chainextender selects 1, the synthetic elongation at break such as 4-butyleneglycol is at 300% 2 functional polyurethanes acrylic resins, this structure UV resin paint film surface drying is better, paint film is more pliable and tougher and have a good rebound resilience, can well meet wooden skin films to elastic requirement, because wooden skin coating elasticity factor, can improve the solidification rate of system again when not losing the elastic performance of UV elastic resin, the functionality of requirement monomer can not be too high, containing the existence of more than two monomer of two keys, can cause the increase of the cross-linking density of filming, the snappiness of filming declines, second-order transition temperature rises, the resistance to tortuosity of wood skin elastic coating obviously declines.So, the present invention of monomer aspect selects simple function group monomer to coordinate a small amount of many officials propoxylation monomer to be used in conjunction with, can overcome the deficiency of the curing speed that whole use monofunctional monomers cause, can not sacrifice the resistance to tortuosity of filming again, again by the collocation of photosensitizer additive, just can meet the various requirement of wooden skin elastic coating, it is good that monofunctional monomer iso-bornyl acrylate (IBOA) has sticking power, the feature that tenacity is good, monofunctional monomer (4) ethoxylated nonylphenol acrylate has low contraction, elastomeric feature, these two monofunctional monomers all have the good good and high response characteristic of dilution property, can give matrix resin elastic performance well supplements, it is low that difunctional monomer the third oxidation neopentylglycol diacrylate (NPG2PODA) has cure shrinkage, the features such as snappiness is good, it is good that 3 functional monomer's the third oxidation Viscoat 295s (TMP3POTA) have snappiness, quick solidifying, shrink the features such as low, these two polyfunctional monomers are through propenoxylated reactive thinner, vinylformic acid parent is after propoxylation, still keeping faster curing speed, skin irritation and cure shrinkage and viscosity obtain very large reduction simultaneously, these monomer collocation are used and can finely be met coating to curing speed, elastic performance, the requirement of the aspects such as dilution property, coating all can produce bubble in production and construction process, the existence of bubble can cause the generation defect of filming, need defoamer to improve, defoamer can provide good defoaming effect, prevent the generation of paint film defect, defoamer of the present invention is not for containing organosilyl polymer-type defoamer, preferred Bi Ke chemistry BYK1794, it has quick their defoaming function, this coating needs quick levelling to eliminate slivering effect, so add appropriate flow agent in formulation for coating material, can improve coating flow leveling, flow agent Wei Han propenyl functional group's dimethyl polysiloxane and fluorine-carbon modified polyacrylic ester in the present invention, preferably use LiaoBYK company recent development containing the dimethyl polysiloxane leveling auxiliary agent BYK_-UV3576 of propenyl functional group, it is levelling elimination slivering fast, light trigger can absorb ultraviolet energy, produce radical, cause again coating oligopolymer and monomer, realize polymerization, crosslinked, make system be cross-linked film forming, the present invention is adopted as the mixture of 2-hydroxy-2-methyl-1-phenyl-1-acetone (1173) and benzophenone (BP) and reactive amines (P115).Preferred BASF AG or Beijing Ying Li scientific & technical corporation or Tianjin Jiu scientific & technical corporation corresponding 1173 and BP and reactive amines (P115) product, these several initiator collocation are used, can absorb different ultraviolet waves energy and reach the complete solidification effect of coating, the filling effect that adopts 1250 talcum powder can reach again when keeping fine transparency, the present invention adopts Guangxi court cards talcum powder 1250 orders, in order to prevent talcum powder precipitation, the present invention adopts interpolation dispersing auxiliary and anti-settling agent to prevent talcum powder precipitation, dispersant structure is the high molecular wetting dispersing agent of the polycarboxylic acid salts solution of polyamine acid amides, preferred Bi Ke chemistry BYK204, it has excellent antiflocculation, anti-settling agent is the hydrophilic fumed silica of median size 12 nanometers, preferred Degussa AEROSIL200, the two collocation can be played good result of prevention.
