CN103881237A - 一种抗老化聚丙烯塑料 - Google Patents

一种抗老化聚丙烯塑料 Download PDF

Info

Publication number
CN103881237A
CN103881237A CN201410101026.5A CN201410101026A CN103881237A CN 103881237 A CN103881237 A CN 103881237A CN 201410101026 A CN201410101026 A CN 201410101026A CN 103881237 A CN103881237 A CN 103881237A
Authority
CN
China
Prior art keywords
parts
aging
polypropylene
nano titanium
polypropylene plastic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410101026.5A
Other languages
English (en)
Inventor
叶春会
王泽平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Jia Mu Rubber Industry Co Ltd
Original Assignee
Anhui Jia Mu Rubber Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jia Mu Rubber Industry Co Ltd filed Critical Anhui Jia Mu Rubber Industry Co Ltd
Priority to CN201410101026.5A priority Critical patent/CN103881237A/zh
Publication of CN103881237A publication Critical patent/CN103881237A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种抗老化聚丙烯塑料，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂10100.4-0.6份、光稳定剂0.1-0.3份、紫外线吸收剂0.2-0.3份、炭黑36-40份、纳米二氧化钛2-4份、环氧树脂12-16份、三聚氰胺15-20份、分散剂0.2-0.6份、偶联剂0.5-0.8份。本发明抗老化聚丙烯塑料添加纳米二氧化钛，纳米二氧化钛在聚丙烯塑料中分散性好；本发明抗老化聚丙烯塑料添加三聚氰胺，使得本发明制备得到的聚丙烯塑料具有阻燃性能，满足户外使用要求；本发明制备得到的聚丙烯塑料具有良好的抗冲击性能、抗老化性能、增韧性也得到提高。

Description

一种抗老化聚丙烯塑料
技术领域
    本发明属于塑料技术领域，具体是一种抗老化聚丙烯膜。
背景技术
聚丙烯塑料作为五大通用塑料之一，与其它塑料相比具有来源丰富、质轻、价廉、加工性能好等优点，因此广泛用于汽车、家电、机械和建筑等行业，但户外聚丙烯制品暴露在空气中容易变色、粉化、表面龟裂、丧失光泽以及力学性能下降，因此，作为结构材料和工程塑料使用将会受到很大限制。
发明内容
本发明的目的在于提供一种抗老化聚丙烯塑料。
本发明的目的可以通过以下技术方案实现：
一种抗老化聚丙烯塑料，其特征在于，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.4-0.6份、光稳定剂0.1-0.3份、紫外线吸收剂0.2-0.3份、炭黑36-40份、纳米二氧化钛2-4份、环氧树脂12-16份、三聚氰胺15-20份、分散剂0.2-0.6份、偶联剂0.5-0.8份。
作为优选，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.5份、光稳定剂0.2份、紫外线吸收剂0.25份、炭黑38份、纳米二氧化钛3份、环氧树脂14份、三聚氰胺18份、分散剂0.4份、偶联剂0.7份。
作为优选，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.4份、光稳定剂0.1份、紫外线吸收剂0.2份、炭黑37份、纳米二氧化钛2.5份、环氧树脂13份、三聚氰胺16份、分散剂0.3份、偶联剂0.6份。
本发明的有益效果：本发明抗老化聚丙烯塑料添加纳米二氧化钛，纳米二氧化钛在聚丙烯塑料中分散性好；本发明抗老化聚丙烯塑料添加三聚氰胺，使得本发明制备得到的聚丙烯塑料具有阻燃性能，满足户外使用要求；本发明制备得到的聚丙烯塑料具有良好的抗冲击性能、抗老化性能、增韧性也得到提高。
具体实施方式
下面结合具体实施例对本发明作进一步详细描述。
实施例1
一种抗老化聚丙烯塑料，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.5份、光稳定剂0.2份、紫外线吸收剂0.25份、炭黑38份、纳米二氧化钛3份、环氧树脂14份、三聚氰胺18份、分散剂0.4份、偶联剂0.7份。制备方法为：将所述原料混合放入超高速混合机中混合均匀，将混配物经双螺杆混炼设备熔融挤出造粒，再经注塑成型机注塑成型。
实施例2
一种抗老化聚丙烯塑料，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.4份、光稳定剂0.1份、紫外线吸收剂0.2份、炭黑37份、纳米二氧化钛2.5份、环氧树脂13份、三聚氰胺16份、分散剂0.3份、偶联剂0.6份。制备方法为：将所述原料混合放入超高速混合机中混合均匀，将混配物经双螺杆混炼设备熔融挤出造粒，再经注塑成型机注塑成型。
实施例3
一种抗老化聚丙烯塑料，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.6份、光稳定剂0.3份、紫外线吸收剂0.3份、炭黑40份、纳米二氧化钛4份、环氧树脂16份、三聚氰胺20份、分散剂0.6份、偶联剂0.8份。制备方法为：将所述原料混合放入超高速混合机中混合均匀，将混配物经双螺杆混炼设备熔融挤出造粒，再经注塑成型机注塑成型。

Claims (3)

1.一种抗老化聚丙烯塑料，其特征在于，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.4-0.6份、光稳定剂0.1-0.3份、紫外线吸收剂0.2-0.3份、炭黑36-40份、纳米二氧化钛2-4份、环氧树脂12-16份、三聚氰胺15-20份、分散剂0.2-0.6份、偶联剂0.5-0.8份。
2.根据权利要求1所述的抗老化聚丙烯塑料，其特征在于，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.5份、光稳定剂0.2份、紫外线吸收剂0.25份、炭黑38份、纳米二氧化钛3份、环氧树脂14份、三聚氰胺18份、分散剂0.4份、偶联剂0.7份。
3. 根据权利要求1所述的抗老化聚丙烯塑料，其特征在于，所述抗老化聚丙烯塑料由以下重量份的原料组分组成：聚丙烯100份、抗氧剂1010 0.4份、光稳定剂0.1份、紫外线吸收剂0.2份、炭黑37份、纳米二氧化钛2.5份、环氧树脂13份、三聚氰胺16份、分散剂0.3份、偶联剂0.6份。
 
CN201410101026.5A 2014-03-19 2014-03-19 一种抗老化聚丙烯塑料 Pending CN103881237A (zh)