The preparation method of UV roller coat elasticity bottom-coating for above-mentioned wooden skin, its step is sequentially as follows:
(1) take by weight percentage each component: monomer 10~35%, UV elastic resin 42~70%, light trigger 5~8%, filling powder 5~15%, auxiliary agent 0.4~0.5% and anti-settling agent 0.1-0.3%;
(2), by described monomer and UV elastic resin, drop into and disperse, in cylinder, to use high speed dispersor high speed dispersion 10~15 minutes;
(3) drop into successively each composition in described auxiliary agent, with high speed dispersor, disperse 10~15 minutes;
(4) drop into described filling powder, with high speed dispersor, disperse 10~15 minutes;
(5) drop into described anti-settling agent, with high speed dispersor, disperse 10~15 minutes;
(6) drop into described light trigger, with high speed dispersor, disperse high speed dispersion 10~15 minutes, 100 order filter-cloth filterings, make UV roller coat elasticity bottom-coating for described wooden skin.
The rotating speed of the high speed dispersor of described step (2) and step (3) is 1200~1500 revs/min; The rotating speed of the high speed dispersor of step (4) and step (5) and step (6) is 1000~1200 revs/min.
After testing, the UV roller coat bouncing putty coating of embodiment 1 preparation, color outward appearance is that milky white transparent thick liquid, solid content are 98~99%, viscosity is 20000~30000mpa.s (25 ℃), the UV roller coat elastic primer coating of embodiment 2 preparations, color outward appearance is that milky white transparent liquid, solid content are 98~99%, viscosity is 1200~1500mpa.s (25 ℃), the UV roller coat elasticity sanding primer base of embodiment 3 preparation, color outward appearance is that milky white transparent liquid, solid content are 98~99%, viscosity is 1500~2000mpa.s (25 ℃).
In table one, embodiment 1-3 makes film performance that described wooden skin implements to obtain by wooden skin roller coating machine machinery with UV roller coat elasticity bottom-coating again in Table 2 by above-mentioned preparation method.
Table 2 Physical properties of coating film test result
From table 1-table 2, can find out, above-mentioned UV roller coat elasticity bottom-coating for 3 groups of wood skins, wood skin is after the automatic coating line of wooden skin is covered with paint, lacquer, colour wash, etc. this elasticity bottom-coating processing, the surface effect that has the sense of reality and the traditional paint technique of natural veneer, paint film has good elasticity and sticking power, make that wooden skin is more pliable and tougher has elasticity, wood micromicro is opened equally any folding and paint film does not rupture with sensitive paper, then the wooden skin that these is completed to application UV elastic coating by paste process application in as various mouldings, Composite door pocket, Compound door leaf, edging materials etc. are above abnormal member, use this coating can effectively reduce factory cost, improve product quality, productivity effect is greatly improved.
The present invention is not limited to above-mentioned embodiment, if various changes of the present invention or modification are not departed to the spirit and scope of the present invention, if within these changes and modification belong to claim of the present invention and equivalent technologies scope, the present invention is also intended to comprise these changes and modification.

Claims (10)

1. a UV roller coat elasticity bottom-coating for wooden skin, is characterized in that, it comprises that component and weight percent thereof are:
Described monomer is iso-bornyl acrylate, (4) ethoxylated nonylphenol acrylate, the third oxidation neopentylglycol diacrylate, the mixture of one or more in the third oxidation Viscoat 295.
2. UV roller coat elasticity bottom-coating for wooden skin as claimed in claim 1, is characterized in that: also comprise auxiliary agent, its weight percent that accounts in this formulation for coating material is 0.4~0.5%.
3. UV roller coat elasticity bottom-coating for wooden skin as claimed in claim 1, is characterized in that, it comprises that component and weight percent thereof are: monomer 10~35%, UV elastic resin 52.5~68%, light trigger 7%, powder filler 5~14.5%, anti-settling agent 0.1~0.3%.
4. UV roller coat elasticity bottom-coating for wooden skin as claimed in claim 1, it is characterized in that: described UV elastic resin is to do polyvalent alcohol by PTMG, and isocyanic ester is selected TDI or IPDI, chainextender selects the synthetic elongation at break such as BDO at 300% 2 functional polyurethanes acrylic resins.
5. UV roller coat elasticity bottom-coating for wooden skin as claimed in claim 1, is characterized in that: described light trigger is the mixture of 2-hydroxy-2-methyl-1-phenyl-1-acetone and benzophenone and reactive amines.
6. UV roller coat elasticity bottom-coating for wooden skin as claimed in claim 1, is characterized in that: described anti-settling agent is the hydrophilic fumed silica of median size 12 nanometers.
7. UV roller coat elasticity bottom-coating for wooden skin as claimed in claim 2, is characterized in that: described auxiliary agent is at least one of dispersion agent, flow agent or defoamer; Described dispersant structure is the high molecular wetting dispersing agent of the polycarboxylic acid salts solution of polyamine acid amides, described flow agent Wei Han propenyl functional group's dimethyl polysiloxane and fluorine-carbon modified polyacrylic ester, described defoamer is not for containing organosilyl polymer-type defoamer.
8. a preparation method for UV roller coat elasticity bottom-coating for wooden skin, its step is sequentially as follows:
(1) take by weight percentage each component: monomer 10~35%, UV elastic resin 42~70%, light trigger 5~8%, filling powder 5~15%, auxiliary agent 0.4~0.5%, anti-settling agent 0.1-0.3%;
(2), by described monomer and UV elastic resin, drop into and disperse, in cylinder, to use high speed dispersor high speed dispersion 10~15 minutes;
(3) drop into successively each composition in described auxiliary agent, with high speed dispersor, disperse 10~15 minutes;
(4) drop into described filling powder, with high speed dispersor, disperse 10~15 minutes;
(5) drop into described anti-settling agent, with high speed dispersor, disperse 10~15 minutes;
(6) drop into described light trigger, with high speed dispersor, disperse high speed dispersion 10~15 minutes, 100 order filter-cloth filterings, make UV roller coat elasticity bottom-coating for described wooden skin.
9. the preparation method of UV roller coat elasticity bottom-coating for wooden skin as claimed in claim 8, is characterized in that: the rotating speed of the high speed dispersor of described step (2) and step (3) is 1200~1500 revs/min; The rotating speed of the high speed dispersor of described step (4), step (5) and step (6) is 1000~1200 revs/min.
10. the implementing process of UV roller coat elasticity bottom-coating for wooden skin as described in claim 1 to 9 any one, its step is sequentially as follows:
1) by the 180 order sand paper sandings for skin of collet non-woven fabrics wood, dedusting;
2) sponge roller coat water-based bottom coloring, hairbrush swabbing, ultra red ray drying;
3) the UV bouncing putty of UV roller coat elasticity bottom-coating for roller coat wood skin, glue spread 20-25g/ ㎡, UV energy is controlled at 300mJ/ cm 2, UV solidifies;
4) the UV elastic primer of UV roller coat elasticity bottom-coating for roller coat wood skin, glue spread 20-25g/ ㎡, UV energy is controlled at 300mJ/ cm 2, UV solidifies;
5) by step 4) repeat to implement 2-3 time;
6) roller coat wood skin can sanding priming paint by the UV elasticity of UV roller coat elasticity bottom-coating, glue spread 20-30g/ ㎡, and UV energy is controlled at 300mJ/ cm 2, UV solidifies, and 400 order sand paper sandings are standby;
7) direct roller coat UV elasticity finish paint or spray PU finish paint after cladding process.
CN201410269690.0A 2014-06-17 2014-06-17 A kind of veneer UV roller coat elasticity bottom-coating and preparation method thereof and implementing process Active CN104004395B (en)